This work was supported by the ASEE-NRL postdoctoral fellowship and the Office of Naval Research through the US Naval Research Laboratory's Basic Research Program. The authors thank C. Kindle at NRL for his technical support.

1. Microfabrication of Si Frames
<ol>
	<li>Spin-coat (3,000 rpm and 30 s) SPR220-7 photoresist (PR) on a 180 &#956;m thick Si wafer. Use enough PR to completely coat the wafer. Crystal plane orientation of the wafer is not important.</li>
	<li>Soft bake the wafer with a PR layer (about 7.5 &#181;m thick) at 60 &#176;C for 2 min and then at 115 &#176;C for 90 s on a hot plate.</li>
	<li>Expose the PR layer to ultraviolet light through a patterned chrome/glass photomask that allows light to pass through it to define the Si frame&#39;s shape. Use standard photolithography equipment and processes for this step and the next one (Figure 2a-b).</li>
	<li>Develop the patterns exposed through the photomask by immersing the Si wafer with PR on it in undiluted MF 24A or MF 319 for about 1 minute (Figure 2c). The patterned PR layer serves as a mask during Step 1.6.</li>
	<li>Bond the 180 &#956;m-thick Si wafer to a 500 &#956;m-thick support Si wafer using a low melting point temporary adhesive for easier handling (see Table of Materials for details). Heat adhesive in a glass dish using a hot plate (70 &#176;C) and use just enough adhesive to coat the support wafer. Then lightly press the 180 &#181;m-thick Si wafer onto the 500 &#181;m thick wafer (Figure 2d).</li>
	<li>Etch through the top silicon wafer from above to make free-standing structures. Use any number of commercially available inductively coupled plasma reactive ion etching systems that use the Bosch process with SF6 and C4F8 gases for the etching step. In the Bosch process, alternating cycles of passivation layer deposition and plasma etching result in deeply etched trenches with mostly intact sidewalls) (Figure 2e).
	<ol>
		<li>Start with 3 and 100 sccm flows of SF6 and C4F8 for 5 s during deposition and 100 and 2.5 sccm of SF6 and C4F8 for 7 s during etching, respectively. Tune the instrument-dependent parameters (flow rates, the ratio between gases, and time intervals for deposition and etching steps) as needed.</li>
	</ol>
	</li>
	<li>Every 20 min, measure the depth of the etched trench using a profilometer to calibrate the etch rate that is specific to the instruments and the etching recipe.</li>
	<li>Detach the support Si wafer and clean the thin Si wafer by removing the temporary adhesive and PR using an overnight acetone soak (Figure 2f). Then, rinse the thin wafer thoroughly with deionized (DI) water.</li>
	<li>Deposit an SiO2 insulation layer at 300 &#176;C on both sides of the Si frame using any commercially available plasma-enhanced chemical vapor deposition (PECVD) system with SiH4, N2O, and N2 gases (Figure 2g). Use standard SiO2 deposition recipes, e.g., use 5% SiH4 at 170 sccm and N2O at 710 sccm, to deposit a 2-3 &#956;m thick SiO2 layer.</li>
	<li>Break the tabs connecting individual rectangular Si frames to the surrounding structures. Use sharp tweezers under an optical microscope (Figure 2h).</li>
</ol>
2. Laser Patterning of Metallic Specimens
<ol>
	<li>Cut a 5.0 cm x 5.0 cm piece of copper foil (99.99% purity; see Table of Materials) and adhere it with tape to a glass slide. Spin coat both sides with a 1-&#181;m thick layer of PR. While a foil with a wide range of thickness (up to 100 &#181;m) can be cut by the laser techniques, here use two different thicknesses (13 &#181;m and 25 &#181;m) for demonstration. Use sufficient PR to completely coat the surfaces. Bake the PR at 115 &#176;C for 2 min. The PR is required in order to protect the surface of the copper foil from debris produced during the laser cutting step and to allow chemical etching of the specimen beams (see step 2.4) without affecting the surface of the foil.</li>
	<li>Using a 355 nm, 10 watt, solid-state, frequency tripled Nd:YVO4 pulsed laser at 50 kHz with ~90 ns pulse width, cut an array of 5 by 4 individual specimens, each held by a copper frame 4 mm long by 1 mm wide (Figure 3b).</li>
	<li>Adjust the laser beam to a fluence of 65 mJ/cm2 at the surface of the copper foil. This provides enough laser energy to cut the copper in two passes without excessive heating and/or damage of the adjacent copper. The pattern for each specimen is generated by a Galvo scanning mirror which scans the laser beam to cut the copper foil generating 20 specimens at a time (Figure 3a). Adjust the width of the laser cut specimen beam from 30 &#181;m (for the 13 &#181;m thick foil) to 50 &#181;m (for the 25 &#181;m thick foil).</li>
	<li>Chemically etch the specimen array by immersing it in 40% liquid ferric chloride at 40-60&#160;&#176;C for 30 s (for the 13 &#181;m thick foil) or 40 s (for the 25 &#181;m thick foil) to remove potentially damaged laser-cut edges, reduce the width of the individual specimen beams below 20 &#181;m (Figure 3c), and produce a smooth beam edge profile.</li>
	<li>Remove the protective photoresist by immersing the arrays in separate solvent baths of first acetone, then methanol followed by isopropanol and then dry with nitrogen. Store specimen arrays in a dry nitrogen desiccator. A cross-section schematic of the above fabrication steps is shown in Figure 3d.</li>
	<li>Use the laser to cut a box around the specimen array, releasing it from the rest of the copper foil.</li>
</ol>
3. Assembly and In Situ TEM Experiments
<ol>
	<li>Detach an individual specimen (including its copper frame) using mini-scissors.&#160;Place a small amount of silver epoxy on the silicon frame and carefully align the specimen under an optical microscope so the specimen gauge spans the narrow gap in the center of the frame (Figure 4a).</li>
	<li>Similar to Step 3.1, connect silver wires (50 &#956;m in diameter) to both ends of the specimen by silver epoxy (Figure 5c).</li>
	<li>Use focused ion beam (FIB) milling to create the nanoscale gauge section (100 nm x 10 &#956;m x 10 &#956;m) with multiple shoulders. The progressively thicker cross-sections moving away from the gauge section are meant to produce a smooth transition in current densities, a more uniform current density in the gauge section, and to minimize localized heating at any given shoulder. To minimize damage, use reduced accelerating voltage (5 kV) and current (&#60;80 pA) during the final milling of copper specimens. Measure the cross sectional area of the gauge using scanning electron microscope (SEM) images (Figure 4b-e and 5b).</li>
	<li>Remove the specimen frames by either laser cutting, FIB, or mini-scissors (see inset of Figure 4a). Although not the case in the image, the location of the cut should ideally be away from the gauge section to minimize possible material damage to the gauge section.</li>
	<li>Mount the MEMTS onto a single tilt straining TEM holder (see Table of Materials) under an optical microscope and then attach it by using bolts and nonconductive washers. The washers are used to prevent unwanted torsion during assembly. Use washers (0.5 mm-thick) patterned from a hard fiber electrical grade sheet using a 50 W CO2 laser system (see Table of Materials for specific parameters during laser cutting).</li>
	<li>Connect the silver wires from Step 3.2 to the metallic pins (Figure 5a) on the TEM holder using silver conductive epoxy.</li>
	<li>Using a hand-held or desktop multimeter, check the resistance across the MEMTS (B and C in Figure 1) to verify that the gauge section is not broken. The resistance should be less than 100 &#937;. Also measure the resistance between the MEMTS and the electrically grounded TEM specimen holder to confirm that there is no electrical cross-talk between the specimen and TEM holder. If the specimen is isolated, the measured resistance should be greater than 10 M&#937;.</li>
	<li>Place the TEM holder with the MEMTS into the TEM for in situ experiments.</li>
	<li>Connect an external DC power supply (see Table of Materials) to the built-in electrical feedthroughs in the TEM holder to apply DC input signals to the specimen from outside of the TEM chamber for control of electrical current. Electrical connection locations will depend on TEM holder manufacturers but for this study, the connections were located on the holder handle, and pin connectors were used to apply power from the supply to the TEM specimens. Obtain the nominal current density at the gauge section by dividing input current by the cross-sectional area (obtained from an SEM image in Figure 5b). 
	NOTE: The single tilt straining TEM holder contains a built-in actuator that is controlled by a separate displacement controller (Table of Materials).</li>
	<li>While controlling mechanical and electrical loading, acquire TEM images during the steps that follow. Other strain and current loadings may also be used.</li>
	<li>Apply tensile strain incrementally in small steps depending on the resolution of the built-in piezo actuator (~0.34 nm in this example) until motion of one or many dislocations at the same time are observed. This is a crucial step so that any additional increase in either thermal and/or electrical energy produces additional movement.</li>
	<li>Allow the specimen to equilibrate for one minute.</li>
	<li>Apply an input current density to the specimen. Due to the small cross section, the current should be low enough, even at large current densities, that it will not result in significant temperature rise (<img alt="Equation" src="/files/ftp_upload/55735/55735eq2.jpg" />) in the gauge section. The maximum temperature rise at the center of the gauge section depends on specimen geometry and material properties as discussed below.</li>
	<li>To image a specimen in steady-state condition, keep it under the electron beam for a minute while holding current steady before acquiring images. Allowing the sample to equilibrate in this manner applies after any change in either mechanical or electrical loading.</li>
</ol>

<ol>
	<li>Ross, C. D., Kronenberger, T. J., Roth, J. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+dc+on+the+formability+of+Ti-6Al-4V.">Effect of dc on the formability of Ti-6Al-4V.</a> J Eng Mater-T ASME. 131 (3), 031004 (2009).</li><li>Siopis, M. S., Kinsey, B. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Experimental+investigation+of+grain+and+specimen+size+effects+during+electrical-assisted+forming.">Experimental investigation of grain and specimen size effects during electrical-assisted forming.</a> J Manuf Sci Eng-T ASME. 132 (2), 021004 (2010).</li><li>Green, C. R., McNeal, T. A., Roth, J. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Springback+Elimination+for+Al-6111+Alloys+Using+Electrically+Assisted+Manufacturing+(EAM).">Springback Elimination for Al-6111 Alloys Using Electrically Assisted Manufacturing (EAM).</a> 37th Annual North American Manufacturing Research Conference. 37, 403-410 (2009).</li><li>Okazaki, K., Kagawa, M., Conrad, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+study+of+the+electroplastic+effect+in+metals.">A study of the electroplastic effect in metals.</a> Scr Mater. 12 (11), 1063-1068 (1978).</li><li>Sprecher, A. F., Mannan, S. L., Conrad, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Overview+no.+49.+On+the+mechanisms+for+the+electroplastic+effect+in+metals.">Overview no. 49. On the mechanisms for the electroplastic effect in metals.</a> Acta Metall. 34 (7), 1145-1162 (1986).</li><li>Perkins, T. A., Kronenberger, T. J., Roth, J. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Metallic+forging+using+electrical+flow+as+an+alternative+to+warm/hot+working.">Metallic forging using electrical flow as an alternative to warm/hot working.</a> J Manuf Sci Eng-T ASME. 129 (1), 84-94 (2007).</li><li>Andrawes, J. S., Kronenberger, T. J., Perkins, T. A., Roth, J. T., Warley, R. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effects+of+DC+current+on+the+mechanical+behavior+of+AlMg1SiCu.">Effects of DC current on the mechanical behavior of AlMg1SiCu.</a> Mater Manuf Process. 22 (1), 91-101 (2007).</li><li>Dzialo, C. M., Siopis, M. S., Kinsey, B. L., Weinmann, K. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+current+density+and+zinc+content+during+electrical-assisted+forming+of+copper+alloys.">Effect of current density and zinc content during electrical-assisted forming of copper alloys.</a> CIRP Ann Manuf Techn. 59 (1), 299-302 (2010).</li><li>Fan, R., Magargee, J., Hu, P., Cao, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Influence+of+grain+size+and+grain+boundaries+on+the+thermal+and+mechanical+behavior+of+70/30+brass+under+electrically-assisted+deformation.">Influence of grain size and grain boundaries on the thermal and mechanical behavior of 70/30 brass under electrically-assisted deformation.</a> Mater Sci Eng A. 574, 218-225 (2013).</li><li>Magargee, J., Morestin, F., Cao, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Characterization+of+Flow+Stress+for+Commercially+Pure+Titanium+Subjected+to+Electrically+Assisted+Deformation.">Characterization of Flow Stress for Commercially Pure Titanium Subjected to Electrically Assisted Deformation.</a> J Eng Mater Technol. 135 (4), 041003 (2013).</li><li>Kinsey, B., Cullen, G., Jordan, A., Mates, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Investigation+of+electroplastic+effect+at+high+deformation+rates+for+304SS+and+Ti-6Al-4V.">Investigation of electroplastic effect at high deformation rates for 304SS and Ti-6Al-4V.</a> CIRP Ann - Manuf Technol. 62 (1), 279-282 (2013).</li><li>Williams, D. B., Carter, C. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Transmission electron microscopy. , (2008).</li><li>Kang, W., Beniam, I., Qidwai, S. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+situ+electron+microscopy+studies+of+electromechanical+behavior+in+metals+at+the+nanoscale+using+a+novel+microdevice-based+system.">In situ electron microscopy studies of electromechanical behavior in metals at the nanoscale using a novel microdevice-based system.</a> Rev Sci Instrum. 87 (9), (2016).</li><li>Kim, M. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electric+current-induced+annealing+during+uniaxial+tension+of+aluminum+alloy.">Electric current-induced annealing during uniaxial tension of aluminum alloy.</a> Scr Mater. 75, 58-61 (2014).</li><li>Knowles, M. R. H., Rutterford, G., Karnakis, D., Ferguson, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Micro-machining+of+metals,+ceramics+and+polymers+using+nanosecond+lasers.">Micro-machining of metals, ceramics and polymers using nanosecond lasers.</a> Int J Adv Manuf Tech. 33 (1-2), 95-102 (2007).</li><li>Kang, W., Saif, M. T. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+novel+SiC+MEMS+apparatus+for+in+situ+uniaxial+testing+of+micro/nanomaterials+at+high+temperature.">A novel SiC MEMS apparatus for in situ uniaxial testing of micro/nanomaterials at high temperature.</a> J Micromech Microeng. 21 (10), (2011).</li><li>Callister, W. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Materials Science and Engineering: An Introduction. , (2007).</li><li>Kang, W., Saif, M. T. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+Novel+Method+for+In+Situ+Uniaxial+Tests+at+the+Micro/Nano+Scale-Part+I:+Theory.">A Novel Method for In Situ Uniaxial Tests at the Micro/Nano Scale-Part I: Theory.</a> J Microelectromech Syst. 19 (6), 1309-1321 (2010).</li><li>Kang, W., Han, J. H., Saif, M. T. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+Novel+Method+for+In+Situ+Uniaxial+Tests+at+the+Micro/Nanoscale-Part+II:+Experiment.">A Novel Method for In Situ Uniaxial Tests at the Micro/Nanoscale-Part II: Experiment.</a> J Microelectromech Syst. 19 (6), 1322-1330 (2010).</li><li>Kang, W. M., Saif, M. T. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+Situ+Study+of+Size+and+Temperature+Dependent+Brittle-to-Ductile+Transition+in+Single+Crystal+Silicon.">In Situ Study of Size and Temperature Dependent Brittle-to-Ductile Transition in Single Crystal Silicon.</a> Adv Func Mater. 23 (6), 713-719 (2013).</li><li>Sim, G. D., Vlassak, J. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-temperature+tensile+behavior+of+freestanding+Au+thin+films.">High-temperature tensile behavior of freestanding Au thin films.</a> Scr Mater. 75, 34-37 (2014).</li><li>Haque, M. A., Saif, M. T. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Deformation+mechanisms+in+free-standing+nanoscale+thin+films:+A+quantitative+in+situ+transmission+electron+microscope+study.">Deformation mechanisms in free-standing nanoscale thin films: A quantitative in situ transmission electron microscope study.</a> Proc Natl Acad Sci U S A. 101 (17), 6335-6340 (2004).</li><li>Zhu, Y., Espinosa, H. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+electromechanical+material+testing+system+for+in+situ+electron+microscopy+and+applications.">An electromechanical material testing system for in situ electron microscopy and applications.</a> Proc Natl Acad Sci U S A. 102 (41), 14503-14508 (2005).</li><li>Hosseinian, E., Pierron, O. N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Quantitative+in+situ+TEM+tensile+fatigue+testing+on+nanocrystalline+metallic+ultrathin+films.">Quantitative in situ TEM tensile fatigue testing on nanocrystalline metallic ultrathin films.</a> Nanoscale. 5 (24), 12532-12541 (2013).</li><li>Kang, W., Rajagopalan, J., Saif, M. T. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+Situ+Uniaxial+Mechanical+Testing+of+Small+Scale+Materials-A+Review.">In Situ Uniaxial Mechanical Testing of Small Scale Materials-A Review.</a> Nanosci Nanotechnol Lett. 2 (4), 282-287 (2010).</li><li>Kang, W., Merrill, M., Wheeler, J. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+Situ+Thermomechanical+Testing+Methods+for+Micro/Nano-Scale+Materials.">In Situ Thermomechanical Testing Methods for Micro/Nano-Scale Materials.</a> Nanoscale. , (2016).</li><li>Thompson, K., Gorman, B., Larson, D., Bv Leer, ., Hong, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Minimization+of+Ga+Induced+FIB+Damage+Using+Low+Energy+Clean-up.">Minimization of Ga Induced FIB Damage Using Low Energy Clean-up.</a> Microsc Microanal. 12 (S02), 1736-1737 (2006).</li><li>Mayer, J., Giannuzzi, L. A., Kamino, T., Michael, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=TEM+sample+preparation+and+FIB-induced+damage.">TEM sample preparation and FIB-induced damage.</a> MRS Bulletin. 32 (5), 400-407 (2007).</li></ol>

The authors declare that they have no competing financial interests.

Micro/nanotechnology has offered powerful tools to characterize material behavior in analytical chambers including scanning16,18,19,20,21 and transmission electron microscopes13,22,23,24. Such in situ testing capability is highly attractive to the materials science and engineering community, as fundamental microstructures and underlying deformation mechanisms can be directly observed utilizing high resolution electron microscopy25,26.
Here we have presented a microdevice-based method to investigate coupled electrical and mechanical behavior of material samples utilizing unique advantages of in situ TEM. The steps in this approach require average experience using photolithography, reactive ion etching equipment, electron microscopes, and access to and training on a high-quality laser machining system such as the one used here. Although assembly of specimens and silicon holders is accomplished using simple means: silver epoxy and a basic light microscope, care must be taken so as to not damage the specimen gauge section. This is true at all times when handling the specimen. Care must also be taken during the final FIB milling processes of copper specimens. Reducing accelerating voltage (5 kV) and current (&#60;80 pA)27 during the final polishing will reduce possible specimen damage28 and produce a smooth, defect-free gauge section. Another important item to remember is to check that the specimen in electrically isolated from the TEM holder to ensure that the applied current passes through the gauge section once the experiment begins.
The wafer etching process includes some steps that are critical to fabricate a good frame for the EAD specimen. Temporarily bonding the 500 &#181;m supporting wafer to the 180 &#181;m wafer with a uniform temporary adhesive coating between the wafers is important, not only to aid in handling the fragile etched wafer, but the support wafer also facilitates heat transfer during the plasma etching process. Insufficient heat transfer may result in etching of the PR mask and subsequent non-target etching of the silicon frame. It is also important to periodically measure etched trench depth. The thinner top silicon wafer must be completely etched through but there should be minimal etching to the support wafer so that it can act as a uniform heat sink to the thinner wafer. Finally, it is important to thoroughly clean the etched wafer with acetone followed by DI water rinse prior to SiO2 deposition to minimize any remaining residues.
The EAD experimental images shown here are representative of what can be expected but modifications can be made to resolution, dosage, and the frame rate to allow better observation and quantification of dislocations. Also, image processing software can be utilized to analyze a series of TEM images with enhanced resolution.
The MEMTS offers several unique advantages for studying electromechanical material behavior. This system enables direct observation of nanoscale phenomena that govern macroscale material deformations under electromechanical loading. Secondly, the specimen gauge sections with small cross-section provides the ability to apply substantial electric current densities using a low current magnitude, thereby removing safety concerns inherent with using high power instruments. For example, applying a current density of 1,000 A/mm2 to a 1 mm2 gauge section would require 1 kA compared to only 1 mA if the gauge cross-section were reduced to 1 &#181;m2. More importantly, using a lower current aids in thermal management. The MEMTS is also unique in that its alignment and assembly do not require expensive equipment and are not time-intensive compared to other microdevice-based assembly methods.
The method described here lends itself well to electromechanical testing of metals, ceramics, and polymers, but it also can be used to explore the microstructure-dependent electromechanical behavior within each of those material classes. For example, the impact of single- and poly-crystallinity, grain orientation, grain size, phase distribution, and defect density on electromechanical behavior could be investigated by preparing representative samples. Insights gained from such a comprehensive study could provide the understanding needed to further understand the EAD driving mechanism(s) and advance EAD manufacturing capabilities. Speaking more broadly, the MEMTS might be a useful platform for studying other devices which utilize a thermoelectric coupling. For example, it could be used to observe materials used in thermoelectric coolers, which convert an applied voltage to a temperature difference via the Seebeck effect.
Although experiments performed using the process outlined here have yet to show electrically assisted deformation occurs in the absence of significant Joule heating, further experiments are needed. The process described here utilized a small set of experimental conditions and focused on a localized region. A more comprehensive set of experiments using multiple materials, current densities, and time scales is needed to more conclusively verify the existence or absence of purely electrical effects in EAD. One technical limitation of the current MEMTS approach is lack of a capability to quantify force acting on a specimen during in situ experiments. The force measure is essential to obtain stress-strain data (e.g. to quantitatively identify when the specimen has reached flow stress) and, when combined with in situ observations, directly provides microstructure-property relations. Towards this unique research opportunity, we are currently working on modifying Si frames to incorporate integrated force sensors.

Electrically assisted deformation (EAD) is a useful tool for metal deformation processes such as forging, stamping, extruding, etc. The EAD process involves applying an electric current through a metal workpiece during deformation, significantly improving metal formability by reducing flow stresses, increasing strains-to-failure, and sometimes eliminating springback after forming1,2,3. Despite its growth in use, there is not a consensus regarding the mechanism by which EAD improves metal formability. This paper describes sample preparation and test procedure for an experiment in which it is possible to isolate potentially competing EAD mechanisms and to enable in situ microstructural examination during testing.
There are two hypotheses for EAD&#39;s effect on metal forming. The first hypothesis, the Joule heating effect, states that the applied current encounters electrical resistance in the forming metal, causing the temperature to increase and leading to material softening and expansion. A second hypothesis is referred to as electroplasticity, in which the electrical current increases deformation by lowering the dislocation activation energy. Both of these hypotheses arose from experiments in the 1970s involving short-duration current pulses applied to mechanically deforming metals4,5. More recent studies typically involve lower-amperage DC pulses, which are more relevant for manufacturing applications, but researchers continue to disagree in their interpretation of EAD data.
Interpreting EAD data is difficult due to the highly-coupled nature of applied electric current and increasing thermal energy. Even small current densities in highly conductive metals can significantly raise material temperature; e.g., 130-240 &#176;C with a current density of 33-120 A/mm2 for various aluminum and copper alloys6,7,8,9. This temperature change can significantly affect elastic modulus, yield strength, and flow stress, making it challenging to distinguish between thermal and electroplasticity effects. Highlighting this difficulty, recent studies can be found supporting either the Joule heating hypothesis or the electroplasticity hypothesis. For example, studying electro-mechanical deformation in various alloys of aluminum, copper, and titanium, researchers have reported that electroplasticity contributed to enhanced deformation because the effect could not be explained by Joule heating alone1,6,7. Contrasting those reports are studies that attribute EAD stress reduction in titanium, stainless steel, and Ti-6Al-4V to thermal effects10,11.
Thermal management is not specific to EAD research but, rather, is a general concern when investigating electromechanical material properties. Especially in large specimens, where the center of mass is deeply insulated from its surrounding, maintaining a uniform temperature can be challenging. Another electromechanical testing challenge related to specimen size is the ability to perform in situ and real-time observations of fundamental microstructural changes related to electromechanical stress. In situ TEM mechanical testing is routinely performed on standard test specimens12 but the samples&#39; non-uniform cross-section would create geometry-dependent variations in current density and heat transfer near the gauge section. To summarize, the principal challenges in observing and interpreting EAD mechanisms are related to specimen size and can be summarized as follows: 1) thermoelectric coupling influences specimen temperature making it difficult to isolate a single proposed EAD mechanism and 2) standard test samples and procedures do not exist for an in situ, real-time study of a material in tension under an applied electric current. Surmounting these challenges is possible by performing EAD experiments on a specimen with an ultra-low volume gauge section in a transmission electron microscope (TEM) while controlling electrical current, mechanical loading, and temperature.
In this paper, we describe the sample preparation and testing procedure for an EAD experiment in which Joule heating effects are made negligible by utilizing a specimen structure with a micro/nanoscale gauge section (10 &#956;m x 10 &#956;m x 100 nm) attached to a larger stabilizing support frame. Through analytical and numerical modeling, it has been shown13 that under this configuration, even high current densities (~3,500 A/mm2) resulted in very little increase of the specimen&#39;s temperature (&#60;0.02 &#176;C). A three-dimensional schematic of the microdevice-based electromechanical testing system (MEMTS) is shown in Figure 1. Another important advantage to the method presented here is that rather than examining samples post-test, as is often done14, the specimen structure and support frame are designed to fit directly into a transmission electron microscope (TEM) sample holder outfitted with the capability of applying both electrical and mechanical loads simultaneously. This setup enables real-time in situ observation of material deformation at nano- to atomic-level resolution. Although single crystal copper specimens are used for the procedure outlined herein, the method is sufficiently flexible to be applied to other material specimens including metals, ceramics, and polymers15,16.

<table><tbody><tr><td>Silicon wafers</td><td></td><td></td><td>Any high-quality polished wafers of the correct thickness will work</td></tr><tr><td>Photoresist</td><td>Dow</td><td>SR220-7</td><td></td></tr><tr><td>Photoresist developer</td><td>Shipley</td><td>MF 24A</td><td></td></tr><tr><td>Photoresist developer</td><td>Rohm and Haas</td><td>MF 319</td><td></td></tr><tr><td>Temporary wafer adhesive</td><td></td><td>Crystalbond 509</td><td>Available from a variety of sources</td></tr><tr><td>Iductively Coupled Plasma Reactive Ion Etching (CP-RIE) system</td><td>Oxford</td><td>Plasmalab system 100 ICP RIE</td><td></td></tr><tr><td>Profilometer</td><td>Veeco</td><td>Dektak 150</td><td></td></tr><tr><td>Plasma-Enhanced Chemical Vapor Deposition (PECVD) system</td><td>Oxford</td><td>Plasmalab system 100 PECVD</td><td></td></tr><tr><td>Thin specimen sheet</td><td>Surepure Chemetals</td><td>3702, 3703, 3704 or 2236</td><td>13 &amp;micro;m and 25 &amp;micro;m-thick copper, 99.99% 4N Pure</td></tr><tr><td>Photoresist</td><td>Shipley</td><td>1818</td><td></td></tr><tr><td>355 nm, 10 W, solid-state, frequency tripled Nd:YVO&lt;sub&gt;4&lt;/sub&gt; pulsed laser</td><td>JDSU</td><td>Q301-HD</td><td></td></tr><tr><td>Liquid ferric chloride</td><td>Sigma-Aldrich</td><td>157740</td><td></td></tr><tr><td>Conductive silver epoxy</td><td>Chemtronics</td><td>CW2400</td><td></td></tr><tr><td>Silver wires</td><td></td><td></td><td>Any highly conductive metallic wires will work (&amp;lt;100 &amp;micro;m in diameter)</td></tr><tr><td>Focused Ion Beam (FIB)</td><td>FEI</td><td>Nova 600</td><td></td></tr><tr><td>Single tilt straining TEM holder</td><td>Gatan</td><td>654</td><td></td></tr><tr><td>Displacement controller</td><td>Gatan</td><td>902 Accutroller</td><td>May be sold with the TEM holder</td></tr><tr><td>CO&lt;sub&gt;2&lt;/sub&gt; laser cutter</td><td>Universal Laser Systems</td><td>VLS 3.50</td><td>Use 50% power and 15% speed</td></tr><tr><td>Electrical insulation sheet</td><td></td><td>0.5 mm-thick Hard Fiber Electrical Grade Sheet (Fishpaper)</td><td>Available from a variety of sources</td></tr><tr><td>Transmission Electron Microscope (TEM)</td><td>FEI</td><td>Tecnai G2</td><td></td></tr><tr><td>External power supply</td><td>Keithley</td><td>2400 SourceMeter</td><td></td></tr></tbody></table>

a novel method for in situ electromechanical characterization of nanoscale specimens

Electrically assisted deformation (EAD) is increasingly being used to improve the formability of metals during processes such as sheet metal rolling and forging. Adoption of this technique is proceeding despite disagreement concerning the underlying mechanism responsible for EAD. The experimental procedure described herein enables a more explicit study compared to previous EAD research by removing thermal effects, which are responsible for disagreement in interpreting previous EAD results. Furthermore, as the procedure described here enables EAD observation in situ and in real time in a transmission electron microscope (TEM), it is superior to existing post-mortem methods that observe EAD effects post-test. Test samples consist of a single crystal copper (SCC) foil having a free-standing tensile test section of nanoscale thickness, fabricated using a combination of laser and ion beam milling. The SCC is mounted to an etched silicon base that provides mechanical support and electrical isolation while serving as a heat sink. Using this geometry, even at high current density (~3,500 A/mm2), the test section experiences a negligible temperature increase (&#60;0.02 &#176;C), thus eliminating Joule heating effects. Monitoring material deformation and identifying the corresponding changes to microstructures, e.g. dislocations, are accomplished by acquiring and analyzing a series of TEM images. Our sample preparation and in situ experiment procedures are robust and versatile as they can be readily utilized to test materials with different microstructures, e.g., single and polycrystalline copper.

Preparing and testing as described above should result in a specimen that fractures at its gauge, similar to the single crystal copper (SCC) specimen shown in Figure 6a. Mechanical failure should be accompanied by a large increase in the resistance, confirming that the SCC specimen is electrically isolated by the insulated washers and oxide-coated silicon frame. Plane dislocations in the specimen should be observed using the TEM&#39;s bright field mode focused near a zone axis. By gradually increasing strain until reaching the flow stress (the post-yield equilibrium state), dislocation motions should be visible (Figure 6b). With additional strain and/or applied current, the corresponding dislocation motions can be continuously monitored.
Figure 7 shows representative images during an EAD experiment on an SCC specimen13. After straining the specimen to its post-yield equilibrium state, additional strain was applied without applying any current (see Figure 7b1). This resulted in a new dislocation loop (or possibly a second dislocation gliding), as indicated by the arrow in Figure 7b2. Without modifying the strain, a current density of 500 A/mm2 was then applied but this did not produce noticeable motion in any dislocation (Figure 7b3). The current was removed, the specimen was held constant for one minute, and the strain was increased again, once again producing noticeable changes to the dislocation loop indicated by the arrow in Figure 7b4. This result illustrates the potential for this procedure to isolate thermal and electric effects involved in electrically assisted deformation. Experiments involving higher current densities (up to 5 kA/mm2) have also been performed using this technique, yielding similar results&#8212;no observable additional dislocation motion in the absence of additional strain. Using higher current densities emphasizes the ability of this technique to remove thermal stresses caused by Joule heating, which have complicated previous EAD datasets.
Considering the small size of the sample gauge section, choosing a high-quality material is of paramount importance. For example, microscale material defects, e.g., voids, near a gauge section would result in catastrophic failure of a specimen during material preparation (Figure 4g). This is particularly challenging as it is difficult to know if there are unseen material defects in the gauge section without performing additional non-destructive testing, such as X-ray diffraction topography.
Another key challenge is possible surface damage during laser or focused ion milling including Ga-ion implantation, ion beam-induced dislocations, and formation of amorphous structures from laser-induced heating. The majority of surface artifacts can be removed by utilizing a gentle FIB milling process (Step 3.3). However use of this microfabrication techniques still requires careful consideration as these surface defects could alter microstructures of the specimen and greatly influence EAD experimental results. In our work, we utilized high resolution TEM images and diffraction patterns to confirm that our specimens were indeed pristine single crystal copper Figure 6c.
It is worth noting that the maximum temperature rise at the center of the gauge section can be calculated using the following equation13: <img alt="Equation" src="/files/ftp_upload/55735/55735eq3.jpg" /> where <img alt="Equation" src="/files/ftp_upload/55735/55735eq4.jpg" /> is the current density, <img alt="Equation" src="/files/ftp_upload/55735/55735eq5.jpg" /> is the gauge section length, <img alt="Equation" src="/files/ftp_upload/55735/55735eq6.jpg" /> is electrical resistivity, and <img alt="Equation" src="/files/ftp_upload/55735/55735eq7.jpg" /> is the thermal conductivity. The equation indicates that the temperature increase in the gauge section is very sensitive to <img alt="Equation" src="/files/ftp_upload/55735/55735eq8.jpg" /> as the maximum specimen temperature rise is directly related to the square of the gauge length. For instance, increasing the gauge section length by an order of magnitude, from 10 &#181;m (used in the present study) to 100 &#181;m, would have increased the temperature rise by two orders of magnitude. Instead of a temperature rise of ~0.02 &#176;C, the temperature would have increased by ~2 &#176;C and that would likely have made a significant difference in this study. In addition, material choice also affects the temperature rise. Copper used in this study has relatively low electrical resistive and high thermal conductive coefficients and, as a result, for a given current density an expected temperature rise in a copper specimen would be much smaller compared to other material specimens. As an example, platinum has 6 times larger resistivity and 5 times smaller conductivity17 compared to copper and, as a result, much larger temperature rise (about 30 times) is expected for a platinum case when the gauge length and given current density are the same.
<img alt="Figure 1" src="/files/ftp_upload/55735/55735fig1.jpg" /> 
Figure 1: The microdevice-based electromechanical testing system (MEMTS). This image is a three-dimensional (3D) schematic showing the important components and how specimens fit into the TEM holder. Only the wires connecting the specimen to the pins on the TEM holder are not shown. <a href="http://cloudflare.jove.com/files/ftp_upload/55735/55735fig1large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 2" src="/files/ftp_upload/55735/55735fig2.jpg" /> 
Figure 2: Silicon frame fabrication process. A bare Si wafer (a) is spin-coated with photoresist (b), which is then patterned using photolithography. The exposed photoresist is developed away to expose the underlying Si wafer (c). The wafer is temporarily bonded to a thicker support wafer and reactive ion etching (RIE) is used to etch through the thinner top wafer (d-e). Acetone is used to remove the photoresist and to detach the support wafer (f). A silicon oxide layer is then deposited on all surface of the etched wafer (g). Finally, individual frames are separated from the wafer by carefully pulling them free of their support tabs (h). <a href="http://cloudflare.jove.com/files/ftp_upload/55735/55735fig2large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 3" src="/files/ftp_upload/55735/55735fig3.jpg" /> 
Figure 3: Metallic specimen fabrication. Optical images of (a) an array of copper specimens (b) an individual specimen, and (c) zoom-in view of a gauge section. Fabrication process steps are shown in (d), which is a cross-section along A---A in (b). Both sides of a thin foil are coated with photoresist to protect the sample during laser cutting (d, top). Structures are laser machined (d, second) and then etched to produce smooth edges (d, third). Many specimens can be produced from a single fabrication run as shown in (a). Finally, the photoresist is stripped and individual specimens are gently removed from the specimen sheet (d, bottom). <a href="http://cloudflare.jove.com/files/ftp_upload/55735/55735fig3large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 4" src="/files/ftp_upload/55735/55735fig4.jpg" /> 
Figure 4: Focused ion beam (FIB) milling images. Image (a) shows the specimen attached to the Si frame and a close-up view (inset) of the specimen support after it was laser-cut. Images (b)-(e) show the gauge section becoming progressively thinner during successive FIB passes. Each pass removes less material to improve surface finish and decrease material property changes due to the milling process. However, it is possible for gauge section defects to remain (f), which can result in material failure even before any strain is applied (g). <a href="http://cloudflare.jove.com/files/ftp_upload/55735/55735fig4large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 5" src="/files/ftp_upload/55735/55735fig5.jpg" /> 
Figure 5: Specimen mounted in a TEM holder. (a) and (b) show an assembled specimen in a TEM holder and final dimension of the gauge section with smooth surfaces using gentle FIB milling. Once the specimen is bonded to the Si frame and silver wires are attached using conductive epoxy (c), the two circular holes in the Si frame are used to mount the specimen in the TEM holder. Nonconductive washers are used to insulate the specimen from the TEM holder. Finally, the silver wires are attached to the TEM holder pins using conductive epoxy. Modified13, with the permission of AIP Publishing. <a href="http://cloudflare.jove.com/files/ftp_upload/55735/55735fig5large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 6" src="/files/ftp_upload/55735/55735fig6.jpg" /> 
Figure 6: A representative Single crystal copper (SSC) specimen. (a) shows the gauge section (location A from Figure 1) taken after failure of the gauge section. (b) is a bright field image of the gauge section showing plane dislocations. (c) shows the diffraction pattern at the gauge section. Modified13, with the permission of AIP Publishing. <a href="http://cloudflare.jove.com/files/ftp_upload/55735/55735fig6large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 7" src="/files/ftp_upload/55735/55735fig7.jpg" /> 
Figure 7: In situ EAD experimental TEM images. These images reveal mechanical and electrical loading effects on the dislocation motion. (b1)-(b4) show the zoom-in view of Area (b) in (a). (b1) shows the specimen in a post-yield equilibrium state. (b2) identifies dislocation loop formation resulting from additional strain beyond the state shown in (b1). No changes were observed when current was applied (b3). Once strain was increased again, further dislocation changes were again noticed (b4). Reprinted13, with the permission of AIP Publishing. <a href="http://cloudflare.jove.com/files/ftp_upload/55735/55735fig7large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>

Watch this Scientific Journal Video about A Novel Method for In Situ Electromechanical Characterization of Nanoscale Specimens at JoVE.com

A Novel Method for In Situ Electromechanical Characterization of Nanoscale Specimens

Isolating electrical and thermal effects on electrically assisted deformation (EAD) is very difficult using macroscopic samples. Metallic sample micro- and nanostructures together with a custom test procedure have been developed to evaluate the impact of applied current on the formation without joule heating and evolution of dislocations on these samples.

A Novel Method for In Situ Electromechanical Characterization of Nanoscale Specimens

Electrically assisted deformation (EAD) is increasingly being used to improve the formability of metals during processes such as sheet metal rolling and ...

a-novel-method-for-situ-electromechanical-characterization-nanoscale

Research

JoVE Journal

Engineering

9.1K Views.  US Naval Research Laboratory. Isolating electrical and thermal effects on electrically assisted deformation (EAD) is very difficult using macroscopic samples. Metallic sample micro- and nanostructures together with a custom test procedure have been developed to evaluate the impact of applied current on the formation without joule heating and evolution of dislocations on these samples.

Video: A Novel Method for In Situ Electromechanical Characterization of Nanoscale Specimens

Quantitative and Qualitative Examination of Particle-particle Interactions Using Colloidal Probe Nanoscopy

Colloidal Probe Nanoscopy (CPN), the study of the nano-scale interactive forces between a specifically prepared colloidal probe and any chosen substrate using the Atomic Force Microscope (AFM), can provide key insights into physical interactions present within colloidal systems. Colloidal systems are widely existent in several applications including, pharmaceuticals, foods, paints, paper, soil and minerals, detergents, printing and much more.1-3 Furthermore, colloids can exist in many states such as emulsions, foams and suspensions. Using colloidal probe nanoscopy one can obtain key information on the adhesive properties, binding energies and even gain insight into the physical stability and coagulation kinetics of the colloids present within. Additionally, colloidal probe nanoscopy can be used with biological cells to aid in drug discovery and formulation development. In this paper we describe a method for conducting colloidal probe nanoscopy, discuss key factors that are important to consider during the measurement, and show that both quantitative and qualitative data that can be obtained from such measurements.

Colloidal probe nanoscopy can be used within a variety of fields to gain insight into the physical stability and coagulation kinetics of colloidal systems and aid in drug discovery and formulation sciences using biological systems. The method described within provides a quantitative and qualitative means to study such systems.

Colloidal Probe Nanoscopy (CPN), the study of the nano-scale interactive forces between a specifically prepared colloidal probe and any chosen substrate ...

Chemistry

Remote Magnetic Actuation of Micrometric Probes for in situ 3D Mapping of Bacterial Biofilm Physical Properties

Bacterial adhesion and growth on interfaces lead to the formation of three-dimensional heterogeneous structures so-called biofilms. The cells dwelling in these structures are held together by physical interactions mediated by a network of extracellular polymeric substances. Bacterial biofilms impact many human activities and the understanding of their properties is crucial for a better control of their development &#8212; maintenance or eradication &#8212; depending on their adverse or beneficial outcome. This paper describes a novel methodology aiming to measure in situ the local physical properties of the biofilm that had been, until now, examined only from a macroscopic and homogeneous material perspective. The experiment described here&#160;involves introducing magnetic particles into a growing biofilm to seed local probes that can be remotely actuated without disturbing the structural properties of the biofilm. Dedicated magnetic tweezers were developed to exert a defined force on each particle embedded in the biofilm. The setup is mounted on the stage of a microscope to enable the&#160;recording of time-lapse images of the particle-pulling period. The particle trajectories are then extracted from the pulling sequence and the local viscoelastic parameters are derived from each particle displacement curve, thereby providing the 3D-spatial distribution of the parameters. Gaining insights into the biofilm mechanical profile is essential from an engineer&#39;s point of view for biofilm control purposes but also from a fundamental perspective to clarify the relationship between the architectural properties and the specific biology of these structures.

Remote Magnetic Actuation of Micrometric Probes for in situ 3D Mapping of Bacterial Biofilm Physical Properties

This paper shows an original methodology based on the remote actuation of magnetic particles seeded in a bacterial biofilm and the development of dedicated magnetic tweezers to measure in situ the local mechanical properties of the complex living material built by micro-organisms at interfaces.

Bacterial adhesion and growth on interfaces lead to the formation of three-dimensional heterogeneous structures so-called biofilms. The cells dwelling in ...

Bioengineering

Characterization Of Multi-layered Fish Scales (Atractosteus spatula) Using Nanoindentation, X-ray CT, FTIR, and SEM

The hierarchical architecture of protective biological materials such as mineralized fish scales, gastropod shells, ram&#8217;s horn, antlers, and turtle shells provides unique design principles with potentials for guiding the design of protective materials and systems in the future. Understanding the structure-property relationships for these material systems at the microscale and nanoscale where failure initiates is essential. Currently, experimental techniques such as nanoindentation, X-ray CT, and SEM provide researchers with a way to correlate the mechanical behavior with hierarchical microstructures of these material systems1-6. However, a well-defined standard procedure for specimen preparation of mineralized biomaterials is not currently available. In this study, the methods for probing spatially correlated chemical, structural, and mechanical properties of the multilayered scale of A. spatula using nanoindentation, FTIR, SEM, with energy-dispersive X-ray (EDX) microanalysis, and X-ray CT are presented.

Characterization Of Multi-layered Fish Scales Atractosteus spatula Using Nanoindentation, X-ray CT, FTIR, and SEM

This paper presents the methods used for probing spatially correlated chemical, structural, and mechanical properties of the multilayered scale of Atractosteus spatula (A. spatula) using nanoindentation, Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), and X-ray computed tomography (X-ray CT). The experimental results have been used to investigate the design principles of protective biological materials.

The hierarchical architecture of protective biological materials such as mineralized fish scales, gastropod shells, ram&#8217;s horn, antlers, and turtle ...

A Standard and Reliable Method to Fabricate Two-Dimensional Nanoelectronics

Two-dimensional (2D) materials have attracted huge attention due to their unique properties and potential applications. Since wafer scale synthesis of 2D materials is still in nascent stages, scientists cannot fully rely on traditional semiconductor techniques for related research. Delicate processes from locating the materials to electrode definition need to be well controlled. In this article, a universal fabrication protocol required in manufacturing nanoscale electronics, such as 2D quasi-heterojunction bipolar transistors (Q-HBT), and 2D back-gated transistors are demonstrated. This protocol includes the determination of material position, electron beam lithography (EBL), metal electrode definition, et al. A step by step narrative of the fabrication procedures for these devices are also presented. Furthermore, results show that each of the fabricated devices has achieved high performance with high repeatability. This work reveals a comprehensive description of process flow for preparing 2D nano-electronics, enables the research groups to access this information, and pave the way toward future electronics.

The article aims to introduce a standard and reliable fabrication procedure for the development of future low dimensional nanoelectronics.

Two-dimensional (2D) materials have attracted huge attention due to their unique properties and potential applications. Since wafer scale synthesis of 2D ...

Probing Surface Electrochemical Activity of Nanomaterials using a Hybrid Atomic Force Microscope-Scanning Electrochemical Microscope (AFM-SECM)

Scanning electrochemical microscopy (SECM) is used to measure the local electrochemical behavior of liquid/solid, liquid/gas and liquid/liquid interfaces. Atomic force microscopy (AFM) is a versatile tool to characterize micro- and nanostructure in terms of topography and mechanical properties. However, conventional SECM or AFM provides limited laterally resolved information on electrical or electrochemical properties at nanoscale. For instance, the activity of a nanomaterial surface at crystal facet levels is difficult to resolve by conventional electrochemistry methods. This paper reports the application of a combination of AFM and SECM, namely, AFM-SECM, to probe nanoscale surface electrochemical activity while acquiring high-resolution topographical data. Such measurements are critical to understanding the relationship between nanostructure and reaction activity, which is relevant to a wide range of applications in material science, life science and chemical processes. The versatility of the combined AFM-SECM is demonstrated by mapping topographical and electrochemical properties of faceted nanoparticles (NPs) and nanobubbles (NBs), respectively. Compared to previously reported SECM imaging of nanostructures, this AFM-SECM enables quantitative assessment of local surface activity or reactivity with higher resolution of surface mapping.

Probing Surface Electrochemical Activity of Nanomaterials using a Hybrid Atomic Force Microscope-Scanning Electrochemical Microscope AFM-SECM

Atomic force microscopy (AFM) combined with scanning electrochemical microscopy (SECM), namely, AFM-SECM, can be used to simultaneously acquire high-resolution topographical and electrochemical information on material surfaces at nanoscale. Such information is critical to understanding heterogeneous properties (e.g., reactivity, defects, and reaction sites) on local surfaces of nanomaterials, electrodes and biomaterials.

Scanning electrochemical microscopy (SECM) is used to measure the local electrochemical behavior of liquid/solid, liquid/gas and liquid/liquid interfaces. ...

Micromechanical Tension Testing of Additively Manufactured 17-4 PH Stainless Steel Specimens

This study presents a methodology for the rapid fabrication and micro-tensile testing of additively manufactured (AM) 17-4PH stainless steels by combining photolithography, wet-etching, focused ion beam (FIB) milling, and modified nanoindentation. Detailed procedures for proper sample surface preparation, photo-resist placement, etchant preparation, and FIB sequencing are described herein to allow for high throughput (rapid) specimen fabrication from bulk AM 17-4PH stainless steel volumes. Additionally, procedures for the nano-indenter tip modification to allow tensile testing are presented and a representative micro specimen is fabricated and tested to failure in tension. Tensile-grip-to-specimen alignment and sample engagement were the main challenges of the micro-tensile testing; however, by reducing the indenter tip dimensions, alignment and engagement between the tensile grip and specimen were improved. Results from the representative micro-scale in situ SEM tensile test indicate a single slip plane specimen fracture (typical of a ductile single crystal failure), differing from macro-scale AM 17-4PH post-yield tensile behavior.

Presented here is a procedure for measuring fundamental material properties through micromechanical tension testing. Described are the methods for micro-tensile specimen fabrication (allowing rapid micro-specimen fabrication from bulk material volumes by combining photolithography, chemical etching, and focused ion beam milling), indenter tip modification, and micromechanical tension testing (including an example).

This study presents a methodology for the rapid fabrication and micro-tensile testing of additively manufactured (AM) 17-4PH stainless steels by combining ...

Optimizing Magnetic Force Microscopy Resolution and Sensitivity to Visualize Nanoscale Magnetic Domains

Magnetic force microscopy (MFM) enables mapping local magnetic fields across a sample surface with nanoscale resolution. To perform MFM, an atomic force microscopy (AFM) probe whose tip has been magnetized vertically (i.e., perpendicular to the probe cantilever) is oscillated at a fixed height above the sample surface. The resultant shifts in the oscillation phase or frequency, which are proportional to the magnitude and sign of the vertical magnetic force gradient at each pixel location, are then tracked and mapped. Although the spatial resolution and sensitivity of the technique increases with decreasing lift height above the surface, this seemingly straightforward path to improved MFM images is complicated by considerations such as minimizing topographical artifacts due to shorter range van der Waals forces, increasing the oscillation amplitude to further improve sensitivity, and the presence of surface contaminants (in particular water due to humidity under ambient conditions). In addition, due to the orientation of the probe's magnetic dipole moment, MFM is intrinsically more sensitive to samples with an out-of-plane magnetization vector. Here, high-resolution topographical and magnetic phase images of single and bicomponent nanomagnet artificial spin-ice (ASI) arrays obtained in an inert (argon) atmosphere glovebox with &lt;0.1 ppm O2 and H2O are reported. Optimization of lift height and drive amplitude for high resolution and sensitivity while simultaneously avoiding the introduction of topographical artifacts is discussed, and detection of the stray magnetic fields emanating from either end of the nanoscale bar magnets (~250 nm long and &lt;100 nm wide) aligned in the plane of the ASI sample surface is shown. Likewise, using the example of a Ni-Mn-Ga magnetic shape memory alloy (MSMA), MFM is demonstrated in an inert atmosphere with magnetic phase sensitivity capable of resolving a series of adjacent magnetic domains each ~200 nm wide.

Magnetic force microscopy (MFM) employs a vertically magnetized atomic force microscopy probe to measure sample topography and local magnetic field strength with nanoscale resolution. Optimizing MFM spatial resolution and sensitivity requires balancing decreasing lift height against increasing drive (oscillation) amplitude, and benefits from operating in an inert atmosphere glovebox.

Magnetic force microscopy (MFM) enables mapping local magnetic fields across a sample surface with nanoscale resolution. To perform MFM, an atomic force ...

Atomic Force Microscopy Cantilever-Based Nanoindentation: Mechanical Property Measurements at the Nanoscale in Air and Fluid

An atomic force microscope (AFM) fundamentally measures the interaction between a nanoscale AFM probe tip and the sample surface. If the force applied by the probe tip and its contact area with the sample can be quantified, it is possible to determine the nanoscale mechanical properties (e.g., elastic or Young&#39;s modulus) of the surface being probed. A detailed procedure for performing quantitative AFM cantilever-based nanoindentation experiments is provided here, with representative examples of how the technique can be applied to determine the elastic moduli of a wide variety of sample types, ranging from kPa to GPa. These include live mesenchymal stem cells (MSCs) and nuclei in physiological buffer, resin-embedded dehydrated loblolly pine cross-sections, and Bakken shales of varying composition.
Additionally, AFM cantilever-based nanoindentation is used to probe the rupture strength (i.e., breakthrough force) of phospholipid bilayers. Important practical considerations such as method choice and development, probe selection and calibration, region of interest identification, sample heterogeneity, feature size and aspect ratio, tip wear, surface roughness, and data analysis and measurement statistics are discussed to aid proper implementation of the technique. Finally, co-localization of AFM-derived nanomechanical maps with electron microscopy techniques that provide additional information regarding elemental composition is demonstrated.

Quantifying the contact area and force applied by an atomic force microscope (AFM) probe tip to a sample surface enables nanoscale mechanical property determination. Best practices to implement AFM cantilever-based nanoindentation in air or fluid on soft and hard samples to measure elastic modulus or other nanomechanical properties are discussed.

An atomic force microscope (AFM) fundamentally measures the interaction between a nanoscale AFM probe tip and the sample surface. If the force applied by ...

A Virtual Simulation Experiment of Mechanics: Material Deformation and Failure Based on Scanning Electron Microscopy

This work presents a set of comprehensive virtual experiments to detect material deformation and failure. The most commonly used pieces of equipment in mechanics and material disciplines, such as a metallographic cutting machine and a high-temperature universal creep testing machine, are integrated into a web-based system to provide different experimental services to users in an immersive and interactive learning environment. The protocol in this work is divided into five subsections, namely, the preparation of the materials, molding the specimen, specimen characterization, specimen loading, nanoindenter installation, and SEM in situ experiments, and this protocol aims to provide an opportunity for users regarding the recognition of different equipment and the corresponding operations, as well as the enhancement of laboratory awareness, etc., using a virtual simulation approach. To provide clear guidance for the experiment, the system highlights the equipment/specimen to be used in the next step and marks the pathway that leads to the equipment with a conspicuous arrow. To mimic the hands-on experiment as closely as possible, we designed and developed a three-dimensional laboratory room, equipment, operations, and experimental procedures. Moreover, the virtual system also considers interactive exercises and registration before using chemicals during the experiment. Incorrect operations are also allowed, resulting in a warning message informing the user. The system can provide interactive and visualized experiments to users at different levels.

This work presents a three-dimensional virtual simulation experiment for material deformation and failure that provides visualized experimental processes. Through a set of experiments, users can become familiar with the equipment and learn the operations in an immersive and interactive learning environment.

This work presents a set of comprehensive virtual experiments to detect material deformation and failure. The most commonly used pieces of equipment in ...

High-Speed Magnetic Tweezers for Nanomechanical Measurements on Force-Sensitive Elements

Single-molecule magnetic tweezers (MTs) have served as powerful tools to forcefully interrogate biomolecules, such as nucleic acids and proteins, and are therefore poised to be useful in the field of mechanobiology. Since the method commonly relies on image-based tracking of magnetic beads, the speed limit in recording and analyzing images, as well as the thermal fluctuations of the beads, has long hampered its application in observing small and fast structural changes in target molecules. This article describes detailed methods for the construction and operation of a high-resolution MT setup that can resolve nanoscale, millisecond dynamics of biomolecules and their complexes. As application examples, experiments with DNA hairpins and SNARE complexes (membrane-fusion machinery) are demonstrated, focusing on how their transient states and transitions can be detected in the presence of piconewton-scale forces. We expect that high-speed MTs will continue to enable high-precision nanomechanical measurements on molecules that sense, transmit, and generate forces in cells, and thereby deepen our molecular-level understanding of mechanobiology.

Here, we describe a high-speed magnetic tweezer setup that performs nanomechanical measurements on force-sensitive biomolecules at the maximum rate of 1.2 kHz. We introduce its application to DNA hairpins and SNARE complexes as model systems, but it will be also applicable to other molecules involved in mechanobiological events.

Single-molecule magnetic tweezers (MTs) have served as powerful tools to forcefully interrogate biomolecules, such as nucleic acids and proteins, and are ...

A Novel Method for In Situ Electromechanical Characterization of Nanoscale Specimens

Summary

Explore More Videos

Chapters in this video

Quantitative and Qualitative Examination of Particle-particle Interactions Using Colloidal Probe Nanoscopy

Remote Magnetic Actuation of Micrometric Probes for in situ 3D Mapping of Bacterial Biofilm Physical Properties

Characterization Of Multi-layered Fish Scales (Atractosteus spatula) Using Nanoindentation, X-ray CT, FTIR, and SEM

A Standard and Reliable Method to Fabricate Two-Dimensional Nanoelectronics

Probing Surface Electrochemical Activity of Nanomaterials using a Hybrid Atomic Force Microscope-Scanning Electrochemical Microscope (AFM-SECM)

Micromechanical Tension Testing of Additively Manufactured 17-4 PH Stainless Steel Specimens

Optimizing Magnetic Force Microscopy Resolution and Sensitivity to Visualize Nanoscale Magnetic Domains

Atomic Force Microscopy Cantilever-Based Nanoindentation: Mechanical Property Measurements at the Nanoscale in Air and Fluid

A Virtual Simulation Experiment of Mechanics: Material Deformation and Failure Based on Scanning Electron Microscopy

High-Speed Magnetic Tweezers for Nanomechanical Measurements on Force-Sensitive Elements