This work was supported partially from startup funds from University of Nebraska Medical Center and National Institute of Health (grant number 1R15 AR063901-01).

1. Preparation of the Solution
<ol>
	<li>Prepare a solution of Poly (&#949;-caprolactone) (PCL) (Mw= 80,000 g/mol) at an approximate concentration of 100 mg/ml. Dissolve PCL in a mixture of dichloromethane (DCM) and N, N-dimethlyformamide (DMF) at a ratio of 4:1 (v/v) with a concentration of 10% (w/v).</li>
	<li>Place the solution in a 20 ml glass tube for mixing. Place glass tube into ultrasonic cleaner for 30 minutes, or until solution is translucent.</li>
</ol>
2. Apparatus Preparation
<ol>
	<li>Add the prepared PCL solution into a 5 ml syringe with a 21 gauge blunt needle attached.</li>
	<li>Place syringe pump in a vertical electrospinning position, according to Figure 1.</li>
	<li>Use a stainless steel-gap collector with an open space of 2 cm x 5 cm for the aligned fiber substrate. Place the collector 12 cm from the needle tip.</li>
	<li>Connect the Direct Current (DC) High Voltage power supply to the needle and ground the collector. Ensure that the collector is individually grounded with no contact to the other lab equipment.</li>
</ol>
3. Electrospinning
<ol>
	<li>Set syringe pump to 1.50 ml/hr, until the droplets forming at the needle tip are immediately replaced when removed. Then, set the flow rate to 0.50 ml/hr.</li>
	<li>Turn the voltage operator to 12 kV.</li>
	<li>Electrospin until the uniaxially aligned fibers completely cover the gap on the collector.</li>
	<li>Apply glue to the edges of a small glass plate and transfer the fibers from the gap collector to the glass plate. Place the glass plate on the top of a piece of aluminum foil that has the same size as the glass plate and is grounded.</li>
	<li>Position the second syringe collector according to Figure 3.</li>
	<li>Attach the plastic mask to the second syringe pump and position it 2 mm above the collector.</li>
	<li>Add Coumarin 6 at 1% (w/w) to the PCL solution&#8212;if nanoencapsulation is desired&#8212; and mix until the solution is translucent.</li>
	<li>Load the PCL or PCL/Coumarin 6 solution into a 5 ml needle with a blunt 21 gauge needle. Set vertical pump to 0.50 ml/hr and horizontal to pull at 9 ml/hr or at an approximate speed of 1 mm/min.</li>
	<li>Electrospin until the mask has moved almost completely off the collector, but with the edge area still under the mask.</li>
</ol>
4. Fiber Characterization
<ol>
	<li>Place samples with double-sided conductive tape to the metallic stud and coat with platinum for 40 sec using a sputter coater at 40 mA.
	<ol>
		<li>Examine fibers through scanning electron microscope (SEM) according to our previous studies17,18.</li>
		<li>Collect images at an accelerating voltage of 15 kV.</li>
	</ol>
	</li>
	<li>Perform fast Fourier transform (FFT) analysis on a separate fiber sample to measure fiber alignment. The detailed information on measuring fiber alignment by FFT can refer to previous studies19,20.</li>
</ol>
5. Seeding Stem Cells.
<ol>
	<li>Sterilize the fiber samples by soaking in a 70% ethanol solution for 2 hr. Then wash the fibers with distilled water to remove any contaminants.</li>
	<li>Obtain human ADSCs and culture cells in a 25 cm2 flask at 37 &#176;C in an atmosphere of 95% air/5% CO2. Change the cell culture medium every other day10.</li>
	<li>Trypsinize the cells and count the number of cells. Specifically, remove all culture medium from the cell culture flask and wash the cells with phosphate buffered saline (PBS) twice. Then add 1 ml of a 0.25% trypsin-EDTA solution (pre-warm in water bath to 37 &#176;C) to cover the cell monolayer and incubate the flask in the cell culture incubator for 2-3 minutes. Add 4 ml culture medium and wash out all the cells from the surface by pipetting the medium all over the surface. Centrifuge the cell suspension and re-disperse the cell pellet in the culture medium. Count cells via hemacytometer. Seed around 1 &#215; 104 cells to the nanofiber scaffold placed in a 35 mm -culture dish and incubate for 3 and 7 days.</li>
	<li>Stain cells using fluorescein diacetate (5 mg/ml in acetone) (FDA) then image the samples using a fluorescent microscope. Specifically, add 100 &#956;l of FDA solution to the culture dish and incubate for 30 min. Wash cells with PBS three times before fluorescent imaging. Analyze cell orientation by a customized mat-lab program based on our previous studies10.</li>
</ol>

<ol>
	<li>Xie, J., Li, X., Xia, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Putting+electrospun+nanofibers+to+work+for+biomedical+research.">Putting electrospun nanofibers to work for biomedical research.</a> Macromol. Rapid Commun. 29 (22), 1775-1792 (2008).</li><li>Genin, G. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Functional+grading+of+mineral+and+collagen+in+the+attachment+of+tendon+to+bone.">Functional grading of mineral and collagen in the attachment of tendon to bone.</a> Biophys. J. 97 (4), 976-985 (2009).</li><li>Thomopoulos, S., Marquez, J. P., Weinberger, B., Birman, V., Genin, G. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Collagen+fiber+orientation+at+the+tendon+to+bone+insertion+and+its+influence+on+stress+concentrations.">Collagen fiber orientation at the tendon to bone insertion and its influence on stress concentrations.</a> J. Biomech. 39 (10), 1842-1851 (2006).</li><li>Thomopoulos, S., Williams, G. R., Gimbel, J. A., Favata, M., Soslowsky, L. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Variation+of+biomechanical,+structural,+and+compositional+properties+along+the+tendon+to+bone+insertion+site.">Variation of biomechanical, structural, and compositional properties along the tendon to bone insertion site.</a> J. Orthop. Res. 21 (3), 413-419 (2003).</li><li>Thomopoulos, S., Genin, G. M., Galatz, L. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+development+and+morphogenesis+of+the+tendon-to-bone+insertion+-+What+development+can+teach+us+about+healing.">The development and morphogenesis of the tendon-to-bone insertion - What development can teach us about healing.</a> Musculoskelet Neuronal Interact. 10 (1), 35-45 (2010).</li><li>Li, X., Xie, J., Lipner, J., Yuan, X., Thomopoulos, S., Xia, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanofiber+scaffolds+with+gradations+in+mineral+content+for+mimicking+the+tendon-to-bone+insertion+site.">Nanofiber scaffolds with gradations in mineral content for mimicking the tendon-to-bone insertion site.</a> Nano Lett. 9 (7), 2763-2768 (2009).</li><li>Kunzler, T. P., Huwiler, C., Drobek, T., V&#246;r&#246;s, J., Spencer, N. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Systematic+study+of+osteoblast+response+to+nanotopography+by+means+of+nanoparticle-density+gradients.">Systematic study of osteoblast response to nanotopography by means of nanoparticle-density gradients.</a> Biomaterials. 28 (33), 5000-5006 (2007).</li><li>Huwiler, C., Kunzler, T. P., Textor, M., V&#246;r&#246;s, J., Spencer, N. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Functionalizable+nanomorphology+gradients+via+colloidal+self-assembly.">Functionalizable nanomorphology gradients via colloidal self-assembly.</a> Langmuir. 23 (11), 5929-5935 (2007).</li><li>Xie, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term='Aligned-to-random'+nanofiber+scaffolds+for+mimicking+the+structure+of+the+tendon-to-bone+insertion+site.">'Aligned-to-random' nanofiber scaffolds for mimicking the structure of the tendon-to-bone insertion site.</a> Nanoscale. 2 (6), 923-926 (2010).</li><li>Xie, J., Ma, B., Michael, P. L., Shuler, F. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fabrication+of+nanofiber+scaffolds+with+gradations+in+fiber+organization+and+their+potential+applications.">Fabrication of nanofiber scaffolds with gradations in fiber organization and their potential applications.</a> Macromol. Biosci. 12 (10), 1336-1341 (2012).</li><li>James, R., Kumbar, S. G., Laurencin, C. T., Balian, G., Chhabra, A. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Tendon+tissue+engineering:+adipose-derived+stem+cell+and+GDF-5+mediated+regeneration+using+electrospun+matrix+systems.">Tendon tissue engineering: adipose-derived stem cell and GDF-5 mediated regeneration using electrospun matrix systems.</a> Biomed. Mater. 6 (2), 025011 (2011).</li><li>Bodle, J. C., Hanson, A. D., Loboa, E. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Adipose-derived+stem+cells+in+functional+bone+tissue+engineering:+lessons+from+bone+mechanobiology.">Adipose-derived stem cells in functional bone tissue engineering: lessons from bone mechanobiology.</a> Tissue Eng. Part B Rev. 17 (3), 195-211 (2011).</li><li>Lee, J. H., Rhie, J. W., Oh, D. Y., Ahn, S. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Osteogenic+differentiation+of+human+adipose+tissue-derived+stromal+cells+(hASCs)+in+a+porous+three-dimensional+scaffold.">Osteogenic differentiation of human adipose tissue-derived stromal cells (hASCs) in a porous three-dimensional scaffold.</a> Biochem. Biophys. Res. Commun. 370 (3), 456-460 (2008).</li><li>Tapp, H., Hanley, E. N., Patt, J. C., Gruber, H. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Adipose-derived+stem+cells:+characterization+and+current+application+in+orthopaedic+tissue+repair.">Adipose-derived stem cells: characterization and current application in orthopaedic tissue repair.</a> Exp. Biol. Med. 234 (1), 1-9 (2009).</li><li>Gimble, J. M., Guilak, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Adipose-derived+adult+stem+cells:+isolation,+characterization,+and+differentiation+potential.">Adipose-derived adult stem cells: isolation, characterization, and differentiation potential.</a> Cytotherapy. 5 (5), 362-369 (2003).</li><li>Zuk, P. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Multilineage+cells+from+human+adipose+tissue:+implications+for+cell-based+therapies.">Multilineage cells from human adipose tissue: implications for cell-based therapies.</a> Tissue Eng. 7 (2), 211-228 (2001).</li><li>Xie, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+differentiation+of+embryonic+stem+cells+seeded+on+electrospun+nanofibers+into+neural+lineages.">The differentiation of embryonic stem cells seeded on electrospun nanofibers into neural lineages.</a> Biomaterials. 30 (3), 354-362 (2009).</li><li>Xie, J., MacEwan, M. R., Li, X., Sakiyama-Elbert, S. E., Xia, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Neurite+outgrowth+on+nanofiber+scaffolds+with+different+orders,+structures,+and+surface+properties.">Neurite outgrowth on nanofiber scaffolds with different orders, structures, and surface properties.</a> ACS Nano. 3 (5), 1151-1159 (2009).</li><li>Ayres, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Modulation+of+anisotropy+in+electrospun+tissue+engineering+scaffolds:+analysis+of+fiber+alignment+by+the+fast+Fourier+transform.">Modulation of anisotropy in electrospun tissue engineering scaffolds: analysis of fiber alignment by the fast Fourier transform.</a> Biomaterials. 27 (32), 5524-5534 (2006).</li><li>Ayres, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Measuring+fiber+alignment+in+electrospun+scaffolds:+a+user&#8217;s+guide+to+the+2D+fast+Fourier+transform+approach.">Measuring fiber alignment in electrospun scaffolds: a user&#8217;s guide to the 2D fast Fourier transform approach.</a> J. Biomater. Sci. Poly. Ed. 19 (5), 603-621 (2008).</li></ol>

The authors have nothing to disclose.

The most critical part of the protocol is generation of the gradient scaffold. It is imperative that the mask covering the collector moves at a constant velocity so there is a gradual change within the fiber scaffold. The correct preparation of PCL solution is also important to ensure electrospinning success. Checking the fiber morphology prior to electrospinning is recommendable, especially after the encapsulation of Coumarin-6, which may require a higher voltage to electrospin correctly. 
Fu...

Nanofibers are a popular utility for tissue engineering because of their ability to mimic the extracellular matrix in its structure and relative size1. However, some native tissue interfaces, such as the tendon-to-bone insertion site, contain collagen fibers, which exhibit a variable organizational structure that increases in alignment towards the tendon and decreases at the bone site2-5. So, for effective tissue regeneration there is a need to fabricate a scaffold that could effectively mimic this structural gradient.
Previously, there has been research conducted on gradual changes in fiber composition, specifically, mineral content6. However, recreating the structural component of connective tissues remains largely unexplored. An earlier study examined morphological gradients by studying the effect of surface silica particle density on the proliferation of rat calvarial osteoblasts and found an inverse relationship between silica particle density and cell proliferation7. But the morphological changes that mediated cell proliferation in previous work were mostly related to surface roughness lacking the capability in mimicking fiber organizational changes7,8. One recent study attempted to fabricate a scaffold that mimicked the unique collagen fiber orientations by using a novel collector for electrospinning9. While this study succeeded in producing a scaffold with both aligned and random fibers, it failed to mimic the gradual changes exhibited in the native tissues. Also, in producing separate components, with an immediate change from aligned to random orientation, the biomechanical properties of this scaffold decreased significantly. No previous work has been able to produce applicable nanofiber scaffolds with continuous gradations in fiber orientations from aligned and random. Our recent study has shown successful recreation of nanofiber scaffolds with gradations in fiber organization that can potentially mimic the native collagen organization at tendon-to-bone insertion10. This work aims to present the protocols used for the production of nanofiber scaffolds with a structure that closely resembles that of fiber organization in the native tendon-to-bone tissue interface.
Gradient nanofiber structures have potentially far-reaching applications across a variety of fields. We focused on the applications to tissue engineering of the tendon-to-bone insertion site by combining our scaffolds with adipose-derived stem cells (ADSCs) which are already utilized for tissue regeneration on various substrates11-14. In addition, ADSCs are very similar in nature to bone marrow stem cells in terms of multipotency and their resource is abundant which can be harvested using a simple liposuction procedure15,16. Seeding these cells to gradated nanofiber scaffolds further enhances their tissue engineering applications by allowing for the controlled distribution of the cells that can potentially differentiate into various tissues. In addition to seeding stem cells, nanofibers can be encapsulated with signaling molecules for regulation of cellular response. Coupling nanoencapsulation with the organizational gradient of these scaffolds allows for the study of cellular behavior or possible implant designs and coatings. Encapsulation of functional molecules like bone morphogenetic protein 2 (BMP2), which has been shown to induce osteoblast differentiation15,16, could further enhance the tissue engineering applications of these scaffolds10.

<table border="0" cellpadding="0" cellspacing="0">
	<tbody>
		<tr>
			<td>Polycaprolactone</td>
			<td>Sigma-Aldrich</td>
			<td>440744</td>
			<td></td>
		</tr>
		<tr>
			<td>N,N-Dimethlyformamide</td>
			<td>Fisher Chemical</td>
			<td>D-119-1</td>
			<td></td>
		</tr>
		<tr>
			<td>Dichloromethane</td>
			<td>Fisher Chemical</td>
			<td>AC61093-1000</td>
			<td></td>
		</tr>
		<tr>
			<td>Coumarin 6</td>
			<td>Sigma-Aldrich</td>
			<td>546283</td>
			<td></td>
		</tr>
		<tr>
			<td>Adipose Derived Stem Cells</td>
			<td>Cellular engineering Technologies</td>
			<td>HMSC.AD-100</td>
			<td></td>
		</tr>
		<tr>
			<td>Fetal Bovine Serum</td>
			<td>Life Technologies</td>
			<td>26140-111</td>
			<td></td>
		</tr>
		<tr>
			<td>Fluorescein Diacetate</td>
			<td>Sigma-Aldrich</td>
			<td>F7378</td>
			<td></td>
		</tr>
		<tr>
			<td>Ethanol</td>
			<td>Sigma-Aldrich</td>
			<td>E7023</td>
			<td></td>
		</tr>
		<tr>
			<td>Trypsin-EDTA</td>
			<td>Invitrogen</td>
			<td>25300-054</td>
			<td></td>
		</tr>
		<tr>
			<td>&#945;-Modified Eagle&#39;s Medium</td>
			<td>Invitrogen</td>
			<td>a10490-01</td>
			<td></td>
		</tr>
		<tr>
			<td>Acetone</td>
			<td>Fisher Scientific</td>
			<td>s25120a</td>
			<td></td>
		</tr>
		<tr>
			<td>Phosphate Buffered Saline</td>
			<td>Invitrogen</td>
			<td>10010023</td>
			<td></td>
		</tr>
		<tr>
			<td>Glass Slides</td>
			<td>VWR international, LLC</td>
			<td>101412-842</td>
			<td></td>
		</tr>
		<tr>
			<td>Syringe Pump</td>
			<td>Fisher Scientific</td>
			<td>14-831-200</td>
			<td>Single syringe</td>
		</tr>
		<tr>
			<td>Ultrasonic Cleaner</td>
			<td>Branson</td>
			<td>1510</td>
			<td></td>
		</tr>
		<tr>
			<td>High Voltage DC Power Supply</td>
			<td>Gamma High Voltage Research</td>
			<td>ES30</td>
			<td></td>
		</tr>
		<tr>
			<td>Scanning Electron Microscope</td>
			<td>FEI</td>
			<td>Nova 2300</td>
			<td></td>
		</tr>
		<tr>
			<td>Fluorescence Microscope</td>
			<td>Zeiss</td>
			<td>Axio Imager 2</td>
			<td></td>
		</tr>
	</tbody>
</table>

electrospun nanofiber scaffolds with gradations in fiber organization

The goal of this protocol is to report a simple method for generating nanofiber scaffolds with gradations in fiber organization and test their possible applications in controlling cell morphology/orientation. Nanofiber organization is controlled with a new fabrication apparatus that enables the gradual decrease of fiber organization in a scaffold. Changing the alignment of fibers is achieved through decreasing deposition time of random electrospun fibers on a uniaxially aligned fiber mat. By covering the collector with a moving barrier/mask, along the same axis as fiber deposition, the organizational structure is easily controlled. For tissue engineering purposes, adipose-derived stem cells can be seeded to these scaffolds. Stem cells undergo morphological changes as a result of their position on the varied organizational structure, and can potentially differentiate into different cell types depending on their locations. Additionally, the graded organization of fibers enhances the biomimicry of nanofiber scaffolds so they more closely resemble the natural orientations of collagen nanofibers at tendon-to-bone insertion site compared to traditional scaffolds. Through nanoencapsulation, the gradated fibers also afford the possibility to construct chemical gradients in fiber scaffolds, and thereby further strengthen their potential applications in fast screening of cell-materials interaction and interfacial tissue regeneration. This technique enables the production of continuous gradient scaffolds, but it also can potentially produce fibers in discrete steps by controlling the movement of the moving barrier/mask in a discrete fashion.

Using this protocol, a fiber mat with an organizational gradient was formed. Figure 3 shows the SEM images taken at various locations on the nanofiber scaffold. Qualitatively, it can be determined that there is a progression from the uniaxially aligned fibers at 0 mm (Figure 3A) to a random fiber assortment at 6 mm (Figure 3D). The FFT gives a quantitative value to the fiber alignment, specifics on the quantitative processes are detailed here19. Fibers at 0 mm...

Watch this Scientific Journal Video about Electrospun Nanofiber Scaffolds with Gradations in Fiber Organization at JoVE.com

Electrospun Nanofiber Scaffolds with Gradations in Fiber Organization

Here, we present a protocol to fabricate electrospun nanofiber scaffolds with gradated organization of fibers and explore their applications in regulating cell morphology/orientation. Gradients with regard to physical and chemical properties of the nanofiber scaffolds offer a wide variety of applications in the biomedical field.

The goal of this protocol is to report a simple method for generating nanofiber scaffolds with gradations in fiber organization and test their possible ...

electrospun-nanofiber-scaffolds-with-gradations-in-fiber-organization

Research

JoVE Journal

Bioengineering

9.7K Views.  University of Nebraska Medical Center. Here, we present a protocol to fabricate electrospun nanofiber scaffolds with gradated organization of fibers and explore their applications in regulating cell morphology/orientation. Gradients with regard to physical and chemical properties of the nanofiber scaffolds offer a wide variety of applications in the biomedical field.