Electrospun Fibrous Scaffolds of Poly(glycerol-dodecanedioate) for Engineering Neural Tissues From Mouse Embryonic Stem Cells

Podsumowanie

Synthesis and fabrication of electrospun long fibers spanning a larger deposit area via a newly designed collector from a novel biodegradable polymer named poly(glycerol-dodecanoate) (PGD) was reported. The fibers were able to support the growth of cells derived from mouse pluripotent stem cells.

Streszczenie

For tissue engineering applications, the preparation of biodegradable and biocompatible scaffolds is the most desirable but challenging task.  Among the various fabrication methods, electrospinning is the most attractive one due to its simplicity and versatility. Additionally, electrospun nanofibers mimic the size of natural extracellular matrix ensuring additional support for cell survival and growth. This study showed the viability of the fabrication of long fibers spanning a larger deposit area for a novel biodegradable and biocompatible polymer named poly(glycerol-dodecanoate) (PGD)¹ by using a newly designed collector for electrospinning. PGD exhibits unique elastic properties with similar mechanical properties to nerve tissues, thus it is suitable for neural tissue engineering applications. The synthesis and fabrication set-up for making fibrous scaffolding materials was simple, highly reproducible, and inexpensive. In biocompatibility testing, cells derived from mouse embryonic stem cells could adhere to and grow on the electrospun PGD fibers. In summary, this protocol provided a versatile fabrication method for making PGD electrospun fibers to support the growth of mouse embryonic stem cell derived neural lineage cells.

Wprowadzenie

Electrospinning is one of the effective processing methods to produce micro-to-nanometer size fiber scaffolds. The basic principle of electrospinning involves a Taylor cone of solution that is held at the orifice of a needle by applying high voltage between the tip of the needle and a grounded collector. When the electrostatic repulsion in the solution overcomes the surface tension, a charged fluid jet is ejected out of the needle tip, travels through the air with solvent evaporation, and is finally deposited on the grounded collector. The syringe pump provides a continuous flow of solution emerging from the spinneret and thus multiple copies of the electrospun fibers can be fabricated within a short period of time. During the course of leaving the spinneret to arrive at the collector, the charged jet will undergo stretching and whipping according to a number of parameters that include the viscosity and surface tension of the polymeric solution, the electrostatic force in the solution, and the interaction of the external electric field, etc².

In the electrospinning process, a collector serves as a conductive substrate where the micro-to-nanometer fibers could be deposited. In this study, a new type of fiber collector was designed to obtain fiber mats with the desired size (length x width). Traditionally, aluminum foil is used as a collector but it is difficult to transfer the fibers from the flat surface to another substrate. The difficulty of harvesting an intact fiber mat from a traditional collector was mainly due to the fact that the electrospun fibers attach strongly to the collector's surface. Therefore, we modified the collector by folding a piece of aluminum foil into a rectangular strip and attaching it perpendicular to a flat metal plate. The electrospun fibers are stretched across the area between the tip of the strip and the metal plate, which can be easily transferred to another substrate.

Interest in thermally crosslinked elastomeric polymers is rapidly growing because of the pioneering work of Robert Langer's group, who introduced poly(glycerol sebacate) (PGS), a polyester which is analogous to vulcanized rubber in 2002 ³. Similar to PGS, we have successfully developed poly(glycerol-dodecanoate) (PGD) by thermal condensation of glycerol and dodecanedioic acid and demonstrated its unique shape memory property¹. Unlike stiffer synthetic materials poly(hydroxyl butyrate) or poly(L-lactide) (Young's moduli of 250 MPa and 660 MPa, respectively), PGD exhibits elastomeric property like rubber, with a Young's modulus of 1.08 MPa when the temperature is above 37 °C, which is a close match to the in-situ peripheral nerve (0.45 MPa). In addition, PGD is biodegradable and the degradation time can be fine-tuned by varying the ratio of glycerol and dodecanedioic acid. Dodecanedioic acid is a twelve-carbon substance with two terminal carboxylic groups, HOOC(CH₂)₁₀COOH. Even numbered dicarboxylic acids like sebacic acid and dodecanedioic acid can be metabolized to acetyl-CoA and enter the tricarboxylic acid (TCA)/(citric acid) cycle. The metabolic product of dicarboxylic acids, succinyl-CoA, is a gluconeogenetic precursor and intermediate of TCA cycle⁴. Thus, some studies suggested that they could be utilized as an alternative fuel substrate for enteral and parenteral nutrition, especially in the pathological conditions. In addition, PGD exhibits unique shape memory because its glass transition temperature is 31 °C, thus it shows distinct mechanical properties at room temperature and at body temperature. In sum, PGD is biodegradable, biocompatible, exhibiting unique elastic properties with mechanical properties similar to nerve tissues; therefore, it is a suitable material for nerve tissue engineering applications. In this protocol, the electrospun long fibers spanning a large deposit area were fabricated via the newly-designed collector from PGD. The fiber scaffolds can support the mouse pluripotent stem cells growth and differentiation.

Protokół

1. Electrospinning Collector Setup

1. Cut the aluminum foil into a rectangular piece.
2. Fold the rectangular piece into a rectangular strip, and attach it perpendicular to a flat metal plate with tape (Figure 1). Note: The size of the fiber mat depends on the length and width of the strip. Thus, the strip dimensions can be adjusted as needed.

2. Polymeric Solution Preparation

1. Mix glycerol and dodecanedioic acid (DDA) in 1:1 molar ratio in a beaker at 120 °C for 100 hr to obtain PGD polymer.
2. Dissolve poly(ethylene oxide) (PEO) and gelatin in 65% ethanol with a weight ratio of 1.5:3:95.5 in a 15 ml tube, tighten the cap and heat the mixture in an oven at 60 °C for 1 hr with stirring until it becomes a homogeneous solution (Basal solution).
3. For electrospinning, mix the PGD polymer and the basal solution in 4:6 weight ratio. Note: PGD concentration has a big effect on fiber diameter. 30%-50% percent PGD is acceptable to produce fibers longer than 5 cm with increased fiber diameters.
4. Add 0.1% riboflavin to the polymeric solution and mix well.

3. Electrospinning

1. Feed the polymeric solution into a 5 ml standard syringe with an 18 G blunted stainless steel needle.
2. Insert the syringe into a syringe pump.
3. Attach the grounded lead of a high voltage power source to the metal plate and the positively charged lead to the needle.
4. Adjust the distance between the needle and the aluminum foil strip to 15 cm.
5. Place the syringe pump in an angle of about 15° with the horizontal to prevent aggregation of the fibers at the front of the strip.
6. Turn on the syringe pump and adjust the flow rate of the pump to 0.6 ml/hr.
7. Turn on the high voltage power source and set the operating voltage to 14.6 kV.

4. Fiber Processing

1. After the collection is complete, expose the fiber mat to UV light for 60 min for cross-linking.
2. Transfer the fiber mat from the aluminum foil strip to a 100 mm Petri dish, and expose it to UV light for another 20 min for sterilization.
3. In a biosafety cabinet, cut the fiber mat into round pieces of the same size with a surgical blade and place the pieces into a 24-well plate.
4. For cell pre-seeding treatment, immerse fiber samples in 1 ml of phosphate buffered saline (PBS) and incubate at 37 °C overnight.
5. On the following day, aspirate PBS carefully, add 1 ml of differentiation medium (DMEM/F12, N2, and FGF2) (see recipe in Materials table) to each well and incubate at 37 °C for 3 hr.
6. Aspirate differentiation medium carefully, add 0.2 ml of matrigel to each fiber sample and incubate at 37 °C for 30 min. Note: Laminin can also be used for fiber coating. Add 0.2 ml of 20 µg/ml laminin to the fiber and incubate at room temperature for 3 hr.
7. Carefully remove excess matrigel from each well. Rinse with 2 ml of differentiation medium once. Note: The fiber samples are ready for cell culture.

5. Cell Seeding on Fibers

1. Add 1 ml of Accutase to the mES cell culture dish and incubate for 10 min at 37 °C.
2. After 10 min, the mES cells are detached from the culture dish. Add 4 ml of differentiation medium to the plate. Collect the floating mES cells into a 15 ml tube and pipette cells up and down to break colonies (about 15x).
3. Centrifuge at 400 x g for 5 min and re-suspend cells in 4 ml of differentiation medium.
4. Count the cells using a hemocytometer. Transfer 200 µl of the cell suspension into a 15 ml tube and dilute it 10x with differentiation medium. Transfer 15 µl of the diluted cell suspension to a chamber on the hemocytometer with a cover-slip in place. Count the cells in the 1 mm center square and the four corner squares of the hemocytometer under the microscope. Note: Cell per ml = the average count per square x the dilution factor x 10⁴
5. Place approximately 5 x 10⁴ mES cells onto each well. Slowly drop the cell suspension onto the middle of the fiber samples, instead of sliding off to the side of the well, to prevent the solution from draining off the fiber mat.
6. Add 1 ml of differentiation medium to each well, and keep the plate in an incubator at 37 °C and 5% CO₂ to allow cells attachment, growth and differentiation.
7. Aspirate the old medium from each well and replace with 1 ml of fresh differentiation medium every other day.

6. Cell Viability

1. Aspirate the old medium from each well.
2. Mix 1/10^th volume of Resazurin fluorescence reagent with culture medium and add 1 ml to each well.
3. Incubate at 37 °C and 5% CO₂ for 4 hr, protected from direct light.
4. After 4 hr, transfer 100 µl 3x of the reagent from each well to a 96-well plate, and then the samples are ready to be measured on a fluorescence spectrophotometer using 560EX nm/590EM filter settings.

7. Real Time PCR

1. After 14 days of culture, add lysis buffer to the samples and isolate total RNA from the cells on the fiber samples.
2. Use 4 µl of total RNA to synthesize cDNA in 20 µl reaction scales by reverse transcription.
3. Prepare the PCR reaction mixture in each optical tube: 10 µl Master Mix (2x), 0.2 µl dye, 8 µl Nuclease-Free water, 1 µl cDNA, and 1 µl primer (Primers used in this study are listed in Table 1).
4. Set up the PCR program: a. 95 °C 2:20 min, 1 cycle b. 95 °C 3 sec→60° C 1 min, 40 cycle c. 95° C 15 sec, 1 cycle d. 60° C 1 min, 1 cycle e. 95° C 15 sec, 1 cycle. Choose comparative C_T method to determine relative gene expression levels.
5. After PCR is finished, analyze the real-time PCR results with StepOne software and export the results to Excel.

Wyniki

The major components of the electrospinning are shown in Figure 1. A large size fiber mat was typically obtained through the perpendicularly attached aluminum foil strip and a flat metal plate. Figure 2 shows the collector design and the electrospinning fiber mat. The width and length can be adjusted for different applications. The length of the fiber made with PGD polymer and basal solution mixture is up to 10 cm. The morphology of electrospun fibers is shown in Figure 3

Dyskusje

The limitations of simple collectors or the complexities of rotating collectors that are currently used for electrospinning increase the restriction of obtaining the desired length and size of fiber mat for some applications. Additionally, transferring fibers from the ground collector to the culture dish or other substrates is a challenge⁵. In this report, a newly designed collector, made simply by attaching an aluminum foil strip to the grounded collector, was able to obtain large size fiber mats up to 10 cm ...

Materiały

Name	Company	Catalog Number	Comments
Glycerol	Sigma-Aldrich	G7757
Dodecanedioic acid	Sigma-Aldrich	D1009
Gelatin	Sigma-Aldrich	D1890
Poly(ethylene oxide) (PEO)	Sigma-Aldrich	182028
Riboflavin	Sigma-Aldrich	132350250	0.10%
Mouse embryonic stem cells	GlobalStem	GSC-5002
Matrigel	Becton Dickinson	356234
DMEM/F12	Thermo Scientific	SH30272.02
N2 supplement	Invitrogen	17502048	1%
FGF2	Stemgent	03-0002	10 ng/ml
Accutase	Invitrogen	A11105-01
Phosphate buffered saline (PBS)	Invitrogen	10010-031
Resazurin fluorescence dye	Sigma-Aldrich	62758-13-8
SV Total RNA Isolation System	Promega	Z3100
GoScript Reverse Transcription System	Promega	A5000
GoTaq qPCR Master Mix	Promega	A6001
Syringe pump	Fisher scientific	14-831-200
High voltage power source	Spellman High Voltage Electronics Corporation		SL30
UV light	Philips	308643	15W/G15T8
Synergy HT Multi-Mode Microplate Reader	BioTek
Perkin Elmer GeneAmp PCR System 9600	Perkin Elmer	8488
StepOne Real-time PCR System	Applied Biosystems	4376357