The authors thank Mr. Dylan Errulat and Prof. Muralee Murugesu from the Department of Chemistry and Biomolecular Sciences of the University of Ottawa for the provision of [TbEu(bpm)(tfaa)6] single crystals. E.M.R, N.R., and E.H. gratefully acknowledge the financial support provided by the University of Ottawa, the Canadian Foundation for Innovation (CFI), and the Natural Sciences and Engineering Research Council Canada (NSERC).

CAUTION: It is recommended to use safety goggles specific for the excitation wavelength being used at all times when operating the imager.
1. Configuration of the hyperspectral microscope
NOTE: An overview of the hyperspectral imaging system is given in Figure 2a, with the main components of the imager being described. The imaging system can be used for the detection of the visible or the near-infrared (NIR) emission from a sample. Depending on which detection is desired (visible or NIR), the light goes through two different light paths (Figure 2e). A combination of different beam turning cubes and dichroic filter cubes (optical cubes) must be positioned at specific positions in the instrument to select the respective path.
<ol>
	<li>Power on the computer which is connected to the imaging system. Turn on the computer&#8217;s monitor.</li>
	<li>Set the appropriate optical cube configuration (Figure 2b,c). 
	NOTE: Here, the imager configuration (optical cube configuration) for HSI mapping using UV excitation and visible emission detection is described. However, it is also possible to change it for NIR excitation and visible or NIR emission detection, depending on the sample analyzed. Refer to the section Representative Results for an example.
	<ol>
		<li>Starting from the microscope stage (1 in Figure 2a) and following the emission beam pathway towards the detectors (3 in Figure 2a), leave the first position for an optical cube (4 in Figure 2b) vacant and place the confocal microscope optical cube (DFM1-P01) in the position indicated as 5 in Figure 2b, so that the emission from the sample is directed through the visible light path.</li>
		<li>Looking along the optical path towards the detector, place the visible optical cube (CM1-P01), which contains the dichroic mirror and the filters to direct the visible emission to the detection paths, in the position indicated as 6 in Figure 2b.</li>
		<li>Continuing the path towards the detector, place the confocal pinhole optical cube (DFM1-P01) in the position indicated as 7 in the Figure 2b to direct the light through the visible light detection path. Then, following the path, place the confocal spectrometer optical cube (DFM1-P01) in position 8 in Figure 2c so that the emitted light reaches the detector.</li>
		<li>For the HSI mapping, manually control the detector slit opening (9 in Figure 2c) in order to match with the size of the pinholes that are used (around 50 mm is optimal).</li>
		<li>In the PHySpec software, choose the aperture of the pinhole (5 in Figure 3). 
		NOTE: The smaller the pinhole aperture, the better is the HSI resolution, at the cost of signal intensity.</li>
	</ol>
	</li>
	<li>Turn on the broadband lamp (Figure 2d, inset) by positioning the switch (10 in Figure 2d) into the ON position. To control the intensity of the excitation light, turn the knob indicated by 11 (Figure 2d) to higher (32 &#8211; lowest intensity) or lower values (1 &#8211; highest intensity). Keep the broadband lamp shutter (12 in Figure 2d) closed during the set-up. 
	NOTE: The higher values correspond to higher attenuation of the power density emitted by the lamp, while lower values correspond to lower attenuation.</li>
	<li>Turn on the following hardware in the order given below by setting their switches into the ON position:
	<ol>
		<li>Turn on the ThorLabs motion controller.</li>
		<li>Turn on the Nikon power source.</li>
		<li>Turn on the ASI controller.</li>
		<li>Turn on the Galvo controller.</li>
		<li>Turn on the ProEm detector.</li>
		<li>Turn on the Bayspec detector.</li>
	</ol>
	</li>
	<li>At the computer, open the PHySpec software by double clicking on its icon.
	<ol>
		<li>Press the F8 key on the keyboard in order to initialize the IMA Upconversion system and click the OK button on the Connect to System window. 
		NOTE: Step 1.5.1. can also be performed by clicking on the System tab and then clicking on Connect to arrive to the Connect to System window. Then, the OK button can be clicked to connect the imaging system to the software.</li>
		<li>Ensure that all menus appear on the interface (Color camera, ProEm and Bayspec) as well as the instrument control panel, on the left side of the screen, as shown in Figure 3.</li>
	</ol>
	</li>
</ol>
2. Hyperspectral imaging of a [TbEu(bpm)(tfaa)6] single crystal
<ol>
	<li>In order to prepare the sample, place the crystal on a microscopy glass slide. In case it is needed to use higher magnification, cover the crystal with a thin cover glass and secure it with tape, so that the sample can be placed with the thin cover glass facing toward the objective lens.</li>
	<li>Place the glass slide on which the sample has been prepared on the microscope stage and secure it using the metal arms (Figure 4a,b).</li>
	<li>Move the sample using the joystick (Figure 4c) of the ASI controller in order to position the sample over the objectives in use.</li>
	<li>Manually position the right filter cube in the wheel underneath the objectives (3 in Figure 5) to select the UV excitation of the lamp and to let pass the visible emission towards the detector. 
	NOTE: Additional filter cubes are available to use either green or blue light excitation, thus, having the right filter cube in place is important for the appropriate excitation wavelength.</li>
	<li>Manually position the 20X objective (indicated by 5 in Figure 5) under the sample and press the white button (6 in Figure 5) on the left side of the microscope to turn on the white light.
	<ol>
		<li>Adjust the brightness by turning the knob underneath the white light power button (7 in Figure 5).</li>
	</ol>
	</li>
	<li>In the PHySpec software, press the Play (video) button on the color camera window, which will cause the acquisition of a live scan.
	<ol>
		<li>If the color camera window shows a black image, increase the Exposure Time (2 in Figure 3) and/or the Gain Value (3 in Figure 3) found in the instrument control panel, under the Color Camera tab. If the image viewed is too bright, decrease the exposure time and/or gain value.</li>
		<li>Ensure the forward knob on the right side of the microscope (2 in Figure 5) is set to R in order to send 20% of the signal to the camera/binoculars and 80% of the signal to the detector.</li>
	</ol>
	</li>
	<li>Focus on the sample by adjusting the distance between the objective and the stage (Figure 4b). This is done by turning the knobs shown in Figure 4d on the right side of the microscope. 
	NOTE: The larger knob is used for coarse adjustments, while the smaller knob is for more delicate and small focus changes.</li>
	<li>Ensure that the manually chosen objective is also selected at the software. First, click on the View button in the top menu bar and then click one Show/hide scale bar to display the scale bar on the image (1 in Figure 3). Then, go to the Galvanometer tab in the instruction control panel and select the Objective used (4 in Figure 3). Ensure that the displayed scale bar is correct by selecting the proper objective in the software.</li>
	<li>In the software, select the appropriate detector by going to the tab Diverter (ProEM &#8211; 6 in Figure 3) and gratings by going to the tab Filter (1200 gr/mm in case of ProEM &#8211; 7 in Figure 3) under the SpectraPro SP-2300 tab.</li>
	<li>Open the broadband lamp shutter (12 in Figure 2) to allow the UV excitation of the sample to take place. Turn the intensity knob (11 in Figure 2d) to the desired position (e.g., 8 &#8211; intermediate intensity) to control the intensity of the broadband lamp (UV) excitation.
	<ol>
		<li>To choose between wide field illumination (open aperture) or a smaller spot illumination (more closed aperture), control the size of the UV lamp field aperture using the stick and knobs shown in 4 in Figure 5.</li>
	</ol>
	</li>
	<li>Under the SpectraPro SP-2300 tab, select a wavelength to observe the sample emission.</li>
	<li>If the emission wavelengths of the sample are unknown, acquire an emission spectrum.
	<ol>
		<li>In the sequencer, click on the + sign to add a new sequence (&#8220;node&#8221;) for the acquisition of an emission spectrum.
		<ol>
			<li>Click on Spectrometer and then Spectrum Acquisition (with spectral scan).</li>
			<li>Input a Minimum Wavelength (i.e., 400 nm) and a Maximum Wavelength (i.e., 700 nm) and click OK to set the spectral range in which the spectrum will be recorded.</li>
			<li>Choose the adequate Exposure Time in the left side menu of the software. Choose shorter times (e.g., 0.1 s) for very bright samples and longer times (e.g., 2 s) for dim emitters.</li>
			<li>Adjust the excitation power in case of the broadband lamp (UV) excitation (see step 1.3 above). 
			NOTE: In case of NIR diode excitation, it can be adjusted from the Neutral Density drop-down menu at the left side of the PHySpec software.</li>
		</ol>
		</li>
		<li>On the sequencer, click on the double play button to run the entire sequence. Once the spectrum is shown, note the regions of interest for the detection of the sample emission (e.g. 580 to 640 nm in case of Tb3+- and Eu3+-based samples).</li>
		<li>As needed, optimize signal detection by either changing the focus of the sample or by adjusting the Exposure Time in the PHySpec software. Achieve further optimization of signal detection through the increase of the sample emission intensity by changing the power of the excitation source (broadband lamp), as described above.</li>
	</ol>
	</li>
	<li>Adjust the Exposure Time (e.g., 0.5 s &#8211; 2 in Figure 3) and Gain (3 in Figure 3) of the Color Camera accordingly, to obtain a good quality image. If needed, add the scale bar to the image by clicking at the button Show/hide scale bar at the second row of the menu in the top of the PHySpec software window.</li>
	<li>Recommendation: Prior to acquiring the hyperspectral cube, record a bright field optical microscopy image of the crystal under white light (Figure 6a) and/or UV full (Figure 6b) or confined (Figure 6c) illumination (UV illumination controlled by the shutter aperture, shown as 4 in Figure 5). To do so, with the sample in focus, click on the play button of the color camera.</li>
	<li>Click on File and then Export Window View, choose the desired format to export the obtained image, and save the file with the desired extension (.h5, .JPEG).</li>
	<li>Before acquiring the hyperspectral image, turn off the white light illumination as well as the room light.</li>
	<li>To obtain the hyperspectral cube, write a new sequence. Therefore, in the sequencer, click on the + sign to add a new node.
	<ol>
		<li>Click on Confocal Imager.
		<ol>
			<li>Click on Multi-Spectrum Acquisition. Here, the desired field of view is defined by the number of points to acquire in the x and y directions and the step size. For example, use 100 points in x and 100 points in y with a 5 &#181;m step size to obtain an image of 500 by 500 &#181;m. 
			Note: The total number of acquisition points and the integration time at each point will directly affect the total acquisition time of the hyperspectral cube.
			<ol>
				<li>Input the desired X Position (e.g., 100) and Y Position (e.g., 100) counts as well as the desired Step Size (e.g., 5 &#181;m). Select the Hardware option for the camera sync, for visible emission mapping (and Software option in case of NIR detection). Click OK.</li>
			</ol>
			</li>
		</ol>
		</li>
	</ol>
	</li>
	<li>In the sequencer, click on the newly added Multi-Spectrum Acquisition line to highlight the node.</li>
	<li>Click the Play button to run the selected node. 
	NOTE: The remaining time that the acquisition will take will appear next to the node (in minutes, e.g., 28 min).</li>
	<li>Once the acquisition is complete, save the hyperspectral cube in the appropriate file format (.h5).</li>
</ol>
3. Hyperspectral data analysis
<ol>
	<li>Right after the acquisition, if the saved hyperspectral cube does not open automatically in the software, recover the hyperspectral cube, which was saved as .h5 file, by clicking on File in the top menu bar and then hovering the cursor and click at Open File&#8230;. When the window titled Select data(s) to open pops up, choose the folder where the .h5 file is saved and double click on the file to open it.</li>
	<li>Once the hyperspectral cube file is imported, modify the displayed hyperspectral cube image to show the intensity of a specific spectral wavelength by moving the bar on the top of the cube image to the left (lower wavelength, e.g., 580 nm) or right (higher wavelength, e.g., 638 nm). 
	NOTE: The selected wavelength is displayed in the left side of this upper bar (1 in Figure 7).</li>
	<li>After choosing the wavelength of interest for the analysis (e.g., the maximum intensity, which in the case of [TbEu(bpm)(tfaa)6] is 613.26 nm), make one (or all) of the three possible types of spectral analysis: (A) the spectral distribution in form of an image (2 in Figure 7); (B) an emission intensity profile across a region of interest (3 in Figure 7); (C) extraction of a spectrum at a specific point or region of interest (4 in Figure 7).
	<ol>
		<li>In case of the spectral distribution from an image, use the Crop and Bin function to increase the signal-to-noise ratio in the image. In order to do that, click in the top menu Processing then choose Data and then the option Crop and Bin.</li>
		<li>For an emission intensity profile, on the cube image, right click and select the Create Target or Create X profile or Create Y profile depending if only one point (Target - 5 and 6 in Figure 7) or a line (Profile - 7 and 8 in Figure 7) needs to be analyzed. Select the area of analysis by dragging the target, the horizontal or the vertical line profile with the cursor and move it across the cube.
		<ol>
			<li>Once the profile has been properly selected, right click on the region and select the Add Target to Graph. Chose the option to create a new graph to display the emission intensity (y axis) as a function of the physical position of the target (x axis). The spectrum will appear on the new graph which was inserted (6 and 7 in Figure 7). 
			NOTE: Multiple targets can be created, and these will show up as different colored emission profiles (5 and 6 in Figure 7).</li>
		</ol>
		</li>
		<li>Alternatively, obtain an emission spectrum of a specific area of the sample (9 in Figure 7). To begin with, hover the cursor over the cube image and right click. Click on the Rectangle Selection or Ellipse Selection options on the tab that pops-up.
		<ol>
			<li>Draw the selection shape (e.g., a rectangle) over the desired region by clicking and dragging the cursor across the cube. Once the area has been properly selected, right click on the region and select the Add Selection to Graph.</li>
			<li>At the appearing window Add to Graph, select Create a New Graph to display the emission spectra of the target and click OK. 
			NOTE: A new colored line (8 in Figure 7) will appear on the graph in which the target emission is being shown, with the emission intensity as the y axis and the wavelength at the x axis. This spectrum corresponds to the averaged intensity of the selected area for each wavelength.</li>
		</ol>
		</li>
	</ol>
	</li>
	<li>Once the spectrum is obtained, save it before selecting a new region because only one region can be selected at a time. To do so, select the window in which contains the graph. In the File menu, select Save as and choose to save the graph in the folder of choice, using the name of choice, either in .h5 format, which can be opened in the PHySpec software, or in .csv format, which can be imported in Excel.</li>
</ol>

<ol><li>ElMasry, G., Sun, D. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Principles+of+Hyperspectral+Imaging+Technology%5BTitle%5D)+AND+%22Hyperspectral+Imaging+for+Food+Quality+Analysis+and+Control%22%5BJournal%5D)">Principles of Hyperspectral Imaging Technology.</a> Hyperspectral Imaging for Food Quality Analysis and Control. , 3-43 (2010).</li>
<li>Dong, X., Jakobi, M., Wang, S., Köhler, M. H., Zhang, X., Koch, A. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+review+of+hyperspectral+imaging+for+nanoscale+materials+research%5BTitle%5D)+AND+%22Applied+Spectroscopy+Reviews%22%5BJournal%5D)">A review of hyperspectral imaging for nanoscale materials research.</a> Applied Spectroscopy Reviews. 54 (4), 285-305 (2019).</li>
<li>Yakovliev, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Hyperspectral+Multiplexed+Biological+Imaging+of+Nanoprobes+Emitting+in+the+Short-Wave+Infrared+Region%5BTitle%5D)+AND+%22Nanoscale+Research+Letters%22%5BJournal%5D)">Hyperspectral Multiplexed Biological Imaging of Nanoprobes Emitting in the Short-Wave Infrared Region.</a> Nanoscale Research Letters. 14 (243), 1-11 (2019).</li>
<li>Cheng, W., Sun, D. W., Pu, H., Wei, Q. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Heterospectral+two-dimensional+correlation+analysis+with+near-infrared+hyperspectral+imaging+for+monitoring+oxidative+damage+of+pork+myofibrils+during+frozen+storage%5BTitle%5D)+AND+%22Food+Chemistry%22%5BJournal%5D)">Heterospectral two-dimensional correlation analysis with near-infrared hyperspectral imaging for monitoring oxidative damage of pork myofibrils during frozen storage.</a> Food Chemistry. 248, 119-127 (2018).</li>
<li>Liu, Y., Liu, L., He, Y., Zhu, L., Ma, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Decoding+of+quantum+dots+encoded+microbeads+using+a+hyperspectral+fluorescence+imaging+method%5BTitle%5D)+AND+%22Analytical+Chemistry%22%5BJournal%5D)">Decoding of quantum dots encoded microbeads using a hyperspectral fluorescence imaging method.</a> Analytical Chemistry. 87 (10), 5286-5293 (2015).</li>
<li>Leavesley, S. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Colorectal+cancer+detection+by+hyperspectral+imaging+using+fluorescence+excitation+scanning%5BTitle%5D)+AND+%22Optical+Biopsy+XVI%3A+Toward+Real-Time+Spectroscopic+Imaging+and+Diagnosis%22%5BJournal%5D)">Colorectal cancer detection by hyperspectral imaging using fluorescence excitation scanning.</a> Optical Biopsy XVI: Toward Real-Time Spectroscopic Imaging and Diagnosis. 10489, (2018).</li>
<li>Zhang, H., Salo, D., Kim, D. M., Komarov, S., Tai, Y. -C., Berezin, M. Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Penetration+depth+of+photons+in+biological+tissues+from+hyperspectral+imaging+in+shortwave+infrared+in+transmission+and+reflection+geometries%5BTitle%5D)+AND+%22Journal+of+Biomedical+Optics%22%5BJournal%5D)">Penetration depth of photons in biological tissues from hyperspectral imaging in shortwave infrared in transmission and reflection geometries.</a> Journal of Biomedical Optics. 21 (12), 126006(2016).</li>
<li>Naccache, R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Terahertz+Thermometry%3A+Combining+Hyperspectral+Imaging+and+Temperature+Mapping+at+Terahertz+Frequencies%5BTitle%5D)+AND+%22Laser+and+Photonics+Reviews%22%5BJournal%5D)">Terahertz Thermometry: Combining Hyperspectral Imaging and Temperature Mapping at Terahertz Frequencies.</a> Laser and Photonics Reviews. 11 (5), 1-9 (2017).</li>
<li>Jacques, S. D. M., Egan, C. K., Wilson, M. D., Veale, M. C., Seller, P., Cernik, R. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+laboratory+system+for+element+specific+hyperspectral+X-ray+imaging%5BTitle%5D)+AND+%22Analyst%22%5BJournal%5D)">A laboratory system for element specific hyperspectral X-ray imaging.</a> Analyst. 138 (3), 755-759 (2013).</li>
<li>Birmingham, B., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Probing+the+Effect+of+Chemical+Dopant+Phase+on+Photoluminescence+of+Monolayer+MoS2+Using+in+Situ+Raman+Microspectroscopy%5BTitle%5D)+AND+%22Journal+of+Physical+Chemistry+C%22%5BJournal%5D)">Probing the Effect of Chemical Dopant Phase on Photoluminescence of Monolayer MoS2 Using in Situ Raman Microspectroscopy.</a> Journal of Physical Chemistry C. 123 (25), 15738-15743 (2019).</li>
<li>Marin, R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Harnessing+the+Synergy+between+Upconverting+Nanoparticles+and+Lanthanide+Complexes+in+a+Multiwavelength-Responsive+Hybrid+System%5BTitle%5D)+AND+%22ACS+Photonics%22%5BJournal%5D)">Harnessing the Synergy between Upconverting Nanoparticles and Lanthanide Complexes in a Multiwavelength-Responsive Hybrid System.</a> ACS Photonics. 6 (2), 436-445 (2019).</li>
<li>Gonell, F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Aggregation-induced+heterogeneities+in+the+emission+of+upconverting+nanoparticles+at+the+submicron+scale+unfolded+by+hyperspectral+microscopy%5BTitle%5D)+AND+%22Nanoscale+Advances%22%5BJournal%5D)">Aggregation-induced heterogeneities in the emission of upconverting nanoparticles at the submicron scale unfolded by hyperspectral microscopy.</a> Nanoscale Advances. 1, 2537-2545 (2019).</li>
<li>Errulat, D., Gabidullin, B., Murugesu, M., Hemmer, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Probing+Optical+Anisotropy+and+Polymorph-Dependent+Photoluminescence+in+%5BLn2%5D+Complexes+by+Hyperspectral+Imaging+on+Single+Crystals%5BTitle%5D)+AND+%22Chemistry+-+A+European+Journal%22%5BJournal%5D)">Probing Optical Anisotropy and Polymorph-Dependent Photoluminescence in [Ln2] Complexes by Hyperspectral Imaging on Single Crystals.</a> Chemistry - A European Journal. 24 (40), 10146-10155 (2018).</li>
<li>Panov, N., Marin, R., Hemmer, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Microwave-Assisted+Solvothermal+Synthesis+of+Upconverting+and+Downshifting+Rare-Earth-Doped+LiYF4+Microparticles%5BTitle%5D)+AND+%22Inorganic+Chemistry%22%5BJournal%5D)">Microwave-Assisted Solvothermal Synthesis of Upconverting and Downshifting Rare-Earth-Doped LiYF4 Microparticles.</a> Inorganic Chemistry. 57 (23), 14920-14929 (2018).</li>
<li>Debasu, M. L., Brites, C. D. S., Balabhadra, S., Oliveira, H., Rocha, J., Carlos, L. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoplatforms+for+Plasmon-Induced+Heating+and+Thermometry%5BTitle%5D)+AND+%22ChemNanoMat%22%5BJournal%5D)">Nanoplatforms for Plasmon-Induced Heating and Thermometry.</a> ChemNanoMat. 2 (6), 520-527 (2016).</li>
<li>Nadort, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Quantitative+Imaging+of+Single+Upconversion+Nanoparticles+in+Biological+Tissue%5BTitle%5D)+AND+%22PLoS+ONE%22%5BJournal%5D)">Quantitative Imaging of Single Upconversion Nanoparticles in Biological Tissue.</a> PLoS ONE. 8 (5), 1-13 (2013).</li>
<li>Sava Gallis, D. F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Tunable+Metal-Organic+Framework+Materials+Platform+for+Bioimaging+Applications%5BTitle%5D)+AND+%22ACS+Applied+Materials+and+Interfaces%22%5BJournal%5D)">Tunable Metal-Organic Framework Materials Platform for Bioimaging Applications.</a> ACS Applied Materials and Interfaces. 9 (27), 22268-22277 (2017).</li>
<li>Varghese, S., Das, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Role+of+molecular+packing+in+determining+solid-state+optical+properties+of+%CF%80-conjugated+materials%5BTitle%5D)+AND+%22Journal+of+Physical+Chemistry+Letters%22%5BJournal%5D)">Role of molecular packing in determining solid-state optical properties of π-conjugated materials.</a> Journal of Physical Chemistry Letters. 2 (8), 863-873 (2011).</li>
<li>Yan, D., Evans, D. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Molecular+crystalline+materials+with+tunable+luminescent+properties%3A+From+polymorphs+to+multi-component+solids%5BTitle%5D)+AND+%22Materials+Horizons%22%5BJournal%5D)">Molecular crystalline materials with tunable luminescent properties: From polymorphs to multi-component solids.</a> Materials Horizons. 1 (1), 46-57 (2014).</li>
<li>Mu, S., Oniwa, K., Jin, T., Asao, N., Yamashita, M., Takaishi, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+highly+emissive+distyrylthieno%5B3%2C2-b%5Dthiophene+based+red+luminescent+organic+single+crystal%3A+Aggregation+induced+emission%2C+optical+waveguide+edge+emission%2C+and+balanced+ambipolar+carrier+transport%5BTitle%5D)+AND+%22Organic+Electronics%3A+Physics%2C+Materials%2C+Applications%22%5BJournal%5D)">A highly emissive distyrylthieno[3,2-b]thiophene based red luminescent organic single crystal: Aggregation induced emission, optical waveguide edge emission, and balanced ambipolar carrier transport.</a> Organic Electronics: Physics, Materials, Applications. 34, 23-27 (2016).</li>
<li>Binnemans, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Interpretation+of+europium%28III%29+spectra%5BTitle%5D)+AND+%22Coordination+Chemistry+Reviews%22%5BJournal%5D)">Interpretation of europium(III) spectra.</a> Coordination Chemistry Reviews. 295, 1-45 (2015).</li>
<li>Koyama, H., Fauchet, P. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Anisotropic+polarization+memory+in+thermally+oxidized+porous+silicon%5BTitle%5D)+AND+%22Applied+Physics+Letters%22%5BJournal%5D)">Anisotropic polarization memory in thermally oxidized porous silicon.</a> Applied Physics Letters. 77 (15), 2316-2318 (2000).</li>
<li>Kushida, T., Takushi, E., Oka, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Memories+of+photon+energy%2C+polarization+and+phase+in+luminescence+of+rare+earth+ions+under+resonant+light+excitation%5BTitle%5D)+AND+%22Journal+of+Luminescence%22%5BJournal%5D)">Memories of photon energy, polarization and phase in luminescence of rare earth ions under resonant light excitation.</a> Journal of Luminescence. 12-13, 723-727 (1976).</li>
<li>Onuma, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Spectroscopic+ellipsometry+studies+on+%CE%B2-Ga2O3+films+and+single+crystal%5BTitle%5D)+AND+%22Japanese+Journal+of+Applied+Physics%22%5BJournal%5D)">Spectroscopic ellipsometry studies on β-Ga2O3 films and single crystal.</a> Japanese Journal of Applied Physics. 55 (12), (2016).</li>
<li>Favreau, P. F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Excitation-scanning+hyperspectral+imaging+microscope%5BTitle%5D)+AND+%22Journal+of+Biomedical+Optics%22%5BJournal%5D)">Excitation-scanning hyperspectral imaging microscope.</a> Journal of Biomedical Optics. 19 (4), 046010(2014).</li>
</ol>

The authors have nothing to disclose. The authors have no competing financial interests.

The hyperspectral imaging protocol here described provides a straightforward approach that allows to obtain spectroscopic information at precise locations of the sample. Using the described setup, the spatial resolution (x and y mapping) can reach down to 0.5 &#181;m while the spectral resolution can be of 0.2 nm for the mapping at the visible range and 0.6 nm for the NIR range.
In order to conduct hyperspectral mapping on a single crystal, sample preparation follows an easy ...

Hyperspectral Imaging (HSI) is a technique that generates a spatial map where each x-y coordinate contains a spectral information that could be based on any kind of spectroscopy, namely photoluminescence, absorption and scattering spectroscopies1,2,3. As a result, a 3-dimensional set of data (also called &#8220;hyperspectral cube&#8221;) is obtained, where the x-y coordinates are the spatial axes and the z coordinate is the spectral information from the analyzed sample. Therefore, the hyperspectral cube contains both spatial and spectral information, providing a more detailed spectroscopic investigation of the sample than traditional spectroscopy. While HSI has been known for years in the field of remote sensing (e.g., geology, food industries4), it recently emerged as an innovative technique for the characterization of nanomaterials2,5 or probes for biomedical applications3,6,7,8. Generally speaking, it is not limited to the UV/visible/near-infrared (NIR) domain, but can also be extended using other radiation sources, such as X-rays &#8211; for instance in order to characterize elemental distribution in different materials9 &#8211; or Terahertz radiation, where HSI was used to perform thermal sensing in biological tissues8. Further, photoluminescence mapping has been combined with Raman mapping to probe the optical properties of monolayer MoS210. Yet, amongst the reported applications of optical HSI, there are still only a few examples on HSI of lanthanide-based materials11,12,13,14,15,16,17. For instance, we can cite: detection of cancer in tissues6, analysis of the light penetration depth in biological tissues7, multiplexed biological imaging3, analysis of multicomponent energy transfer in hybrid systems11, and investigation of aggregation-induced changes in spectroscopic properties of upconverting nanoparticles12. Clearly, the attractiveness of HSI arises from its suitability for generating knowledge about environment-specific luminescence, providing simultaneous spatial and spectral information about the probe.
Taking advantage of this powerful technique we herein describe a protocol to investigate the optical anisotropy of the heterodinuclear Tb3+-Eu3+ single crystal [TbEu(bpm)(tfaa)6] (Figure 1a)13. The optical anisotropy observed resulted from the different molecular packing of the Ln3+ ions in the different crystallographic directions (Figure 1b), resulting in some crystal faces showing brighter, others showing dimmer photoluminescence. It was suggested that the increased luminescence intensity at specific faces of the crystal was correlated with more efficient energy transfer along those crystallographic directions where the Ln3+&#183;&#183;&#183;Ln3+ ion distances were the shortest13.
Motivated by these results, we propose the establishment of a detailed methodology to analyze optical anisotropy through HSI, opening the path for better understanding of ion-ion energy transfer processes and tunable luminescent properties stemming from specific molecular arrangement18,19. These structure-properties relationships have been recognized as important aspects for innovative optical materials design including, but not limited to waveguide systems and opto-magnetic storage devices at nano and microscale &#8211; addressing the demand for more efficient and miniaturized optic systems20.

<table><tbody><tr><td>Microscope glass slides</td><td>FisherBrand</td><td>12-550-15</td><td>Glass slides used for sample preparation</td></tr><tr><td>Visible and Near Infrared Hyperspectral Confocal Imager</td><td>PhotonETC</td><td></td><td>Microscope used for the analysis, builted according to the user needs, therefore it is no catalog number</td></tr></tbody></table>

hyperspectral imaging as a tool to study optical anisotropy in lanthanide-based molecular single crystals

In this work, we describe a protocol for a novel application of hyperspectral imaging (HSI) in the analysis of luminescent lanthanide (Ln3+)-based molecular single crystals. As representative example, we chose a single crystal of the heterodinuclear Ln-based complex [TbEu(bpm)(tfaa)6] (bpm=2,2&#8217;-bipyrimidine, tfaa&#8211; =1,1,1-trifluoroacetylacetonate) exhibiting bright visible emission under UV excitation. HSI is an emerging technique that combines 2-dimensional spatial imaging of a luminescent structure with spectral information from each pixel of the obtained image. Specifically, HSI on single crystals of the [Tb-Eu] complex provided local spectral information unveiling variation of the luminescence intensity at different points along the studied crystals. These changes were attributed to the optical anisotropy present in the crystal, which results from the different molecular packing of Ln3+ ions in each one of the directions of the crystal structure. The HSI herein described is an example of the suitability of such technique for spectro-spatial investigations of molecular materials. Yet, importantly, this protocol can be easily extended for other types of luminescent materials (such as micron-sized molecular crystals, inorganic microparticles, nanoparticles in biological tissues, or labelled cells, among others), opening many possibilities for deeper investigation of structure-property relationships. Ultimately, such investigations will provide knowledge to be leveraged into the engineering of advanced materials for a wide range of applications from bioimaging to technological applications, such as waveguides or optoelectronic devices.

To illustrate the configuration of the hyperspectral microscope for the data acquisition on a Ln-based, molecular single crystal (i.e., [TbEu(bpm)(tfaa)6], Figure 1a), Figure 2 shows an overview of the system as well as the right placement of the optical cubes in the setup. Figure 3 shows a screen shot of the PHySpec software containing the menus used during the HSI acquisition. Figure 4 and ...

Watch this Scientific Journal Video about Hyperspectral Imaging as a Tool to Study Optical Anisotropy in Lanthanide-Based Molecular Single Crystals at JoVE.com

Hyperspectral Imaging as a Tool to Study Optical Anisotropy in Lanthanide-Based Molecular Single Crystals

Here, we present a protocol to obtain luminescent hyperspectral imaging data and to analyze optical anisotropy features of lanthanide-based single crystals using a Hyperspectral Imaging System.

In this work, we describe a protocol for a novel application of hyperspectral imaging (HSI) in the analysis of luminescent lanthanide (Ln3+)-based ...

hyperspectral-imaging-as-tool-to-study-optical-anisotropy-lanthanide

Research

JoVE Journal

Chemistry

16.9K Views.  University of Ottawa. Here, we present a protocol to obtain luminescent hyperspectral imaging data and to analyze optical anisotropy features of lanthanide-based single crystals using a Hyperspectral Imaging System.

Video: Hyperspectral Imaging as a Tool to Study Optical Anisotropy in Lanthanide-Based Molecular Single Crystals

High Resolution Phonon-assisted Quasi-resonance Fluorescence Spectroscopy

High resolution optical spectroscopy methods are demanding in terms of either technology, equipment, complexity, time or a combination of these. Here we demonstrate an optical spectroscopy method that is capable of resolving spectral features beyond that of the spin fine structure and homogeneous linewidth of single quantum dots (QDs) using a standard, easy-to-use spectrometer setup. This method incorporates both laser and photoluminescence spectroscopy, combining the advantage of laser line-width limited resolution with multi-channel photoluminescence detection. Such a scheme allows for considerable improvement of resolution over that of a common single-stage spectrometer. The method uses phonons to assist in the measurement of the photoluminescence of a single quantum dot after resonant excitation of its ground state transition. The phonon&#39;s energy difference allows one to separate and filter out the laser light exciting the quantum dot. An advantageous feature of this method is its straight forward integration into standard spectroscopy setups, which are accessible to most researchers.

The manuscript describes a method of phonon-assisted quasi-resonant fluorescence spectroscopy that incorporates both laser-limited resolution and photoluminescence (PL) spectroscopy. This method utilizes optical phonons to provide linewidth-limited resolution spectra of atom-like semiconductor structures in the energy domain. The method is also easily realized with a single spectrometer optical spectroscopy setup.

High resolution optical spectroscopy methods are demanding in terms of either technology, equipment, complexity, time or a combination of these. Here we ...

Engineering

Fabrication Procedures and Birefringence Measurements for Designing Magnetically Responsive Lanthanide Ion Chelating Phospholipid Assemblies

Bicelles are tunable disk-like polymolecular assemblies formed from a large variety of lipid mixtures. Applications range from membrane protein structural studies by nuclear magnetic resonance (NMR) to nanotechnological developments including the formation of optically active and magnetically switchable gels. Such technologies require high control of the assembly size, magnetic response and thermal resistance. Mixtures of 1,2-dimyristoyl-sn-glycero-3-phosphocholine (DMPC) and its lanthanide ion (Ln3+) chelating phospholipid conjugate, 1,2-dimyristoyl-sn-glycero-3-phospho-ethanolamine-diethylene triaminepentaacetate (DMPE-DTPA), assemble into highly magnetically responsive assemblies such as DMPC/DMPE-DTPA/Ln3+ (molar ratio 4:1:1) bicelles. Introduction of cholesterol (Chol-OH) and steroid derivatives in the bilayer results in another set of assemblies offering unique physico-chemical properties. For a given lipid composition, the magnetic alignability is proportional to the bicelle size. The complexation of Ln3+ results in unprecedented magnetic responses in terms of both magnitude and alignment direction. The thermo-reversible collapse of the disk-like structures into vesicles upon heating allows tailoring of the assemblies&#39; dimensions by extrusion through membrane filters with defined pore sizes. The magnetically alignable bicelles are regenerated by cooling to 5 &#176;C, resulting in assembly dimensions defined by the vesicle precursors. Herein, this fabrication procedure is explained and the magnetic alignability of the assemblies is quantified by birefringence measurements under a 5.5 T magnetic field. The birefringence signal, originating from the phospholipid bilayer, further enables monitoring of polymolecular changes occurring in the bilayer. This simple technique is complementary to NMR experiments that are commonly employed to characterize bicelles.

Fabrication procedures for highly magnetically responsive lanthanide ion chelating polymolecular assemblies are presented. The magnetic response is dictated by the assembly size, which is tailored by extrusion through nanopore membranes. The assemblies&#39; magnetic alignability and temperature-induced structural changes are monitored by birefringence measurements, a complimentary technique to nuclear magnetic resonance and small angle neutron scattering.

Bicelles are tunable disk-like polymolecular assemblies formed from a large variety of lipid mixtures. Applications range from membrane protein structural ...

Novel Techniques for Observing Structural Dynamics of Photoresponsive Liquid Crystals

We discuss in this article the experimental measurements of the molecules in liquid crystal (LC) phase using the time-resolved infrared (IR) vibrational spectroscopy and time-resolved electron diffraction. Liquid crystal phase is an important state of matter that exists between the solid and liquid phases and it is common in natural systems as well as in organic electronics. Liquid crystals are orientationally ordered but loosely packed, and therefore, the internal conformations and alignments of the molecular components of LCs can be modified by external stimuli. Although advanced time-resolved diffraction techniques have revealed picosecond-scale molecular dynamics of single crystals and polycrystals, direct observations of packing structures and ultrafast dynamics of soft materials have been hampered by blurry diffraction patterns. Here, we report time-resolved IR vibrational spectroscopy and electron diffractometry to acquire ultrafast snapshots of a columnar LC material bearing a photoactive core moiety. Differential-detection analyses of the combination of time-resolved IR vibrational spectroscopy and electron diffraction are powerful tools for characterizing structures and photoinduced dynamics of soft materials.

Here, we present the protocols of differential-detection analyses of time-resolved infrared vibrational spectroscopy and electron diffraction which enable observations of the deformations of local structures around photoexcited molecules in a columnar liquid crystal, giving an atomic perspective on the relationship between the structure and the dynamics of this photoactive material.

We discuss in this article the experimental measurements of the molecules in liquid crystal (LC) phase using the time-resolved infrared (IR) vibrational ...

Methods of Ex Situ and In Situ Investigations of Structural Transformations: The Case of Crystallization of Metallic Glasses

We demonstrate the use of two nuclear-based analytical methods that can follow the modifications of microstructural arrangement of iron-based metallic glasses (MGs). Despite their amorphous nature, the identification of hyperfine interactions unveils faint structural modifications. For this purpose, we have employed two techniques that utilize nuclear resonance among nuclear levels of a stable 57Fe isotope, namely M&#246;ssbauer spectrometry and nuclear forward scattering (NFS) of synchrotron radiation. The effects of heat treatment upon (Fe2.85Co1)77Mo8Cu1B14 MG are discussed using the results of ex situ and in situ experiments, respectively. As both methods are sensitive to hyperfine interactions, information on structural arrangement as well as on magnetic microstructure is readily available. M&#246;ssbauer spectrometry performed ex situ describes how the structural arrangement and magnetic microstructure appears at room temperature after the annealing under certain conditions (temperature, time), and thus this technique inspects steady states. On the other hand, NFS data are recorded in situ during dynamically changing temperature and NFS examines transient states. The use of both techniques provides complementary information. In general, they can be applied to any suitable system in which it is important to know its steady state but also transient states.

Methods of Ex Situ and In Situ Investigations of Structural Transformations: The Case of Crystallization of Metallic Glasses

Here, we present a protocol to describe ex situ and in situ investigations of structural transformations in metallic glasses. We employed nuclear-based analytical methods which inspect hyperfine interactions. We demonstrate the applicability of M&#246;ssbauer spectrometry and nuclear forward scattering of synchrotron radiation during temperature-driven experiments.

We demonstrate the use of two nuclear-based analytical methods that can follow the modifications of microstructural arrangement of iron-based metallic ...

Synchrotron X-ray Microdiffraction and Fluorescence Imaging of Mineral and Rock Samples

In this report, we describe a detailed procedure for acquiring and processing&#160;x-ray microfluorescence (&#956;XRF), and Laue and powder microdiffraction two-dimensional (2D) maps at beamline 12.3.2 of the Advanced Light Source (ALS), Lawrence Berkeley National Laboratory. Measurements can be performed on any sample that is less than 10 cm x 10 cm x 5 cm, with a flat exposed surface. The experimental geometry is calibrated using standard materials (elemental standards for XRF, and crystalline samples such as Si, quartz, or Al2O3 for diffraction). Samples are aligned to the focal point of the x-ray microbeam, and raster scans are performed, where each pixel of a map corresponds to one measurement, e.g., one XRF spectrum or one diffraction pattern. The data are then processed using the in-house developed software XMAS, which outputs text files, where each row corresponds to a pixel position. Representative data from moissanite and an olive snail shell are presented to demonstrate data quality, collection, and analysis strategies.

We describe a beamline setup meant to carry out rapid two-dimensional x-ray fluorescence and x-ray microdiffraction mapping of single crystal or powder samples using either Laue (polychromatic radiation) or powder (monochromatic radiation) diffraction. The resulting maps give information about strain, orientation, phase distribution, and plastic deformation.

In this report, we describe a detailed procedure for acquiring and processing&#160;x-ray microfluorescence (&#956;XRF), and Laue and powder ...

Spectral and Angle-Resolved Magneto-Optical Characterization of Photonic Nanostructures

Photonic crystals are periodic nanostructures that can support a variety of confined electromagnetic modes. Such confined modes are usually accompanied by local enhancement of electric field intensity that strengthens light-matter interactions, enabling applications such as surface-enhanced Raman scattering (SERS) and surface plasmon enhanced sensing. In the presence of magneto-optically active materials, the local field enhancement gives rise to anomalous magneto-optical activity. Typically, the confined modes of a given photonic crystal depend strongly on the wavelength and incidence angle of the incident electromagnetic radiation. Thus, spectral and angular-resolved measurements are needed to fully identify them as well as to establish their relationship with the magneto-optical activity of the crystal. In this article, we describe how to use a Fourier-plane (back focal plane) microscope to characterize magneto-optically active samples. As a model system, here we use a plasmonic grating built out of magneto-optically active Au/Co/Au multilayer. In the experiments, we apply a magnetic field on the grating in situ and measure its reciprocal space response, obtaining the magneto-optical response of the grating over a range of wavelengths and incident angles. This information enables us to build a complete map of the plasmonic band structure of the grating and the angle and wavelength dependent magneto-optical activity. These two images allow us to pinpoint the effect that the plasmon resonances have on the magneto-optical response of the grating. The relatively small magnitude of magneto-optical effects requires a careful treatment of the acquired optical signals. To this end, an image processing protocol for obtaining magneto-optical response from the acquired raw data is laid out.

Photonic band structure enables understanding how confined electromagnetic modes propagate within a photonic crystal. In photonic crystals that incorporate magnetic elements, such confined and resonant optical modes are accompanied by enhanced and modified magneto-optical activity. We describe a measurement procedure to extract the magneto-optical band structure by Fourier space microscopy.

Photonic crystals are periodic nanostructures that can support a variety of confined electromagnetic modes. Such confined modes are usually accompanied by ...

Sample Preparation and Transfer Protocol for In-Vacuum Long-Wavelength Crystallography on Beamline I23 at Diamond Light Source

Long-wavelength macromolecular crystallography (MX) exploits the anomalous scattering properties of elements, such as sulfur, phosphorus, potassium, chlorine, or calcium, that are often natively present in macromolecules. This enables the direct structure solution of proteins and nucleic acids via experimental phasing without the need of additional labelling. To eliminate the significant air absorption of X-rays in this wavelength regime, these experiments are performed in a vacuum environment. Beamline I23 at Diamond Light Source, UK, is the first synchrotron instrument of its kind, designed and optimized for MX experiments in the long wavelength range towards 5 &#197;. 
To make this possible, a large vacuum vessel encloses all endstation components of the sample environment. The necessity to maintain samples at cryogenic temperatures during storage and data collection in vacuum requires the use of thermally conductive sample holders. This facilitates efficient heat removal to ensure sample cooling to approximately 50 K. The current protocol describes the procedures used for sample preparation and transfer of samples into vacuum on beamline I23. Ensuring uniformity in practices and methods already established within the macromolecular crystallography community, sample cooling to liquid nitrogen temperature can be performed in any laboratory setting equipped with standard MX tools. 
Cryogenic storage and transport of samples only require standard commercially available equipment. Specialized equipment is required for the transfer of cryogenically cooled crystals from liquid nitrogen into the vacuum endstation. Bespoke sample handling tools and a dedicated Cryogenic Transfer System (CTS) have been developed in house. Diffraction data collected on samples prepared using this protocol show excellent merging statistics, indicating that the quality of samples is unaltered during the procedure. This opens unique opportunities for in-vacuum MX in a wavelength range beyond standard synchrotron beamlines.

Here, we present a protocol for cryogenic sample preparation and transfer of crystals into the vacuum endstation on beamline I23 at Diamond Light Source, for long-wavelength macromolecular X-ray crystallography experiments.

Long-wavelength macromolecular crystallography (MX) exploits the anomalous scattering properties of elements, such as sulfur, phosphorus, potassium, ...

Biochemistry

Time-Resolved Photoluminescence Spectroscopy of Semiconductor Nanocrystals and Other Fluorophores

Time-resolved photoluminescence (TRPL) is a key technique for understanding the photophysics of semiconductor nanocrystals and light-emitting materials in general. This work is a primer for setting up and conducting TRPL on nanocrystals and related materials using single-photon-counting (SPC) systems. Basic sources of error in the measurement can be avoided by consideration of the experimental setup and calibration. The detector properties, count rate, the spectral response, reflections in optical setups, and the specific instrumentation settings for single photon counting will be discussed. Attention to these details helps ensure reproducibility and is necessary for obtaining the best possible data from an SPC system. The main aim of the protocol is to help a student of TRPL understand the experimental setup and the key hardware parameters one must generally comprehend in order to gain useful TRPL data in many common single-photon-counting setups. The secondary purpose is to serve as a condensed primer for the student of experimental time-resolved luminescence spectroscopy.

This paper presents an experimental how-to on time-resolved photoluminescence. The hardware used in many single photon-counting setups will be described and a basic how-to will be presented. This is intended to help students and experimenters understand the key system parameters and how to correctly set them in time-resolved photoluminescence setups.

Time-resolved photoluminescence (TRPL) is a key technique for understanding the photophysics of semiconductor nanocrystals and light-emitting materials in ...

Using a VSFG Microscope for Multimodal, Rapid, Hyperspectral Chemical Analysis

Multimodal Nonlinear Hyperspectral Chemical Imaging Using Line-Scanning Vibrational Sum-Frequency Generation Microscopy

Vibrational sum-frequency generation (VSFG), a second-order nonlinear optical signal, has traditionally been used to study molecules at interfaces as a spectroscopy technique with a spatial resolution of ~100 &#181;m. However, the spectroscopy is not sensitive to the heterogeneity of a sample. To study mesoscopically heterogeneous samples, we, along with others, pushed the resolution limit of VSFG spectroscopy down to ~1 &#181;m level and constructed the VSFG microscope. This imaging technique not only can resolve sample morphologies through imaging, but also record a broadband VSFG spectrum at every pixel of the images. Being a second-order nonlinear optical technique, its selection rule enables the visualization of non-centrosymmetric or chiral self-assembled structures commonly found in biology, materials science, and bioengineering, among others. In this article, the audience will be guided through an inverted transmission design that allows for imaging unfixed samples. This work also showcases that VSFG microscopy can resolve chemical-specific geometric information of individual self-assembled sheets by combining it with a neural network function solver. Lastly, the images obtained under brightfield, SHG, and VSFG configurations of various samples briefly discuss the unique information revealed by VSFG imaging.

Author Spotlight: Unveiling the Potential of VSFG Microscopy in Studying Mesoscopically Heterogeneous Self-Assembled Structures 

A multimodal, rapid hyperspectral imaging framework was developed to obtain broadband vibrational sum-frequency generation (VSFG) images, along with brightfield, second harmonic generation (SHG) imaging modalities. Due to the infrared frequency being resonant with molecular vibrations, microscopic structural and mesoscopic morphology knowledge is revealed of symmetry-allowed samples.

Vibrational sum-frequency generation (VSFG), a second-order nonlinear optical signal, has traditionally been used to study molecules at interfaces as a ...

Preparation, Purification, and Characterization of Lanthanide Complexes for Use as Contrast Agents for Magnetic Resonance Imaging

Polyaminopolycarboxylate-based ligands are commonly used to chelate lanthanide ions, and the resulting complexes are 
useful as contrast agents for magnetic resonance imaging (MRI). Many commercially available ligands are especially useful because they contain 
functional groups that allow for fast, high-purity, and high-yielding conjugation to macromolecules and biomolecules via amine-reactive 
activated esters and isothiocyanate groups or thiol-reactive maleimides. While metalation of these ligands is considered common 
knowledge in the field of bioconjugation chemistry, subtle differences in metalation procedures must be taken into account when 
selecting metal starting materials. Furthermore, multiple options for purification and characterization exist, and selection of the most 
effective procedure partially depends on the selection of starting materials. These subtle differences are often neglected in published 
protocols. Here, our goal is to demonstrate common methods for metalation, purification, and characterization of lanthanide complexes 
that can be used as contrast agents for MRI (Figure 1). We expect that this publication will enable biomedical scientists to incorporate 
lanthanide complexation reactions into their repertoire of commonly used reactions by easing the selection of starting materials and 
purification methods.

We demonstrate the metalation, purification, and characterization of lanthanide complexes. The complexes described here can be conjugated to macromolecules to enable tracking of these molecules using magnetic resonance imaging.

Polyaminopolycarboxylate-based ligands are commonly used to chelate lanthanide ions, and the resulting complexes are 
useful as contrast agents for ...

Hyperspectral Imaging as a Tool to Study Optical Anisotropy in Lanthanide-Based Molecular Single Crystals

Podsumowanie

Przeglądaj więcej filmów

High Resolution Phonon-assisted Quasi-resonance Fluorescence Spectroscopy

Fabrication Procedures and Birefringence Measurements for Designing Magnetically Responsive Lanthanide Ion Chelating Phospholipid Assemblies

Novel Techniques for Observing Structural Dynamics of Photoresponsive Liquid Crystals

Methods of Ex Situ and In Situ Investigations of Structural Transformations: The Case of Crystallization of Metallic Glasses

Synchrotron X-ray Microdiffraction and Fluorescence Imaging of Mineral and Rock Samples

Spectral and Angle-Resolved Magneto-Optical Characterization of Photonic Nanostructures

Sample Preparation and Transfer Protocol for In-Vacuum Long-Wavelength Crystallography on Beamline I23 at Diamond Light Source

Time-Resolved Photoluminescence Spectroscopy of Semiconductor Nanocrystals and Other Fluorophores

Multimodal Nonlinear Hyperspectral Chemical Imaging Using Line-Scanning Vibrational Sum-Frequency Generation Microscopy

Preparation, Purification, and Characterization of Lanthanide Complexes for Use as Contrast Agents for Magnetic Resonance Imaging