Name: reaction kinetics and combustion dynamics of i4o9 and aluminum mixtures
Uploaded: 2016-11-07T15:00:00.000+00:00
Duration: 9 min 16 s
Description: Watch this Scientific Journal Video about Reaction Kinetics and Combustion Dynamics of I4O9 and Aluminum Mixtures at JoVE.com

The authors Smith and Pantoya are grateful for partial support from DTRA under award HDTRA1-15-1-0029; and, ARO (and Dr. Ralph Anthenien) under award W911NF-14-1-0250 and equipment grant W911NF-14-10417. The authors J. Parkey and M. Kesmez are grateful for support from DTRA under award HDTRA1-15-P-0037. Thank you to Dr. Douglas Allen Dalton for helpful discussion.

NOTE: Six different oxidizers were investigated for the purpose of characterizing the kinetics of I4O9 in comparison to other iodine oxides. Each oxidizer is described below. The fuel used for all mixtures was constant: Al powder with 80 nm average spherical particle diameter. Mixture preparation is described following discussion of each oxidizer.
1. Preparation of Iodine(V) Oxides
NOTE: Nano-aluminum/oxidizer mixtures are highly volatile and can exhibit explosive behavior. These mixtures are susceptible to unintended ignition by electrostatic discharge, friction, impact, and other forms of accidental ignition. All equipment should be grounded to decrease the likelihood of accidental spark ignition. Quantities should be minimized and protective equipment should be used when handling these materials. More information on safety and handling procedures can be found in Maienschein et al.18
<ol>
	<li>Preparation commercial I2O5
	<ol>
		<li>Crush 10 g of I2O5 crystals with a mortar and pestle until a consistent powder is created.</li>
		<li>After the crystals are in a powder form, evenly spread the 10 g of powder in a ceramic crucible suitable for heating up to 250 &#176;C.</li>
		<li>Place entire crucible in an oven and heat to 250 &#176;C at 10&#176;C/min and hold at 250 &#176;C for 5 min.</li>
	</ol>
	</li>
	<li>Preparation of amorphous I2O5
	<ol>
		<li>Place 3 g of the crushed and dehydrated commercial I2O5 in a glass beaker with a magnetic stirrer and add 3 g of distilled water. To ensure the sample is completely dissolved, add a 1:1 ratio of water to commercial I2O5 and mix for 20 min. Dissolution of I2O5 in water forms an aqueous phase of IO3.17</li>
		<li>Pour the IO3 solution into a beaker that is suitable for heating. To ensure enough amorphous I2O5 is produced, use three times the mass of IO3 solution than the mass needed of amorphous I2O5. For example, if one gram of amorphous I2O5 is needed, use 3 g of IO3 solution.</li>
		<li>Place the beaker with the IO3 solution into an oven and heat at 20 &#176;C/min to 250 &#176;C and hold for 10 min.</li>
		<li>Store the sample in a sealed container to limit exposure to atmospheric water from the environment.</li>
	</ol>
	</li>
	<li>Preparation crystalline HIO3
	<ol>
		<li>Repeat step 1.2.1 and place IO3 solution on a magnetic stirrer in a low humidity environment (below 50% RH) until all of the excess water has evaporated. Upon evaporation, the aqueous phase of IO3 will precipitate out as HIO317.</li>
		<li>Store the sample in a sealed container to limit exposure to atmospheric water from the environment.</li>
		<li>To ensure all excess water is evaporated, place a sample into a differential scanning calorimeter (DSC) and heat to 250 &#176;C at 10 &#176;C/min. 
		NOTE: The weight loss at 110 &#176;C will equal 5% and there will be no mass loss at 210 &#176;C if the sample is pure HIO3. Any additional mass loss is excess water, which means the sample needs more time to evaporate. Weight loss at 210 &#176;C means the I2O5 has not completely dissolved and more water with agitation is needed to dissolve the sample.</li>
	</ol>
	</li>
</ol>
2. Mixture Preparation
NOTE: The mixtures are prepared in two different ways: one using a carrier fluid to aid in intermixing and another without a carrier fluid but instead dry mixed. For processing using a carrier fluid, mixtures were prepared for only three oxidizers: I4O9, nano I2O5 and commercial I2O5.
<ol>
	<li>Preparation of mixtures in a carrier fluid
	<ol>
		<li>To prepare the samples mixed in a carrier fluid, mix 80 nm Al powder with each oxidizer for a total of two grams of Al and oxidizer mixture to an equivalence ratio of 1.0 in a beaker.</li>
		<li>Add 60 ml of isopropanol into the beaker and sonicate the solution with a sonic wand set at an output power of 4 watts programmed for 10 sec on and 10 sec off for a total of 2 min.</li>
		<li>Pour solution into a glass dish and allow the solution to evaporate in a fume hood at room temperature with a relative humidity of 20% for 24 hr, which will leave powder samples. 
		NOTE: Before proceeding with step 2.1.4, assure razor blade is connected to an electrical ground with a conductive wire to avoid accidental ignition.</li>
		<li>Reclaim the powder with a grounded razor blade and sieve the sample to break up agglomerates directly into a container that can be sealed to limit sample exposure to atmospheric water.</li>
	</ol>
	</li>
	<li>Preparation of dry mixed samples
	<ol>
		<li>Sieve and mix two grams of Al and oxidizer mixture with a spatula into a sample container to a fuel to oxygen equivalence ratio of 1.0. Seal the sample container to limit sample exposure to atmospheric water.</li>
		<li>Hold samples on a vibration table for 3 minute to aid intermixing. Refer to samples prepared in this way as dry mixed.</li>
	</ol>
	</li>
</ol>
3. Thermal Equilibrium Analysis
<ol>
	<li>Preparation of samples for thermal equilibrium analysis 
	NOTE: These samples react easily with atmospheric water. Relative humidity should be reduced below 30% and exposure to the atmosphere should be limited (i.e., store sample in sealed containers and use lids on DSC-TGA crucibles).
	<ol>
		<li>Heat alumina crucibles (supplied with the DSC-TGA diagnostic) to 1,500 &#176;C and hold for 30 min to remove any residue on the crucibles in the DSC-TGA.</li>
		<li>Weigh crucibles before the samples are placed in the crucible. This measurement is needed by the DSC-TGA.</li>
		<li>After the crucible is weighed, add 10 mg of each sample into a crucible.</li>
		<li>Place the sample crucible on the thermocouple in the DSC-TGA with an empty crucible in the reference holder on the DSC thermocouple.</li>
		<li>Heat the samples at 10 &#176;C/min to 600 &#176;C in an argon atmosphere.</li>
	</ol>
	</li>
</ol>
4. Energy Propagation
<ol>
	<li>Preparation of flame tubes
	<ol>
		<li>Use quartz tubes with an inside diameter of 3 mm and length of 7 cm to contain the powder mixture.</li>
		<li>Put tape on one end so powder cannot escape from the tube.</li>
		<li>Place each 7 cm tube with one end taped on a scale and zero the scale. This will allow the measurement of just the mass of powder.</li>
		<li>Using a spatula with a small end, insert the powder samples into the tube. For each of the mixtures, make three tubes filled with each mixture for repeatability testing.</li>
		<li>Using a rod that has a diameter smaller than 3 mm, compact the powder inside the tube for the samples with low bulk densities (i.e., Al + I4O9 and Al + amorphous I2O5) until the volume of the sample does not change. This procedure is necessary to maintain consistent bulk densities between multiple experiments. This may require 200 mg of powder mixture.</li>
		<li>For all other mixtures, which have higher densities, do not compact the powder using external force. Keep the bulk density constant between samples with similar bulk densities. The amount of powder in the tubes will vary depending on bulk density of the powder. This may require up to 500 mg of powder mixture.</li>
		<li>Measure the mass of powder mixture in each tube using the balance that was tared for each tube, add mass until the density of the powder is within 5% of the other samples in each group. Make sure each tube is completely filled.</li>
	</ol>
	</li>
	<li>Preparation of hot wire ignite
	<ol>
		<li>To prepare the hot wire, use a nickel-chromium (i.e., nichrome) wire cut into sections 10 cm long.</li>
		<li>Make a &#34;v&#34; shape in the middle of the wire and place the wire so the &#34;v&#34; shape is inside the tube.</li>
		<li>Tape this end of the tube so the wire is stationary and no powder can escape the tube.</li>
	</ol>
	</li>
	<li>Preparation of high speed camera
	<ol>
		<li>Place the high speed camera outside the combustion chamber perpendicular to the direction of flame propagation and focus the camera on the tube through a viewing port in the combustion chamber. 
		&#8203;NOTE: The primary function of the combustion chamber is to protect personnel and equipment from the reacting material and should be ventilated through a fume hood.</li>
		<li>Adjust placement and lens of the camera so the lowest resolution (i.e., highest frame rate) can be used.</li>
		<li>To allow distance calibration, place a ruler with mm and cm increments in the field of view and take a snapshot with the high speed camera prior to recording flame speeds.</li>
		<li>As the flame front is significantly brighter than ambient light and the camera will over-saturate when exposed to the light generated by the reaction, lower the exposure time in the camera settings or add neutral density filters to the lens of the camera to reduce the amount of light received by the camera sensors. Lower the amount of light received by the camera until the propagation front of the reaction can be seen clearly. Here, set up neutral density filters allowing only 5% of the light to pass, and an exposure time of 1 &#181;sec.</li>
		<li>Attach a voltage generator to the ends of the wire. The combustion chamber should have insulated leads through the chamber which will allow the chamber to be sealed and allow remote heating of the wire.</li>
		<li>After the chamber is sealed, set the voltage generator to 10 volts and simultaneously begin the camera recording. When the voltage is applied, the reaction should start almost immediately.</li>
		<li>Export the video into a software program that will track the position of the flame front as a function of time in each individual frame.</li>
		<li>Export the distance and time step information into a spread sheet and plot a linear trend line with R2 values. For slower reactions, time is needed for the reaction to reach a steady state. The curve before the steady state will be an exponentially increasing curve. Remove the data that are not in steady state until the R2 value is greater than 0.95. The slope of the line is the flame speed.</li>
	</ol>
	</li>
</ol>

<ol>
	<li>Selte, K., Kjekshus, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Iodine+Oxides+Part+II+on+the+system+H2O+I2O5.">Iodine Oxides Part II on the system H2O I2O5.</a> Acta. Chem. Scand. 22, 3309-3320 (1968).</li><li>Little, B. K., Emery, S. B., Nittinger, J. C., Fantasia, R. C., Lindsay, C. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Physiochemical+Characterization+of+Iodine+(+V+)+Oxide+,+Part+1+Hydration+Rates.+(V).">Physiochemical Characterization of Iodine ( V ) Oxide , Part 1 Hydration Rates. (V).</a> Propell. Explos. Pyrot. 40, 595-603 (2015).</li><li>Smith, D. K., McCollum, J., Pantoya, M. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+Environment+of+Iodine+Oxidation+State+on+Reactivity+with+Aluminum.">Effect of Environment of Iodine Oxidation State on Reactivity with Aluminum.</a> Phys. Chem. Chem. Phys. 18, 11243-11250 (2016).</li><li>Farley, C., Pantoya, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Reaction+kinetics+of+nanometric+aluminum+and+iodine+pentoxide.">Reaction kinetics of nanometric aluminum and iodine pentoxide.</a> J. Therm. Anal. Calorim. 02 (2), 609-613 (2010).</li><li>Little, B. K., Emery, S. B., Lindsay, M. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Physiochemical+Characterization+of+Iodine+(V)+Oxide+Part+II+Morphology+and+Crystal+Structure+of+Particulat+Films.">Physiochemical Characterization of Iodine (V) Oxide Part II Morphology and Crystal Structure of Particulat Films.</a> Crystals. 05 (4), 534-550 (2015).</li><li>Wikjord, A., Taylor, P., Torgerson, D., Hachkowski, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Thermal+behaviour+of+Corona-Precipitated+Iodine+Oxides.">Thermal behaviour of Corona-Precipitated Iodine Oxides.</a> Thermochim. Acta. 36, 367-375 (1980).</li><li>Little, B. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Chemical+dynamics+of+nano-aluminum/iodine+(V)+oxide.">Chemical dynamics of nano-aluminum/iodine (V) oxide.</a> J. Phys. Conf. Ser. 500 (5), 052025 (2014).</li><li>Feng, J., Jian, G., Liu, Q., Zachariah, M. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Passivated+iodine+pentoxide+oxidizer+for+potential+biocidal+nanoenergetic+applications.">Passivated iodine pentoxide oxidizer for potential biocidal nanoenergetic applications.</a> ACS Appl. Mater. Inter. 5 (18), 8875-8880 (2013).</li><li>Wang, H., DeLisio, J. B., Jian, G., Zhou, W., Zachariah, M. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrospray+formation+and+combustion+characteristics+of+iodine-containing+Al/CuO+nanothermite+microparticles.">Electrospray formation and combustion characteristics of iodine-containing Al/CuO nanothermite microparticles.</a> Combust. Flame. 162 (7), 2823-2829 (2015).</li><li>Sunder, S., Wren, J. C., Vikis, A. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Raman+Spectra+of+1409+Formed+by+the+Reaction+of+Iodine+with+Ozone.">Raman Spectra of 1409 Formed by the Reaction of Iodine with Ozone.</a> J. Raman Spectrosc. 16 (6), 424-426 (1985).</li><li>Selte, K., Kjekshus, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Iodine+Oxides+Part+III.+The+Crystal+Structure+of+I2O5.">Iodine Oxides Part III. The Crystal Structure of I2O5.</a> Acta. Chem. Scand. 6 (24), 1913-1924 (1970).</li><li>Sherwood, P. M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=X-Ray+Photoelectron+Spectroscopic+Studies+of+Some+Iodine+Compounds.">X-Ray Photoelectron Spectroscopic Studies of Some Iodine Compounds.</a> J. Chem. Soc. 72, 1805-1820 (1976).</li><li>Russell, R., Bless, S., Pantoya, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Impact-Driven+Thermite+Reactions+with+Iodine+Pentoxide+and+Silver+Oxide.">Impact-Driven Thermite Reactions with Iodine Pentoxide and Silver Oxide.</a> J. Energ. Mater. 29 (2), 175-192 (2011).</li><li>Skulski, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Organic+iodine(I,+III,+and+V)+chemistry:+10+Years+of+development+at+the+Medical+University+of+Warsaw,+Poland.">Organic iodine(I, III, and V) chemistry: 10 Years of development at the Medical University of Warsaw, Poland.</a> Molecules. 5 (12), 1331-1371 (2000).</li><li>Nicolaou, K. C., Montagnon, T., Baran, P. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=HIO3+and+I2O5+Mild+and+Selective+Alternative+Reagents+to+IBX+for+the+Dehydrogenation+of+Aldehydes+and+Ketones.">HIO3 and I2O5 Mild and Selective Alternative Reagents to IBX for the Dehydrogenation of Aldehydes and Ketones.</a> Angew. Chem. Int. Edit. 293 (8), 1386-1389 (2002).</li><li>Lide, D. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> CRC Handbook of Chemistry and Physics. , 3485 (2005).</li><li>Kumar, R., Saunders, R. W., Mahajan, a. S., Plane, J. M. C., Murray, B. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Physical+properties+of+iodate+solutions+and+the+deliquescence+of+crystalline+I2O5+and+HIO3.">Physical properties of iodate solutions and the deliquescence of crystalline I2O5 and HIO3.</a> Atmos. Chem. Phys. 10 (24), 12251-12260 (2010).</li><li>Maienschein, J., Pantoya, M. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Safety+in+Energetic+Materials+Research+and+Development-Approaches+in+Academia+and+a+National+Laboratory.">Safety in Energetic Materials Research and Development-Approaches in Academia and a National Laboratory.</a> Propell. Explos. Pyrot. 39 (4), 483-485 (2014).</li><li>Osborne, D. T., Pantoya, M. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+Al+Particle+Size+on+the+Thermal+Degradation+of+Al/Teflon+Mixtures.">Effect of Al Particle Size on the Thermal Degradation of Al/Teflon Mixtures.</a> Combust. Sci. Technol. 179, 1467-1480 (2007).</li><li>Pantoya, M. L., Dean, S. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+influence+of+alumina+passivation+on+nano-Al/Teflon+reactions.">The influence of alumina passivation on nano-Al/Teflon reactions.</a> Thermochim. Acta. 493 (1-2), 109-110 (2009).</li><li>Mulamba, O., Pantoya, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Exothermic+surface+reactions+in+alumina-aluminum+shell-core+nanoparticles+with+iodine+oxide+decomposition+fragments.">Exothermic surface reactions in alumina-aluminum shell-core nanoparticles with iodine oxide decomposition fragments.</a> J. Nanopart. Res. 16 (3), 2310 (2014).</li><li>Nelyubina, Y., Antipin, M. Y., Lyssenko, K. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Extremely+short+halogen+bond:+the+nature+and+energy+of+iodine-oxygen+interactions+in+crystalline+iodic+acid.">Extremely short halogen bond: the nature and energy of iodine-oxygen interactions in crystalline iodic acid.</a> Mendeleev. Commun. 21, 250-252 (2011).</li><li>Bockmon, B. S., Pantoya, M. L., Son, S. F., Asay, B. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Combustion+velocities+and+propagation+mechanisms+of+meta-stable+intermolecular+composites.">Combustion velocities and propagation mechanisms of meta-stable intermolecular composites.</a> J. Appl. Phys. 98 (6), 064903 (2005).</li><li>Pantoya, M. L., Levitas, V. I., Granier, J. J., Henderson, J. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+bulk+density+on+reaction+propagation+in+nanothermites+and+micron+thermites.">Effect of bulk density on reaction propagation in nanothermites and micron thermites.</a> J. Propul. Power. 25 (2), 465-470 (2009).</li></ol>

All authors have no competing financial interests or other conflicts of interest.

The I4O9 powder studied here was synthesized using a &#34;dry&#34; approach to form I4O9 by combining elemental iodine and oxygen. This sample is referred to as I4O9. Nano-particle I2O5 was also synthesized for this study. Specifically, a portion of I4O9 was heated past the dissociation temperature of I4O9 (i.e., 180 &#176;C) but under the dissociation temperature of I2O5 (400 &#176;C). This process results in particles with a diameter between 200-400 nm. This sample is referred to as nano I2O5. Particle size measurements were obtained by TEM which requires the sample to be in a vacuum. However, I4O9 dissociates into I2O5 in a vacuum, so dimensions of I4O9 were not obtained directly. Because the nano I2O5 particle diameters are between 200-400 nm and synthesized by heating the I4O9 sample, it is assumed that I4O9 has similar diameters.
A more common approach to synthesizing I2O5 is by thermal dehydration of iodic acid to form I2O51,2,8 and material made using this process is commercially available. The commercial I2O5 is received as coarse crystals and can have different concentrations of iodic acids depending on storage and handling conditions. To ensure samples are pure I2O5, the samples are dehydrated prior to use as explained in step 2.1.1.3. The diameter of the particles in this sample are between 1-5&#181;m. This sample is referred to as commercial I2O5.
The amorphous I2O5 sample is made from this saturated IO3 solution. When I2O5 is mixed with water, a solution of IO3 is created. This is done in step 2.1.2 and these steps will leave a saturated IO3 solution. Water catalyzes the formation of crystals in iodic acids. To form amorphous I2O5 the temperature must be above the dehydration temperature of HI3O8 and heated at a rate that will not allow a crystal structure to form, this is done in step 1.2. The concentration of IO3 in solution will determine the amount of amorphous I2O5 created during dehydration. These samples should turn red after dehydration indicating the sample is an amorphous form of I2O5. This sample is referred to as amorphous I2O5. Also, XRD analysis (not included) was preformed and confirmed the amorphous structure of the I4O9 and amorphous I2O5 samples.
When in solution, HIO3 will release excess water and create a crystal structure. The time needed to evaporate the excess water is dependent on the size of the beaker, RH, and concentration of the IO3 solution. In our lab at 20% RH mixing in the manner discussed above, 3-5 days were required to evaporate excess water from the samples. The solution will turn into a solid clear crystal. This process is shown in step 2.1.3 and the sample referred to as HIO3 dehydrate. Iodic acid will be referred to as commercial HIO3.
When exposed to solution or atmospheric water, iodine(V) oxide undergoes chemical reactions that change the composition of the final product. To mitigate this transformation, all six oxides are also mixed with Al without solution.
Thermal analysis using DSC-TGA was calibrated in an argon atmosphere using samples with known onset temperatures and mass losses. A flame tube apparatus known as a Bockmon Tube23 is used to measure flame speeds. Flame speed experiments are sensitive to the bulk density of the mixture. Pantoya et al. showed that for nano-Al based thermites, increasing bulk density can suppress the Al reaction mechanism and reduced the role of convective energy transport thereby retarding flame speed24. For this reason, experiments performed for different mixtures are usually designed to keep a constant bulk density. However, the physical and chemical properties of the oxidizers examined here vary dramatically such that it was not possible to obtain consistent bulk density with all six dry mixtures. Because of this, multiple iodine oxides with different physical and chemical properties are tested to provide a basis of comparison which includes differences in %TMD, crystal structure, and hydration states. After the powder has been placed inside the tubes and measured, hot wire is used to remotely ignite the mixture.
After the flame tubes are prepared with powder mixture, flame speeds are measured in a combustion chamber using a high-speed camera. The frame rate of the camera can be increased by lowering the resolution. Reducing the resolution to increase frame rate will produce less error than higher resolution at a slower frame rate. This is why, in step 4.2.2, the lowest resolution that can still image the entire flame tube is used, this will increase the maximum frames per second the camera can record without losing information. For our chamber, a resolution of 256 x 86 was used which allowed the camera to record at 300,000 fps.
Quantifying flame speeds in highly reactive mixtures is inherently difficult because of the large number of variables that can influence reactivity (i.e., mixture homogeneity, particle size, density, propagation direction, propagation velocity, etc.). By using a quartz tube with an inside diameter less than 4 mm in combination with a high speed camera with neutral density filters, the direction of propagation is controlled (i.e., 1-D) and the amount of light that is received by the camera can be reduced to a minimum threshold such that the leading edge of light emitted by the reaction can be seen and measured clearly. This measurement assumes that the progression of this low light level is at the same rate as the reaction front. For this reason, photodiodes may not be as accurate for tracking the reaction propagation because the high light intensity of emission may cause light to travel and saturate the sensors faster than the reaction. Also, the first 1-2 cm of tube length is considered an entrance region, or region of unsteady or accelerating propagation. Linear measurements of distance as a function of time must be taken beyond this entry region to determine steady state flame speed.
The DSC/TGA is a thermal equilibrium analysis that shows detailed reaction kinetics that cannot be observed in highly reactive materials (i.e., cannot be observed under non thermal equilibrium conditions). The combination of DSC/TGA analysis and flame speeds give specific information on differences in the reaction kinetics that may have implications for differences in the flame speed results. Because of this, the combination of these two measurement methods is a powerful tool for understanding and controlling highly reactive materials.

There are many iodine oxide compounds (e.g., HIO3, HI3O8, I2O5, I4O9) but the one most commonly studied for reaction with aluminum (Al) is diiodide pentoxide, I2O51-16. There are reasons for favoring I2O5 for combustion with Al: (1) I2O5 has an oxidation state of five which makes it a strong oxidizer for combustion applications; (2) I2O5 is semi-stable, depending on atmospheric conditions, and easily handled in powder form; and (3) I2O5 is relatively easy to produce and readily available.
Other forms of iodine oxide that have been studied are HIO3, HI3O8, and I4O9. When heated to low temperatures (i.e., 180 &#176;C), I4O9 thermally decomposes into I2O56 as shown in Equation (1) and the decomposition reaction is exothermic.
(1) 5I4O9&#8594;9I2O5+I2&#8203;
If I4O9 could be used in place of I2O5, the total energy liberated from reaction could increase due to the exothermic decomposition of I4O9 at temperatures below the Al ignition and reaction temperatures (i.e., &#60; 660 &#176;C) and below the dissociation temperature of I2O5 (i.e., about 350 &#176;C). Also, I4O9 generates 8 wt.% more I2 gas when compared to I2O5 that could be used to neutralize biological agents. However, I4O9 has a higher molecular weight when compared to I2O5 and it is unknown if more energy is released per mass or per volume when using I4O9 compared to I2O5. Using I4O9 could provide a way to transport large quantities of solid iodine and upon ignition, release gaseous iodine. But, I4O9 powder is usually unstable. In fact, Wikjord et al.6 showed that over very short times I4O9 decomposed into I2O5 even with limited exposure to the atmosphere. This instability limits the usefulness of I4O9 as an oxidizer in combustion applications.
Iodic acids, such as HIO3 and HI3O8, form when I2O5 is exposed to water either from the relative humidity (RH) of the atmosphere or from immersion in a fluid1,3. For combustion applications, I2O5 is usually preferred over the hydrated iodic acids because evaporation of water upon combustion absorbs energy and reduces the overall heat produced. Despite the endothermic nature of this phase change, Smith et al.3 showed rapid evaporation of water during combustion of Al with I2O5 comprised partially of iodic acids produced significant gas generation that increased convective energy transport and produced higher flame speeds than Al + I2O5 alone. Specifically, mixtures with higher concentrations of iodic acids had up to 300% higher flame speeds than mixtures with lower concentrations of iodic acids. 3
The rate of absorption from atmospheric water is dependent on RH. There is a RH threshold where absorption begins and dependent on the hydration state2. Little et al. showed a RH threshold of 70% for HIO3 and a RH threshold of 40% for HI3O82. From this, it is assumed that the RH threshold increases with increasing hydration states. Because of its deliquescent properties, most studies that use I2O5 as an oxidizer are actually using I2O5 with significant concentrations of iodic acid2,5,7,17. However, the initial concentrations of the samples can be controlled by heating the samples above 210 &#176;C until all of the hydrated species have dehydrated. This follows the hydration and dehydration mechanism of I2O5 shown in Selte et al.1 in Equation (2).
(2a) Hydration: 3I2O5+3H2O&#8594;2HI3O8+2H2O&#8594;6HIO3
(2b) Dehydration: 6HIO3&#8594;2HI3O8+2H2O&#8594; 3I2O5+3H2O
The first step in dehydration happens at 110 &#176;C when HIO3 dehydrates into HI3O8. The second step of dehydration happens at 210 &#176;C when HI3O8 dehydrates into I2O5. Because the initial concentration of commercially available I2O5 is composed mostly of iodic acids, the absorption characteristics of pure I2O5 have not been studied thoroughly. It is assumed that the RH threshold and absorption rates are dependent on physical properties (i.e., particle size, crystal structure) along with initial hydration state and that an iodine oxide that is amorphous may have a lower RH threshold and increased hydration rates. Isolating iodine oxides from atmospheric water is needed to control the initial state of iodine oxide compounds. One method of isolating I2O5 from the atmosphere is blocking water absorption with coatings. For example, Little et al. was able to reduce the absorption rate and total amount of hydrated iodine oxides by sputter coating samples with Au/Pd2. Feng et al.8 passivated the surface of I2O5 particles with an Fe2O3 coating which prevented water absorption over long durations of exposure to ambient atmosphere. A similar approach could be applied to help stabilize I4O9.
Another way to improve the stability of I4O9 may be new approaches for its synthesis. If the material could be synthesized in a way that prevents introduction of hydrated species, then the topochemical effect that catalyzes water absorption could be inhibited thereby stabilizing the oxidizer. The I4O9 examined here was synthesized using a &#39;dry&#39; process that does not introduce hydrated species and enables analysis of a more stable form of I4O9 powder. Our objective is to analyze the fundamental kinetics associated with I4O9 decomposition and reaction with Al as well as the basic energy propagation behavior of the Al + I4O9 reaction. Reaction kinetics are analyzed using thermal equilibrium diagnostics including differential scanning calorimetry and thermal gravimetric analysis (DSC-TGA). Energy propagation is analyzed using high speed imaging of reaction propagation through a powder mixture upon ignition in a transparent tube. Development of synthesis methods to produce I4O9 and methods to stabilize I4O9 have been slow in comparison to other forms of iodine oxide. A goal of this study is to show that the energy and gas liberated from reactions involving I4O9 are greater than reactions involving other iodine oxides. In this way, future research on synthesis and characterization of I4O9 may be beneficial for many applications.

<table><tbody><tr><td>Iodine pentoxide (Commercial I&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;5&lt;/sub&gt;)</td><td>Sigma Aldrich</td><td>229709</td><td>Commercial I&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;5&lt;/sub&gt;</td></tr><tr><td>Iodic Acid (Commercial HIO&lt;sub&gt;3&lt;/sub&gt;)</td><td>Alfa Aesar</td><td>A11925</td><td>Comercial HIO&lt;sub&gt;3&lt;/sub&gt;</td></tr><tr><td>Tetraiodine nonoxide (I&lt;sub&gt;4&lt;/sub&gt;O&lt;sub&gt;9&lt;/sub&gt;)</td><td>Lynntech Inc</td><td></td><td>synthesized using a dry process</td></tr><tr><td>Water</td><td></td><td></td><td>Local distilled water run through micron filter</td></tr><tr><td>80 nm Aluminum</td><td>NovaCentrix</td><td>AL-80-P</td><td>Nano Aluminum</td></tr><tr><td>Differential Scanning Calorimeter with Thermal Gravimetric Analyzer (DSC-TGA)</td><td>Netzsch</td><td>STA-449</td><td>Equilibrium analysis of heat flow and mass loss</td></tr><tr><td>Sonic Wand</td><td>Misonix</td><td>Sonicator 3000</td><td>Provides ultrasonic waves to aid intermixing of reactant powders</td></tr><tr><td>Phantom High Speed Camera</td><td>Vision Research</td><td>Phantom 2512</td><td>High speed camera for visualzing flame front</td></tr><tr><td>Mass Balance</td><td>Ohaus</td><td>Ohaus Explorer</td><td>Weigh powders with a 0.1 mg resolution up to a 110 g capacity</td></tr></tbody></table>

reaction kinetics and combustion dynamics of i4o9 and aluminum mixtures

Tetraiodine nonoxide (I4O9) has been synthesized using a dry approach that combines elemental oxygen and iodine without the introduction of hydrated species. The synthesis approach inhibits the topochemical effect promoting rapid hydration when exposed to the relative humidity of ambient air. This stable, amorphous, nano-particle material was analyzed using differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA) and showed an exothermic energy release at low temperature (i.e., 180 &#176;C) for the transformation of I4O9 into I2O5. This additional exothermic energy release contributes to an increase in overall reactivity of I4O9 when dry mixed with nano-aluminum (Al) powder, resulting in a minimum of 150% increase in flame speed compared to Al + I2O5. This study shows that as an oxidizer, I4O9 has more reactive potential than other forms of iodine(V) oxide when combined with Al, especially if I4O9 can be passivated to inhibit absorption of water from its surrounding environment.

Figure 1a shows the endothermic and exothermic behavior of the initial states for all six oxidizers examined from DSC analysis and Figure 1b shows the corresponding mass loss from TGA analysis. It is noted that all oxidizers when heated beyond the dissociation temperature of I2O5 (350 &#176;C) lose 100% mass but the I4O9 sample releases I2 gas instead of water liberated by dehydration of hydrated species at temperatures below the dissociation temperature of I2O5. The abundance of I2 gas released from the I4O9 samples is specified in Figure 1b at over 7 wt.%. Figure 1a shows that the only iodine compounds that produce exothermic behavior is I4O9 and I2O5 formed by decomposition of I4O9, and the exotherm corresponds to an onset temperature of about 180 &#176;C for decomposition into I2O5. Figure 1b also shows that the iodine compound with the greatest overall iodine gas generation is I4O9.
There are no endotherms for commercial and amorphous I2O5 samples between 110 &#176;C and 210 &#176;C. This shows that these samples are purely I2O5 with no iodic acids. The nano I2O5 and I4O9 have exotherms with onset temperature at 150 &#176;C. This shows those samples contain I4O96. The nano I2O5 is thermally treated I4O9. The small exotherm at 150 &#176;C shows that there is some residual I4O9 in the nano I2O5 sample. Using the TGA data from Figure 1b, the residual I4O9 in the sample is less than 15 wt.%. The HIO3 dehydrate has a single endotherm starting at 130 &#176;C and indicates this sample is crystalline HIO3. The commercial HIO3 sample has two distinct endotherms starting at 160 &#176;C and 210 &#176;C. An endotherm with an onset temperature of 160 &#176;C is outside of the range of HIO3 dehydration in the CRC handbook16. However, TGA results show a mass loss of 2.47 wt.% over this range indicating it is the dehydration of a hydrated species.
Figure 2a shows the heat flow behavior from DSC analysis of four Al and iodine oxide mixtures. The Al + I4O9 dry mixture has an exotherm at 180 &#176;C indicating the oxidizer is still I4O9 with an increased onset temperature. The Al + I4O9 and Al + nano I2O5 samples are almost identical. Both of these mixtures were processed using isopropanol as the carrier fluid to aid intermixing and identical thermal behavior seen in Figure 2a indicating that mixing powders in isopropanol transformed I4O9 into I2O5.
Figure 2b shows I4O9, I4O9 exposed to 20% RH for 4 hours, and nano I2O5 exposed to 20% RH for 4 hours. After 4 hours exposure to 20% RH, I4O9 is identical to nano I2O5 and there are endotherms at 110 &#176;C and 210 &#176;C showing the samples are partially composed of HIO3 and HI3O8. This may be explained by the I4O9 &#34;dry&#34; synthesis method which is then heated and transformed into I2O5. The crystal structure of I4O9 is not known, but because hydration is observed (Figure 2b bottom two curves with endotherms shaded), the low density of the powder (i.e., fluffy, highly porous nature), and the lack of a reported crystalline structure, an amorphous structure is assumed. Nano I2O5 is formed by thermal decomposition of amorphous I4O9, according to Eq. (1) such that I2 is released from amorphous I4O9 leaving amorphous I2O5. Crystal structure formation of iodine(V) oxides is catalyzed by water. Since the synthesis method is dry, there is no water to catalyze crystal formation. The first step required for absorption of water is to raise the relative humidity to disrupt the bonds between molecules. Without this crystal structure (that wants to release the weakly bonded water) the dynamic equilibrium is shifted so I2O5 will absorb any available water. As soon as water is absorbed by I2O5, formation of HIO3 molecules begin. HIO3 has a hydrogen that attracts oxygen in amorphous I2O5 and creates an HI3O8 crystal structure. Water is still the catalyst in crystal structure formation. The synthesis method of I2O5 and I4O9 which form an amorphous structure instead of a crystalline structure is the reason water absorption is seen at lower RH (i.e., 20%) than what was required to start absorption in previous studies (i.e., 70-80% RH)5,17. In summary, the iodine compounds&#39; amorphous structure may promote absorption of hydrated species and formation of iodic acids.
In Figure 2a the main exotherms around 500 &#176;C are all similar. In the Al + I4O9 dry mix, the exotherm at about 180 &#176;C indicates phase transition from I4O9 to I2O5. Also, all mixtures have a pre-ignition reaction (PIR) between 300 - 400 &#176;C, but Al + I4O9 and Al + nano I2O5 have a PIR with lower onset temperature and greater magnitude but also show unique endotherms followed by exotherms at 210 &#176;C. These samples were processed in isopropanol and the behavior at 210 &#176;C indicates these samples are partially HI3O8. The exotherm may be reaction between HI3O8 and I4O9 because HI3O8 is dissociating at nearly the same temperature as I4O9 decomposition. These reactions may help promote greater exothermicity in the PIR and catalyze earlier onset of the PIR. Osborne and Pantoya 20 first showed an exothermic reaction preceding the main exothermic reaction in Al combustion and coined this a PIR. Their analysis indicated the PIR reaction was between the alumina shell surrounding an aluminum core particle with fluorine from decomposing fluoropolymer19,20. Farley et al.4 then extended observations of the PIR to aluminum-alumina core-shell particles reacting with iodine based oxidizers. The Al + commercial I2O5 sample has an endotherm at 210 &#176;C indicating HI3O8 presence and a mild PIR exotherm with delayed onset temperature. Mulamba et al.21 also showed that the PIR onset temperature is concentration dependent.
Table 1 shows measured flame speed results for Al mixed with the indicated oxidizer as a dry mixture and also mixed using isopropanol as the processing carrier fluid. Only the first three samples were tested after being mixed in isopropanol and the Al + commercial HIO3 dry mix either did not ignite or did not sustain reaction long enough to obtain measureable results. The percent uncertainty is determined based on repeatability of up to three separate experiments for each mixture. Bulk density is determined as a function of mixture powder mass and volume of the tube.
When interpreting reactivity with flame speed measurements, there are many factors that influence results such as homogeneity of the mixture, particle size, and bulk density. Mixture homogeneity can be optimized using a carrier fluid to aid intermixing of the reactants. The I4O9 examined in this study is more stable than previously studied I4O9 samples and did not appear to decompose into I2O5 or form hydrated species seen in Wikjord et al.6 (as seen in Figure 1a with only an exotherm corresponding to I4O9 decomposition). However, the only way to observe the combustion performance of Al + I4O9 is by dry mixing with as little exposure to the atmosphere as possible in order to maintain the integrity of I4O9. Additionally, the flame speed measurements of Al with the oxidizers in different states allowed us to narrow the effects that cause variance in flame speed results and reveal differences attributed specifically to particular iodine compounds. These comparisons will be discussed below. Overall Table 1 shows that I4O9 significantly improves reactivity when compared with other iodine compounds.
Mixing in a carrier fluid provides improved distribution of fuel and oxidizer particles that increases mixture homogeneity and reactivity. This is seen in the difference in flame speeds in Table 1 for the dry and isopropanol mixed Al + nano I2O5 and Al + commercial I2O5 samples where the flame speeds increased by 1.07 and 3.34 times, respectively. Mixture homogeneity implicit from the measured flame speed is only slightly improved for the Al + nano I2O5 mixture, whereas the Al + micron scale commercial I2O5 exhibits a three times increase in flame speed when the carrier fluid aids intermixing. Clearly particle size and carrier fluid contribute to measured flame speed. The homogeneity effects can also be seen by the uncertainty between flame speeds. The samples that are mixed in isopropanol and the samples with smaller particles have less uncertainty in measured flame speeds. This small uncertainty is also seen in all of the amorphous samples, which suggests that an amorphous structure facilitates improved homogeneity in dry mixing. It is further noted that each sample was sieved before dry mixing to break up agglomerates and help eliminate uncertainty caused by poor homogeneity.
The HIO3 molecules have a hydrogen end cap, which is electropositive, and an oxygen end cap, which is electronegative and causes an attraction between the ends of individual HIO3 molecules22. Because of this attraction, during sieving the HIO3 particles instantly agglomerated before the Al can be mixed. This caused extremely poor homogeneity and is the reason Al + commercial HIO3 samples could not sustain the reaction. The Al + HIO3 dehydrate sample had water available to catalyze crystal structure formation (Figure 1a), which reduced, but did not eliminate this effect.
Energy propagation is dependent on the bulk density of the reactant mixture. The density will change based on the concentration of the reactants, so the bulk density of the mixture is usually reported as the percentage of the theoretical maximum density (TMD). The %TMD is calculated using a weighted average of the concentration and the densities of the reactants and accounts for the density of the actual sample according to its mass and volume occupied. In this way, bulk density in terms of %TMD represents the amount of solid space occupied by the volume (i.e., 60% TMD is equivalent to 40% air voids and 60% solids). Low %TMD usually result in higher flame speeds than high %TMD powders. The higher concentration of air voids with lower %TMD provide convective pathways to enhance flame speeds. For this reason, the flame speeds reported in Table 1 are not comparable as a function of mixture, because each was prepared at a discretely different bulk density.
Two conclusions can be drawn from Table 1: (1) I4O9 cannot be processed in isopropanol because it changes into I2O5 and thus alters its reactivity; and (2) I4O9 is more reactive than I2O5 because at higher and lower bulk densities (i.e., 11% TMD compared with 8 or 17% TMD), I4O9 demonstrates increased reactivity. This finding suggests that I4O9 would be advantageous for reactive applications if it could be passivated to improve stability.
Through reactivity and thermal analysis, results show I4O9 can be more reactive than other forms of iodine(V) oxides when combined with aluminum (Al) powder. The I4O9 sample used here was synthesized using a &#39;dry&#39; method that combines elemental oxygen and iodine such that hydrated species are not introduced at any point during synthesis. For this reason, the I4O9 sample is initially devoid of iodic acids and produces a large exotherm at a low temperature (i.e., 180 &#176;C) corresponding to its decomposition into I2O5. The nano-scale I2O5 particles that are created by thermal decomposition of I4O9 are likely amorphous and produce flame speeds over 1,000 m/sec when combined with Al powder (Table 1). The Al + I4O9 reaction produces flame speeds over 1,500 m/sec. This is the first study to explore the potential of I4O9 as an alternative to I2O5 for energy generation technologies, especially motivated by high iodine gas generation.
<img alt="Figure 1" src="/files/ftp_upload/54661/54661fig1.jpg" /> 
Figure 1. DSC Analysis of Heat Flow / TGA Analysis of Mass Loss. a) Heat flow behavior from DSC analysis of six oxidizers and shows different states of iodine(V) oxides used in the range of iodic acid dehydration. b) Mass loss from corresponding TG analysis.
<img alt="Figure 2" src="/files/ftp_upload/54661/54661fig2.jpg" /> 
Figure 2. DSC Analysis of Heat flow. a) Heat flow behavior from DSC analysis for Al + I4O9 dry mix and Al + I4O9, Al + nano I2O5 and Al + commercial I2O5 mixed in isopropanol. Temperature range includes iodic acid dehydration and main reaction temperature range. b) I4O9 initially and I4O9 exposed to 20% RH for 4 hours. Also, the I2O5 was exposed to 20% RH for 4 hours.
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Oxidizer</td>
			<td>Isopropanol Mixed Flame Speed (m/sec)</td>
			<td>% Uncertainty</td>
			<td>Dry Mix Flame Speed</td>
			<td>% Uncertainty</td>
			<td>Bulk Density Dry Mix (g/cm3)</td>
			<td>Dry Mix %TMD</td>
		</tr>
		<tr>
			<td>I4O9</td>
			<td>1,261*</td>
			<td>0.4</td>
			<td>1,551</td>
			<td>3</td>
			<td>0.48</td>
			<td>11.7</td>
		</tr>
		<tr>
			<td>Nano I2O5</td>
			<td>1,146</td>
			<td>4.5</td>
			<td>1,070</td>
			<td>3.7</td>
			<td>0.33</td>
			<td>8</td>
		</tr>
		<tr>
			<td>Commercial I2O5</td>
			<td>719</td>
			<td>5.5</td>
			<td>215</td>
			<td>46.5</td>
			<td>0.93</td>
			<td>22.6</td>
		</tr>
		<tr>
			<td>Amorphous I2O5</td>
			<td>NM</td>
			<td>NM</td>
			<td>1,085</td>
			<td>0.3</td>
			<td>0.73</td>
			<td>17.8</td>
		</tr>
		<tr>
			<td>HIO3 Dehydrate</td>
			<td>NM</td>
			<td>NM</td>
			<td>393</td>
			<td>12</td>
			<td>0.8</td>
			<td>19.3</td>
		</tr>
		<tr>
			<td>Commercial HIO3</td>
			<td>NM</td>
			<td>NM</td>
			<td>NM</td>
			<td>NM</td>
			<td>1.11</td>
			<td>27.1</td>
		</tr>
	</tbody>
</table>
Table 1. Flame Speed Results. Flame speed results for Al + oxidizer indicated in first column. NM indicates not measurable. * Indicates I4O9 was decomposed into I2O5 during mixing.

Watch this Scientific Journal Video about Reaction Kinetics and Combustion Dynamics of I4O9 and Aluminum Mixtures at JoVE.com

Reaction Kinetics and Combustion Dynamics of I4O9 and Aluminum Mixtures

A protocol for measuring flame speeds of a reactive mixture composed of tetraiodine nonoxide (I4O9) and aluminum (Al) is presented. A method for resolving reaction kinetics using differential scanning calorimetry (DSC) is also presented. It was found that I4O9 is 150% more reactive than other iodine(V) oxides.

Reaction Kinetics and Combustion Dynamics of I4O9 and Aluminum Mixtures

Tetraiodine nonoxide (I4O9) has been synthesized using a dry approach that combines elemental oxygen and iodine without the introduction of hydrated ...

reaction-kinetics-combustion-dynamics-i4o9-aluminum

Research

Education

JoVE Journal

JoVE Core

Civil Engineering

Analytical Chemistry

Engineering

Unit 1

Admixtures

Chemical Equilibria

SCIENTISTS IN ACTION

10.8K Views.  Texas Tech University. A protocol for measuring flame speeds of a reactive mixture composed of tetraiodine nonoxide (I4O9) and aluminum (Al) is presented. A method for resolving reaction kinetics using differential scanning calorimetry (DSC) is also presented. It was found that I4O9 is 150% more reactive than other iodine(V) oxides.

Video: Reaction Kinetics and Combustion Dynamics of I4O9 and Aluminum Mixtures

Measurement and Analysis of Atomic Hydrogen and Diatomic Molecular AlO, C2, CN, and TiO Spectra Following Laser-induced Optical Breakdown

In this work, we present time-resolved measurements of atomic and diatomic spectra following laser-induced optical breakdown. A typical LIBS arrangement is used. Here we operate a Nd:YAG laser at a frequency of 10 Hz at the fundamental wavelength of 1,064 nm. The 14 nsec pulses with anenergy of 190 mJ/pulse are focused to a 50 &#181;m spot size to generate a plasma from optical breakdown or laser ablation in air. The microplasma is imaged onto the entrance slit of a 0.6 m spectrometer, and spectra are recorded using an 1,800 grooves/mm grating an intensified linear diode array and optical multichannel analyzer (OMA) or an ICCD. Of interest are Stark-broadened atomic lines of the hydrogen Balmer series to infer electron density. We also elaborate on temperature measurements from diatomic emission spectra of aluminum monoxide (AlO), carbon (C2), cyanogen (CN), and titanium monoxide (TiO).
The experimental procedures include wavelength and sensitivity calibrations. Analysis of the recorded molecular spectra is accomplished by the fitting of data with tabulated line strengths. Furthermore, Monte-Carlo type simulations are performed to estimate the error margins. Time-resolved measurements are essential for the transient plasma commonly encountered in LIBS.

Measurement and Analysis of Atomic Hydrogen and Diatomic Molecular AlO, C2, CN, and TiO Spectra Following Laser-induced Optical Breakdown

Time-resolved atomic and diatomic molecular species are measured using LIBS. The spectra are collected at various time delays following the generation of optical breakdown plasma with Nd:YAG laser radiation&#160;and are analyzed to infer electron density and temperature.

In this work, we present time-resolved measurements of atomic and diatomic spectra following laser-induced optical breakdown. A typical LIBS arrangement ...

Flame Experiments at the Advanced Light Source: New Insights into Soot Formation Processes

The following experimental protocols and the accompanying video are concerned with the flame experiments that are performed at the Chemical Dynamics Beamline of the Advanced Light Source (ALS) of the Lawrence Berkeley National Laboratory1-4. This video demonstrates how the complex chemical structures of laboratory-based model flames are analyzed using flame-sampling mass spectrometry with tunable synchrotron-generated vacuum-ultraviolet (VUV) radiation. This experimental approach combines isomer-resolving capabilities with high sensitivity and a large dynamic range5,6. The first part of the video describes experiments involving burner-stabilized, reduced-pressure (20-80 mbar) laminar premixed flames. A small hydrocarbon fuel was used for the selected flame to demonstrate the general experimental approach. It is shown how species&#8217; profiles are acquired as a function of distance from the burner surface and how the tunability of the VUV photon energy is used advantageously to identify many combustion intermediates based on their ionization energies. For example, this technique has been used to study gas-phase aspects of the soot-formation processes, and the video shows how the resonance-stabilized radicals, such as C3H3, C3H5, and i-C4H5, are identified as important intermediates7. The work has been focused on soot formation processes, and, from the chemical point of view, this process is very intriguing because chemical structures containing millions of carbon atoms are assembled from a fuel molecule possessing only a few carbon atoms in just milliseconds. The second part of the video highlights a new experiment, in which an opposed-flow diffusion flame and synchrotron-based aerosol mass spectrometry are used to study the chemical composition of the combustion-generated soot particles4. The experimental results indicate that the widely accepted H-abstraction-C2H2-addition (HACA) mechanism is not the sole molecular growth process responsible for the formation of the observed large polycyclic aromatic hydrocarbons (PAHs).

Gas sampling from laboratory-scale flames with online analysis of all species by mass spectrometry is a powerful method to investigate the complex mixture of chemical compounds occurring during combustion processes. Coupled with tunable soft ionization via synchrotron-generated vacuum-ultraviolet radiation, this technique provides isomer-resolved information and potentially fragment-free mass spectra.

The following experimental protocols and the accompanying video are concerned with the flame experiments that are performed at the Chemical Dynamics ...

Preparation and Reactivity of Gasless Nanostructured Energetic Materials

High-Energy Ball Milling (HEBM) is a ball milling process where a powder mixture placed in the ball mill is subjected to high-energy collisions from the balls. Among other applications, it is a versatile technique that allows for effective preparation of gasless reactive nanostructured materials with high energy density per volume (Ni+Al, Ta+C, Ti+C). The structural transformations of reactive media, which take place during HEBM, define the reaction mechanism in the produced energetic&#160;composites. Varying the processing conditions permits fine tuning of the milling-induced microstructures of the fabricated composite particles. In turn, the reactivity, i.e., self-ignition temperature, ignition delay time, as well as reaction kinetics, of high energy density materials depends on its microstructure. Analysis of the milling-induced microstructures suggests that the formation of fresh oxygen-free intimate high surface area contacts between the reagents is responsible for the enhancement of their reactivity. This manifests itself in a reduction of ignition temperature and delay time, an increased rate of chemical reaction, and an overall decrease of the effective activation energy of the reaction. The protocol provides a detailed description for the preparation of reactive nanocomposites with tailored microstructure using short-term HEBM method. It also describes a high-speed thermal imaging technique to determine the ignition/combustion characteristics of the energetic materials. The protocol can be adapted to preparation and characterization of a variety of nanostructured energetic composites.

This protocol describes the preparation of gasless nanostructured energetic materials (Ni+Al, Ta+C, Ti+C) using the short-term high-energy ball milling (HEBM) technique. It also describes a high-speed thermal imaging method to study the reactivity of mechanically fabricated nanocomposites. These protocols can be extended to other reactive nanostructured energetic materials.

High-Energy Ball Milling (HEBM) is a ball milling process where a powder mixture placed in the ball mill is subjected to high-energy collisions from the ...

Research and Development of High-performance Explosives

Developmental testing of high explosives for military applications involves small-scale formulation, safety testing, and finally detonation performance tests to verify theoretical calculations. For newly developed formulations, the process begins with small-scale mixes, thermal testing, and impact and friction sensitivity. Only then do subsequent larger scale formulations proceed to detonation testing, which will be covered in this paper. Recent advances in characterization techniques have led to unparalleled precision in the characterization of early-time evolution of detonations. The new technique of Photonic Doppler Velocimetry (PDV) for the measurement of detonation pressure will be shared and compared with traditional fiber-optic detonation velocity and plate-dent calculation of detonation pressure. In particular, the role of aluminum in explosive formulations will be discussed. Recent developments led to the development of explosive formulations that result in reaction of aluminum very early in the detonation product expansion. This enhanced reaction leads to changes in the detonation velocity and pressure due to reaction of the aluminum with oxygen in the expanding gas products.

Developmental testing of high explosives for military applications involves small-scale formulation, safety testing, and finally detonation performance tests to verify theoretical calculations. This paper will share typical development tests associated with the measurement of detonation velocity and detonation pressure.

Developmental testing of high explosives for military applications involves small-scale formulation, safety testing, and finally detonation performance ...

Combustion Characterization and Model Fuel Development for Micro-tubular Flame-assisted Fuel Cells

Combustion based power generation has been accomplished for many years through a number of heat engine systems. Recently, a move towards small scale power generation and micro combustion as well as development in fuel cell research has created new means of power generation that combine solid oxide fuel cells with open flames and combustion exhaust. Instead of relying upon the heat of combustion, these solid oxide fuel cell systems rely on reforming of the fuel via combustion to generate syngas for electrochemical power generation. Procedures were developed to assess the combustion by-products under a wide range of conditions. While theoretical and computational procedures have been developed for assessing fuel-rich combustion exhaust in these applications, experimental techniques have also emerged. The experimental procedures often rely upon a gas chromatograph or mass spectrometer analysis of the flame and exhaust to assess the combustion process as a fuel reformer and means of heat generation. The experimental techniques developed in these areas have been applied anew for the development of the micro-tubular flame-assisted fuel cell. The protocol discussed in this work builds on past techniques to specify a procedure for characterizing fuel-rich combustion exhaust and developing a model fuel-rich combustion exhaust for use in flame-assisted fuel cell testing. The development of the procedure and its applications and limitations are discussed.

A protocol for creating a model fuel-rich combustion exhaust is developed through combustion characterization and is applied for micro-tubular flame-assisted fuel cell testing and research.

Combustion based power generation has been accomplished for many years through a number of heat engine systems. Recently, a move towards small scale power ...

Facile Preparation of Ultrafine Aluminum Hydroxide Particles with or without Mesoporous MCM-41 in Ambient Environments

An aqueous suspension of nanogibbsite was synthesized via the titration of aluminum aqua acid [Al(H2O)6]3+ with L-arginine to pH 4.6. Since the hydrolysis of aqueous aluminum salts is known to produce a wide array of products with a wide range of size distributions, a variety of state-of-the-art instruments (i.e., 27Al/1H NMR, FTIR, ICP-OES, TEM-EDX, XPS, XRD, and BET) were used to characterize the synthesis products and identification of byproducts. The product, which was comprised of nanoparticles (10-30 nm), was isolated using gel permeation chromatography (GPC) column technique. Fourier transform infrared (FTIR) spectroscopy and powder X-ray diffraction (PXRD) identified the purified material as the gibbsite polymorph of aluminum hydroxide. The addition of inorganic salts (e.g., NaCl) induced electrostatic destabilization of the suspension, thereby agglomerating the nanoparticles to yield Al(OH)3 precipitate with large particle sizes. By utilizing the novel synthetic method described here, Al(OH)3 was partially loaded inside the highly ordered mesoporous framework of MCM-41, with average pore dimensions of 2.7 nm, producing an aluminosilicate material with both octahedral and tetrahedral Al (Oh/Td = 1.4). The total Al content, measured using energy-dispersive X-ray spectrometry (EDX), was 11% w/w with a Si/Al molar ratio of 2.9. A comparison of bulk EDX with surface X-ray photoelectron spectroscopy (XPS) elemental analysis provided insight into the distribution of Al within the aluminosilicate material. Furthermore, a higher ratio of Si/Al was observed on the external surface (3.6) as compared to the bulk (2.9). Approximations of O/Al ratios suggest a higher concentration of Al(O)3 and Al(O)4 groups near the core and external surface, respectively. The newly developed synthesis of Al-MCM-41 yields a relatively high Al content while maintaining the integrity of the ordered silica framework and can be used for applications where hydrated or anhydrous Al2O3 nanoparticles are advantageous.

An ultrafine aluminum hydroxide nanoparticle suspension was prepared via the controlled titration of [Al(H2O)]3+ with L-arginine to pH 4.6 with and without cage-effect confinement within mesoporous channels of MCM-41.

An aqueous suspension of nanogibbsite was synthesized via the titration of aluminum aqua acid [Al(H2O)6]3+ with L-arginine to pH 4.6. Since the hydrolysis ...

Chemistry

Nanothermite with Meringue-like Morphology: From Loose Powder to Ultra-porous Objects

The goal of the protocol described in this article is to prepare aluminothermic compositions (nanothermites) in the form of porous, monolithic objects. Nanothermites are combustible materials made up of inorganic fuel and an oxidizer. In nanothermite foams, aluminum is the fuel and aluminum phosphate and tungsten trioxide are the oxidizing moieties. The highest flame propagation velocities (FPVs) in nanothermites are observed in loose powders and FPVs are strongly decreased by pelletizing nanothermite powders. From a physical standpoint, nanothermite loose powders are metastable systems. Their properties can be altered by unintentional compaction induced by shocks or vibrations or by the segregation of particles over time by settling phenomena, which originates from the density differences of their components. Moving from a powder to an object is the challenge that must be overcome to integrate nanothermites in pyrotechnic systems. Nanothermite objects must have both a high open porosity and good mechanical strength. Nanothermite foams meet both of these criteria, and they are prepared by dispersing a nano-sized aluminothermic mixture (Al/WO3) in orthophosphoric acid. The reaction of aluminum with the acid solution gives the AlPO4 &#34;cement&#34; in which Al and WO3 nanoparticles are embedded. In nanothermite foams, aluminum phosphate plays the dual role of binder and oxidizer. This method can be used with tungsten trioxide, which is not altered by the preparation process. It could probably be extended to some oxides, which are commonly used for the preparation of high performance nanothermites. The WO3-based nanothermite foams described in this article are particularly insensitive to impact and friction, which makes them far safer to handle than loose Al/WO3 powder. The fast combustion of these materials has interesting applications in pyrotechnic igniters. Their use in detonators as primers would require the incorporation of a secondary explosive in their composition.

This manuscript describes the synthesis of combustible aluminophosphate matrices by the reaction of orthophosphoric acid (H3PO4) with aluminum nanopowder. When this reaction is carried out with excess aluminum in the presence of tungsten trioxide nanopowder, it leads to a solid, porous nanothermite foam.

The goal of the protocol described in this article is to prepare aluminothermic compositions (nanothermites) in the form of porous, monolithic objects. ...

Combustion Chemistry of Fuels: Quantitative Speciation Data Obtained from an Atmospheric High-temperature Flow Reactor with Coupled Molecular-beam Mass Spectrometer

This manuscript describes a high-temperature flow reactor experiment coupled to the powerful molecular beam mass spectrometry (MBMS) technique. This flexible tool offers a detailed observation of chemical gas-phase kinetics in reacting flows under well-controlled conditions. The vast range of operating conditions available in a laminar flow reactor enables access to extraordinary combustion applications that are typically not achievable by flame experiments. These include rich conditions at high temperatures relevant for gasification processes, the peroxy chemistry governing the low temperature oxidation regime or investigations of complex technical fuels. The presented setup allows measurements of quantitative speciation data for reaction model validation of combustion, gasification and pyrolysis processes, while enabling a systematic general understanding of the reaction chemistry. Validation of kinetic reaction models is generally performed by investigating combustion processes of pure compounds. The flow reactor has been enhanced to be suitable for technical fuels (e.g. multi-component mixtures like Jet A-1) to allow for phenomenological analysis of occurring combustion intermediates like soot precursors or pollutants. The controlled and comparable boundary conditions provided by the experimental design allow for predictions of pollutant formation tendencies. Cold reactants are fed premixed into the reactor that are highly diluted (in around 99 vol% in Ar) in order to suppress self-sustaining combustion reactions. The laminar flowing reactant mixture passes through a known temperature field, while the gas composition is determined at the reactors exhaust as a function of the oven temperature. The flow reactor is operated at atmospheric pressures with temperatures up to 1,800 K. The measurements themselves are performed by decreasing the temperature monotonically at a rate of -200 K/h. With the sensitive MBMS technique, detailed speciation data is acquired and quantified for almost all chemical species in the reactive process, including radical species.

An investigation of the oxidative combustion chemistry of novel biofuels, fuel components, or jet fuels by comparison of quantitative speciation data is presented. The data can be used for kinetic model validation and enables fuel assessment strategies.This manuscript describes the atmospheric high-temperature flow reactor and demonstrates its capabilities.

This manuscript describes a high-temperature flow reactor experiment coupled to the powerful molecular beam mass spectrometry (MBMS) technique. This ...

Identification and Quantification of Decomposition Mechanisms in Lithium-Ion Batteries; Input to Heat Flow Simulation for Modeling Thermal Runaway

The risks and possible accidents related to the normal use of lithium-ion batteries remain a serious concern. In order to get a better understanding of thermal runaway (TR), the exothermic decomposition reactions in anode and cathode were studied, using a Simultaneous Thermal Analysis (STA)/Gas Chromatography-Mass Spectrometry (GC-MS)/Fourier Transform Infrared (FTIR) spectrometer system. These techniques allowed the identification of the reaction mechanisms in each electrode, owing to the analysis of evolved gaseous species, the amount of heat released and mass loss. These results provided insight into the thermal events happening within a broader temperature range than covered in previously published models. This allowed the formulation of an improved thermal model to depict TR. The heat of reaction, activation energy, and frequency factor (thermal triplets) for each major exothermic process at material level were investigated in a Lithium Nickel-Manganese-Cobalt-Oxide (NMC (111))-Graphite battery cell. The results were analyzed, and their kinetics were derived. These data can be used to successfully simulate the experimental heat flow.

This work aims at determining the reaction kinetics of Li-ion battery cathode and anode materials undergoing thermal runaway (TR). Simultaneous Thermal Analysis (STA)/Fourier Transform Infrared (FTIR) spectrometer/Gas Chromatography Mass Spectrometry (GC-MS) were used to reveal thermal events and to detect evolved gases.

The risks and possible accidents related to the normal use of lithium-ion batteries remain a serious concern. In order to get a better understanding of ...

Metal Oxide Heterojunction for Photocatalytic Activities

There is a significant global demand for improvements in synthesis techniques and their optimal characteristics, especially for industrial-scale applications. Sol-gel-based solution combustion synthesis (SG-SCS) is a simple method to produce ordered porous materials. In this regard, Pearson&#39;s hard and soft acids and bases theory assists in selecting host-dopant reactivity to form a proper heterojunction.
The formation of a heterojunction also changes the essential properties of the materials, improving photocatalysis via charge transfer or synergistic activities. A calcination temperature of 500 &#176;C is ideal for this process based on the results of the stability assessment via a differential thermogravimetry ratio analysis (DTG).
The nanoscale dimensions of the nanoparticles (NPs) and nanocomposites (NCs) generated were validated using X-ray diffraction and high-resolution transmission electron microscopy (HRTEM). Furthermore, the scanning electron microscopy micrographs and BET analyses confirmed the porosity nature of the materials. HRTEM, X-ray photoelectron spectroscopy, and energy-dispersive X-ray investigations established the materials composition. The study found that NCs degraded the acid orange 8 (AO8) color more efficiently than bare ZnO.

The development of a heterojunction boosts the photocatalytic activities of solution combustion synthesis, which is a time-/energy-efficient process. Advanced analytical characterization techniques were used in this protocol to evaluate the materials&#39; characteristics, and nanocomposites demonstrated improved acid orange-8 dye degradation.

Reaction Kinetics and Combustion Dynamics of I₄O₉and Aluminum Mixtures

Summary

Explore More Videos

Chapters in this video

Measurement and Analysis of Atomic Hydrogen and Diatomic Molecular AlO, C₂, CN, and TiO Spectra Following Laser-induced Optical Breakdown