Name: template directed synthesis of plasmonic gold nanotubes with tunable ir absorbance
Uploaded: 2013-04-01T12:00:00
Description: Watch this Scientific Journal Video about Template Directed Synthesis of Plasmonic Gold Nanotubes with Tunable IR Absorbance at JoVE.com

This work was supported by the University of Toronto, the Natural Sciences and Engineering Research Council of Canada, the Canadian Foundation for Innovation, and the Ontario Research Fund. DSS thanks the Ontario Ministry for an Early Researcher Award.

1. Forming the Silver Working Electrode
<ol>
	<li>Secure the AAO membrane substrate top side up on a glass plate using a 2-sided adhesive. Note: minimize the membrane area in contact with the adhesive, as it will clog the pores.</li>
	<li>Install the glass plate into the substrate holder of the metal evaporator, close the chamber, and evacuate to a pressure of below 1.0 &mu;Torr.</li>
	<li>Using a resistive source, evaporate silver pellets (&gt;99.99% purity) onto the substrate at a rate of 0.8 &Aring;/sec until a laye...

<ol>
	<li>Lee, W., Ji, R., G&#246;sele, U., Nielsch, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fast+fabrication+of+long-range+ordered+porous+alumina+membranes+by+hard+anodization.">Fast fabrication of long-range ordered porous alumina membranes by hard anodization.</a> Nature Publishing Group. 5 (9), 741-747 (2006).</li><li>Li, F., Zhang, L., Metzger, R. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=On+the+growth+of+highly+ordered+pores+in+anodized+aluminum+oxide.">On the growth of highly ordered pores in anodized aluminum oxide.</a> Chemistry of Materials. 10 (9), 2470-2480 (1998).</li><li>Martin, C. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Template+synthesis+of+electronically+conductive+polymer+nanostructures.">Template synthesis of electronically conductive polymer nanostructures.</a> Accounts of Chemical Research. 28 (2), 61-68 (1995).</li><li>Martin, C. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Membrane-based+synthesis+of+nanomaterials.">Membrane-based synthesis of nanomaterials.</a> Chemistry of Materials. 8 (8), 1739-1746 (1996).</li><li>Possin, G. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+method+for+forming+very+small+diameter+wires.">A method for forming very small diameter wires.</a> Review of Scientific Instruments. 41 (5), 772-774 (1970).</li><li>Goad, D. G. W., Moskovits, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Colloidal+metal+in+aluminum-oxide.">Colloidal metal in aluminum-oxide.</a> Journal of Applied Physics. 49 (5), 2929-2934 (1978).</li><li>Huesmann, D., DiCarmine, P. M., Seferos, D. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Template-synthesized+nanostructure+morphology+influenced+by+building+block+structure.">Template-synthesized nanostructure morphology influenced by building block structure.</a> Journal of Materials Chemistry. 21 (2), 408-40 (2011).</li><li>Steinhart, M., Wendorff, J. H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Polymer+nanotubes+by+wetting+of+ordered+porous+templates.">Polymer nanotubes by wetting of ordered porous templates.</a> Science. 296 (5575), 1997 (2002).</li><li>Hulteen, J. C., Martin, C. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+general+template-based+method+for+the+preparation+of+nanomaterials.">A general template-based method for the preparation of nanomaterials.</a> Journal of Materials Chemistry. 7 (7), 1075-1087 (1997).</li><li>DiCarmine, P. M., Fokina, A., Seferos, D. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Solvent/Electrolyte+Control+of+the+Wall+Thickness+of+Template-Synthesized+Nanostructures.">Solvent/Electrolyte Control of the Wall Thickness of Template-Synthesized Nanostructures.</a> Chemistry of Materials. 23 (16), 3787-3794 (2011).</li><li>Wei, W., Li, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surprisingly+long-range+surface-enhanced+Raman+scattering+(SERS)+on+Au-Ni+multisegmented+nanowires.">Surprisingly long-range surface-enhanced Raman scattering (SERS) on Au-Ni multisegmented nanowires.</a> Angewandte Chemie International Edition. 48 (23), 4210-4212 (2009).</li><li>Qin, L., Zou, S., Xue, C., Atkinson, A., Schatz, G. C., Mirkin, C. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Designing,+fabricating,+and+imaging+Raman+hot+spots.">Designing, fabricating, and imaging Raman hot spots.</a> Proceedings of the National Academy of Sciences of the United States of America. 103 (36), 13300-13303 (2006).</li><li>Ruan, C., Eres, G., Wang, W., Zhang, Z., Gu, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Controlled+Fabrication+of+Nanopillar+Arrays+as+Active+Substrates+for+Surface-Enhanced+Raman+Spectroscopy.">Controlled Fabrication of Nanopillar Arrays as Active Substrates for Surface-Enhanced Raman Spectroscopy.</a> Langmuir. 23 (10), 5757-5760 (2007).</li><li>McPhillips, J., Murphy, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-Performance+Biosensing+Using+Arrays+of+Plasmonic+Nanotubes.">High-Performance Biosensing Using Arrays of Plasmonic Nanotubes.</a> ACS Nano. 4 (4), 2210-2216 (2010).</li><li>Bridges, C. R., DiCarmine, P. M., Seferos, D. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Gold+Nanotubes+as+Sensitive,+Solution-Suspendable+Refractive+Index+Reporters.">Gold Nanotubes as Sensitive, Solution-Suspendable Refractive Index Reporters.</a> Chemistry of Materials. 24 (6), 963-965 (2012).</li><li>Bridges, C. R., DiCarmine, P. M., Fokina, A., Huesmann, D., Seferos, D. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+of+Gold+Nanotubes+with+Variable+Wall+Thicknesses.">Synthesis of Gold Nanotubes with Variable Wall Thicknesses.</a> Journal of Materials Chemistry A. 1, 1127-1133 (2013).</li><li>Kennedy, L. C., Bickford, L. R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+New+Era+for+Cancer+Treatment:+Gold-Nanoparticle-Mediated+Thermal+Therapies.">A New Era for Cancer Treatment: Gold-Nanoparticle-Mediated Thermal Therapies.</a> Small. 7 (2), 169-183 (2010).</li><li>Lee, S. B., Martin, C. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=pH-Switchable,+Ion-Permselective+Gold+Nanotubule+Membrane+Based+on+Chemisorbed+Cysteine.">pH-Switchable, Ion-Permselective Gold Nanotubule Membrane Based on Chemisorbed Cysteine.</a> Analytical Chemistry. 73 (4), 768-775 (2001).</li><li>Velleman, L., Shapter, J. G., Losic, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Gold+nanotube+membranes+functionalised+with+fluorinated+thiols+for+selective+molecular+transport.">Gold nanotube membranes functionalised with fluorinated thiols for selective molecular transport.</a> Journal of Membrane Science. 328 (1-2), 1-2 (2009).</li><li>Sanchez-Castillo, M. A., Couto, C., Kim, W. B., Dumesic, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Gold-Nanotube+Membranes+for+the+Oxidation+of+CO+at+Gas-Water+Interfaces.">Gold-Nanotube Membranes for the Oxidation of CO at Gas-Water Interfaces.</a> Angewandte Chemie( International ed. in English). 43 (9), 1140-1142 (2004).</li><li>Kim, B. Y., Swearingen, C. B., Ho, J. -. A. A., Romanova, E. V., Bohn, P. W., Sweedler, J. V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Direct+Immobilization+of+Fab'+in+Nanocapillaries+for+Manipulating+Mass-Limited+Samples.">Direct Immobilization of Fab' in Nanocapillaries for Manipulating Mass-Limited Samples.</a> Journal of the American Chemical Society. 129 (24), 7620-7626 (2007).</li><li>Delvaux, M., Walcarius, A., Demoustier-Champagne, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrocatalytic+H2O2+amperometric+detection+using+gold+nanotube+electrode+ensembles.">Electrocatalytic H2O2 amperometric detection using gold nanotube electrode ensembles.</a> Analytica Chimica Acta. 525 (2), 221-230 (2004).</li><li>Kohli, P., Wirtz, M., Martin, C. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanotube+Membrane+Based+Biosensors.">Nanotube Membrane Based Biosensors.</a> Electroanalysis. 16 (12), 9-18 (2004).</li><li>Ruppin, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Electromagnetic Surface Modes. , (1982).</li><li>Sonninchsen, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Plasmons in Metal Nanostructures. , (2001).</li><li>Barnes, W. L., Dereux, A., Ebbesen, T. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface+plasmon+subwavelength+optics.">Surface plasmon subwavelength optics.</a> Nature. 424, 824-830 (2003).</li><li>Maier, S. A., Kik, P. G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Local+detection+of+electromagnetic+energy+transport+below+the+diffraction+limit+in+metal+nanoparticle+plasmon+waveguides.">Local detection of electromagnetic energy transport below the diffraction limit in metal nanoparticle plasmon waveguides.</a> Nature Materials. 2 (4), 229-232 (2003).</li><li>Barhoumi, A., Zhang, D., Tam, F., Halas, N. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface-Enhanced+Raman+Spectroscopy+of+DNA.">Surface-Enhanced Raman Spectroscopy of DNA.</a> Journal of the American Chemical Society. 130 (16), 5523-5529 (2008).</li><li>Yin, J., Wu, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=SERS-Active+Nanoparticles+for+Sensitive+and+Selective+Detection+of+Cadmium+Ion+(Cd2.">SERS-Active Nanoparticles for Sensitive and Selective Detection of Cadmium Ion (Cd2.</a> Chemistry of Materials. 23 (21), 4756-4764 (2011).</li><li>Schmucker, A. L., Harris, N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Correlating+Nanorod+Structure+with+Experimentally+Measured+and+Theoretically+Predicted+Surface+Plasmon+Resonance.">Correlating Nanorod Structure with Experimentally Measured and Theoretically Predicted Surface Plasmon Resonance.</a> ACS Nano. 4 (9), 5453-5463 (2010).</li><li>Payne, E. K., Shuford, K. L., Park, S., Schatz, G. C., Mirkin, C. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Multipole+Plasmon+Resonances+in+Gold+Nanorods.">Multipole Plasmon Resonances in Gold Nanorods.</a> The Journal of Physical Chemistry B. 110 (5), 2150-2154 (2006).</li><li>Moskovits, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface-enhanced+spectroscopy.">Surface-enhanced spectroscopy.</a> Reviews of Modern Physics. 57 (3), 783 (1985).</li><li>Sieb, N. R., Wu, N. -. C., Majidi, E., Kukreja, R., Branda, N. R., Gates, B. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Hollow+metal+nanorods+with+tunable+dimensions,+porosity,+and+photonic+properties.">Hollow metal nanorods with tunable dimensions, porosity, and photonic properties.</a> ACS Nano. 3 (6), 1365-1372 (2009).</li><li>Muench, F., Kunz, U., Neetzel, C., Lauterbach, S., Kleebe, H. -. J., Ensinger, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=4-(Dimethylamino)pyridine+as+a+Powerful+Auxiliary+Reagent+in+the+Electroless+Synthesis+of+Gold+Nanotubes.">4-(Dimethylamino)pyridine as a Powerful Auxiliary Reagent in the Electroless Synthesis of Gold Nanotubes.</a> Langmuir. 27 (1), 430-435 (2011).</li><li>Wirtz, M., Martin, C. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Template-Fabricated+Gold+Nanowires+and+Nanotubes.">Template-Fabricated Gold Nanowires and Nanotubes.</a> Advanced Materials. 15 (5), 455-458 (2003).</li><li>Sehayek, T., Lahav, M., Popovitz-Biro, R., Vaskevich, A., Rubinstein, I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Template+Synthesis+of+Nanotubes+by+Room-Temperature+Coalescence+of+Metal+Nanoparticles.">Template Synthesis of Nanotubes by Room-Temperature Coalescence of Metal Nanoparticles.</a> Chemistry of Materials. 17 (14), 3743-3748 (2005).</li><li>Lahav, M., Sehayek, T., Vaskevich, A., Rubinstein, I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanoparticle+Nanotubes.">Nanoparticle Nanotubes.</a> Angewandte Chemie (International ed. in English). 42 (45), 5576-5579 (2003).</li><li>Hua, Z., Yang, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Metal+nanotubes+prepared+by+a+sol-gel+method+followed+by+a+hydrogen+reduction+procedure.">Metal nanotubes prepared by a sol-gel method followed by a hydrogen reduction procedure.</a> Nanotechnology. 17 (20), 5106-5110 (2006).</li><li>Lee, W., Scholz, R., Nielsch, K., G&#246;sele, U. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+Template-Based+Electrochemical+Method+for+the+Synthesis+of+Multisegmented+Metallic+Nanotubes.">A Template-Based Electrochemical Method for the Synthesis of Multisegmented Metallic Nanotubes.</a> Angewandte Chemie (International ed. in English). 44 (37), 6050-6054 (2005).</li><li>Cui, C. -. H., Li, H. -. H., Yu, S. -. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+general+approach+to+electrochemical+deposition+of+high+quality+free-standing+noble+metal+(Pd,+Pt,+Au,+Ag)+sub-micron+tubes+composed+of+nanoparticles+in+polar+aprotic+solvent.">A general approach to electrochemical deposition of high quality free-standing noble metal (Pd, Pt, Au, Ag) sub-micron tubes composed of nanoparticles in polar aprotic solvent.</a> Chemical Communications. 46 (6), 940 (2010).</li><li>Han, X. -. F., Shamaila, S., Sharif, R., Chen, J. -. Y., Liu, H. -. R., Liu, D. -. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Structural+and+Magnetic+Properties+of+Various+Ferromagnetic+Nanotubes.">Structural and Magnetic Properties of Various Ferromagnetic Nanotubes.</a> Advanced Materials. 21 (45), 4619-4624 (2009).</li><li>Hendren, W. R., Murphy, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fabrication+and+optical+properties+of+gold+nanotube+arrays.">Fabrication and optical properties of gold nanotube arrays.</a> Journal of Physics: Condensed Matter. 20 (36), 362203 (2008).</li><li>Lahav, M., Weiss, E. A., Xu, Q., Whitesides, G. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Core-Shell+and+Segmented+Polymer-Metal+Composite+Nanostructures.">Core-Shell and Segmented Polymer-Metal Composite Nanostructures.</a> Nano Letters. 6 (9), 2166-2171 (2006).</li><li>Chen, X., Li, S., Xue, C., Banholzer, M. J., Schatz, G. C., Mirkin, C. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Plasmonic+Focusing+in+Rod-Sheath+Heteronanostructures.">Plasmonic Focusing in Rod-Sheath Heteronanostructures.</a> ACS Nano. 3 (1), 87-92 (2009).</li><li>Banholzer, M. J., Qin, L., Millstone, J. E., Osberg, K. D., Mirkin, C. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=On-wire+lithography:+synthesis,+encoding+and+biological+applications.">On-wire lithography: synthesis, encoding and biological applications.</a> Nature Protocols. 4 (6), 838-848 (2009).</li></ol>

Template directed synthesis of nanorods in AAO membranes has become increasingly popular, however syntheses of nanorods tend to be very sensitive towards minor changes in material and synthesis conditions. Here, a comprehensive understanding of the advantages and limitations of using AAO membranes is outlined, as well as a general guideline for using AAO membranes for electrochemical synthesis of nanostructures.
When purchasing AAO membranes, there are two general types available: asymmetric a...

When their dimensions approach the penetration depth of light (~50 nm; the nanoscale), noble metals, and most importantly gold, exhibit exquisite size, shape and environment dependent optical properties 24, 25. On this scale, direct illumination causes a coherent oscillation of conduction electrons known as the surface plasmon resonance (SPR). SPR is highly dependent on nanostructure size, shape, and the dielectric properties of the surrounding medium. There is great interest in characterizing SPR properties in new materials, as SPR-based devices are emerging for use in sub-wavelength optics, SERS substrates, and ultra-sensitive optical sensors 11-16, 26-29. As such, developing computational methods to more accurately predict how size and structure can vary plasmonic response remains a major goal. The use of AAO membranes affords a convenient way to vary the particle diameter or length, and several important studies use this to correlate measured and calculated plasmonic response with varying particle diameter, length, and aspect ratio 30, 31. Perhaps the most studied and successful use of plasmonic materials is as refractive index based biosensors. For this, resonances in the red to near infrared (NIR) range (~800 - 1,300 nm) are desirable since they are more sensitive to refractive index change, and lie in the "water window" such that they are transmitted through both water and human tissues. Solution-suspendable nanostructures with SPR peaks in this range open intriguing possibilities for in vivo plasmonic biosensing.
Porous AAO has been used to prepare polymer nanotubes or nanowires by electrochemical synthesis or template wetting, and proven to be applicable to a wide variety of materials. AAO membranes are now being used to synthesize solution-suspendable high aspect ratio nanorods and nanostructured arrays that function as high performance plasmonic biosensors or SERS substrates. While AAO membranes have mostly been used as templates for synthesizing solid rods, in some cases it may be desirable for the structure to be hollow. Plasmonic and SERS sensing applications, for example, are surface based, and hollow structures with large surface-area-to-volume ratios may lead to stronger signal generation and higher sensitivity 14, 15, 32. With respect to this, gold nanotubes have been synthesized from various methods including galvanic replacement reactions on silver nanorods 33, electroless plating 34, 35, surface modification of the template pores 36, 37, sol-gel methods 38, and electrodeposition 39-41. These syntheses typically leave poorly formed, porous nanotubes or allow for little control over the size and morphology. Syntheses have also been reported wherein a metallic shell is deposited over a polymer core in an AAO membrane 42, 43. These synthesis leave the gold nanotubes bound to the substrate and rely on template etching to allow for growth of gold around the polymer, thus they cannot be studied in solution. Moreover, template etching has some potential drawbacks. First, non-uniform pore etching along the template wall may lead to a non-uniform gold shell thickness. Second, significant etching (i.e. to make very thick wall tubes) may dissolve pore walls completely.
Very recently, Bridges et al. reported an etchant free method to synthesize gold nanotubes in AAO membranes that uses a sacrificial poly(3-hexyl)thiophene core and yields solution-suspendable gold nanotubes with extremely high refractive index sensitivity 15. From that and subsequent work, it was discovered that in order to deposit gold shells around the polymer core without chemical etching, the polymer must be tubular such that there is interior space for it to collapse, and the polymer must be hydrophobic such that it will collapse onto itself rather than adhere to the template pore walls 16. When hydrophilic polymers are used, a gold "sheath" partially covering the polymer core is observed, indicating the polymer core adheres to one of the walls of the template during gold deposition 44. Herein, the detailed protocol for the synthesis of hollow gold nanotubes that allows for control over length and diameter is described (Figure 1). These solution-suspendable gold nanotubes are promising materials for a wide range of applications including plasmonic biosensing or SERS substrates.

<table border="1">
 <tbody>
 <tr>
 <td></td>
 <td></td>
 <td></td>
 <td>Reagent/Material</td>
 </tr>
 <tr>
 <td>UniKera Standard Membrane</td>
 <td>Synkera Technologies Inc.</td>
 <td>SM-X-Y-13</td>
 <td>Anodic aluminum oxide membranes are available from synkera in various pore sizes ranging from 13 - 150 nm, and thicknesses from 50 to 100 &mu;m. We use the 50 &mu;m ones. They are symmetric, meaning the pore size is uniform from top to bottom.</td>
 </tr>
 <tr>
 <td>Anopore Inorganic Membranes</td>
 <td>Whatman</td>
 <td>6809-7023</td>
 <td>13 mm diameter, 200 nm pore size. These membranes are very fragile. The pore diameters are not uniform throughout, so it is important to always use the bottom of the membrane as the working electrode</td>
 </tr>
 <tr>
 <td>Silver Pellets %99.99</td>
 <td>Kurt J. Lesker</td>
 <td>EVMAG40EXE-D</td>
 <td></td>
 </tr>
 <tr>
 <td>Copper(II) sulfate pentahydrate</td>
 <td>Sigma-Aldrich</td>
 <td>209189</td>
 <td></td>
 </tr>
 <tr>
 <td>Sulfuric acid</td>
 <td>ACP</td>
 <td>S8780</td>
 <td>Caution: corrosive liquid</td>
 </tr>
 <tr>
 <td>Hydrogen peroxide (30%)</td>
 <td>ACP</td>
 <td>H7000</td>
 <td>Caution: oxidizing liquid</td>
 </tr>
 <tr>
 <td>Nitric Acid</td>
 <td>ACP</td>
 <td>N2800</td>
 <td>Caution: corrosive fuming liquid</td>
 </tr>
 <tr>
 <td>Sodium Hydroxide</td>
 <td>Fisher Scientific</td>
 <td>S318-1</td>
 <td>Caution: caustic powder</td>
 </tr>
 <tr>
 <td>Watts Nickel Pure</td>
 <td>Technic Inc.</td>
 <td>130859</td>
 <td>Product is no longer available from Technic inc., however other commercial nickelplating solutions will work. </td>
 </tr>
 <tr>
 <td>Techni-Gold 434HS</td>
 <td>Technic Inc.</td>
 <td>X6763600</td>
 <td>Contains cyanide, do not acidify</td>
 </tr>
 <tr>
 <td>Boron trifluoride diethyl etherate</td>
 <td>Sigma-Aldrich</td>
 <td>175501-100ML</td>
 <td>Must be stored and used under inert atmosphere</td>
 </tr>
 <tr>
 <td>3-hexylthiophene</td>
 <td>Sigma-Aldrich</td>
 <td>399051-5G</td>
 <td></td>
 </tr>
 <tr>
 <td>Deuterium Oxide</td>
 <td>Sigma-Aldrich</td>
 <td>151880-100G</td>
 <td></td>
 </tr>
 <tr>
 <td>Acetonitrile (anhydrous)</td>
 <td>Sigma-Aldrich</td>
 <td>271004</td>
 <td></td>
 </tr>
 <tr>
 <td>Ethanol (anhydrous)</td>
 <td>Caledon Labs</td>
 <td>1500-1-05</td>
 <td></td>
 </tr>
 <tr>
 <td></td>
 <td></td>
 <td></td>
 <td>Equipment</td>
 </tr>
 <tr>
 <td>EC Epsilon potentiostat/galvanostat</td>
 <td>BASi (Bioanalytical Systems, Inc.)</td>
 <td>N/A</td>
 <td>Reference electrodes and platinum wires were included with the potentiostat, and replacements can be purchaes from BASi <a href="http://www.basinc.com/products/ec/epsilon/features.html" target="_blank">http://www.basinc.com/products/ec/epsilon/features.html</a></td>
 </tr>
 <tr>
 <td>Cary 5000 UV-Vis-NIR spectrophotometer</td>
 <td>Agilent Technologies</td>
 <td>N/A</td>
 <td><a href="http://www.chem.agilent.com/en-US/products-services/Instruments-Systems/Molecular-Spectroscopy/Cary-5000-UV-Vis-NIR/Pages/default.aspx" target="_blank">http://www.chem.agilent.com/en-US/products-services/Instruments-Systems/Molecular-Spectroscopy/Cary-5000-UV-Vis-NIR/Pages/default.aspx</a></td>
 </tr>
 <tr>
 <td>Thermomixer R</td>
 <td>Eppendorf</td>
 <td>N/A</td>
 <td><a href="http://www.eppendorf.com/int/index.php?action=products&amp;contentid=1&amp;catalognode=9832" target="_blank">http://www.eppendorf.com/int/index.php?action=products&amp;contentid=1&amp;catalognode=9832</a></td>
 </tr>
 <tr>
 <td>Branson 2510 Ultrasonic Cleaner</td>
 <td>Bransonic</td>
 <td>Z244810 (From Sigma Aldrich)</td>
 <td><a href="http://www.sigmaaldrich.com/catalog/product/aldrich/Z244910?lang=en&amp;region=CA" target="_blank">http://www.sigmaaldrich.com/catalog/product/aldrich/Z244910?lang=en&amp;region=CA</a></td>
 </tr>
 <tr>
 <td>Covap 2 thermal evaporator</td>
 <td>Angstrom Engineering</td>
 <td>N/A</td>
 <td><a href="http://www.angstromengineering.com/covap.html" target="_blank">http://www.angstromengineering.com/covap.html</a></td>
 </tr>
 <tr>
 <td>Millipore Synergy water purification system</td>
 <td>Millipore</td>
 <td>N/A</td>
 <td><a href="http://www.millipore.com/catalogue/module/c9209" target="_blank">http://www.millipore.com/catalogue/module/c9209</a></td>
 </tr>
 </tbody>
</table>

template directed synthesis of plasmonic gold nanotubes with tunable ir absorbance

A nearly parallel array of pores can be produced by anodizing aluminum foils in acidic environments1, 2. Applications of anodic aluminum oxide (AAO) membranes have been under development since the 1990's and have become a common method to template the synthesis of high aspect ratio nanostructures, mostly by electrochemical growth or pore-wetting. Recently, these membranes have become commercially available in a wide range of pore sizes and densities, leading to an extensive library of functional nanostructures being synthesized from AAO membranes. These include composite nanorods, nanowires and nanotubes made of metals, inorganic materials or polymers 3-10. Nanoporous membranes have been used to synthesize nanoparticle and nanotube arrays that perform well as refractive index sensors, plasmonic biosensors, or surface enhanced Raman spectroscopy (SERS) substrates 11-16, as well as a wide range of other fields such as photo-thermal heating 17, permselective transport 18, 19, catalysis 20, microfluidics 21, and electrochemical sensing 22, 23. Here, we report a novel procedure to prepare gold nanotubes in AAO membranes. Hollow nanostructures have potential application in plasmonic and SERS sensing, and we anticipate these gold nanotubes will allow for high sensitivity and strong plasmon signals, arising from decreased material dampening 15.

After each step, one can visibly determine whether or not the synthesis is successful by observing the color of the membrane. After copper deposition (step 2.3) the template will appear purple. During nickel deposition (step 2.5) the template will slowly turn black. After the polymer deposition (step 3.3) the template should appear darker purple/black and more glossy (Figure 2). Typical chronoapmerograms of successful polymer and gold are included (Figure 3). During the final etching ste...

Watch this Scientific Journal Video about Template Directed Synthesis of Plasmonic Gold Nanotubes with Tunable IR Absorbance at JoVE.com

Template Directed Synthesis of Plasmonic Gold Nanotubes with Tunable IR Absorbance

Solution-suspendable gold nanotubes with controlled dimensions can be synthesized by electrochemical deposition in porous anodic aluminum oxide (AAO) membranes using a hydrophobic polymer core. Gold nanotubes and nanotube arrays hold promise for applications in plasmonic biosensing, surface-enhanced Raman spectroscopy, photo-thermal heating, ionic and molecular transport, microfluidics, catalysis and electrochemical sensing.

A nearly parallel array of pores can be produced by anodizing aluminum foils in acidic environments1, 2. Applications of anodic aluminum oxide (AAO) ...

Research

JoVE Journal

Chemistry

Synthesis of Immunotargeted Magneto-plasmonic Nanoclusters

Magnetic and plasmonic properties combined in a single nanoparticle provide a synergy that is advantageous in a number of biomedical applications ...

Synthesis and Catalytic Performance of Gold Intercalated in the Walls of Mesoporous Silica

As a promising catalytically active nano reactor, gold nanoparticles intercalated in mesoporous silica (GMS) were successfully synthesized and properties ...

Hydroquinone Based Synthesis of Gold Nanorods

Gold nanorods are an important kind of nanoparticles characterized by peculiar plasmonic properties. Despite their widespread use in nanotechnology, the ...

Synthesis and Characterization of Fe-doped Aluminosilicate Nanotubes with Enhanced Electron Conductive Properties

The goal of the protocol is to synthesize Fe-doped aluminosilicate nanotubes of the imogolite type with the formula (OH)3Al2-xFexO3SiOH. Doping with Fe ...

Rapid Nanoprobe Signal Enhancement by In Situ Gold Nanoparticle Synthesis

Rapid Nanoprobe Signal Enhancement by In Situ Gold Nanoparticle Synthesis

The use of nanoprobes such as gold, silver, silica or iron-oxide nanoparticles as detection reagents in bioanalytical assays can enable high sensitivity ...

Synthesis and Characterization of Amphiphilic Gold Nanoparticles

Gold nanoparticles covered with a mixture of 1-octanethiol (OT) and 11-mercapto-1-undecane sulfonic acid (MUS) have been extensively studied because of ...

Assembly of Gold Nanorods into Chiral Plasmonic Metamolecules Using DNA Origami Templates

The inherent addressability of DNA origami structures makes them ideal templates for the arrangement of metal nanoparticles into complex plasmonic ...

Synthesis of Information-bearing Peptoids and their Sequence-directed Dynamic Covalent Self-assembly

This protocol presents the use of Lewis acidic multi-role reagents to circumvent kinetic trapping observed during the self-assembly of information-encoded ...

Synthesis of Aptamer-PEI-g-PEG Modified Gold Nanoparticles Loaded with Doxorubicin for Targeted Drug Delivery

Due to drug resistance and toxicity in healthy cells, use of doxorubicin (DOX) has been limited in clinical cancer therapy. This protocol describes the ...

Quantitative SERS Detection of Uric Acid via Formation of Precise Plasmonic Nanojunctions within Aggregates of Gold Nanoparticles and Cucurbit[n]uril

Quantitative SERS Detection of Uric Acid via Formation of Precise Plasmonic Nanojunctions within Aggregates of Gold Nanoparticles and Cucurbit[n]uril

This work describes a rapid and highly sensitive method for the quantitative detection of an important biomarker, uric acid (UA), via surface-enhanced ...