The authors have no acknowledgements.

An exempt approval (3002-13) to carry out research using de-identified tissue samples pursuant to the Department of Health and Human Services regulations, 45 CFR 46.101(b)(4) was granted. Full thickness skin is received from elective surgery. In this article, the tissue source is 66-year-old Caucasian female breast.
1. Preparation of Elastomer Coated Coverslips
<ol>
	<li>In a 20 mL glass vial, mix 0.107 g of Sylgard 184 curing agent with 5.893 g base. The total mixture mass is 6 g with a bas...

<ol>
	<li>Van Hal, D., Jeremiasse, E., Junginger, H. E., Spies, F., Bouwstra, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Structure+of+fully+hydrated+human+stratum+corneum:+a+freeze-fracture+electron+microscopy+study.">Structure of fully hydrated human stratum corneum: a freeze-fracture electron microscopy study.</a> J. Invest. Dermatol. 106 (1), 89-95 (1996).</li><li>Norl&#233;n, L., Al-Amoudi, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Stratum+corneum+keratin+structure,+function,+and+formation:+the+cubic+rod-packing+and+membrane+templating+model.">Stratum corneum keratin structure, function, and formation: the cubic rod-packing and membrane templating model.</a> J. Invest. Dermatol. 123 (4), 715-732 (2004).</li><li>Liu, X., Cleary, J., German, G. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+global+mechanical+properties+and+multi-scale+failure+mechanics+of+heterogeneous+human+stratum+corneum.">The global mechanical properties and multi-scale failure mechanics of heterogeneous human stratum corneum.</a> Acta Biomater. , (2016).</li><li>Geerligs, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Skin layer mechanics. , (2010).</li><li>Farage, M. S., Miller, K. W., Maibach, H. I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Textbook of Aging Skin. , (2010).</li><li>Levi, K., Kwan, A., Rhines, A. S., Gorcea, M., Moore, D. J., Dauskardt, R. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Emollient+molecule+effects+on+the+drying+stresses+in+human+stratum+corneum.">Emollient molecule effects on the drying stresses in human stratum corneum.</a> Br. J. Dermatol. 163 (4), 695-703 (2010).</li><li>German, G. K., Pashkovski, E., Dufresne, E. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surfactant+treatments+influence+drying+mechanics+in+human+stratum+corneum.">Surfactant treatments influence drying mechanics in human stratum corneum.</a> J. Biomech. 46 (13), 2145-2151 (2013).</li><li>Liu, X., German, G. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+effects+of+barrier+disruption+and+moisturization+on+the+dynamic+drying+mechanics+of+human+stratum+corneum.">The effects of barrier disruption and moisturization on the dynamic drying mechanics of human stratum corneum.</a> J. Mech. Behav. Biomed. Mater. 49 (13), 80-89 (2015).</li><li>Levi, K., Weber, R. J., Do, J. Q., Dauskardt, R. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Drying+stress+and+damage+processes+in+human+stratum+corneum.">Drying stress and damage processes in human stratum corneum.</a> Int. J. Cosmet. Sci. 32 (4), 276-293 (2010).</li><li>Levi, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+glycerin+on+drying+stresses+in+human+stratum+corneum.">Effect of glycerin on drying stresses in human stratum corneum.</a> J. Dermatol. Sci. 61, 129-131 (2011).</li><li>Fluhr, J. W., Darlenski, R., Surber, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Glycerol+and+the+skin:+holistic+approach+to+its+origin+and+functions.">Glycerol and the skin: holistic approach to its origin and functions.</a> Br. J. Dermatol. 159 (1), 23-34 (2008).</li><li>German, G. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Heterogeneous+drying+stresses+in+stratum+corneum.">Heterogeneous drying stresses in stratum corneum.</a> Biophys. J. 102 (11), 2424-2432 (2012).</li><li>Willert, C. E., Gharib, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Digital+particle+image+velocimetry.">Digital particle image velocimetry.</a> Exp. Fluids. 10 (4), 181-193 (1991).</li><li>Mertz, A. F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Scaling+of+traction+forces+with+the+size+of+cohesive+cell+colonies.">Scaling of traction forces with the size of cohesive cell colonies.</a> Phys. Rev. Lett. 108 (19), 1-5 (2012).</li><li>Banerjee, S., Marchetti, M. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Substrate+rigidity+deforms+and+polarizes+active+gels.">Substrate rigidity deforms and polarizes active gels.</a> Euro Phys. Lett. 96 (2), 28003 (2011).</li><li>Edwards, C. M., Schwarz, U. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Force+localization+in+contracting+cell+layers.">Force localization in contracting cell layers.</a> Phys. Rev. Lett. 107 (12), 128101 (2011).</li><li>Cesa, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Micropatterned+silicone+elastomer+substrates+for+high+resolution+analysis+of+cellular+force+patterns.">Micropatterned silicone elastomer substrates for high resolution analysis of cellular force patterns.</a> Rev. Sci. Instrum. 78 (3), 34301 (2007).</li><li>Wu, K. S., Van Osdol, W. W., Dauskardt, R. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Mechanical+And+Microstructural+Properties+Of+Stratum+Corneum.">Mechanical And Microstructural Properties Of Stratum Corneum.</a> Mater. Res. Soc. 724, 27-33 (2002).</li><li>Yuan, Y., Verma, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Measuring+microelastic+properties+of+stratum+corneum.">Measuring microelastic properties of stratum corneum.</a> Colloids Surf. B. 48 (1), 6-12 (2006).</li><li>Christensen, M. S., Hargens, C. W., Nacht, S., Gans, E. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Viscoelastic+properties+of+intact+human+skin:+instrumentation,+hydration+effects,+and+the+contribution+of+the+stratum+corneum.">Viscoelastic properties of intact human skin: instrumentation, hydration effects, and the contribution of the stratum corneum.</a> J Invest. Dermatol. 69 (3), (1977).</li><li>Pailler-Mattei, C., Bec, S., Zahouani, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+vivo+measurements+of+the+elastic+mechanical+properties+of+human+skin+by+indentation+tests.">In vivo measurements of the elastic mechanical properties of human skin by indentation tests.</a> Med. Eng.Phys. 30 (5), 599-606 (2008).</li></ol>

The authors have nothing to disclose.

In this article, we describe a technique that can be used to measure the dynamic drying behavior and mechanical properties of human SC. Previous studies have demonstrated that this technique can be used to quantify the effects of environmental conditions and chemical products commonly used in cosmetic cleansers and moisturizers on the dynamic drying behavior of SC7,8. There are a number of key steps in the protocol. Firstly, SC swells notably with water content; ...

The outer most layer of the epidermis, or stratum corneum (SC) consists of cohesive corneocyte cells surrounded by a lipid rich matrix1,2. The composition and structural integrity of SC is essential for maintaining correct barrier functionality3, which prevents invasion from microorganisms and resists both mechanical forces and excessive water loss4. The capacity of personal care products to maintain or degrade skin barrier function is of great interest to skin healthcare and the cosmetic industry5. The daily application of personal care products is known to alter the mechanical properties of the SC6,7,8. For example, surfactants contained in cosmetic cleansers can cause significant increases in the elastic modulus and a build-up of drying stresses in SC, increasing the tissue&#39;s propensity to crack7,9. Glycerol contained in nearly all cosmetic moisturizers can soften SC and decrease the build-up of drying stresses8,10,11, reducing the likelihood of tissue rupture.
The method detailed in this article is capable of quantifying the dynamic drying behavior and mechanical properties of SC drying in controlled environments7,8. Previously, this technique has been demonstrated to be capable of elucidating the effect of different cosmetic products on changes in the dynamic drying behavior and mechanical properties of SC tissue. This is achieved by quantifying drying-induced shrinkage of human SC tissue adhered to a soft elastomer substrate, fitting drying displacements with a simple contractility model, and then extracting the elastic modulus and drying stress from the fitted profile. When testing of multiple SC samples is required, this method offers a more rapid alternative to uniaxial tensometry, utilizes significantly less tissue and provides more physiologically relevant drying by preventing evaporation from the sample underside.

<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Silicone elastomer base</td>
			<td>Dow-Corning</td>
			<td>1064291</td>
		</tr>
		<tr>
			<td>Silicone elastomer Curing Agent</td>
			<td>Dow-Corning</td>
			<td>1015311</td>
		</tr>
		<tr>
			<td>FluoSpheres Carboxylate 0.1 &#181;m yellow green fluorescent 505/515&#160;</td>
			<td>Thermo Fisher</td>
			<td>F8803</td>
		</tr>
		<tr>
			<td>FluoSpheres Carboxylate 1 &#181;m yellow green fluorescent 505/515&#160;</td>
			<td>Thermo Fisher</td>
			<td>F8823</td>
		</tr>
		<tr>
			<td>FluoSpheres Carboxylate 1 &#181;m nile red fluorescent 535/575&#160;</td>
			<td>Thermo Fisher</td>
			<td>F8819</td>
		</tr>
		<tr>
			<td>Trypsin from porcine pancreas</td>
			<td>Sigma-Aldrich</td>
			<td>T6567</td>
		</tr>
		<tr>
			<td>Trypsin inhibitor type II-s</td>
			<td>Sigma-Aldrich</td>
			<td>T9128</td>
		</tr>
		<tr>
			<td>(3-aminopropyl)triethoxysilane</td>
			<td>Sigma-Aldrich</td>
			<td>440140</td>
		</tr>
		<tr>
			<td>Sodium tetraborate</td>
			<td>Sigma-Aldrich</td>
			<td>221732</td>
		</tr>
		<tr>
			<td>Boric acid</td>
			<td>Sigma-Aldrich</td>
			<td>B0294</td>
		</tr>
		<tr>
			<td>Phosphate buffered saline</td>
			<td>Sigma-Aldrich</td>
			<td>P7059</td>
		</tr>
		<tr>
			<td>N-(3-Dimethylaminopropyl)-N-ethylcarbodiimide hydrochloride&#160;</td>
			<td>Sigma-Aldrich</td>
			<td>E7750</td>
		</tr>
		<tr>
			<td>Vortexer mixer</td>
			<td>VWR</td>
			<td>58816-123</td>
		</tr>
		<tr>
			<td>6mm diameter hole punch</td>
			<td>Sigma-Aldrich</td>
			<td>Z708860</td>
		</tr>
		<tr>
			<td>SOLA 6-LCR-SB&#160;</td>
			<td>Lummencor light engine</td>
			<td>No.3526</td>
		</tr>
		<tr>
			<td>Cfi Plan Achro Uw 1x Objective</td>
			<td>Nikon Plan UW</td>
			<td>MRL00012</td>
		</tr>
		<tr>
			<td>CFI Plan Fluor 40x Oil Objective 1.3 na - 0.20mm wd</td>
			<td>Nikon Plan Fluor</td>
			<td>MRH01401</td>
		</tr>
		<tr>
			<td>Nikon Eclipse Ti-U inverted microscope&#160;</td>
			<td>Nikon</td>
			<td>MEA53200</td>
		</tr>
		<tr>
			<td>Clara-E Camera</td>
			<td>Andor</td>
			<td>DR-328G-C02-SIL</td>
		</tr>
		<tr>
			<td>Remote Focus Attachment E-RFA Ergo Design</td>
			<td>Nikon</td>
			<td>99888</td>
		</tr>
		<tr>
			<td>Ti-S-E Motorized Stage</td>
			<td>Nikon</td>
			<td>MEC56110</td>
		</tr>
	</tbody>
</table>

measuring and modeling contractile drying in human stratum corneum

Stratum corneum (SC) is the most superficial skin layer. Its contact with the external environment means that this tissue layer is subjected to both cleansing agents and daily variations in ambient moisture; both of which can alter the water content of the tissue. Reductions in water content from severe barrier dysfunction or low humidity environments can alter SC stiffness and cause a build-up of drying stresses. In extreme conditions, these factors can cause mechanical rupture of the tissue. We have established a high throughput method of quantifying dynamic changes in the mechanical properties of SC upon drying. This technique can be employed to quantify changes in the drying behavior and mechanical properties of SC with cosmetic cleanser and moisturizer treatments. This is achieved by measuring dynamic variations in spatially resolved in-plane drying displacements of circular tissue samples adhered to an elastomer substrate. In-plane radial displacements acquired during drying are azimuthally averaged and fitted with a profile based on a linear elastic contractility model. Dynamic changes in drying stress and SC elastic modulus can then be extracted from the fitted model profiles.

Figure 1(a) shows a representative fluorescent image of an SC sample coated with fluorescent beads (section 3). The corresponding transmitted light image of the sample is shown in Figure 1(b) overlaid with a quiver plot of spatially resolved drying displacements that form after 16 h drying at 25% R.H. Due to the circular symmetry of the samples, these displacements can be azimuthally averaged. Figure 1(c) shows radial (ur, soli...

Watch this Scientific Journal Video about Measuring and Modeling Contractile Drying in Human Stratum Corneum at JoVE.com

Measuring and Modeling Contractile Drying in Human Stratum Corneum

This article describes a method of quantifying the dynamic drying behavior and mechanical properties of stratum corneum by measuring spatially resolved in-plane drying displacements of circular tissue samples adhered to an elastomer substrate. This technique can be used to measure how different chemical treatments alter drying and tissue mechanical properties.

Stratum corneum (SC) is the most superficial skin layer. Its contact with the external environment means that this tissue layer is subjected to both ...

The overall goal of this method is to quantify the dynamic mechanical stiffness and build up of drying stresses in ex vivo samples of human stratum corneum, after different chemical treatments. This method can help answer key questions in the biomechanics and cosmetic science fields, such as how the composition of of the stratum corneum or treatment of the skin tissue with a personal care products can influence, it's mechanical properties and dynamic drying behavior. The main advantage of this technique is that it offers a more rapid alternative to other mechanical assessment methods, requires significantly less skin tissue and provides more physiologically relevant drying by preventing evaporation from the sample underside.To prepare elastomer coated coverslips, first make Sylgard 184 curing agent with base solids at a base to curing agent ratio of 55 to one, until it is homogenous. Six grams in total are needed. Next, de-gas the solution.Then use the solution to coat the coverslips on a spin coater. Using a wide bore pipette, drop one milliliter of the mixture centrally on a coverslip. Then spin coat the coverslip at 2, 000 rpm for 60 seconds.Make five or six coated coverslips in this manner. To cure the coverslips, keep them in a 60 degree Celsius oven for 12 hours. The next day, measure the elastomer films thicknesess.Use a razor blade to lift one edge of the elastomer film off the coverslip. Then use an indelible marker to mark the top side of the elastomer film and to mark the treated coverslip beneath. Now, using an inverted microscope, measure the Z height between the focal planes of the marks to measure the films thicknesses.Follow standard procedures to prepare the SC tissue. To make samples, take six millimeter diameter punches from the SC.On the samples, place a mark at the center of the outmost face using an indelible marker. Next, deposit fluorescent marker beads onto the SC surface by floating the samples in 15 milliliters of water, containing about 90 microliters of bead concentrate.Use gentle agitation for 30 minutes and adjust the bead concentration as needed. After the treatment, immerse each sample in water to mount it onto the elastomer. Position a coated coverslip at a shallow angle, 15 to 30 degrees under the SC with the elastomer towards the bottom side of the SC.Then lift the coverslip from the water with the SC attached above, thus smoothly laminating the SC sample without wrinkles or trapped air.Next, dry the mounted samples at ambient conditions for about an hour. Once dried, transfer the samples to a hermetically sealed chamber containing a dish of water. Allow the samples to equilibrate to the humidity for 24 hours.The next day, mount a sample to a perfusion chamber for a prolonged imaging session. Place the perfusion chamber over the substrate and seal the edges of the perfusion chamber to the elastomer using vacuum grease. Then record fluorescent and transmitted light images with a field of view large enough to capture the full SC sample.Over the next 16 hours, take an image every 10 minutes. In a chemical fume hood, load a small plastic cap with one milliliter of silane. Transfer the cap into a sealed container with one elastomer lined coverslip, not in direct contact.Allow them to incubate at room temperature for five hours. While waiting, prepare 20 milliliters of bead solution according to the text protocol and then pour it into a 10 centimeter dish. After five hours, slowly place the silanated substrates elastomer side down, into the bead solution.Load two substrates into each dish and let the substrates react with the beads for 45 minutes. Later, using tweezers, remove the substrates and rinse them in distilled water to remove the unbound beads. Then dry them under a gentle stream of compressed air and store them in a sealed, opaque box.Using the previously described technique, transfer the SC samples onto a treated substrate in a water bath. Immediately after mounting the SC, apply a five microliter drop of un-diluted fluorescent marker bead solution onto it. Then allow the SC to dry for 60 minutes.Now, measure the SC thickness using the microscope with a 40x subjective lens in a perfusion chamber. Measure the thickness of SC over time, using a remote focus accessory to record the difference in Z height between the two bead layers. One layer is at the SC substrate interface and the other is on top of the SC.Using the described techniques, an SC sample was prepared and coated with fluorescent beads.After 16 hours of drying, at 25%relative humidity, displacements were measured. Due to the circular symmetry of the samples, these displacements were azimuthally averaged. Throughout drying, azimuthal displacements remain small.Radial displacement profiles however, increased monotonically from the center to the edge and grew in magnitude until an equilibrium was reached. Profiles recorded at 30 minute intervals show the time evolution of in-plane displacements. The average SC thickness decreased during drying, primarily over the first two hours.The drying dynamic was then analyzed by fitting the displacement profiles to a linear, elastic contractility model using a minimum least squares approach. From the model, the contractual drying stress was extracted, as well as the elastic modulus. Both parameters increased rapidly over the first two hours of drying.While attempting this procedure, it is important to remember to adhere the samples onto the substrate completely. Following this procedure, other methods like lipid staining can be performed in order to answer additional questions such as how particular cosmetic treatments alter tissue lipid composition.

measuring-and-modeling-contractile-drying-in-human-stratum-corneum

Research

JoVE Journal

Bioengineering

6.5K visualizações.  Binghamton University. The overall goal of this method is to quantify the dynamic mechanical stiffness and build up of drying stresses in ex vivo samples of human stratum corneum, after different chemical treatments. This method can help answer key questions in the biomechanics and cosmetic science fields, such as how the composition of of the stratum corneum or treatment of the skin tissue with a personal care products can influence, it's mechanical properties and dynamic drying behavior. The main advantage of thi...