Name: fluid-cell raman spectroscopy for operando studies of reaction and transport phenomena during silicate glass corrosion
Uploaded: 2025-05-09T13:20:00.000+00:00
Duration: 6 min 48 s
Description: Fluid-cell Raman Spectroscopy (FCRS) enables the real-time and space-resolved (operando) study of reaction mechanisms, kinetics, and their mutual ...

<ol>
	<li>Belan&#231;on, M. P., Sandrini, M., Zanuto, V. S., Muniz, R. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Glassy+materials+for+Silicon-based+solar+panels:+Present+and+future.">Glassy materials for Silicon-based solar panels: Present and future.</a> J Non-Crystalline Solids. 619, 122548 (2023).</li><li>Iacocca, R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Factors+affecting+the+chemical+durability+of+glass+used+in+the+pharmaceutical+industry.">Factors affecting the chemical durability of glass used in the pharmaceutical industry.</a> AAPS PharmSciTech. 11 (3), 1340-1349 (2010).</li><li>Grambow, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+general+rate+equation+for+nuclear+waste+glass+corrosion.">A general rate equation for nuclear waste glass corrosion.</a> MRS Online Proc Lib. 44, 15-27 (1984).</li><li>Gin, S., Taron, M., Arena, H., Delaye, J. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+structural+disorder+induced+by+external+irradiation+with+heavy+ions+on+the+alteration+of+a+four+oxide+borosilicate+glass.">Effect of structural disorder induced by external irradiation with heavy ions on the alteration of a four oxide borosilicate glass.</a> NPJ Mater Degrad. 8, 64 (2024).</li><li>Geisler, T., Dohmen, L., Lenting, C., Fritzsche, M. B. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Real-time+in+situ+observations+of+reaction+and+transport+phenomena+during+silicate+glass+corrosion+by+fluid-cell+Raman+spectroscopy.">Real-time in situ observations of reaction and transport phenomena during silicate glass corrosion by fluid-cell Raman spectroscopy.</a> Nat Mater. 18, 342-348 (2019).</li><li>Stroncik, N. A., Schmincke, H. U. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Evolution+of+palagonite:+Crystallization,+chemical+changes,+and+element+budget.">Evolution of palagonite: Crystallization, chemical changes, and element budget.</a> Geochem Geophys Geosyst. 2 (7), 1017 (2001).</li><li>Staudigel, H., Hart, S. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Alteration+of+basaltic+glass:+Mechanisms+and+significance+for+the+oceanic+crust-seawater+budget.">Alteration of basaltic glass: Mechanisms and significance for the oceanic crust-seawater budget.</a> Geochim Cosmochim Acta. 47, 337-350 (1983).</li><li>Udi, U. J., Yussof, M. M., Ayagi, K. M., Bedon, C., Kamarudin, M. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Environmental+degradation+of+structural+glass+systems:+A+review+of+experimental+research+and+main+influencing+parameters.">Environmental degradation of structural glass systems: A review of experimental research and main influencing parameters.</a> Ain Shams Eng J. 14, 101970 (2023).</li><li>Maj&#233;rus, O., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Glass+alteration+in+atmospheric+conditions:+crossing+perspectives+from+cultural+heritage,+glass+industry,+and+nuclear+waste+management.">Glass alteration in atmospheric conditions: crossing perspectives from cultural heritage, glass industry, and nuclear waste management.</a> NPJMater Degrad. 4, 27 (2020).</li><li>Grambow, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nuclear+waste+glasses+-+How+durable.">Nuclear waste glasses - How durable.</a> Elements. 2, 357-364 (2006).</li><li>Hellmann, R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanometre-scale+evidence+for+interfacial+dissolution-reprecipitation+control+of+silicate+glass+corrosion.">Nanometre-scale evidence for interfacial dissolution-reprecipitation control of silicate glass corrosion.</a> Nat Mater. 14, 307-311 (2015).</li><li>Gin, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Origin+and+consequences+of+silicate+glass+passivation+by+surface+layers.">Origin and consequences of silicate glass passivation by surface layers.</a> Nat Comm. 6, 6360-6360 (2015).</li><li>Gin, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+controversial+role+of+inter-diffusion+in+glass+alteration.">The controversial role of inter-diffusion in glass alteration.</a> Chem Geol. 440, 115-123 (2016).</li><li>Gin, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+international+initiative+on+long-term+behavior+of+high-level+nuclear+waste+glass.">An international initiative on long-term behavior of high-level nuclear waste glass.</a> Mater Today. 16, 243-248 (2013).</li><li>Frugier, P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=SON68+Nuclear+glass+dissolution+kinetics:+Current+state+of+knowledge+and+basis+of+the+new+GRAAL+model.">SON68 Nuclear glass dissolution kinetics: Current state of knowledge and basis of the new GRAAL model.</a> J Nuclear Mater. 380, 8-21 (2008).</li><li>Bunker, B. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Molecular+mechanisms+for+corrosion+of+silica+and+silicate+glasses.">Molecular mechanisms for corrosion of silica and silicate glasses.</a> J Non-Crystalline Solids. 179, 300-308 (1994).</li><li>Cailleteau, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Insight+into+silicate-glass+corrosion+mechanisms.">Insight into silicate-glass corrosion mechanisms.</a> Nat Mater. 7, 978-983 (2008).</li><li>Gin, S., Ryan, J. V., Schreiber, D. K., Neeway, J., Cabi&#233;, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Contribution+of+atom-probe+tomography+to+a+better+understanding+of+glass+alteration+mechanisms:+Application+to+a+nuclear+glass+specimen+altered+25years+in+a+granitic+environment.">Contribution of atom-probe tomography to a better understanding of glass alteration mechanisms: Application to a nuclear glass specimen altered 25years in a granitic environment.</a> Chem Geol. 349 - 350, 99-109 (2013).</li><li>Geisler, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+mechanism+of+borosilicate+glass+corrosion+revisited.">The mechanism of borosilicate glass corrosion revisited.</a> Geochim Cosmochim Acta. 158, 112-129 (2015).</li><li>Geisler, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Aqueous+corrosion+of+borosilicate+glass+under+acidic+conditions:+A+new+corrosion+mechanism.">Aqueous corrosion of borosilicate glass under acidic conditions: A new corrosion mechanism.</a> J Non-Crystalline Solids. 356, 1458-1465 (2010).</li><li>Putnis, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Why+mineral+interfaces+matter.">Why mineral interfaces matter.</a> Science. 343, 1441-1442 (2014).</li><li>Putnis, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Mineral+replacement+reactions:+from+macroscopic+observations+to+microscopic+mechanisms.">Mineral replacement reactions: from macroscopic observations to microscopic mechanisms.</a> Mineralogical Magazine. 66, 689-708 (2002).</li><li>Lenting, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Towards+a+unifying+mechanistic+model+for+silicate+glass+corrosion.">Towards a unifying mechanistic model for silicate glass corrosion.</a> NPJ Mater Degrad. 2, 28 (2018).</li><li>Fritzsche, M. B. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> The aqueous corrosion of borosilicate glasses studied in operando by in situ fluid-cell Raman spectroscopy. Dissertation. , (2023).</li><li>Iler, K. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> The chemistry of silica: Solubility, polymerization, colloid and surface properties and biochemistry of silica. , (1979).</li><li>Gin, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+fate+of+silicon+during+glass+corrosion+under+alkaline+conditions:+A+mechanistic+and+kinetic+study+with+the+International+Simple+Glass.">The fate of silicon during glass corrosion under alkaline conditions: A mechanistic and kinetic study with the International Simple Glass.</a> Geochim Cosmochim Acta. 151, 68-85 (2015).</li><li>Putnis, C., Ruiz-Agudo, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+mineral-water+interface:+Where+minerals+react+with+the+environment.">The mineral-water interface: Where minerals react with the environment.</a> Elements. 9, 177-182 (2013).</li><li>Icenhower, J. P., Steefel, C. I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dissolution+rate+of+borosilicate+glass+SON68:+A+method+of+quantification+based+upon+interferometry+and+implications+for+experimental+and+natural+weathering+rates+of+glass.">Dissolution rate of borosilicate glass SON68: A method of quantification based upon interferometry and implications for experimental and natural weathering rates of glass.</a> Geochim Cosmochim Acta. 157, 147-163 (2015).</li><li>Icenhower, J. P., Steefel, C. I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Experimentally+determined+dissolution+kinetics+of+SON68+glass+at+90&#176;C+over+a+silica+saturation+interval:+Evidence+against+a+linear+rate+law.">Experimentally determined dissolution kinetics of SON68 glass at 90&#176;C over a silica saturation interval: Evidence against a linear rate law.</a> J Nuc Mater. 439, 137-147 (2013).</li><li>Lenting, C., Geisler, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Corrosion+of+ternary+borosilicate+glass+in+acidic+solution+studied+in+operando+by+fluid-cell+Raman+spectroscopy.">Corrosion of ternary borosilicate glass in acidic solution studied in operando by fluid-cell Raman spectroscopy.</a> NPJ Mater Degrad. 5, 37 (2021).</li><li>L&#246;nartz, M. I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+effect+of+heavy+ion+irradiation+on+the+forward+dissolution+rate+of+borosilicate+glasses+studied+in+situ+and+real+time+by+fluid-cell+raman+spectroscopy.">The effect of heavy ion irradiation on the forward dissolution rate of borosilicate glasses studied in situ and real time by fluid-cell raman spectroscopy.</a> Materials. 12 (9), 1480 (2019).</li><li>M&#252;ller, G., Fritzsche, M. B. K., Dohmen, L., Geisler, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Feedbacks+and+non-linearity+of+silicate+glass+alteration+in+hyperalkaline+solution+studied+by+in+operando+fluid-cell+Raman+spectroscopy.">Feedbacks and non-linearity of silicate glass alteration in hyperalkaline solution studied by in operando fluid-cell Raman spectroscopy.</a> Geochim Cosmochim Acta. 329, 1-21 (2022).</li><li>M&#252;ller, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Raman spectroscopic ex situ and in situ. investigations of the aqueous corrosion of soda-lime silicate glasses. , (2019).</li><li>Sulzbach, M., Geisler, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+replacement+of+celestine+(SrSO4)+by+strontianite+(SrCO3)+in+aqueous+solution+studied+in+situ+and+in+real+time+using+fluid-cell+Raman+spectroscopy.">The replacement of celestine (SrSO4) by strontianite (SrCO3) in aqueous solution studied in situ and in real time using fluid-cell Raman spectroscopy.</a> Minerals. 14 (2), 164 (2024).</li><li>Dohmen, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> In situ .observations of reaction and transport phenomena during silicate glass corrosion by fluid-cell Raman spectroscopy: Method development and applications. Unpubl. PhD thesis. , (2019).</li><li>Everall, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Confocal+Raman+microscopy:+Why+the+depth+resolution+and+spatial+accuracy+can+be+much+worse+than+you+think.">Confocal Raman microscopy: Why the depth resolution and spatial accuracy can be much worse than you think.</a> Appl Spectrosc. 54, 1515-1520 (2000).</li><li>Everall, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Depth+profiling+with+confocal+raman+microscopy,+part+II.">Depth profiling with confocal raman microscopy, part II.</a> Spectroscopy. 19, 22-27 (2004).</li><li>Everall, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+influence+of+out-of-focus+sample+regions+on+the+surface+specificity+of+confocal+Raman+microscopy.">The influence of out-of-focus sample regions on the surface specificity of confocal Raman microscopy.</a> Appl Spectrosc. 62, 591-598 (2008).</li><li>Hauke, K., Kehren, J., B&#246;hme, N., Zimmer, S., Geisler-Wierwille, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+situ+hyperspectral+Raman+Imaging:+A+new+method+to+investigate+sintering+processes+of+ceramic+material+at+high-temperature.">In situ hyperspectral Raman Imaging: A new method to investigate sintering processes of ceramic material at high-temperature.</a> Appl Sci. 9, 1310 (2019).</li><li>Davis, K. M., Tomozawa, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+infrared+spectroscopic+study+of+water-related+species+in+silica+glasses.">An infrared spectroscopic study of water-related species in silica glasses.</a> J Non-Crystalline Solids. 201, 177-198 (1996).</li><li>Long, D. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Raman spectroscopy. , (1977).</li></ol>

<table><tbody><tr><td>Cross screws (6 pieces)</td><td>---</td><td>---</td><td></td></tr><tr><td>Blue silicone wire</td><td>Reichelt Elektronik</td><td></td><td>cross-section:&amp;nbsp; 1.5 mm&amp;sup2;, length: 2 m</td></tr><tr><td>Capacitor</td><td>Reichelt Elektronik</td><td></td><td>capacity: 100 nF</td></tr><tr><td>Connectors according to user&amp;lsquo;s choice</td><td>Reichelt Elektronik</td><td></td><td></td></tr><tr><td>Eurotherm Controller 3216</td><td>Eurotherm/Emerson</td><td>Order Code 3216 CC VH LXXX X XXX G ENG XXXXX</td><td></td></tr><tr><td>Flangeless Ferrules ETFE&amp;nbsp;</td><td>Darwin Microfluidics</td><td>SKU: ID-P-200X</td><td>1/4&quot;-28 for 1/16&quot; OD&amp;nbsp;</td></tr><tr><td>Fluid Cell (container + lid)</td><td>home made</td><td>---</td><td>technical drawing provided in the appendix (S1-S2)</td></tr><tr><td>Heating element, metal-ceramic heater (MCH) disc</td><td>Alibaba</td><td></td><td>D: 30 mm, H: 1.5 mm; https://german.alibaba.com/product-detail/DC-Power-Supply-30mm-MCH-Round-1600118228465.html?spm=a&lt;br/&gt; 2700.7724857.0.0.7cde5nqq5nqq2n</td></tr><tr><td>Horiba HR800 Raman spectrometer</td><td>HORIBA</td><td></td><td></td></tr><tr><td>LabSpec 6.5.1.24 Spectroscopy Suite</td><td></td><td></td><td></td></tr><tr><td>Mains Cable with plug, load+neutral (L+N)</td><td>Reichelt Elektronik</td><td></td><td>length: 2 m</td></tr><tr><td>Mains Fuse 1A&amp;nbsp;</td><td>Reichelt Elektronik</td><td></td><td>5x20 mm&amp;sup2;</td></tr><tr><td>Mains Fuse Holder&amp;nbsp;</td><td>Reichelt Elektronik</td><td></td><td>5x20 mm&amp;sup2;</td></tr><tr><td>Mains rocker switch&amp;nbsp;</td><td>Reichelt Elektronik</td><td></td><td>230VAC 2A</td></tr><tr><td>Microfluidic Fittings Adapter Female Luer to 1/4-28 Male&amp;nbsp;</td><td>Darwin Microfluidics</td><td>SKU: ID-P-618</td><td></td></tr><tr><td>Millex Syringe filters</td><td>Merck</td><td>SLGPR33RS</td><td></td></tr><tr><td>NaHCO&lt;sub&gt;3&lt;/sub&gt;</td><td>Merck</td><td>CAS-144-55-8</td><td></td></tr><tr><td>NMOS Mosfet F1010N</td><td>Reichelt Elektronik</td><td></td><td></td></tr><tr><td>Plastic Enclosure</td><td>Reichelt Elektronik</td><td>TEKO KL22</td><td>Enclosure 178x128x72</td></tr><tr><td>PTFE sample holder</td><td>home made</td><td>---</td><td></td></tr><tr><td>PTFE Tubing&amp;nbsp;</td><td>Darwin Microfluidics</td><td>BL-PTFE-1608-20</td><td>1/16&quot; OD</td></tr><tr><td>Red silicone wire</td><td>Reichelt Elektronik</td><td></td><td>cross-section: 1.5 mm&amp;sup2;, length: 2 m</td></tr><tr><td>Resistor</td><td>Reichelt Elektronik</td><td></td><td>1/4W, 10kOhm</td></tr><tr><td>Resistor</td><td>Reichelt Elektronik</td><td></td><td>1/4W, 2.2kOhm</td></tr><tr><td>Sapphire Window&amp;nbsp;</td><td>Edmund Optics GmbH</td><td>#71-225</td><td>D: 15 mm H: 100 &amp;micro;m</td></tr><tr><td>Shut-Off Valve 1/4-28&amp;nbsp;</td><td>Darwin Microfluidics</td><td>SKU: ID-P-782&amp;nbsp;</td><td></td></tr><tr><td>Silicone washer</td><td>ART Elektromechanik</td><td>customized for institute</td><td>OD: 15mm, ID: 8 mm; H: 0.5 mm</td></tr><tr><td>Switching-mode power supply&amp;nbsp;</td><td>Reichelt Elektronik</td><td>SNT RS 25 5</td><td>5V, 5A</td></tr><tr><td>Thermocouple Extension Cable, Plug/Socket, Type K</td><td>RS Components GmbH</td><td></td><td>2 m</td></tr><tr><td>Thermocouple Socket, Type K, Case Mount</td><td>RS Components GmbH</td><td></td><td></td></tr><tr><td>Thermocouple, Type K</td><td>TC Direct</td><td></td><td>D: 1 mm, L: 50-100mm</td></tr><tr><td>Various cables for in-box wiring</td><td>Reichelt Elektronik</td><td></td><td></td></tr></tbody></table>

fluid-cell raman spectroscopy for operando studies of reaction and transport phenomena during silicate glass corrosion

用于硅酸盐玻璃腐蚀过程中反应和传递现象 的原位 研究的流池拉曼光谱

Fluid-cell Raman Spectroscopy (FCRS) enables the real-time and space-resolved (operando) study of reaction mechanisms, kinetics, and their mutual ...

fluid-cell-raman-spectroscopy-for-operando-studies-reaction-transport

Research

JoVE Journal

Chemistry

Fluid-cell Raman Spectroscopy for operando Studies of Reaction and Transport Phenomena during Silicate Glass Corrosion

120 次观看.  University of Bonn. 液池拉曼光谱 （FCRS） 能够在微观水平、高温下对硅酸盐玻璃水腐蚀过程中的反应和传输现象进行 原位 实时观察。在不中断正在进行的过程的情况下，FCRS 提供有关反应机理、动力学和传输过程的信息。

视频: 用于硅酸盐玻璃腐蚀过程中反应和传递现象 的原位 研究的流池拉曼光谱

Exfoliation of Egyptian Blue and Han Blue, Two Alkali Earth Copper Silicate-based Pigments

In a visualized example of the ancient past connecting with modern times, we describe the preparation and exfoliation of CaCuSi4O10 and BaCuSi4O10, the colored components of the historic Egyptian blue and Han blue pigments. The bulk forms of these materials are synthesized by both melt flux and solid-state routes, which provide some control over the crystallite size of the product. The melt flux process is time intensive, but it produces relatively large crystals at lower reaction temperatures. In comparison, the solid-state method is quicker yet requires higher reaction temperatures and yields smaller crystallites. Upon stirring in hot water, CaCuSi4O10 spontaneously exfoliates into monolayer nanosheets, which are characterized by TEM and PXRD. BaCuSi4O10 on the other hand requires ultrasonication in organic solvents to achieve exfoliation. Near infrared imaging illustrates that both the bulk and nanosheet forms of CaCuSi4O10 and BaCuSi4O10 are strong near infrared emitters. Aqueous CaCuSi4O10 and BaCuSi4O10 nanosheet dispersions are useful because they provide a new way to handle, characterize, and process these materials in colloidal form.

The preparation and exfoliation of CaCuSi4O10&#160;and BaCuSi4O10 are described. Upon stirring in hot water, CaCuSi4O10 spontaneously exfoliates into monolayers, whereas BaCuSi4O10&#160;requires ultrasonication in organic solvents. Near infrared (NIR) imaging illustrates the NIR emission properties of these materials, and aqueous dispersions of these nanomaterials are useful for solution processing.

埃及蓝色和汉蓝，两碱地球铜硅酸盐类颜料剥落

In a visualized example of the ancient past connecting with modern times, we describe the preparation and exfoliation of CaCuSi4O10 and BaCuSi4O10, the ...

科研

化学

Transport of Surface-modified Carbon Nanotubes through a Soil Column

Carbon nanotubes (CNTs) are widely manufactured nanoparticles, which are being utilized in a number of consumer products, such as sporting goods, electronics and biomedical applications. Due to their accelerating production and use, CNTs constitute a potential environmental risk if they are released to soil and groundwater systems. It is therefore essential to improve the current understanding of environmental fate and transport of CNTs. The transport and retention of CNTs in both natural and artificial media have been reported in literature, but the findings widely vary and are thus not conclusive. There are a number of physical and chemical parameters responsible for variation in retention and transport. In this study, a complete procedure of selected multiwalled carbon nanotubes (MWCNTs) is presented starting from their surface modification to a complete set of laboratory column experiments at critical physical and chemical scenarios. Results indicate that the stability of the commercially available MWCNTs are critical with their attached surface functional group which can also influence the transport and retention of MWCNT through the surrounding medium.

Surface properties of a nanoparticle are important for their interaction with the surrounding medium. Therefore the surface modification of carbon nanotubes can be critical for their transport and retention through porous media. Here, lab scale column experiments are used to understand the possible transport and retention of these nanoparticles.

表面修饰碳纳米管通过土柱运输

Carbon nanotubes (CNTs) are widely manufactured nanoparticles, which are being utilized in a number of consumer products, such as sporting goods, ...

X-ray Powder Diffraction in Conservation Science: Towards Routine Crystal Structure Determination of Corrosion Products on Heritage Art Objects

The crystal structure determination and refinement process of corrosion products on historic art objects using laboratory high-resolution X-ray powder diffraction (XRPD) is presented in detail via two case studies.
The first material under investigation was sodium copper formate hydroxide oxide hydrate, Cu4Na4O(HCOO)8(OH)2&#8729;4H2O (sample 1) which forms on soda glass/copper alloy composite historic objects (e.g., enamels) in museum collections, exposed to formaldehyde and formic acid emitted from wooden storage cabinets, adhesives, etc. This degradation phenomenon has recently been characterized as &#34;glass induced metal corrosion&#34;.
For the second case study, thecotrichite, Ca3(CH3COO)3Cl(NO3)2&#8729;6H2O (sample 2), was chosen, which is an efflorescent salt forming needlelike crystallites on tiles and limestone objects which are stored in wooden cabinets and display cases. In this case, the wood acts as source for acetic acid which reacts with soluble chloride and nitrate salts from the artifact or its environment.
The knowledge of the geometrical structure helps conservation science to better understand production and decay reactions and to allow for full quantitative analysis in the frequent case of mixtures.

Modern high resolution X-ray powder diffraction (XRPD) in the laboratory is used as an efficient tool to determine crystal structures of long-known corrosion products on historic objects.

X射线粉末衍射在保护科学:迈向文物艺术品腐蚀产物的常规晶体结构测定

The crystal structure determination and refinement process of corrosion products on historic art objects using laboratory high-resolution X-ray powder ...

Preparation of Biopolymer Aerogels Using Green Solvents

Although the first reports on aerogels made by Kistler1 in the 1930s dealt with aerogels from both inorganic oxides (silica and others) and biopolymers (gelatin, agar, cellulose), only recently have biomasses been recognized as an abundant source of chemically diverse macromolecules for functional aerogel materials. Biopolymer aerogels (pectin, alginate, chitosan, cellulose, etc.) exhibit both specific inheritable functions of starting biopolymers and distinctive features of aerogels (80-99% porosity and specific surface up to 800 m2/g). This synergy of properties makes biopolymer aerogels promising candidates for a wide gamut of applications such as thermal insulation, tissue engineering and regenerative medicine, drug delivery systems, functional foods, catalysts, adsorbents and sensors. This work demonstrates the use of pressurized carbon dioxide (5 MPa) for the ionic cross linking of amidated pectin into hydrogels. Initially a biopolymer/salt dispersion is prepared in water. Under pressurized CO2 conditions, the pH of the biopolymer solution is lowered to 3 which releases the crosslinking cations from the salt to bind with the biopolymer yielding hydrogels. Solvent exchange to ethanol and further supercritical CO2 drying (10 - 12 MPa) yield aerogels. Obtained aerogels are ultra-porous with low density (as low as 0.02 g/cm3), high specific surface area (350 - 500 m2/g) and pore volume (3 - 7 cm3/g for pore sizes less than 150 nm).

A new way for the production of biopolymer-based aerogels by carbon dioxide (CO2) induced gelation is shown. The technique utilizes pressurized carbon dioxide (5 MPa) for the production of biopolymer hydrogels and supercritical CO2 (12 MPa) to convert gels into aerogels. The only solvents needed besides CO2 are water and ethanol.

生物聚合物气凝胶制备使用绿色溶剂

Although the first reports on aerogels made by Kistler1 in the 1930s dealt with aerogels from both inorganic oxides (silica and others) and biopolymers ...

A Novel Technique for Raman Analysis of Highly Radioactive Samples Using Any Standard Micro-Raman Spectrometer

A novel approach for the Raman measurement of nuclear materials is reported in this paper. It consists of the enclosure of the radioactive sample in a tight capsule that isolates the material from the atmosphere. The capsule can optionally be filled with a chosen gas pressurized up to 20 bars. The micro-Raman measurement is performed through an optical-grade quartz window. This technique permits accurate Raman measurements with no need for the spectrometer to be enclosed in an alpha-tight containment. It therefore allows the use of all options of the Raman spectrometer, like multi-wavelength laser excitation, different polarizations, and single or triple spectrometer modes. Some examples of measurements are shown and discussed. First, some spectral features of a highly radioactive americium oxide sample (AmO2) are presented. Then, we report the Raman spectra of neptunium oxide (NpO2) samples, the interpretation of which is greatly improved by employing three different excitation wavelengths, 17O doping, and a triple mode configuration to measure the anti-stokes Raman lines. This last feature also allows the estimation of the sample surface temperature. Finally, data that were measured on a sample from Chernobyl lava, where phases are identified by Raman mapping, are shown.

We present a technique for Raman spectroscopic analysis of highly radioactive samples compatible with any standard micro-Raman spectrometer, without any radioactive contamination of the instrument. We also show some applications using actinide compounds and irradiated fuel materials.

一种新技术用于拉曼分析高放射性样品使用任何标准的微拉曼光谱仪

A novel approach for the Raman measurement of nuclear materials is reported in this paper. It consists of the enclosure of the radioactive sample in a ...

Quantifying X-Ray Fluorescence Data Using MAPS

The quantification of X-ray fluorescence (XRF) microscopy maps by fitting the raw spectra to a known standard is crucial for evaluating chemical composition and elemental distribution within a material. Synchrotron-based XRF has become an integral characterization technique for a variety of research topics, particularly due to its non-destructive nature and its high sensitivity. Today, synchrotrons can acquire fluorescence data at spatial resolutions well below a micron, allowing for the evaluation of compositional variations at the nanoscale. Through proper quantification, it is then possible to obtain an in-depth, high-resolution understanding of elemental segregation, stoichiometric relationships, and clustering behavior.
This article explains how to use the MAPS fitting software developed by Argonne National Laboratory for the quantification of full 2-D XRF maps. We use as an example results from a Cu(In,Ga)Se2 solar cell, taken at the Advanced Photon Source beamline 2-ID-D at Argonne National Laboratory. We show the standard procedure for fitting raw data, demonstrate how to evaluate the quality of a fit and present the typical outputs generated by the program. In addition, we discuss in this manuscript certain software limitations and offer suggestions for how to further correct the data to be numerically accurate and representative of spatially resolved, elemental concentrations.

Here, we demonstrate the use of the X-ray fluorescence fitting software, MAPS, created by Argonne National Laboratory for the quantification of fluorescence microscopy data. The quantified data that results is useful for understanding the elemental distribution and stoichiometric ratios within a sample of interest.

利用地图量化 X 射线荧光数据

The quantification of X-ray fluorescence (XRF) microscopy maps by fitting the raw spectra to a known standard is crucial for evaluating chemical ...

The Effect of Interfacial Chemical Bonding in TiO2-SiO2 Composites on Their Photocatalytic NOx Abatement Performance

The chemical bonding of particulate photocatalysts to supporting material surfaces is of great importance in engineering more efficient and practical photocatalytic structures. However, the influence of such chemical bonding on the optical and surface properties of the photocatalyst and thus its photocatalytic activity/reaction selectivity behavior has not been systematically studied. In this investigation, TiO2 has been supported on the surface of SiO2 by means of two different methods: (i) by the in situ formation of TiO2 in the presence of sand quartz via a sol-gel method employing tetrabutyl orthotitanium (TBOT); and (ii) by binding the commercial TiO2 powder to quartz on a surface silica gel layer formed from the reaction of quartz with tetraethylorthosilicate (TEOS). For comparison, TiO2 nanoparticles were also deposited on the surfaces of a more reactive SiO2 prepared by a hydrolysis-controlled sol-gel technique as well as through a sol-gel route from TiO2 and SiO2 precursors. The combination of TiO2 and SiO2, through interfacial Ti-O-Si bonds, was confirmed by FTIR spectroscopy and the photocatalytic activities of the obtained composites were tested for photocatalytic degradation of NO according to the ISO standard method (ISO 22197&#8722;1). The electron microscope images of the obtained materials showed that variable photocatalyst coverage of the support surface can successfully be achieved but the photocatalytic activity towards NO removal was found to be affected by the preparation method and the nitrate selectivity is adversely affected by Ti-O-Si bonding.

The Effect of Interfacial Chemical Bonding in TiO2-SiO2 Composites on Their Photocatalytic NOx Abatement Performance

The focus of the present work is to establish means to generate and quantify levels of Ti-O-Si linkages and to correlate these with the photocatalytic properties of the supported TiO2.

界面化学键合在TiO中的作用<sub&gt; 2</sub&gt; -SiO<sub&gt; 2</sub&gt;复合材料对其光催化NOx消除性能的影响

The chemical bonding of particulate photocatalysts to supporting material surfaces is of great importance in engineering more efficient and practical ...

Observation and Analysis of Blinking Surface-enhanced Raman Scattering

From a single molecule at a silver nanoaggregate junction, blinking surface-enhanced Raman scattering (SERS) is observed. Here, a protocol is presented on how to prepare the SERS-active silver nanoaggregate, record a video of certain blinking spots in the microscopic image, and analyze the blinking statistics. In this analysis, a power law reproduces the probability distributions for bright events relative to their duration. The probability distributions for dark events are fitted by a power law with an exponential function. The parameters of the power law represent molecular behavior in both bright and dark states. The random walk model and the speed of the molecule across the entire silver surface can be estimated. It is difficult to estimate even when using averages, autocorrelation functions, and super-resolution SERS imaging. In the future, power law analyses should be combined with spectral imaging, because the origins of blinking cannot be confirmed by this analysis method alone.

This protocol describes the analysis of blinking surface-enhanced Raman scattering due to the random walk of a single molecule on a silver surface using power laws.

闪烁表面增强拉曼散射的观测与分析

From a single molecule at a silver nanoaggregate junction, blinking surface-enhanced Raman scattering (SERS) is observed. Here, a protocol is presented on ...

In Situ Lithiated Reference Electrode: Four Electrode Design for In-operando Impedance Spectroscopy

Extending operating voltage of Li-ion batteries results in higher energy output from these devices. High voltages, however, may trigger or accelerate multiple processes responsible for long-term performance decay. Given the complexity of physical processes occurring inside the cell, it is often challenging to achieve a full understanding of the root causes of this performance degradation. This difficulty arises in part from the fact that any electrochemical measurement of a battery will return the combined contributions of all components in the cell. Incorporation of a reference electrode can solve part of the problem, as it allows the electrochemical reactions of the cathode and the anode to be individually probed. A variation in the voltage range experienced by the cathode, for example, can indicate alterations in the pool of cyclable lithium ions in the full-cell. The structural evolution of the many interphases existing in the battery can also be monitored, by measuring the contributions of each electrode to the overall cell impedance. Such wealth of information amplifies the reach of diagnostic analysis in Li-ion batteries and provides valuable input to the optimization of individual cell components. In this work, we introduce the design of a test cell able to accommodate multiple reference electrodes, and present reference electrodes that are appropriate for each specific type of measurement, detailing the assembly process in order to maximize the accuracy of the experimental results.

The incorporation of reference electrodes in a Li-ion battery provides valuable information to elucidate degradation mechanisms at high voltages. In this article, we present a cell design that accommodates multiple reference electrodes, along with the assembly steps to assure maximum accuracy of the data obtained in electrochemical measurements.

原位锂化参考电极: 四原位阻抗谱的电极设计

Extending operating voltage of Li-ion batteries results in higher energy output from these devices. High voltages, however, may trigger or accelerate ...

The Effect of Charging and Discharging Lithium Iron Phosphate-graphite Cells at Different Temperatures on Degradation

The effect of charging and discharging lithium iron phosphate-graphite cells at different temperatures on their degradation is evaluated systematically. The degradation of the cells is assessed by using 10 charging and discharging temperature permutations ranging from -20 &#176;C to 30 &#176;C. This allows an analysis of the effect of charge and discharge temperatures on aging, and their associations. A total of 100 charge/discharge cycles were carried out. Every 25 cycles a reference cycle was performed to assess the reversible and irreversible capacity degradation. A multi-factor analysis of variance was used, and the experimental results were fitted showing: i) a quadratic relationship between the rate of degradation and the temperature of charge, ii) a linear relationship with the temperature of discharge, and iii) a correlation between the temperature of charge and discharge. It was found that the temperature combination for charging at +30 &#176;C and discharging at -5 &#176;C led to the highest rate of degradation. On the other hand, the cycling in a temperature range from -20 &#176;C to 15 &#176;C (with various combinations of temperatures of charge and discharge), led to a much lower degradation. Additionally, when the temperature of charge is 15 &#176;C, it was found that the degradation rate is nondependent on the temperature of discharge.

This article describes the effect of dissimilar charging/discharging temperatures on the degradation of lithium iron phosphate-graphite pouch cells, aiming at simulating close to real case scenarios. In total, 10 temperature combinations are investigated in the range -20 to 30 &#176;C in order to analyze the impact of temperature on degradation.

不同温度下的磷酸铁锂-石墨电池充放电对降解的影响

The effect of charging and discharging lithium iron phosphate-graphite cells at different temperatures on their degradation is evaluated systematically. ...

用于硅酸盐玻璃腐蚀过程中反应和传递现象的原位研究的流池拉曼光谱

摘要

探索更多视频

此视频中的章节

埃及蓝色和汉蓝，两碱地球铜硅酸盐类颜料剥落

表面修饰碳纳米管通过土柱运输

X射线粉末衍射在保护科学:迈向文物艺术品腐蚀产物的常规晶体结构测定

生物聚合物气凝胶制备使用绿色溶剂

一种新技术用于拉曼分析高放射性样品使用任何标准的微拉曼光谱仪

利用地图量化 X 射线荧光数据

界面化学键合在TiO中的作用

闪烁表面增强拉曼散射的观测与分析

原位锂化参考电极: 四原位阻抗谱的电极设计

不同温度下的磷酸铁锂-石墨电池充放电对降解的影响

用于硅酸盐玻璃腐蚀过程中反应和传递现象 的原位 研究的流池拉曼光谱

摘要

探索更多视频

此视频中的章节

埃及蓝色和汉蓝，两碱地球铜硅酸盐类颜料剥落

表面修饰碳纳米管通过土柱运输

X射线粉末衍射在保护科学:迈向文物艺术品腐蚀产物的常规晶体结构测定

生物聚合物气凝胶制备使用绿色溶剂

一种新技术用于拉曼分析高放射性样品使用任何标准的微拉曼光谱仪

利用地图量化 X 射线荧光数据

界面化学键合在TiO中的作用

闪烁表面增强拉曼散射的观测与分析

原位锂化参考电极: 四原位阻抗谱的电极设计

不同温度下的磷酸铁锂-石墨电池充放电对降解的影响

用于硅酸盐玻璃腐蚀过程中反应和传递现象的原位研究的流池拉曼光谱