The authors thank the AME Machine Shop at the University of Oklahoma for helping to make the mold and the fabrication set-up and the members of the Composite Manufacturing Research Laboratory, Drs. Yousef K. Hamidi, M. Akif Yalcinkaya, and Jacob Anderson for helpful discussions.

Caution: Please consult all relevant material safety data sheets (MSDS) before use. Use personal protective equipment (safety glasses, gloves, lab coat, full-length pants, and closed-toe shoes).
1. Materials
<ol>
	<li>Cut 6 plies of 20.3 cm &#1093; 15.2 cm, plain weave glass fabric with a rotary fabric cutter. 
	NOTE: The plain weave fabric can be replaced by other fabric types including non-woven, random mats. Carbon fibers can also be used in this method.</li>
	<li>Prepare the resin system by first weighing the epoxy resin, INF (40 g), on a tared balance, and then adding the hardener, INF (10.96 g), using a weight ratio of 100 to 27.4. Stir the resin/hardener mixture (at 37 rad s-1) until fully dispersion is reached (for 5 min). 
	NOTE: (1) The type of resin can be substituted with any type of resin suitable for wet lay-up vacuum bag processes. (2) The selection of epoxy resin-to-hardener ratio is dependent on the resin and hardener combination. (3) The selection of the weight of the resin/hardener mixture depends on the desired fiber volume fraction of finished part and the expected waste amount such as the amount of resin bleeding out, remaining resin on the brush, etc. Considering the weight of the 6-plies of fabric to be approximately 34 g, the resin to fiber ratio of 60 to 40, by weight, was chosen.</li>
	<li>Degas the resin (approximately 15 min) in the resin trap to remove all the trapped air formed during the mixing of the epoxy resin and hardener.</li>
</ol>
2. Composite Manufacturing Using Magnetic Pressure in a Wet Lay-up Vacuum Bag Process
NOTE: Figure 1 shows a simplified schematic of preparation of composite lay-up and applying magnetic pressure, which is described in sections 2.1-2.15.
<ol>
	<li>Prepare all the material required for the experiment:
	<ol>
		<li>Place twenty-five N52 Neodymium-Iron-Boron (NdFeB) permanent magnets (2.54 cm length, 2.54 cm width, and 1.27 cm thickness), magnetized through their thickness, on a 4.76 mm-thick steel top plate. Arrange the magnets in 5 &#215; 5 square configuration in alternating polarity. During arrangement and placement of permanent magnets, care must be taken as there is a risk of injury.</li>
		<li>Place a 0.3 mm-thick aluminum caul plate (20.3 &#1093; 15.2 cm2) pre-coated with PTFE release agent exactly in the middle of a perforated release film (26.7 &#1093; 21.6 cm2).</li>
		<li>Use 12.7-mm wide polyester tape to tape the perimeter of the caul plate to the release film.</li>
	</ol>
	</li>
	<li>Place a 12.7-mm wide tacky tape around the periphery of a 43.2 &#215; 27.9 cm2 area on the surface of a 6.35 mm-thick, 61.0 &#215; 61.0 cm2, steel bottom tool plate.</li>
	<li>Prior to laying the fabric, apply a coat of resin on the tool plate, covered by a layer of nonporous PTFE-coated fiberglass release film (76 &#181;m-thick). Apply just enough resin to saturate the first ply of fabric.</li>
	<li>Place the first ply of fabric, and then, with a roller, press and squeeze out excess resin.</li>
	<li>Fully saturate the fiber bed by pouring a small amount of additional resin on top of the fabric and then spreading evenly over the entire area with squeegees.</li>
	<li>Repeat steps 2.4 and 2.5 for all the plies (6-ply in this case). Ensure that all the plies are fully saturated with resin and that approximately the same amount of resin (~8.5 g) is used for each ply.</li>
	<li>Place the caul plate, attached to the perforated release film, on top of the fiber preform, followed by a layer of 0.5-inch wide polyester tape around the perimeter of the release film.</li>
	<li>Insert two pieces of breather/bleeder cloth on to the fiber preform and place the bottom piece of the twist lock vacuum valve on top of the breather cloth. Ensure that the valve is located far enough from the saturated preform to protect the valve from contact with the excess resin.</li>
	<li>Remove the paper backing of the tacky tape and place the vacuum bag on the tool plate while pressing it firmly against the tape to seal it.</li>
	<li>Connect one side of the vacuum hose to the top piece of vacuum valve and the other side to the pressure regulator, connected to the vacuum pump.</li>
	<li>Put a small slit in the bag where the bottom piece of the valve is, insert the top piece of the vacuum valve into the hole, and then gently twist it shut so that the bag underneath does not wrinkle.</li>
	<li>Start the vacuum pump until a constant vacuum pressure of 93 kPa (13.5 psi) is reached to remove any volatiles generated during cure and excess resin. Ensure that the vacuum system is leakage free.</li>
	<li>Clamp the four edges of the bottom tool plate to a support base. The bottom tool plate must be fixed against movement prior to placement of magnets because the magnetic attraction force may move and shift the plate upward.</li>
	<li>Allow the laminate to cure for 45 min at room temperature, then place the set of magnets (prepared in section 2.1.1) on the vacuum bag, followed by increasing the temperature of the tool plate to 60 &#176;C at a ramp rate of ~5 &#176;C/min. 
	NOTE: (1) The cure cycle is dependent on the resin selected. (2) Silicone rubber heat sheets are placed under the tool plate for heating.</li>
	<li>After curing for 8 h at 60 &#176;C, remove the vacuum bag and demold the composite laminate. 
	NOTE: To assess the improvement in the quality of laminates as a result of applying magnetic pressure, we fabricated a series of laminates using a conventional wet lay-up vacuum bag process without applying any external pressure. The quality of these laminates was compared with those made under magnetic pressure. To fabricate laminates using conventional wet lay-up vacuum bag, steps 2.1.2 to 2.15 were followed, except for the placement of magnets. To assess the repeatability of each fabrication process, a second laminate was fabricated under identical conditions.</li>
</ol>
3. Measurement of Magnetic Compaction Pressure
<ol>
	<li>Attach the top plate to the end of the load cell on a mechanical testing instrument.</li>
	<li>Place one N52 Neodymium-Iron-Boron permanent magnet on the bottom movable plate, which is positioned at a sufficient distance (at least 25 mm) away from the top fixed plate at the beginning of the test. 
	NOTE: For measurement of magnetic force, both top and bottom plates should be made of magnetic material such as steel.</li>
	<li>Move the bottom plate upward at a low speed of 1-2 mm/min toward the top plate and record the generated magnetic force while measuring the corresponding displacement from the linear variable differential transformer (LVDT) at a sampling rate of 6 Hz. 
	NOTE: (1) The speed of this test is critical because the force generated by magnets depends exponentially on the air gap in between. (2) All magnetic measurements are performed at room temperature.</li>
	<li>Continue to monitor the magnetic compaction force until the top surface of the magnet touches the top plate.</li>
	<li>Calculate the magnetic compaction pressure by dividing the magnetic force by the cross-sectional area of the magnet.</li>
</ol>
4. Resin Burn-off and Thermogravimetric Analysis (TGA)
<ol>
	<li>Resin burn-off
	<ol>
		<li>Cut three specimens from each laminate for a resin burn-off test according to the ASTM D2584-11 specifications41.</li>
		<li>Place each specimen in a separate porcelain crucible and note the weights of specimens as well as the crucibles.</li>
		<li>Place the crucibles containing samples in a furnace, turn on the furnace, raise the furnace temperature to 600 &#176;C, and allow the resin to burn-off for about 4 h.</li>
		<li>Turn off the furnace, carefully open the furnace door, and allow it to cool to room temperature before removing the crucibles.</li>
		<li>After cool-down, remove the crucibles from the furnace and weigh the recovered glass fibers. 
		NOTE: The fibers may lose weight during the resin burn-off. The amount of weight loss of fibers when they are exposed to high temperatures can be determined by the thermogravimetric analysis (TGA).</li>
	</ol>
	</li>
	<li>Thermogravimetric analysis (TGA)
	<ol>
		<li>Measure the weight loss of fiber as a function of increasing temperature in air at atmospheric pressure using TGA. Place approximately 30 mg of the fiber in a platinum pan and load it into the TGA device.</li>
		<li>Ramp the temperature from 25 &#176;C to 600 &#176;C at a rate of 15 &#176;C/min, hold the temperature for 4 h, and calculate the percent reduction in weight. The weight loss percentage of the fibers are accounted for during fiber volume fraction and void volume fraction calculations. 
		NOTE: According to the TGA test results at 600 &#176;C, the weight loss for plain weave and random mat preforms used in this study are 0.2% and 5.46%, respectively.</li>
	</ol>
	</li>
</ol>
5. Void and Fiber Volume Fraction Calculation
<ol>
	<li>Determine the density of the composite specimen, matrix, and fiber:
	<ol>
		<li>Use the suspension method42 to determine the density of bulk composite specimen. 
		NOTE: For this method, a transparent heavy liquid with a density of 2.49 g/cm3 is used so that the composite specimen initially floats when immersed in the heavy liquid.
		<ol>
			<li>Reduce the density of the heavy liquid by adding 3 mL water and mixing the solution by magnetic stirrer at 105 rad s-1 for 5 min. Repeat this step until the composite specimen begins to slowly suspend in the heavy liquid/water mixture.</li>
			<li>Once the solution density has been adjusted so that the specimen remains suspended in the heavy liquid and water mixture, measure the solution density using a specific gravity cup.</li>
		</ol>
		</li>
		<li>Prepare void-free resin specimens using the same cure cycle given in steps 2.14 and 2.15 and then determine the density of cured resin specimens using the same procedure as 5.1.1.1 and 5.1.1.2. 
		NOTE: The density of cured INF and EPON specimens are 1.152 &#177; 0.003 g/cm3 and 1.171 &#177; 0.003 g/cm3, respectively.</li>
		<li>Use a nitrogen pycnometer43 with a 10-cm3 cup to obtain the density of fiber. 
		NOTE: The density of plain weave and random mat fabrics are 2.600 &#177; 0.003 g/cm3 and 2.470 &#177; 0.004 g/cm3, respectively.</li>
	</ol>
	</li>
	<li>Calculate the weight fraction of the fiber and resin according to ASTM D2584-1141.</li>
	<li>Calculate the void and fiber volume fraction following ASTM D3171-15 procedures44 
	<img alt="Equation 1" src="/files/ftp_upload/57254/57254eq1.jpg" />&#160;&#160;&#160;&#160;&#160;&#160;&#160;(1) 
	<img alt="Equation 2" src="/files/ftp_upload/57254/57254eq2.jpg" />&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160; (2) 
	<img alt="Equation 3" src="/files/ftp_upload/57254/57254eq3.jpg" />&#160;&#160;&#160;&#160;&#160;&#160; (3) 
	where <img alt="Equation 4" src="/files/ftp_upload/57254/57254eq4.jpg" /> is the resin volume fraction, <img alt="Equation 5" src="/files/ftp_upload/57254/57254eq5.jpg" /> is the fiber volume fraction, <img alt="Equation 6" src="/files/ftp_upload/57254/57254eq6.jpg" /> is the void volume fraction, <img alt="Equation 7" src="/files/ftp_upload/57254/57254eq7.jpg" /> is the density of composite, <img alt="Equation 8" src="/files/ftp_upload/57254/57254eq8.jpg" /> is the density of resin, <img alt="Equation 9" src="/files/ftp_upload/57254/57254eq9.jpg" /> is the density of fiber, <img alt="Equation 10" src="/files/ftp_upload/57254/57254eq10.jpg" /> is the sample weight, and <img alt="Equation 11" src="/files/ftp_upload/57254/57254eq11.jpg" /> is the fiber weight. 
	NOTE: The uncertainty for the void volume content is calculated to be &#177;0.21%45. This level of accuracy is sufficient for the composite laminates, even when the laminate has a low-void content of less than 1%.</li>
</ol>
6. Scanning Electron Microscopy (SEM) Imaging
<ol>
	<li>Cut two 25.4 mm &#215; 6.4 mm specimens from each laminate and embed them in a rapid-cure acrylic for SEM imaging. 
	NOTE: The specimens are embedded such that the side surface (through-the-thickness surface) of the laminate along the 25.4 mm sample length is exposed for imaging.</li>
	<li>Use a polishing machine to polish the surface of embedded composite samples with grit sizes ranging from 30 to 0.04 &#181;m.</li>
	<li>Sputter coat approximately 5 nm of gold/palladium onto the prepared specimen to provide a conductive layer.</li>
	<li>Mount the specimen onto a sample holder and put it into the chamber of the SEM.</li>
	<li>Set the SEM imaging parameters such as acceleration voltage to 20 kV and the working distance to 25.5 mm.</li>
	<li>Capture multiple images of the laminate at 35X or higher magnification at various locations. 
	NOTE: The selected magnification allows the assessment of voids over a large cross-sectional area as well as a visual comparison of the laminate thickness. Accurate measurements of the laminate thickness can be made using these images.</li>
</ol>
7. Characterization of Flexural Properties
<ol>
	<li>Cut a set of seven 12.7 mm wide specimens from each composite laminate for three-point bending flexural tests according to ASTM D790-1546 using a diamond-grit saw.</li>
	<li>Measure the width and thickness of each specimen with a caliper.</li>
	<li>Use a span to thickness ratio of 24:1 and adjust the support span of the three-point bending test fixture. Place the specimen on the three-point bending flexural test fixture assembled at the mechanical testing instrument.</li>
	<li>Perform the flexural test at the crosshead speed of 2 mm/min and record the load-deflection behavior of the specimen.</li>
	<li>Repeat the above steps for all specimens to confirm and ensure repeatability of results.</li>
	<li>Once the experiment is finished, calculate the flexural strength as well as flexural modulus of the specimens39,40.</li>
</ol>

The authors do not have any disclosures.

The application of a high consolidation pressure during the cure of a composite laminate is particularly important for manufacturing a high-quality composite part47. If the external pressure is not applied and the laminate is cured only under vacuum, the final part will generally contain high void content, possibly exceeding 5% by volume, and undesirable resin rich regions48. High void content, low fiber volume fraction, and resin rich areas are factors adversely affecting the mechanical properties of composite laminates. In this work, an experimental protocol for applying high consolidation pressure during cure of a laminate in the wet lay-up vacuum bag process is described29. In this technique, first, the composite lay-up is prepared on a magnetic bottom tool plate according to the conventional wet lay-up vacuum bag process. Then, a set of permanent magnets, attached to a magnetic top steel plate, is placed on the vacuum bag. In this study, magnets are applied while increasing the lay-up temperature to 60 &#176;C, where the resin viscosity decreases significantly. Applying pressure at a different time, such as the gelation point, may yield laminates with different properties13,40,49. The level of applied magnetic pressure depends on the gap between the magnets and magnetic bottom plate. Thus, we present a procedure to measure magnetic pressure generated by a magnet as a function of the gap (i.e., lay-up thickness).
To determine the effectiveness of MACM, wet lay-up vacuum bag laminates with different material constituents are fabricated by using six scenarios with and without magnetic compaction pressure. Then, we demonstrate the detailed steps for characterization of void and fiber volume fractions, microstructure, and flexural properties of composite laminates. To evaluate volume fractions of the composite constituents, the resin-burn off and suspension methods are utilized42. The presented results show that using magnetic compaction pressure significantly increases the fiber volume fraction and decreases the void content of the parts. In addition, for microstructural analysis of composite, scanning electron microscopy (SEM) imaging is used, and gives insight into the location and geometrical features of voids15. For example, Figure 3 shows that the use of magnetic pressure during cure is also beneficial in reducing both the size and number of voids, and hence decreases the probability of premature failure20,24. Consequently, these factors greatly improve the flexural properties of laminates. However, the effectiveness of MACM is different depending upon the type of the composite constituents (fiber and resin).
Although fabrication of laminates with this method is simple, care must be taken during arrangement and placement of permanent magnets as they generate a very high pressure (i.e., a maximum pressure of 0.64 MPa). The limitation of this method is that the bottom tool plate needs to be magnetic, such as a 400-series stainless steel, and it must be fixed against movement prior to placement of magnets, because the magnetic attraction force may move and shift the plate upwards. Additionally, the applied pressure by magnets depends on the thickness of the laminate. For example, NdFeB, N52-2.54 &#215; 2.54 &#215; 1.27 cm3 permanent magnets are not able to generate a high consolidation pressure (&#62; 0.1 MPa) when the composite lay-up thickness exceeds 6.5 mm. In this case, stronger magnets need to be utilized to achieve high consolidation levels.
The presented method is convenient to use and has the advantage over autoclaves in that it does not require expensive equipment and tooling. Although not elucidated here, this method is broadly applicable not only to wet lay-up vacuum bag but also to other manufacturing processes for composites, such as out-of-autoclave curing of prepregs and vacuum assisted resin transfer molding (VARTM). Moreover, large composite components can be fabricated with relative ease by sliding the magnets along the vacuum bag if a suitable lubricant is used between the magnets and the vacuum bag. In addition, to the best of our knowledge, this is the only method which allows the application of local as well as non-uniform pressure on the composite lay-up. A future direction of this method is to manufacture geometrically complex composite parts, but instead of placing the magnets on a flat plate, they may be placed on a matched, upper mold.

Fiber-reinforced polymer composites have been widely used in the automotive1,2, aerospace3,4, marine5,6, and construction7,8 industries because of their unique properties such as high specific strength and modulus, favorable fatigue behavior, and corrosion resistance. Currently, high-quality composite laminates are predominantly fabricated using layers of pre-impregnated fabric (prepreg) cured in an autoclave under elevated temperature and high consolidation pressure of 0.27-0.69 MPa (40-100 psi)9. Somewhat lower quality composite laminates are produced by the wet lay-up process, where a higher consolidation pressure is not applied. This process is labor-intensive, does not require expensive equipment, and is performed by placing one ply of dry fabric on a mold and subsequently applying resin. In most applications, a hand-held roller is used to force the resin into the fiber reinforcement and squeeze out excess resin. This sequence is repeated until the desired thickness is obtained. The quality of the laminates produced by wet lay-up can be greatly improved by applying a combination of vacuum (called the wet lay-up vacuum bag process) and an additional consolidation pressure in an autoclave during cure. Applying high consolidation pressure during cure facilitates the resin flow, leading to an increase in the fiber volume fraction and a removal of voids10,11 which results in enhancement of mechanical properties. Abraham et al.12 showed that high-quality plain weave E-glass composite laminates with a high fiber volume fraction of approximately 64% and low void volume fraction of 1.6% can be fabricated using the wet lay-up vacuum bag when a consolidation pressure of 1.2 MPa is applied in an autoclave.
Voids are one of the most common defects that are formed during the manufacturing of composite laminates. Voids ranging from a few microns to several hundred microns are formed primarily due to the entrapped air during lay-up, dissolved moisture in the resin, and expelled volatiles during cure13,14,15. Also, the dynamics of impregnation of fibrous reinforcement are found to have a significant effect on void entrapment16,17. It is widely accepted that the presence of voids in a composite laminate can lead to a substantial reduction of the strength13,18,19, modulus20,21, fracture toughness22, and fatigue life23,24 of the laminates. For instance, Judd and Wright25 found that each 1% increase in void content (up to 4%), results in an approximately 7% drop in the short beam shear properties. Moreover, Ghiorse26 found that, in carbon/epoxy composites, for each 1% increase in void content, a 10% reduction in interlaminar shear and flexural strength and a 5% reduction in flexural modulus may be seen. In addition, voids have adverse effects on crack initiation and propagation as well as moisture absorption27,28. It is well-known that the rate of moisture absorption for laminates with higher void contents is greater, and the absorbed moisture may cause the deterioration of the fiber-matrix interface and inferior long-term mechanical properties29,30,31,32. Thus, to ensure consistency of the mechanical properties and achieve the highest quality of composite products, the void content should be minimized.
Although curing a composite laminate in an autoclave produces reliable, high-quality parts, the product cost would be high due to initial capital investment and excessive energy usage. In addition to autoclave cure, a wide variety of techniques such as vacuum assisted resin transfer molding (VARTM) and Quickstep process have been developed and used to fabricate composite laminates out of autoclave32,33,34,35,36. However, due to the absence of a uniform, high pressure, the laminates produced by these methods often have lower mechanical properties compared to those made in autoclaves37. Recently, a novel technique referred to as magnet assisted composite manufacturing (MACM) has been utilized for improving the quality of wet lay-up vacuum bag composite laminates by applying a consolidation pressure generated by a set of high power permanent magnets38,39. The application of this technique was then extended to produce high-quality, structural composite laminates out of an autoclave using high-temperature permanent magnets40.
In this paper, a protocol for manufacturing wet lay-up vacuum bag composite laminates using MACM technique is presented. In MACM, Neodymium-Iron-Boron permanent magnets are utilized to apply a sufficiently high consolidation pressure during cure, and thus, improve the quality of laminates. First, the preparation of 6-ply, plain weave E-glass/epoxy composite lay-up on a bottom steel plate is described. Then, the arrangement of permanent magnets in alternating polarity on a top steel plate is demonstrated, along with its placement on the vacuum bag to apply a consolidation pressure on the composite lay-up. Finally, we outline the steps for measurement of magnetic compaction pressure, as well as the methods used for the characterization of void and fiber volume fractions, microstructure, and mechanical properties of composite laminates. The effectiveness of the MACM process is examined by fabricating wet lay-up vacuum bag laminates made under magnetic pressure and comparing their properties to those fabricated by the conventional wet lay-up vacuum bag without magnets. The results obtained prove the capability of the MACM method to improve the overall laminate quality. This method is a low-cost and simple way of manufacturing high-quality laminates and can be applied to fabricate large and geometrically complex composite components with relative ease.

<table><tbody><tr><td>Plain weave glass fiber</td><td>Hexcel</td><td>HexForce 3733</td><td>The type of fibers can be substituted with any type of fabrics</td></tr><tr><td>Randomly oriented chopped strand glass fiber</td><td>Fiberglast</td><td>248</td><td></td></tr><tr><td>TenCate EX-1522/IM7</td><td>Tencate</td><td></td><td>it is a plain weave carbon/epoxy prepreg</td></tr><tr><td>PRO-SET INF-114 Infusion Epoxy</td><td>Composite Envisions</td><td>1758</td><td>The type of resin can be substituted with any type of resin suitable for wet lay-up vacuum bag process</td></tr><tr><td>PRO-SET INF-211 Medium Infusion Hardener</td><td>Composite Envisions</td><td>1760</td><td></td></tr><tr><td>EPON 862</td><td>Hexion Inc.</td><td></td><td></td></tr><tr><td>EPIKURE Curing Agent 3300</td><td>Hexion Inc.</td><td></td><td></td></tr><tr><td>NdFeB, N52-2.54 &amp;times; 2.54 &amp;times; 1.27 cm3</td><td>K&amp;amp;J Magnetics, Inc.</td><td>BX0X08-N52</td><td>Magnets can be substitued with any type depending on the required pressure and application</td></tr><tr><td>OLFA rotary cutter</td><td>Fibre Glast</td><td>1706-A</td><td></td></tr><tr><td>Tacky tape</td><td>De-Comp Composites</td><td>D413Y</td><td></td></tr><tr><td>Polyester tape</td><td>De-Comp Composites</td><td>D574A</td><td></td></tr><tr><td>Squeegees</td><td>Fibre Glast</td><td>62-A</td><td>Any type of squeegees can be used</td></tr><tr><td>Roller</td><td>De-Comp Composites</td><td>D205</td><td>Any type of rollers can be used</td></tr><tr><td>PTFE-Coated&amp;nbsp;fiberglass fabric sheets</td><td>McMaster-Carr Supply Company</td><td>8577K81</td><td></td></tr><tr><td>PTFE release agent dry lubricant</td><td>Miller-Stephenson</td><td>MS122AD</td><td></td></tr><tr><td>Perforated release film</td><td>Fibre Glast</td><td>1787-C</td><td></td></tr><tr><td>Breather cloth</td><td>De-Comp Composites</td><td></td><td></td></tr><tr><td>Vacuum&amp;nbsp;bag&amp;nbsp;film</td><td>Rock West Composite</td><td>WRIGHTLON 7400</td><td></td></tr><tr><td>Aluminum twist lock vacuum valve</td><td>De-Comp Composites</td><td>D401</td><td></td></tr><tr><td>Vacuum pump</td><td>Best Value Vacs</td><td>BVVRS1</td><td></td></tr><tr><td>Flexible silicone-rubber heat sheets, adhesive backing</td><td>McMaster-Carr Supply Company</td><td>35765K429</td><td></td></tr><tr><td>400-series steel plate, 6.35 mm-thick</td><td></td><td></td><td>The lay-up is prepared on this plate</td></tr><tr><td>steel plate, 4.76 mm-thick</td><td></td><td></td><td>The magnets are attached to this plate</td></tr><tr><td>Aluminum sheet, 0.3-mm thick</td><td></td><td></td><td></td></tr><tr><td>Lab stirrer mixer</td><td>Caframo</td><td></td><td></td></tr><tr><td>Laboratory weigh scale</td><td></td><td></td><td></td></tr><tr><td>AccuPyc II 1340 automatic gas pycnometer</td><td>Micromeritics Instrument Corporation</td><td>134/00000/00</td><td></td></tr><tr><td>Specific gravity cup, 83.2 mL</td><td>Gardco</td><td>EW-38000-12</td><td></td></tr><tr><td>Acrylic cold mounting resin</td><td>Struers</td><td>LevoCit</td><td></td></tr><tr><td>Grinder/polisher</td><td>Struers</td><td>LaboSystem</td><td></td></tr><tr><td>Porcelain crucibles, 30 mL</td><td>United Scientific Supplies</td><td>JCT030</td><td></td></tr><tr><td>Plastic Cups, 12 Oz, clear</td><td></td><td></td><td>It is used as epoxy mixing cups</td></tr></tbody></table>

magnet assisted composite manufacturing: a flexible new technique for achieving high consolidation pressure in vacuum bag/lay-up processes

This work demonstrates a protocol to improve the quality of composite laminates fabricated by wet lay-up vacuum bag processes using the recently developed magnet assisted composite manufacturing (MACM) technique. In this technique, permanent magnets are utilized to apply a sufficiently high consolidation pressure during the curing stage. To enhance the intensity of the magnetic field, and thus, to increase the magnetic compaction pressure, the magnets are placed on a magnetic top plate. First, the entire procedure of preparing the composite lay-up on a magnetic bottom steel plate using the conventional wet lay-up vacuum bag process is described. Second, placement of a set of Neodymium-Iron-Boron permanent magnets, arranged in alternating polarity, on the vacuum bag is illustrated. Next, the experimental procedures to measure the magnetic compaction pressure and volume fractions of the composite constituents are presented. Finally, methods used to characterize microstructure and mechanical properties of composite laminates are discussed in detail. The results prove the effectiveness of the MACM method in improving the quality of wet lay-up vacuum bag laminates. This method does not require large capital investment for tooling or equipment and can also be used to consolidate geometrically complex composite parts by placing the magnets on a matching top mold positioned on the vacuum bag.

To investigate the effect of MACM on the quality of the laminates, several scenarios that use different fabric types and resin systems were considered. Table 1 reports the manufacturing process and composite constituents of 6-ply, E-glass/epoxy composite laminates manufactured under six different fabrication scenarios. In the baseline scenarios (W-PW-INF, W-RM-INF, and W-RM-EPON), the laminates are fabricated by wet lay-up vacuum bag without external pressure. The other three scenarios (WM-PW-INF, WM-RM-INF, and WM-RM-EPON) are used to fabricate wet lay-up vacuum bag laminates under magnetic compaction pressure. The quality of these laminates is then compared to those made by the baseline scenarios. In the first and second scenarios, W-PW-INF and WM-PW-INF, plain weave E-glass/INF laminates are fabricated. In the third and fourth scenarios, W-RM-INF and WM-RM-INF, the plain weave fabric is replaced with random mat, and the same resin system (i.e., INF) is used. In the fifth and sixth scenarios, W-RM-EPON and WM-RM-EPON, the fabric is random mat E-glass, while the resin system is replaced with EPON which has a moderately higher viscosity of 766.9 mPa s compared to 296 mPa s for INF resin. A more detailed analysis of the last four scenarios can be found in Pishvar et al. 2017 and Amirkhosravi et al. 201738,39.
Figure 2a presents the magnetic pressure generated by NdFeB, N52-2.54 &#215; 2.54 &#215; 1.27 cm3 magnet as a function of the distance between the magnet and steel plate. This distance would correspond to the lay-up thickness during fabrication of the composite laminate, and thus can be used to determine the variation of the compaction pressure applied by the magnets. The inset in Figure 2a shows a photograph of the experimental set-up used for measuring the variation of the magnetic pressure as a function of distance. As explained in section 3 of the protocol, the set-up consists of two parallel steel plates (12.5 cm &#215; 12.5 cm &#215; 1.8 cm). The top plate is connected to a 4.45 kN (1000 lb) load-cell. The bottom plate is assembled on the cross-head of a mechanical testing instrument. By using this set-up, the attraction force of the permanent magnet placed on the bottom plate is measured as a function of the gap (i.e., the distance between the magnet and the top steel plate). The dashed line in Figure 2a represents the measured magnetic pressure (force over the area of the magnet) by the mechanical testing instrument, and the solid line represents the pressure determined from the data provided by the supplier of the magnets. There is generally good agreement between the measured pressure and the values obtained from the technical data sheet provided by the supplier. It is seen that the increase in magnetic pressure depends exponentially on the reduction of the gap. Therefore, as the laminate consolidates during the curing process, the thickness of the lay-up gradually decreases, and consequently, the pressure applied by the magnet increases. Figure 2b shows the same experimental data presented in Figure 2a but for the gap (i.e., lay-up thickness) range of 1-4.5 mm. In addition, the initial and final magnetic pressure applied during the cure of the laminates comprised of different fabric types (i.e., plain weave and random mat) and resin systems (i.e., INF and EPON) are displayed in Figure 2b. The lay-up thickness of plain weave/INF laminates (WM-PW-INF) during consolidation decreases from 1.5 mm to 1.4 mm due to resin outflow and cure. Accordingly, the magnetic pressure slightly increases from 0.38 to 0.39 MPa. The lay-up thickness of random mat/INF laminates (WM-RM-INF) changes from 2.8 mm to 1.7 mm, and, as a result, the magnetic pressure significantly increases from 0.27 to 0.36 MPa. The lay-up thickness of the laminates made with random mat/EPON (WM-RM-EPON) decreases from 3.7 mm to 2.5 mm, and thus, the generated pressure moderately rises from 0.22 to 0.29 MPa.
Table 2 presents the average thickness, fiber volume fraction, and void volume fraction of the laminates manufactured with and without magnetic consolidation pressure. As shown in Table 2, utilizing magnetic compaction pressure substantially reduces the average thickness of the laminates by 12-47%. As expected, the reduction in the laminate thickness is strongly correlated with the increase in the fiber volume fraction of the laminates, where the fiber volume fraction of the laminates significantly improves by 13-98% due to magnetic pressure. Among all scenarios, the effect of applying magnetic pressure on random mat/INF laminates is more pronounced (i.e., 98% increase in fiber volume fraction) because of two factors: (1) a significantly lower initial fiber volume fraction of uncompacted random mat laminates compared to plain weave laminates, and (2) the use of resin with a low viscosity of 296 mPa s, thereby allowing easier removal of excess resin. It is also notable that applying magnetic pressure has an additional advantage in decreasing the void volume fraction of laminates from 3.4-5.8% to 1.5-2.7%. Thus, the magnetic pressure drives not only the excess resin but also the voids out of the laminate.
Figure 3 displays the SEM images of E-glass/epoxy laminates manufactured under 6 different scenarios at 35X magnification. For easy visual comparison, the images of the laminates made without an external pressure are shown on the left and the laminates made under magnetic compaction are presented on the right. From these images, it is evident that utilizing the magnetic compaction pressure results in much-improved consolidation between the plies and, consequently, leads to a significant reduction in the resin-rich areas. As a result, the laminate thickness is remarkably reduced and the fiber volume fraction is increased, especially in the laminates made from random mat fabric and INF resin (WM-RM-INF). These images also show that the morphology of the voids is quite different in the laminates made with and without external pressure. Applying magnetic pressure reduces the number of voids and makes the voids smaller, leading to a lower void volume fraction in the laminates. Finally, compacting the voids that are located between the plies leads to more elongated voids.
Table 3 shows the flexural strength and modulus of all laminates and the percentage increase in flexural properties of the laminates made under magnetic consolidation pressure. The results clearly show that the flexural strength and modulus of laminates are significantly improved by utilizing the magnetic pressure. An increase of 98% in the fiber volume fraction of the random mat/INF laminates (WM-RM-INF), while having a minimum void content of 1.46%, causes a 62% and 67% increase in the flexural strength and modulus of the laminates, respectively. As expected, the plain weave/INF laminates (WM-PW-INF) which initially exhibited the lowest improvement of 13% in fiber volume fraction, showed the lowest increase, 7% and 22%, in flexural strength and modulus, respectively. Consequently, the enhancement in flexural properties of a variety of composite laminates made under magnetic consolidation pressure proves the capability of the MACM to improve the overall laminate quality.
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Fabrication 
			scenario</td>
			<td>Fabric type</td>
			<td>Resin system</td>
			<td>Manufacturing process</td>
		</tr>
		<tr>
			<td>W-PW-INF</td>
			<td>Plain weave E-glass</td>
			<td>INF</td>
			<td>Conventional wet lay-up vacuum bag without using external pressure</td>
		</tr>
		<tr>
			<td>WM-PW-INF</td>
			<td>Plain weave E-glass</td>
			<td>INF</td>
			<td>Wet lay-up vacuum bag with using magnetic consolidation pressure</td>
		</tr>
		<tr>
			<td>W-RM-INF</td>
			<td>Random mat E-glass</td>
			<td>INF</td>
			<td>Conventional wet lay-up vacuum bag without using external pressure</td>
		</tr>
		<tr>
			<td>WM-RM-INF</td>
			<td>Random mat E-glass</td>
			<td>INF</td>
			<td>Wet lay-up vacuum bag with using magnetic consolidation pressure</td>
		</tr>
		<tr>
			<td>W-RM-EPON</td>
			<td>Random mat E-glass</td>
			<td>EPON</td>
			<td>Conventional wet lay-up vacuum bag without using external pressure</td>
		</tr>
		<tr>
			<td>WM-RM-EPON</td>
			<td>Random mat E-glass</td>
			<td>EPON</td>
			<td>Wet lay-up vacuum bag with using magnetic consolidation pressure</td>
		</tr>
	</tbody>
</table>
Table 1: Details of the constituents and six fabrication scenarios used in the manufacturing of 6-ply composite laminates.
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Fabrication scenario</td>
			<td>Average thickness (mm)</td>
			<td>Fiber volume fraction (%)</td>
			<td>Increase in fiber volume fraction (%)</td>
			<td>Void volume fraction (%)</td>
			<td>Reduction in void volume fraction (%)</td>
		</tr>
		<tr>
			<td>W-PW-INF</td>
			<td>0.98 &#177; 0.01</td>
			<td>45.65 &#177; 0.82</td>
			<td>&#8213;</td>
			<td>3.44 &#177; 0.46</td>
			<td>&#8213;</td>
		</tr>
		<tr>
			<td>WM-PW-INF</td>
			<td>0.86 &#177; 0.01</td>
			<td>51.63 &#177; 0.87</td>
			<td>13</td>
			<td>1.74 &#177; 0.39</td>
			<td>49</td>
		</tr>
		<tr>
			<td>W-RM-INF29</td>
			<td>2.28 &#177; 0.04</td>
			<td>24.84 &#177; 1.14</td>
			<td>&#8213;</td>
			<td>5.09 &#177; 0.69</td>
			<td>&#8213;</td>
		</tr>
		<tr>
			<td>WM-RM-INF29</td>
			<td>1.21 &#177; 0.01</td>
			<td>49.10 &#177; 0.87</td>
			<td>98</td>
			<td>1.46 &#177; 0.24</td>
			<td>71</td>
		</tr>
		<tr>
			<td>W-RM-EPON30</td>
			<td>3.18&#160;&#177;&#160;0.01</td>
			<td>17.34&#160;&#177;&#160;0.84</td>
			<td>&#8213;</td>
			<td>5.81&#160;&#177;&#160;1.24</td>
			<td>&#8213;</td>
		</tr>
		<tr>
			<td>WM-RM-EPON30</td>
			<td>1.99&#160;&#177;&#160;0.03</td>
			<td>26.88&#160;&#177;&#160;1.99</td>
			<td>55</td>
			<td>2.71&#160;&#177;&#160;0.36</td>
			<td>53</td>
		</tr>
	</tbody>
</table>
Table 2: Average thickness, fiber volume fraction, and void volume fraction of the 6-ply laminates manufactured under six different scenarios. The percentage increase in fiber volume fraction and percentage reduction in void volume fraction due to magnetic compaction (n = 6 for fiber volume fraction and void volume fraction and n = 35 for average laminate thickness; 95% confidence intervals for all data) are also given.
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Fabrication scenario</td>
			<td>Flexural strength (MPa)</td>
			<td>Increase in flexural strength (%)</td>
			<td>Flexural modulus (GPa)</td>
			<td>Increase in flexural modulus (%)</td>
		</tr>
		<tr>
			<td>W-PW-INF</td>
			<td>638.9 &#177; 27.0</td>
			<td>&#8213;</td>
			<td>24.1 &#177; 0.5</td>
			<td>&#8213;</td>
		</tr>
		<tr>
			<td>WM-PW-INF</td>
			<td>681.1 &#177; 35.5</td>
			<td>7</td>
			<td>29.5 &#177; 0.9</td>
			<td>22</td>
		</tr>
		<tr>
			<td>W-RM-INF29</td>
			<td>218.9 &#177; 11.4</td>
			<td>&#8213;</td>
			<td>8.4 &#177; 0.3</td>
			<td>&#8213;</td>
		</tr>
		<tr>
			<td>WM-RM-INF29</td>
			<td>354.6 &#177;15.5</td>
			<td>62</td>
			<td>14.0 &#177; 0.8</td>
			<td>67</td>
		</tr>
		<tr>
			<td>W-RM-EPON30</td>
			<td>158.1&#160;&#177;&#160;8.9</td>
			<td>&#8213;</td>
			<td>6.8&#160;&#177;&#160;0.1</td>
			<td>&#8213;</td>
		</tr>
		<tr>
			<td>WM-RM-EPON30</td>
			<td>253.5&#160;&#177;&#160;20.1</td>
			<td>60</td>
			<td>9.9&#160;&#177;&#160;0.6</td>
			<td>46</td>
		</tr>
	</tbody>
</table>
Table 3: Flexural strength and modulus of the composite laminates and the percentage increase in flexural properties due to magnetic compaction (n = 7 for the laminates made by EPON and n = 14 for the rest; 95% confidence intervals for all data).
<img alt="Figure 1" class="xfigimg" src="/files/ftp_upload/57254/57254fig1.jpg" /> 
Figure 1: A simplified schematic of the preparation of composite lay-up and application of magnetic pressure, as described in the Protocol section. For this purpose, twenty-five NdFeB, N52-2.54 &#215; 2.54 &#215; 1.27 cm3 permanent magnets are utilized to apply consolidation pressure on the composite lay-up. <a href="/files/ftp_upload/57254/57254fig1large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 2" class="xfigimg" src="/files/ftp_upload/57254/57254fig2.jpg" /> 
Figure 2: (a) Variation of magnetic pressure generated by NdFeB, N52-2.54 &#215; 2.54 &#215; 1.27 cm3 magnet as a function of the gap (i.e., lay-up thickness). The inset shows a photograph of the experimental set-up used for measuring the magnetic pressure. (b) The initial and final magnetic pressure applied during the curing of plain weave/INF (WM-PW-INF), random mat/INF(WM-RM-INF), and random mat/EPON (WM-RM-EPON) laminates. <a href="/files/ftp_upload/57254/57254fig2large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 3" class="xfigimg" src="/files/ftp_upload/57254/57254fig3.jpg" /> 
Figure 3: SEM images of the 6-ply E-glass/epoxy composite laminates fabricated using a wet lay-up vacuum bag process with and without using magnetic pressure. (a) W-PW-INF (plain weave/INF laminate, without external pressure), (b) WM-PW-INF (plain weave/INF laminate, with magnetic pressure), (c) W-RM-INF (random mat/INF laminate, without external pressure), (d) WM-RM-INF (random mat/INF laminate, with magnetic pressure), (e) W-RM-EPON (random mat/EPON laminate, without external pressure), and (f) WM-RM-EPON (random mat/EPON laminate, with magnetic pressure). <a href="/files/ftp_upload/57254/57254fig3large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>

Watch this Scientific Journal Video about Magnet Assisted Composite Manufacturing: A Flexible New Technique for Achieving High Consolidation Pressure in Vacuum Bag/Lay-Up Processes at JoVE.com

Magnet Assisted Composite Manufacturing: A Flexible New Technique for Achieving High Consolidation Pressure in Vacuum Bag/Lay-Up Processes

A new technique for applying consolidation pressure on the vacuum bag lay-up to fabricate composite laminates is described. The goal of this protocol is to develop a simple, cost-effective technique to improve the quality of laminates fabricated by the wet lay-up vacuum bag method.

This work demonstrates a protocol to improve the quality of composite laminates fabricated by wet lay-up vacuum bag processes using the recently developed ...

magnet-assisted-composite-manufacturing-flexible-new-technique-for

Research

JoVE Journal

Engineering

13.4K Views.  University of Oklahoma. A new technique for applying consolidation pressure on the vacuum bag lay-up to fabricate composite laminates is described. The goal of this protocol is to develop a simple, cost-effective technique to improve the quality of laminates fabricated by the wet lay-up vacuum bag method.

Video: Magnet Assisted Composite Manufacturing: A Flexible New Technique for Achieving High Consolidation Pressure in Vacuum Bag/Lay-Up Processes

Manufacturing of Three-dimensionally Microstructured Nanocomposites through Microfluidic Infiltration

Microstructured composite beams reinforced with complex three-dimensionally (3D) patterned nanocomposite microfilaments are fabricated via nanocomposite in&#64257;ltration of 3D interconnected microfluidic networks. The manufacturing of the reinforced beams begins with the fabrication of microfluidic networks, which involves layer-by-layer deposition of fugitive ink filaments using a dispensing robot, filling the empty space between filaments using a low viscosity resin, curing the resin and finally removing the ink.&#160;Self-supported 3D structures with other geometries and many layers (e.g.&#160;a few hundreds layers) could be built using this method. The resulting tubular micro&#64258;uidic networks are then infiltrated with thermosetting nanocomposite suspensions containing nanofillers (e.g.&#160;single-walled carbon nanotubes), and subsequently cured. The infiltration is done by applying a pressure gradient between two ends of the empty network (either by applying a vacuum or vacuum-assisted microinjection). Prior to the infiltration, the nanocomposite suspensions are prepared by dispersing nanofillers into polymer matrices using ultrasonication and three-roll mixing methods. The nanocomposites (i.e.&#160;materials infiltrated) are then solidified under UV exposure/heat cure, resulting in a 3D-reinforced composite structure. The technique presented here enables the design of functional nanocomposite macroscopic products for microengineering applications such as actuators and sensors.

Three-dimensional (3D) microstructured composite beams are fabricated through the directed and localized infiltration of nanocomposites into 3D porous microfluidic networks. The flexibility of this manufacturing method enables the utilization of different thermosetting materials and nanofillers in order to achieve a variety of functional 3D reinforced nanocomposite macroscopic products.

Microstructured composite beams reinforced with complex three-dimensionally (3D) patterned nanocomposite microfilaments are fabricated via nanocomposite ...

Chemistry

Indirect Fabrication of Lattice Metals with Thin Sections Using Centrifugal Casting

One of the typical methods to manufacture 3D lattice metals is the direct-metal additive manufacturing (AM) process such as Selective Laser Melting (SLM) and Electron Beam Melting (EBM). In spite of its potential processing capability, the direct AM method has several disadvantages such as high cost, poor surface finish of final products, limitation in material selection, high thermal stress, and anisotropic properties of parts. We propose a cost-effective method to manufacture 3D lattice metals. The objective of this study is to provide a detailed protocol on fabrication of 3D lattice metals having a complex shape and a thin wall thickness; e.g., octet truss made of Al and Cu alloys having a unit cell length of 5 mm and a cell wall thickness of 0.5 mm. An overall experimental procedure is divided into eight sections: (a) 3D printing of sacrificial patterns (b) melt-out of support materials (c) removal of residue of support materials (d) pattern assembly (e) investment (f) burn-out of sacrificial patterns (g) centrifugal casting (h) post-processing for final products. The suggested indirect AM technique provides the potential to manufacture ultra-lightweight lattice metals; e.g., lattice structures with Al alloys. It appears that the process parameters should be properly controlled depending on materials and lattice geometry, observing the final products of octet truss metals by the indirect AM technique.

An indirect additive manufacturing method combining a 3D printing of polymers with a centrifugal casting is outlined for manufacturing 3D octet truss metals (Al and Cu alloys) having a unit cell length of 5 mm with a wall thickness of 0.5 mm.

One of the typical methods to manufacture 3D lattice metals is the direct-metal additive manufacturing (AM) process such as Selective Laser Melting (SLM) ...

Strain Sensing Based on Multiscale Composite Materials Reinforced with Graphene Nanoplatelets

The electrical response of NH2-functionalized graphene nanoplatelets composite materials under strain was studied. Two different manufacturing methods are proposed to create the electrical network in this work: (a) the incorporation of the nanoplatelets into the epoxy matrix and (b) the coating of the glass fabric with a sizing filled with the same nanoplatelets. Both types of multiscale composite materials, with an in-plane electrical conductivity of ~10-3 S/m, showed an exponential growth of the electrical resistance as the strain increases due to distancing between adjacent functionalized graphene nanoplatelets and contact loss between overlying ones. The sensitivity of the materials analyzed during this research, using the described procedures, has been shown to be higher than commercially available strain gauges. The proposed procedures for self-sensing of the structural composite material would facilitate the structural health monitoring of components in difficult to access emplacements such as offshore wind power farms. Although the sensitivity of the multiscale composite materials was considerably higher than the sensitivity of metallic foils used as strain gauges, the value reached with NH2 functionalized graphene nanoplatelets coated fabrics was nearly an order of magnitude superior. This result elucidated their potential to be used as smart fabrics to monitor human movements such as bending of fingers or knees. By using the proposed method, the smart fabric could immediately detect the bending and recover instantly. This fact permits precise monitoring of the time of bending as well as the degree of bending.

The integration of conductive nanoparticles, such as graphene nanoplatelets, into glass fiber composite materials creates an intrinsic electrical network susceptible to strain. Here, different methods to obtain strain sensors based on the addition of graphene nanoplatelets into the epoxy matrix or as a coating on glass fabrics are proposed.

The electrical response of NH2-functionalized graphene nanoplatelets composite materials under strain was studied. Two different manufacturing methods are ...

Experimental Implementation of a New Composite Fabrication Method: Exposing Bare Fibers on the Composite Surface by the Soft Layer Method

The bipolar plate is a key component in proton exchange membrane fuel cells (PEMFCs) and vanadium redox flow batteries (VRFBs). It is a multi-functional component that should have high electrical conductivity, high mechanical properties, and high productivity.
In this regard, a carbon fiber/epoxy resin composite can be an ideal material to replace the conventional graphite bipolar plate, which often leads to the catastrophic failure of the entire system because of its inherent brittleness. Though the carbon/epoxy composite has high mechanical properties and is easy to manufacture, the electrical conductivity in the through-thickness direction is poor because of the resin-rich layer that forms on its surface. Therefore, an expanded graphite coating was adopted to solve the electrical conductivity issue. However, the expanded graphite coating not only increases the manufacturing costs but also has poor mechanical properties.
In this study, a method to expose fibers on the composite surface is demonstrated. There are currently many methods that can expose fibers by surface treatment after the fabrication of the composite. This new method, however, does not require surface treatment because the fibers are exposed during the manufacture of the composite. By exposing bare carbon fibers on the surface, the electrical conductivity and mechanical strength of the composite are increased drastically.

A protocol to expose bare fibers on the composite surface by eliminating resin rich area is presented. The fibers are exposed during fabrication of the composites, not by the post surface treatment. The exposed carbon composites exhibit high electrical conductivity in the through-thickness direction and high mechanical property.

The bipolar plate is a key component in proton exchange membrane fuel cells (PEMFCs) and vanadium redox flow batteries (VRFBs). It is a multi-functional ...

Manufacturing Of Robust Natural Fiber Preforms Utilizing Bacterial Cellulose as Binder

A novel method of manufacturing rigid and robust natural fiber preforms is presented here. This method is based on a papermaking process, whereby loose and short sisal fibers are dispersed into a water suspension containing bacterial cellulose. The fiber and nanocellulose suspension is then filtered (using vacuum or gravity) and the wet filter cake pressed to squeeze out any excess water, followed by a drying step. This will result in the hornification of the bacterial cellulose network, holding the loose natural fibers together.
Our method is specially suited for the manufacturing of rigid and robust preforms of hydrophilic fibers. The porous and hydrophilic nature of such fibers results in significant water uptake, drawing in the bacterial cellulose dispersed in the suspension. The bacterial cellulose will then be filtered against the surface of these fibers, forming a bacterial cellulose coating. When the loose fiber-bacterial cellulose suspension is filtered and dried, the adjacent bacterial cellulose forms a network and hornified to hold the otherwise loose fibers together.
The introduction of bacterial cellulose into the preform resulted in a significant increase of the mechanical properties of the fiber preforms. This can be attributed to the high stiffness and strength of the bacterial cellulose network. With this preform, renewable high performance hierarchical composites can also be manufactured by using conventional composite production methods, such as resin film infusion (RFI) or resin transfer molding (RTM). Here, we also describe the manufacturing of renewable hierarchical composites using double bag vacuum assisted resin infusion.

We present a novel method of manufacturing rigid and robust short natural fiber preforms using a papermaking process. Bacterial cellulose acts simultaneously as the binder for the loose fibers and provides rigidity to the fiber preforms. These preforms can be infused with a resin to produce truly green hierarchical composites.

A novel method of manufacturing rigid and robust natural fiber preforms is presented here. This method is based on a papermaking process, whereby loose ...

Bioengineering

Negative Additive Manufacturing of Complex Shaped Boron Carbides

Boron carbide (B4C) is one of the hardest materials in existence. However, this attractive property also limits its machineability into complex shapes for high wear, high hardness, and lightweight material applications such as armors. To overcome this challenge, negative additive manufacturing (AM) is employed to produce complex geometries of boron carbides at various length scales. Negative AM first involves gelcasting a suspension into a 3D-printed plastic mold. The mold is then dissolved away, leaving behind a green body as a negative copy. Resorcinol-formaldehyde (RF) is used as a novel gelling agent because unlike traditional hydrogels, there is little to no shrinkage, which allows for extremely complex molds to be used. Furthermore, this gelling agent can be pyrolyzed to leave behind ~50 wt% carbon, which is a highly effective sintering aid for B4C. Due to this highly homogenous distribution of in situ carbon within the B4C matrix, less than 2% porosity can be achieved after sintering. This protocol highlights in detail the methodology for creating near fully dense boron carbide parts with highly complex geometries.

A method called negative additive manufacturing is used to produce near fully dense complex shaped boron carbide parts of various length scales. This technique is possible via the formulation of a novel suspension involving resorcinol-formaldehyde as a unique gelling agent that leaves behind a homogenous carbon sintering aid after pyrolysis.

Boron carbide (B4C) is one of the hardest materials in existence. However, this attractive property also limits its machineability into complex shapes for ...

Operation of the Collaborative Composite Manufacturing (CCM) System

The automated tape placement and the automated fiber placement (AFP) machines provide a safer working environment and reduce the labor intensity of workers than the traditional manual fiber placement does. Thus, the production accuracy, repeatability and efficiency of composite manufacturing are significantly improved. However, the current AFP systems can only produce the composite components with large open surface or simple revolution parts, which cannot meet the growing interest in small complex or closed structures from industry.
In this research, by employing a 1-degree of freedom (DoF) rotational stage, a 6-RSS parallel robot, and a 6-DoF serial robot, the dexterity of the AFP system can be significantly improved for manufacturing complex composite parts. The rotational stage mounted on the parallel robot is utilized to hold the mandrel and the serial robot carries the placement head to mimic two human hands that have enough dexterity to lay the fiber to the mandrel with complex contour.
Although the CCM system increases the flexibility of composite manufacturing, it is quite time-consuming or even impossible to generate the feasible off-line path, which ensures uniform lay-up of subsequent fibers considering the constraints like singularities, collisions between the fiber placement head and mandrel, smooth fiber direction change and keeping the fiber placement head along the norm of the part&#39;s surface, etc. Moreover, due to the existing positioning error of the robots, the on-line path correction is needed. Therefore, the on-line pose correction algorithm is proposed to correct the paths of both parallel and serial robots, and to keep the relative path between the two robots unchanged through the visual feedback when the constraint or singularity problems in the off-line path planning occur. The experimental results demonstrate the designed CCM system can fulfill the movement needed for manufacturing a composite structure with Y-shape.

Operation of the Collaborative Composite Manufacturing CCM System

A collaborative composite manufacturing system is developed for robotic lay-up of composite laminates using the prepreg tape. The proposed system allows the production of composite laminates with high levels of geometrical complexity. The issues in the path planning, coordination of the robots and control are addressed in the proposed method.

The automated tape placement and the automated fiber placement (AFP) machines provide a safer working environment and reduce the labor intensity of ...

Fabrication and Design of Wood-Based High-Performance Composites

Delignified densified wood is a new promising and sustainable material that possesses the potential to replace synthetic materials, such as glass fiber reinforced composites, due to its excellent mechanical properties. Delignified wood, however, is rather fragile in a wet state, which makes handling and shaping challenging. Here we present two fabrication processes, closed-mold densification and vacuum densification, to produce high-performance cellulose composites based on delignified wood, including an assessment of their advantages and limitations. Further, we suggest strategies for how the composites can be re-used or decomposed at the end-of-life cycle. Closed-mold densification has the advantage that no elaborate lab equipment is needed. Simple screw clamps or a press can be used for densification. We recommend this method for small parts with simple geometries and large radii of curvature. Vacuum densification in an open-mold process is suitable for larger objects and complex geometries, including small radii of curvature. Compared to the closed-mold process, the open-mold vacuum approach only needs the manufacture of a single mold cavity.

Delignified densified wood represents a new promising lightweight, high-performance and bio-based material with great potential to partially substitute natural fiber reinforced- or glass fiber reinforced composites in the future. We here present two versatile fabrication routes and demonstrate the possibility to create complex composite parts.

Delignified densified wood is a new promising and sustainable material that possesses the potential to replace synthetic materials, such as glass fiber ...

A Paired Bead and Magnet Array for Molding Microwells with Variable Concave Geometries

A spheroid culture is a useful tool for understanding cellular behavior in that it provides an in vivo-like three-dimensional environment. Various spheroid production methods such as non-adhesive surfaces, spinner flasks, hanging drops, and microwells have been used in studies of cell-to-cell interaction, immune-activation, drug screening, stem cell differentiation, and organoid generation. Among these methods, microwells with a three-dimensional concave geometry have gained the attention of scientists and engineers, given their advantages of uniform-sized spheroid generation and the ease with which the responses of individual spheroids can be monitored. Even though cost-effective methods such as the use of flexible membranes and ice lithography have been proposed, these techniques incur serious drawbacks such as difficulty in controlling the pattern sizes, achievement of high aspect ratios, and production of larger areas of microwells. To overcome these problems, we propose a robust method for fabricating concave microwells without the need for complex high-cost facilities. This method utilizes a 30 x 30 through-hole array, several hundred micrometer-order steel beads, and magnetic force to fabricate 900 microwells in a 3 cm x 3 cm polydimethylsiloxane (PDMS) substrate. To demonstrate the applicability of our method to cell biological applications, we cultured adipose stem cells for 3 days and successfully produced spheroids using our microwell platform. In addition, we performed a magnetostatic simulation to investigate the mechanism, whereby magnetic force was used to trap the steel beads in the through-holes. We believe that the proposed microwell fabrication method could be applied to many spheroid-based cellular studies such as drug screening, tissue regeneration, stem cell differentiation, and cancer metastasis.

This manuscript introduces a robust method of fabricating concave microwells without the need for complex high-cost facilities. Using magnetic force, steel beads, and a through-hole array, several hundred microwells were formed in a 3 cm x 3 cm polydimethylsiloxane (PDMS) substrate.

A spheroid culture is a useful tool for understanding cellular behavior in that it provides an in vivo-like three-dimensional environment. Various ...

Fabrication and Mechanical Property Assessment of Fiber Composite Laminates

Measuring the Mechanical Properties of Glass Fiber Reinforcement Polymer Composite Laminates Obtained by Different Fabrication Processes

The traditional wet hand lay-up process (WL) has been widely applied in the manufacturing of fiber composite laminates. However, due insufficiency in the forming pressure, the mass fraction of fiber is reduced and lots of air bubbles are trapped inside, resulting in low-quality laminates (low stiffness and strength). The wet hand lay-up/vacuum bag (WLVB) process for the fabrication of composite laminates is based on the traditional wet hand lay-up process, using a vacuum bag to remove air bubbles and provide pressure, and then carrying out the heating and curing process. 
Compared with the traditional hand lay-up process, laminates manufactured by the WLVB process show superior mechanical properties, including better strength and stiffness, higher fiber volume fraction, and lower void volume fraction, which are all benefits for composite laminates. This process is completely manual, and it is greatly influenced by the skills of the preparation personnel. Therefore, the products are prone to defects such as voids and uneven thickness, leading to unstable qualities and mechanical properties of the laminate. Hence, it is necessary to finely describe the WLVB process, finely control steps, and quantify material ratios, in order to ensure the mechanical properties of laminates. 
This paper describes the meticulous process of the WLVB process for preparing woven plain patterned glass fiber reinforcement composite laminates (GFRPs). The fiber volume content of laminates was calculated using the formula method, and the calculated results showed that the fiber volume content of WL laminates was 42.04%, while that of WLVB laminates was 57.82%, increasing by 15.78%. The mechanical properties of the laminates were characterized using tensile and impact tests. The experimental results revealed that with the WLVB process, the strength and modulus of the laminates were enhanced by 17.4% and 16.35%, respectively, and the specific absorbed energy was increased by 19.48%.

Author Spotlight: Enhancing Fiber Composite Laminate Quality with the Wet Hand Lay-Up/Vacuum Bag Process 

This paper describes a fabrication process for fiber-reinforced polymer matrix composite laminates obtained using the wet hand lay-up/vacuum bag method.

The traditional wet hand lay-up process (WL) has been widely applied in the manufacturing of fiber composite laminates. However, due insufficiency in the ...