The authors Smith and Pantoya are grateful for partial support from DTRA under award HDTRA1-15-1-0029; and, ARO (and Dr. Ralph Anthenien) under award W911NF-14-1-0250 and equipment grant W911NF-14-10417. The authors J. Parkey and M. Kesmez are grateful for support from DTRA under award HDTRA1-15-P-0037. Thank you to Dr. Douglas Allen Dalton for helpful discussion.

NOTE: Six different oxidizers were investigated for the purpose of characterizing the kinetics of I4O9 in comparison to other iodine oxides. Each oxidizer is described below. The fuel used for all mixtures was constant: Al powder with 80 nm average spherical particle diameter. Mixture preparation is described following discussion of each oxidizer.
1. Preparation of Iodine(V) Oxides
NOTE: Nano-aluminum/oxidizer mixtures are highly volatile and can exhibit explosive behavior. These mixtures are susceptible to unintended ignition by electrostatic discharge, friction, impact, and other forms of accidental ignition. All equipment should be grounded to decrease the likelihood of accidental spark ignition. Quantities should be minimized and protective equipment should be used when handling these materials. More information on safety and handling procedures can be found in Maienschein et al.18
<ol>
	<li>Preparation commercial I2O5
	<ol>
		<li>Crush 10 g of I2O5 crystals with a mortar and pestle until a consistent powder is created.</li>
		<li>After the crystals are in a powder form, evenly spread the 10 g of powder in a ceramic crucible suitable for heating up to 250 &#176;C.</li>
		<li>Place entire crucible in an oven and heat to 250 &#176;C at 10&#176;C/min and hold at 250 &#176;C for 5 min.</li>
	</ol>
	</li>
	<li>Preparation of amorphous I2O5
	<ol>
		<li>Place 3 g of the crushed and dehydrated commercial I2O5 in a glass beaker with a magnetic stirrer and add 3 g of distilled water. To ensure the sample is completely dissolved, add a 1:1 ratio of water to commercial I2O5 and mix for 20 min. Dissolution of I2O5 in water forms an aqueous phase of IO3.17</li>
		<li>Pour the IO3 solution into a beaker that is suitable for heating. To ensure enough amorphous I2O5 is produced, use three times the mass of IO3 solution than the mass needed of amorphous I2O5. For example, if one gram of amorphous I2O5 is needed, use 3 g of IO3 solution.</li>
		<li>Place the beaker with the IO3 solution into an oven and heat at 20 &#176;C/min to 250 &#176;C and hold for 10 min.</li>
		<li>Store the sample in a sealed container to limit exposure to atmospheric water from the environment.</li>
	</ol>
	</li>
	<li>Preparation crystalline HIO3
	<ol>
		<li>Repeat step 1.2.1 and place IO3 solution on a magnetic stirrer in a low humidity environment (below 50% RH) until all of the excess water has evaporated. Upon evaporation, the aqueous phase of IO3 will precipitate out as HIO317.</li>
		<li>Store the sample in a sealed container to limit exposure to atmospheric water from the environment.</li>
		<li>To ensure all excess water is evaporated, place a sample into a differential scanning calorimeter (DSC) and heat to 250 &#176;C at 10 &#176;C/min. 
		NOTE: The weight loss at 110 &#176;C will equal 5% and there will be no mass loss at 210 &#176;C if the sample is pure HIO3. Any additional mass loss is excess water, which means the sample needs more time to evaporate. Weight loss at 210 &#176;C means the I2O5 has not completely dissolved and more water with agitation is needed to dissolve the sample.</li>
	</ol>
	</li>
</ol>
2. Mixture Preparation
NOTE: The mixtures are prepared in two different ways: one using a carrier fluid to aid in intermixing and another without a carrier fluid but instead dry mixed. For processing using a carrier fluid, mixtures were prepared for only three oxidizers: I4O9, nano I2O5 and commercial I2O5.
<ol>
	<li>Preparation of mixtures in a carrier fluid
	<ol>
		<li>To prepare the samples mixed in a carrier fluid, mix 80 nm Al powder with each oxidizer for a total of two grams of Al and oxidizer mixture to an equivalence ratio of 1.0 in a beaker.</li>
		<li>Add 60 ml of isopropanol into the beaker and sonicate the solution with a sonic wand set at an output power of 4 watts programmed for 10 sec on and 10 sec off for a total of 2 min.</li>
		<li>Pour solution into a glass dish and allow the solution to evaporate in a fume hood at room temperature with a relative humidity of 20% for 24 hr, which will leave powder samples. 
		NOTE: Before proceeding with step 2.1.4, assure razor blade is connected to an electrical ground with a conductive wire to avoid accidental ignition.</li>
		<li>Reclaim the powder with a grounded razor blade and sieve the sample to break up agglomerates directly into a container that can be sealed to limit sample exposure to atmospheric water.</li>
	</ol>
	</li>
	<li>Preparation of dry mixed samples
	<ol>
		<li>Sieve and mix two grams of Al and oxidizer mixture with a spatula into a sample container to a fuel to oxygen equivalence ratio of 1.0. Seal the sample container to limit sample exposure to atmospheric water.</li>
		<li>Hold samples on a vibration table for 3 minute to aid intermixing. Refer to samples prepared in this way as dry mixed.</li>
	</ol>
	</li>
</ol>
3. Thermal Equilibrium Analysis
<ol>
	<li>Preparation of samples for thermal equilibrium analysis 
	NOTE: These samples react easily with atmospheric water. Relative humidity should be reduced below 30% and exposure to the atmosphere should be limited (i.e., store sample in sealed containers and use lids on DSC-TGA crucibles).
	<ol>
		<li>Heat alumina crucibles (supplied with the DSC-TGA diagnostic) to 1,500 &#176;C and hold for 30 min to remove any residue on the crucibles in the DSC-TGA.</li>
		<li>Weigh crucibles before the samples are placed in the crucible. This measurement is needed by the DSC-TGA.</li>
		<li>After the crucible is weighed, add 10 mg of each sample into a crucible.</li>
		<li>Place the sample crucible on the thermocouple in the DSC-TGA with an empty crucible in the reference holder on the DSC thermocouple.</li>
		<li>Heat the samples at 10 &#176;C/min to 600 &#176;C in an argon atmosphere.</li>
	</ol>
	</li>
</ol>
4. Energy Propagation
<ol>
	<li>Preparation of flame tubes
	<ol>
		<li>Use quartz tubes with an inside diameter of 3 mm and length of 7 cm to contain the powder mixture.</li>
		<li>Put tape on one end so powder cannot escape from the tube.</li>
		<li>Place each 7 cm tube with one end taped on a scale and zero the scale. This will allow the measurement of just the mass of powder.</li>
		<li>Using a spatula with a small end, insert the powder samples into the tube. For each of the mixtures, make three tubes filled with each mixture for repeatability testing.</li>
		<li>Using a rod that has a diameter smaller than 3 mm, compact the powder inside the tube for the samples with low bulk densities (i.e., Al + I4O9 and Al + amorphous I2O5) until the volume of the sample does not change. This procedure is necessary to maintain consistent bulk densities between multiple experiments. This may require 200 mg of powder mixture.</li>
		<li>For all other mixtures, which have higher densities, do not compact the powder using external force. Keep the bulk density constant between samples with similar bulk densities. The amount of powder in the tubes will vary depending on bulk density of the powder. This may require up to 500 mg of powder mixture.</li>
		<li>Measure the mass of powder mixture in each tube using the balance that was tared for each tube, add mass until the density of the powder is within 5% of the other samples in each group. Make sure each tube is completely filled.</li>
	</ol>
	</li>
	<li>Preparation of hot wire ignite
	<ol>
		<li>To prepare the hot wire, use a nickel-chromium (i.e., nichrome) wire cut into sections 10 cm long.</li>
		<li>Make a &#34;v&#34; shape in the middle of the wire and place the wire so the &#34;v&#34; shape is inside the tube.</li>
		<li>Tape this end of the tube so the wire is stationary and no powder can escape the tube.</li>
	</ol>
	</li>
	<li>Preparation of high speed camera
	<ol>
		<li>Place the high speed camera outside the combustion chamber perpendicular to the direction of flame propagation and focus the camera on the tube through a viewing port in the combustion chamber. 
		&#8203;NOTE: The primary function of the combustion chamber is to protect personnel and equipment from the reacting material and should be ventilated through a fume hood.</li>
		<li>Adjust placement and lens of the camera so the lowest resolution (i.e., highest frame rate) can be used.</li>
		<li>To allow distance calibration, place a ruler with mm and cm increments in the field of view and take a snapshot with the high speed camera prior to recording flame speeds.</li>
		<li>As the flame front is significantly brighter than ambient light and the camera will over-saturate when exposed to the light generated by the reaction, lower the exposure time in the camera settings or add neutral density filters to the lens of the camera to reduce the amount of light received by the camera sensors. Lower the amount of light received by the camera until the propagation front of the reaction can be seen clearly. Here, set up neutral density filters allowing only 5% of the light to pass, and an exposure time of 1 &#181;sec.</li>
		<li>Attach a voltage generator to the ends of the wire. The combustion chamber should have insulated leads through the chamber which will allow the chamber to be sealed and allow remote heating of the wire.</li>
		<li>After the chamber is sealed, set the voltage generator to 10 volts and simultaneously begin the camera recording. When the voltage is applied, the reaction should start almost immediately.</li>
		<li>Export the video into a software program that will track the position of the flame front as a function of time in each individual frame.</li>
		<li>Export the distance and time step information into a spread sheet and plot a linear trend line with R2 values. For slower reactions, time is needed for the reaction to reach a steady state. The curve before the steady state will be an exponentially increasing curve. Remove the data that are not in steady state until the R2 value is greater than 0.95. The slope of the line is the flame speed.</li>
	</ol>
	</li>
</ol>

<ol>
	<li>Selte, K., Kjekshus, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Iodine+Oxides+Part+II+on+the+system+H2O+I2O5.">Iodine Oxides Part II on the system H2O I2O5.</a> Acta. Chem. Scand. 22, 3309-3320 (1968).</li><li>Little, B. K., Emery, S. B., Nittinger, J. C., Fantasia, R. C., Lindsay, C. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Physiochemical+Characterization+of+Iodine+(+V+)+Oxide+,+Part+1+Hydration+Rates.+(V).">Physiochemical Characterization of Iodine ( V ) Oxide , Part 1 Hydration Rates. (V).</a> Propell. Explos. Pyrot. 40, 595-603 (2015).</li><li>Smith, D. K., McCollum, J., Pantoya, M. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+Environment+of+Iodine+Oxidation+State+on+Reactivity+with+Aluminum.">Effect of Environment of Iodine Oxidation State on Reactivity with Aluminum.</a> Phys. Chem. Chem. Phys. 18, 11243-11250 (2016).</li><li>Farley, C., Pantoya, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Reaction+kinetics+of+nanometric+aluminum+and+iodine+pentoxide.">Reaction kinetics of nanometric aluminum and iodine pentoxide.</a> J. Therm. Anal. Calorim. 02 (2), 609-613 (2010).</li><li>Little, B. K., Emery, S. B., Lindsay, M. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Physiochemical+Characterization+of+Iodine+(V)+Oxide+Part+II+Morphology+and+Crystal+Structure+of+Particulat+Films.">Physiochemical Characterization of Iodine (V) Oxide Part II Morphology and Crystal Structure of Particulat Films.</a> Crystals. 05 (4), 534-550 (2015).</li><li>Wikjord, A., Taylor, P., Torgerson, D., Hachkowski, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Thermal+behaviour+of+Corona-Precipitated+Iodine+Oxides.">Thermal behaviour of Corona-Precipitated Iodine Oxides.</a> Thermochim. Acta. 36, 367-375 (1980).</li><li>Little, B. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Chemical+dynamics+of+nano-aluminum/iodine+(V)+oxide.">Chemical dynamics of nano-aluminum/iodine (V) oxide.</a> J. Phys. Conf. Ser. 500 (5), 052025 (2014).</li><li>Feng, J., Jian, G., Liu, Q., Zachariah, M. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Passivated+iodine+pentoxide+oxidizer+for+potential+biocidal+nanoenergetic+applications.">Passivated iodine pentoxide oxidizer for potential biocidal nanoenergetic applications.</a> ACS Appl. Mater. Inter. 5 (18), 8875-8880 (2013).</li><li>Wang, H., DeLisio, J. B., Jian, G., Zhou, W., Zachariah, M. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrospray+formation+and+combustion+characteristics+of+iodine-containing+Al/CuO+nanothermite+microparticles.">Electrospray formation and combustion characteristics of iodine-containing Al/CuO nanothermite microparticles.</a> Combust. Flame. 162 (7), 2823-2829 (2015).</li><li>Sunder, S., Wren, J. C., Vikis, A. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Raman+Spectra+of+1409+Formed+by+the+Reaction+of+Iodine+with+Ozone.">Raman Spectra of 1409 Formed by the Reaction of Iodine with Ozone.</a> J. Raman Spectrosc. 16 (6), 424-426 (1985).</li><li>Selte, K., Kjekshus, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Iodine+Oxides+Part+III.+The+Crystal+Structure+of+I2O5.">Iodine Oxides Part III. The Crystal Structure of I2O5.</a> Acta. Chem. Scand. 6 (24), 1913-1924 (1970).</li><li>Sherwood, P. M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=X-Ray+Photoelectron+Spectroscopic+Studies+of+Some+Iodine+Compounds.">X-Ray Photoelectron Spectroscopic Studies of Some Iodine Compounds.</a> J. Chem. Soc. 72, 1805-1820 (1976).</li><li>Russell, R., Bless, S., Pantoya, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Impact-Driven+Thermite+Reactions+with+Iodine+Pentoxide+and+Silver+Oxide.">Impact-Driven Thermite Reactions with Iodine Pentoxide and Silver Oxide.</a> J. Energ. Mater. 29 (2), 175-192 (2011).</li><li>Skulski, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Organic+iodine(I,+III,+and+V)+chemistry:+10+Years+of+development+at+the+Medical+University+of+Warsaw,+Poland.">Organic iodine(I, III, and V) chemistry: 10 Years of development at the Medical University of Warsaw, Poland.</a> Molecules. 5 (12), 1331-1371 (2000).</li><li>Nicolaou, K. C., Montagnon, T., Baran, P. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=HIO3+and+I2O5+Mild+and+Selective+Alternative+Reagents+to+IBX+for+the+Dehydrogenation+of+Aldehydes+and+Ketones.">HIO3 and I2O5 Mild and Selective Alternative Reagents to IBX for the Dehydrogenation of Aldehydes and Ketones.</a> Angew. Chem. Int. Edit. 293 (8), 1386-1389 (2002).</li><li>Lide, D. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> CRC Handbook of Chemistry and Physics. , 3485 (2005).</li><li>Kumar, R., Saunders, R. W., Mahajan, a. S., Plane, J. M. C., Murray, B. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Physical+properties+of+iodate+solutions+and+the+deliquescence+of+crystalline+I2O5+and+HIO3.">Physical properties of iodate solutions and the deliquescence of crystalline I2O5 and HIO3.</a> Atmos. Chem. Phys. 10 (24), 12251-12260 (2010).</li><li>Maienschein, J., Pantoya, M. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Safety+in+Energetic+Materials+Research+and+Development-Approaches+in+Academia+and+a+National+Laboratory.">Safety in Energetic Materials Research and Development-Approaches in Academia and a National Laboratory.</a> Propell. Explos. Pyrot. 39 (4), 483-485 (2014).</li><li>Osborne, D. T., Pantoya, M. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+Al+Particle+Size+on+the+Thermal+Degradation+of+Al/Teflon+Mixtures.">Effect of Al Particle Size on the Thermal Degradation of Al/Teflon Mixtures.</a> Combust. Sci. Technol. 179, 1467-1480 (2007).</li><li>Pantoya, M. L., Dean, S. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+influence+of+alumina+passivation+on+nano-Al/Teflon+reactions.">The influence of alumina passivation on nano-Al/Teflon reactions.</a> Thermochim. Acta. 493 (1-2), 109-110 (2009).</li><li>Mulamba, O., Pantoya, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Exothermic+surface+reactions+in+alumina-aluminum+shell-core+nanoparticles+with+iodine+oxide+decomposition+fragments.">Exothermic surface reactions in alumina-aluminum shell-core nanoparticles with iodine oxide decomposition fragments.</a> J. Nanopart. Res. 16 (3), 2310 (2014).</li><li>Nelyubina, Y., Antipin, M. Y., Lyssenko, K. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Extremely+short+halogen+bond:+the+nature+and+energy+of+iodine-oxygen+interactions+in+crystalline+iodic+acid.">Extremely short halogen bond: the nature and energy of iodine-oxygen interactions in crystalline iodic acid.</a> Mendeleev. Commun. 21, 250-252 (2011).</li><li>Bockmon, B. S., Pantoya, M. L., Son, S. F., Asay, B. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Combustion+velocities+and+propagation+mechanisms+of+meta-stable+intermolecular+composites.">Combustion velocities and propagation mechanisms of meta-stable intermolecular composites.</a> J. Appl. Phys. 98 (6), 064903 (2005).</li><li>Pantoya, M. L., Levitas, V. I., Granier, J. J., Henderson, J. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+bulk+density+on+reaction+propagation+in+nanothermites+and+micron+thermites.">Effect of bulk density on reaction propagation in nanothermites and micron thermites.</a> J. Propul. Power. 25 (2), 465-470 (2009).</li></ol>

All authors have no competing financial interests or other conflicts of interest.

The I4O9 powder studied here was synthesized using a &#34;dry&#34; approach to form I4O9 by combining elemental iodine and oxygen. This sample is referred to as I4O9. Nano-particle I2O5 was also synthesized for this study. Specifically, a portion of I4O9 was heated past the dissociation temperature of I4O9 (i.e., 180 &#176;C) but under the dissociation temperature of I2O5 (400 &#176;C). This process results in particles with a diameter between 200-400 nm. This sample is referred to as nano I2O5. Particle size measurements were obtained by TEM which requires the sample to be in a vacuum. However, I4O9 dissociates into I2O5 in a vacuum, so dimensions of I4O9 were not obtained directly. Because the nano I2O5 particle diameters are between 200-400 nm and synthesized by heating the I4O9 sample, it is assumed that I4O9 has similar diameters.
A more common approach to synthesizing I2O5 is by thermal dehydration of iodic acid to form I2O51,2,8 and material made using this process is commercially available. The commercial I2O5 is received as coarse crystals and can have different concentrations of iodic acids depending on storage and handling conditions. To ensure samples are pure I2O5, the samples are dehydrated prior to use as explained in step 2.1.1.3. The diameter of the particles in this sample are between 1-5&#181;m. This sample is referred to as commercial I2O5.
The amorphous I2O5 sample is made from this saturated IO3 solution. When I2O5 is mixed with water, a solution of IO3 is created. This is done in step 2.1.2 and these steps will leave a saturated IO3 solution. Water catalyzes the formation of crystals in iodic acids. To form amorphous I2O5 the temperature must be above the dehydration temperature of HI3O8 and heated at a rate that will not allow a crystal structure to form, this is done in step 1.2. The concentration of IO3 in solution will determine the amount of amorphous I2O5 created during dehydration. These samples should turn red after dehydration indicating the sample is an amorphous form of I2O5. This sample is referred to as amorphous I2O5. Also, XRD analysis (not included) was preformed and confirmed the amorphous structure of the I4O9 and amorphous I2O5 samples.
When in solution, HIO3 will release excess water and create a crystal structure. The time needed to evaporate the excess water is dependent on the size of the beaker, RH, and concentration of the IO3 solution. In our lab at 20% RH mixing in the manner discussed above, 3-5 days were required to evaporate excess water from the samples. The solution will turn into a solid clear crystal. This process is shown in step 2.1.3 and the sample referred to as HIO3 dehydrate. Iodic acid will be referred to as commercial HIO3.
When exposed to solution or atmospheric water, iodine(V) oxide undergoes chemical reactions that change the composition of the final product. To mitigate this transformation, all six oxides are also mixed with Al without solution.
Thermal analysis using DSC-TGA was calibrated in an argon atmosphere using samples with known onset temperatures and mass losses. A flame tube apparatus known as a Bockmon Tube23 is used to measure flame speeds. Flame speed experiments are sensitive to the bulk density of the mixture. Pantoya et al. showed that for nano-Al based thermites, increasing bulk density can suppress the Al reaction mechanism and reduced the role of convective energy transport thereby retarding flame speed24. For this reason, experiments performed for different mixtures are usually designed to keep a constant bulk density. However, the physical and chemical properties of the oxidizers examined here vary dramatically such that it was not possible to obtain consistent bulk density with all six dry mixtures. Because of this, multiple iodine oxides with different physical and chemical properties are tested to provide a basis of comparison which includes differences in %TMD, crystal structure, and hydration states. After the powder has been placed inside the tubes and measured, hot wire is used to remotely ignite the mixture.
After the flame tubes are prepared with powder mixture, flame speeds are measured in a combustion chamber using a high-speed camera. The frame rate of the camera can be increased by lowering the resolution. Reducing the resolution to increase frame rate will produce less error than higher resolution at a slower frame rate. This is why, in step 4.2.2, the lowest resolution that can still image the entire flame tube is used, this will increase the maximum frames per second the camera can record without losing information. For our chamber, a resolution of 256 x 86 was used which allowed the camera to record at 300,000 fps.
Quantifying flame speeds in highly reactive mixtures is inherently difficult because of the large number of variables that can influence reactivity (i.e., mixture homogeneity, particle size, density, propagation direction, propagation velocity, etc.). By using a quartz tube with an inside diameter less than 4 mm in combination with a high speed camera with neutral density filters, the direction of propagation is controlled (i.e., 1-D) and the amount of light that is received by the camera can be reduced to a minimum threshold such that the leading edge of light emitted by the reaction can be seen and measured clearly. This measurement assumes that the progression of this low light level is at the same rate as the reaction front. For this reason, photodiodes may not be as accurate for tracking the reaction propagation because the high light intensity of emission may cause light to travel and saturate the sensors faster than the reaction. Also, the first 1-2 cm of tube length is considered an entrance region, or region of unsteady or accelerating propagation. Linear measurements of distance as a function of time must be taken beyond this entry region to determine steady state flame speed.
The DSC/TGA is a thermal equilibrium analysis that shows detailed reaction kinetics that cannot be observed in highly reactive materials (i.e., cannot be observed under non thermal equilibrium conditions). The combination of DSC/TGA analysis and flame speeds give specific information on differences in the reaction kinetics that may have implications for differences in the flame speed results. Because of this, the combination of these two measurement methods is a powerful tool for understanding and controlling highly reactive materials.

There are many iodine oxide compounds (e.g., HIO3, HI3O8, I2O5, I4O9) but the one most commonly studied for reaction with aluminum (Al) is diiodide pentoxide, I2O51-16. There are reasons for favoring I2O5 for combustion with Al: (1) I2O5 has an oxidation state of five which makes it a strong oxidizer for combustion applications; (2) I2O5 is semi-stable, depending on atmospheric conditions, and easily handled in powder form; and (3) I2O5 is relatively easy to produce and readily available.
Other forms of iodine oxide that have been studied are HIO3, HI3O8, and I4O9. When heated to low temperatures (i.e., 180 &#176;C), I4O9 thermally decomposes into I2O56 as shown in Equation (1) and the decomposition reaction is exothermic.
(1) 5I4O9&#8594;9I2O5+I2&#8203;
If I4O9 could be used in place of I2O5, the total energy liberated from reaction could increase due to the exothermic decomposition of I4O9 at temperatures below the Al ignition and reaction temperatures (i.e., &#60; 660 &#176;C) and below the dissociation temperature of I2O5 (i.e., about 350 &#176;C). Also, I4O9 generates 8 wt.% more I2 gas when compared to I2O5 that could be used to neutralize biological agents. However, I4O9 has a higher molecular weight when compared to I2O5 and it is unknown if more energy is released per mass or per volume when using I4O9 compared to I2O5. Using I4O9 could provide a way to transport large quantities of solid iodine and upon ignition, release gaseous iodine. But, I4O9 powder is usually unstable. In fact, Wikjord et al.6 showed that over very short times I4O9 decomposed into I2O5 even with limited exposure to the atmosphere. This instability limits the usefulness of I4O9 as an oxidizer in combustion applications.
Iodic acids, such as HIO3 and HI3O8, form when I2O5 is exposed to water either from the relative humidity (RH) of the atmosphere or from immersion in a fluid1,3. For combustion applications, I2O5 is usually preferred over the hydrated iodic acids because evaporation of water upon combustion absorbs energy and reduces the overall heat produced. Despite the endothermic nature of this phase change, Smith et al.3 showed rapid evaporation of water during combustion of Al with I2O5 comprised partially of iodic acids produced significant gas generation that increased convective energy transport and produced higher flame speeds than Al + I2O5 alone. Specifically, mixtures with higher concentrations of iodic acids had up to 300% higher flame speeds than mixtures with lower concentrations of iodic acids. 3
The rate of absorption from atmospheric water is dependent on RH. There is a RH threshold where absorption begins and dependent on the hydration state2. Little et al. showed a RH threshold of 70% for HIO3 and a RH threshold of 40% for HI3O82. From this, it is assumed that the RH threshold increases with increasing hydration states. Because of its deliquescent properties, most studies that use I2O5 as an oxidizer are actually using I2O5 with significant concentrations of iodic acid2,5,7,17. However, the initial concentrations of the samples can be controlled by heating the samples above 210 &#176;C until all of the hydrated species have dehydrated. This follows the hydration and dehydration mechanism of I2O5 shown in Selte et al.1 in Equation (2).
(2a) Hydration: 3I2O5+3H2O&#8594;2HI3O8+2H2O&#8594;6HIO3
(2b) Dehydration: 6HIO3&#8594;2HI3O8+2H2O&#8594; 3I2O5+3H2O
The first step in dehydration happens at 110 &#176;C when HIO3 dehydrates into HI3O8. The second step of dehydration happens at 210 &#176;C when HI3O8 dehydrates into I2O5. Because the initial concentration of commercially available I2O5 is composed mostly of iodic acids, the absorption characteristics of pure I2O5 have not been studied thoroughly. It is assumed that the RH threshold and absorption rates are dependent on physical properties (i.e., particle size, crystal structure) along with initial hydration state and that an iodine oxide that is amorphous may have a lower RH threshold and increased hydration rates. Isolating iodine oxides from atmospheric water is needed to control the initial state of iodine oxide compounds. One method of isolating I2O5 from the atmosphere is blocking water absorption with coatings. For example, Little et al. was able to reduce the absorption rate and total amount of hydrated iodine oxides by sputter coating samples with Au/Pd2. Feng et al.8 passivated the surface of I2O5 particles with an Fe2O3 coating which prevented water absorption over long durations of exposure to ambient atmosphere. A similar approach could be applied to help stabilize I4O9.
Another way to improve the stability of I4O9 may be new approaches for its synthesis. If the material could be synthesized in a way that prevents introduction of hydrated species, then the topochemical effect that catalyzes water absorption could be inhibited thereby stabilizing the oxidizer. The I4O9 examined here was synthesized using a &#39;dry&#39; process that does not introduce hydrated species and enables analysis of a more stable form of I4O9 powder. Our objective is to analyze the fundamental kinetics associated with I4O9 decomposition and reaction with Al as well as the basic energy propagation behavior of the Al + I4O9 reaction. Reaction kinetics are analyzed using thermal equilibrium diagnostics including differential scanning calorimetry and thermal gravimetric analysis (DSC-TGA). Energy propagation is analyzed using high speed imaging of reaction propagation through a powder mixture upon ignition in a transparent tube. Development of synthesis methods to produce I4O9 and methods to stabilize I4O9 have been slow in comparison to other forms of iodine oxide. A goal of this study is to show that the energy and gas liberated from reactions involving I4O9 are greater than reactions involving other iodine oxides. In this way, future research on synthesis and characterization of I4O9 may be beneficial for many applications.

<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Iodine pentoxide (Commercial I2O5)</td>
			<td>Sigma Aldrich</td>
			<td>229709</td>
			<td>Commercial I2O5</td>
		</tr>
		<tr>
			<td>Iodic Acid (Commercial HIO3)</td>
			<td>Alfa Aesar</td>
			<td>A11925</td>
			<td>Comercial HIO3</td>
		</tr>
		<tr>
			<td>Tetraiodine nonoxide (I4O9)</td>
			<td>Lynntech Inc</td>
			<td></td>
			<td>synthesized using a dry process&#160;</td>
		</tr>
		<tr>
			<td>Water</td>
			<td></td>
			<td></td>
			<td>Local distilled water run through micron filter</td>
		</tr>
		<tr>
			<td>80 nm Aluminum</td>
			<td>NovaCentrix</td>
			<td>AL-80-P</td>
			<td>Nano Aluminum</td>
		</tr>
		<tr>
			<td>Differential Scanning Calorimeter with Thermal Gravimetric Analyzer (DSC-TGA)</td>
			<td>Netzsch</td>
			<td>STA-449</td>
			<td>Equilibrium analysis of heat flow and mass loss</td>
		</tr>
		<tr>
			<td>Sonic Wand</td>
			<td>Misonix</td>
			<td>Sonicator 3000</td>
			<td>Provides ultrasonic waves to aid intermixing of reactant powders</td>
		</tr>
		<tr>
			<td>Phantom High Speed Camera</td>
			<td>Vision Research</td>
			<td>Phantom 2512</td>
			<td>High speed camera for visualzing flame front</td>
		</tr>
		<tr>
			<td>Mass Balance</td>
			<td>Ohaus</td>
			<td>Ohaus Explorer</td>
			<td>Weigh powders with a 0.1mg resolution up to a 110 g capacity</td>
		</tr>
	</tbody>
</table>

reaction kinetics and combustion dynamics of i4o9 and aluminum mixtures

Tetraiodine nonoxide (I4O9) has been synthesized using a dry approach that combines elemental oxygen and iodine without the introduction of hydrated species. The synthesis approach inhibits the topochemical effect promoting rapid hydration when exposed to the relative humidity of ambient air. This stable, amorphous, nano-particle material was analyzed using differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA) and showed an exothermic energy release at low temperature (i.e., 180 &#176;C) for the transformation of I4O9 into I2O5. This additional exothermic energy release contributes to an increase in overall reactivity of I4O9 when dry mixed with nano-aluminum (Al) powder, resulting in a minimum of 150% increase in flame speed compared to Al + I2O5. This study shows that as an oxidizer, I4O9 has more reactive potential than other forms of iodine(V) oxide when combined with Al, especially if I4O9 can be passivated to inhibit absorption of water from its surrounding environment.

Figure 1a shows the endothermic and exothermic behavior of the initial states for all six oxidizers examined from DSC analysis and Figure 1b shows the corresponding mass loss from TGA analysis. It is noted that all oxidizers when heated beyond the dissociation temperature of I2O5 (350 &#176;C) lose 100% mass but the I4O9 sample releases I2 gas instead of water liberated by dehydration of hydrated species at temperatures below the dissociation temperature of I2O5. The abundance of I2 gas released from the I4O9 samples is specified in Figure 1b at over 7 wt.%. Figure 1a shows that the only iodine compounds that produce exothermic behavior is I4O9 and I2O5 formed by decomposition of I4O9, and the exotherm corresponds to an onset temperature of about 180 &#176;C for decomposition into I2O5. Figure 1b also shows that the iodine compound with the greatest overall iodine gas generation is I4O9.
There are no endotherms for commercial and amorphous I2O5 samples between 110 &#176;C and 210 &#176;C. This shows that these samples are purely I2O5 with no iodic acids. The nano I2O5 and I4O9 have exotherms with onset temperature at 150 &#176;C. This shows those samples contain I4O96. The nano I2O5 is thermally treated I4O9. The small exotherm at 150 &#176;C shows that there is some residual I4O9 in the nano I2O5 sample. Using the TGA data from Figure 1b, the residual I4O9 in the sample is less than 15 wt.%. The HIO3 dehydrate has a single endotherm starting at 130 &#176;C and indicates this sample is crystalline HIO3. The commercial HIO3 sample has two distinct endotherms starting at 160 &#176;C and 210 &#176;C. An endotherm with an onset temperature of 160 &#176;C is outside of the range of HIO3 dehydration in the CRC handbook16. However, TGA results show a mass loss of 2.47 wt.% over this range indicating it is the dehydration of a hydrated species.
Figure 2a shows the heat flow behavior from DSC analysis of four Al and iodine oxide mixtures. The Al + I4O9 dry mixture has an exotherm at 180 &#176;C indicating the oxidizer is still I4O9 with an increased onset temperature. The Al + I4O9 and Al + nano I2O5 samples are almost identical. Both of these mixtures were processed using isopropanol as the carrier fluid to aid intermixing and identical thermal behavior seen in Figure 2a indicating that mixing powders in isopropanol transformed I4O9 into I2O5.
Figure 2b shows I4O9, I4O9 exposed to 20% RH for 4 hours, and nano I2O5 exposed to 20% RH for 4 hours. After 4 hours exposure to 20% RH, I4O9 is identical to nano I2O5 and there are endotherms at 110 &#176;C and 210 &#176;C showing the samples are partially composed of HIO3 and HI3O8. This may be explained by the I4O9 &#34;dry&#34; synthesis method which is then heated and transformed into I2O5. The crystal structure of I4O9 is not known, but because hydration is observed (Figure 2b bottom two curves with endotherms shaded), the low density of the powder (i.e., fluffy, highly porous nature), and the lack of a reported crystalline structure, an amorphous structure is assumed. Nano I2O5 is formed by thermal decomposition of amorphous I4O9, according to Eq. (1) such that I2 is released from amorphous I4O9 leaving amorphous I2O5. Crystal structure formation of iodine(V) oxides is catalyzed by water. Since the synthesis method is dry, there is no water to catalyze crystal formation. The first step required for absorption of water is to raise the relative humidity to disrupt the bonds between molecules. Without this crystal structure (that wants to release the weakly bonded water) the dynamic equilibrium is shifted so I2O5 will absorb any available water. As soon as water is absorbed by I2O5, formation of HIO3 molecules begin. HIO3 has a hydrogen that attracts oxygen in amorphous I2O5 and creates an HI3O8 crystal structure. Water is still the catalyst in crystal structure formation. The synthesis method of I2O5 and I4O9 which form an amorphous structure instead of a crystalline structure is the reason water absorption is seen at lower RH (i.e., 20%) than what was required to start absorption in previous studies (i.e., 70-80% RH)5,17. In summary, the iodine compounds&#39; amorphous structure may promote absorption of hydrated species and formation of iodic acids.
In Figure 2a the main exotherms around 500 &#176;C are all similar. In the Al + I4O9 dry mix, the exotherm at about 180 &#176;C indicates phase transition from I4O9 to I2O5. Also, all mixtures have a pre-ignition reaction (PIR) between 300 - 400 &#176;C, but Al + I4O9 and Al + nano I2O5 have a PIR with lower onset temperature and greater magnitude but also show unique endotherms followed by exotherms at 210 &#176;C. These samples were processed in isopropanol and the behavior at 210 &#176;C indicates these samples are partially HI3O8. The exotherm may be reaction between HI3O8 and I4O9 because HI3O8 is dissociating at nearly the same temperature as I4O9 decomposition. These reactions may help promote greater exothermicity in the PIR and catalyze earlier onset of the PIR. Osborne and Pantoya 20 first showed an exothermic reaction preceding the main exothermic reaction in Al combustion and coined this a PIR. Their analysis indicated the PIR reaction was between the alumina shell surrounding an aluminum core particle with fluorine from decomposing fluoropolymer19,20. Farley et al.4 then extended observations of the PIR to aluminum-alumina core-shell particles reacting with iodine based oxidizers. The Al + commercial I2O5 sample has an endotherm at 210 &#176;C indicating HI3O8 presence and a mild PIR exotherm with delayed onset temperature. Mulamba et al.21 also showed that the PIR onset temperature is concentration dependent.
Table 1 shows measured flame speed results for Al mixed with the indicated oxidizer as a dry mixture and also mixed using isopropanol as the processing carrier fluid. Only the first three samples were tested after being mixed in isopropanol and the Al + commercial HIO3 dry mix either did not ignite or did not sustain reaction long enough to obtain measureable results. The percent uncertainty is determined based on repeatability of up to three separate experiments for each mixture. Bulk density is determined as a function of mixture powder mass and volume of the tube.
When interpreting reactivity with flame speed measurements, there are many factors that influence results such as homogeneity of the mixture, particle size, and bulk density. Mixture homogeneity can be optimized using a carrier fluid to aid intermixing of the reactants. The I4O9 examined in this study is more stable than previously studied I4O9 samples and did not appear to decompose into I2O5 or form hydrated species seen in Wikjord et al.6 (as seen in Figure 1a with only an exotherm corresponding to I4O9 decomposition). However, the only way to observe the combustion performance of Al + I4O9 is by dry mixing with as little exposure to the atmosphere as possible in order to maintain the integrity of I4O9. Additionally, the flame speed measurements of Al with the oxidizers in different states allowed us to narrow the effects that cause variance in flame speed results and reveal differences attributed specifically to particular iodine compounds. These comparisons will be discussed below. Overall Table 1 shows that I4O9 significantly improves reactivity when compared with other iodine compounds.
Mixing in a carrier fluid provides improved distribution of fuel and oxidizer particles that increases mixture homogeneity and reactivity. This is seen in the difference in flame speeds in Table 1 for the dry and isopropanol mixed Al + nano I2O5 and Al + commercial I2O5 samples where the flame speeds increased by 1.07 and 3.34 times, respectively. Mixture homogeneity implicit from the measured flame speed is only slightly improved for the Al + nano I2O5 mixture, whereas the Al + micron scale commercial I2O5 exhibits a three times increase in flame speed when the carrier fluid aids intermixing. Clearly particle size and carrier fluid contribute to measured flame speed. The homogeneity effects can also be seen by the uncertainty between flame speeds. The samples that are mixed in isopropanol and the samples with smaller particles have less uncertainty in measured flame speeds. This small uncertainty is also seen in all of the amorphous samples, which suggests that an amorphous structure facilitates improved homogeneity in dry mixing. It is further noted that each sample was sieved before dry mixing to break up agglomerates and help eliminate uncertainty caused by poor homogeneity.
The HIO3 molecules have a hydrogen end cap, which is electropositive, and an oxygen end cap, which is electronegative and causes an attraction between the ends of individual HIO3 molecules22. Because of this attraction, during sieving the HIO3 particles instantly agglomerated before the Al can be mixed. This caused extremely poor homogeneity and is the reason Al + commercial HIO3 samples could not sustain the reaction. The Al + HIO3 dehydrate sample had water available to catalyze crystal structure formation (Figure 1a), which reduced, but did not eliminate this effect.
Energy propagation is dependent on the bulk density of the reactant mixture. The density will change based on the concentration of the reactants, so the bulk density of the mixture is usually reported as the percentage of the theoretical maximum density (TMD). The %TMD is calculated using a weighted average of the concentration and the densities of the reactants and accounts for the density of the actual sample according to its mass and volume occupied. In this way, bulk density in terms of %TMD represents the amount of solid space occupied by the volume (i.e., 60% TMD is equivalent to 40% air voids and 60% solids). Low %TMD usually result in higher flame speeds than high %TMD powders. The higher concentration of air voids with lower %TMD provide convective pathways to enhance flame speeds. For this reason, the flame speeds reported in Table 1 are not comparable as a function of mixture, because each was prepared at a discretely different bulk density.
Two conclusions can be drawn from Table 1: (1) I4O9 cannot be processed in isopropanol because it changes into I2O5 and thus alters its reactivity; and (2) I4O9 is more reactive than I2O5 because at higher and lower bulk densities (i.e., 11% TMD compared with 8 or 17% TMD), I4O9 demonstrates increased reactivity. This finding suggests that I4O9 would be advantageous for reactive applications if it could be passivated to improve stability.
Through reactivity and thermal analysis, results show I4O9 can be more reactive than other forms of iodine(V) oxides when combined with aluminum (Al) powder. The I4O9 sample used here was synthesized using a &#39;dry&#39; method that combines elemental oxygen and iodine such that hydrated species are not introduced at any point during synthesis. For this reason, the I4O9 sample is initially devoid of iodic acids and produces a large exotherm at a low temperature (i.e., 180 &#176;C) corresponding to its decomposition into I2O5. The nano-scale I2O5 particles that are created by thermal decomposition of I4O9 are likely amorphous and produce flame speeds over 1,000 m/sec when combined with Al powder (Table 1). The Al + I4O9 reaction produces flame speeds over 1,500 m/sec. This is the first study to explore the potential of I4O9 as an alternative to I2O5 for energy generation technologies, especially motivated by high iodine gas generation.
<img alt="Figure 1" src="/files/ftp_upload/54661/54661fig1.jpg" /> 
Figure 1. DSC Analysis of Heat Flow / TGA Analysis of Mass Loss. a) Heat flow behavior from DSC analysis of six oxidizers and shows different states of iodine(V) oxides used in the range of iodic acid dehydration. b) Mass loss from corresponding TG analysis.
<img alt="Figure 2" src="/files/ftp_upload/54661/54661fig2.jpg" /> 
Figure 2. DSC Analysis of Heat flow. a) Heat flow behavior from DSC analysis for Al + I4O9 dry mix and Al + I4O9, Al + nano I2O5 and Al + commercial I2O5 mixed in isopropanol. Temperature range includes iodic acid dehydration and main reaction temperature range. b) I4O9 initially and I4O9 exposed to 20% RH for 4 hours. Also, the I2O5 was exposed to 20% RH for 4 hours.
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Oxidizer</td>
			<td>Isopropanol Mixed Flame Speed (m/sec)</td>
			<td>% Uncertainty</td>
			<td>Dry Mix Flame Speed</td>
			<td>% Uncertainty</td>
			<td>Bulk Density Dry Mix (g/cm3)</td>
			<td>Dry Mix %TMD</td>
		</tr>
		<tr>
			<td>I4O9</td>
			<td>1,261*</td>
			<td>0.4</td>
			<td>1,551</td>
			<td>3</td>
			<td>0.48</td>
			<td>11.7</td>
		</tr>
		<tr>
			<td>Nano I2O5</td>
			<td>1,146</td>
			<td>4.5</td>
			<td>1,070</td>
			<td>3.7</td>
			<td>0.33</td>
			<td>8</td>
		</tr>
		<tr>
			<td>Commercial I2O5</td>
			<td>719</td>
			<td>5.5</td>
			<td>215</td>
			<td>46.5</td>
			<td>0.93</td>
			<td>22.6</td>
		</tr>
		<tr>
			<td>Amorphous I2O5</td>
			<td>NM</td>
			<td>NM</td>
			<td>1,085</td>
			<td>0.3</td>
			<td>0.73</td>
			<td>17.8</td>
		</tr>
		<tr>
			<td>HIO3 Dehydrate</td>
			<td>NM</td>
			<td>NM</td>
			<td>393</td>
			<td>12</td>
			<td>0.8</td>
			<td>19.3</td>
		</tr>
		<tr>
			<td>Commercial HIO3</td>
			<td>NM</td>
			<td>NM</td>
			<td>NM</td>
			<td>NM</td>
			<td>1.11</td>
			<td>27.1</td>
		</tr>
	</tbody>
</table>
Table 1. Flame Speed Results. Flame speed results for Al + oxidizer indicated in first column. NM indicates not measurable. * Indicates I4O9 was decomposed into I2O5 during mixing.

Watch this Scientific Journal Video about Reaction Kinetics and Combustion Dynamics of I4O9 and Aluminum Mixtures at JoVE.com

Reaction Kinetics and Combustion Dynamics of I4O9 and Aluminum Mixtures

A protocol for measuring flame speeds of a reactive mixture composed of tetraiodine nonoxide (I4O9) and aluminum (Al) is presented. A method for resolving reaction kinetics using differential scanning calorimetry (DSC) is also presented. It was found that I4O9 is 150% more reactive than other iodine(V) oxides.

Reaction Kinetics and Combustion Dynamics of I4O9 and Aluminum Mixtures

Tetraiodine nonoxide (I4O9) has been synthesized using a dry approach that combines elemental oxygen and iodine without the introduction of hydrated ...

reaction-kinetics-combustion-dynamics-i4o9-aluminum

Research

Education

JoVE Journal

JoVE Core

Civil Engineering

Analytical Chemistry

Engineering

Unit 1

Admixtures

Chemical Equilibria

SCIENTISTS IN ACTION

10.7K Views.  Texas Tech University. A protocol for measuring flame speeds of a reactive mixture composed of tetraiodine nonoxide (I4O9) and aluminum (Al) is presented. A method for resolving reaction kinetics using differential scanning calorimetry (DSC) is also presented. It was found that I4O9 is 150% more reactive than other iodine(V) oxides.

Video: Reaction Kinetics and Combustion Dynamics of I4O9 and Aluminum Mixtures

Casting Protocols for the Production of Open Cell Aluminum Foams by the Replication Technique and the Effect on Porosity

Metal foams are interesting materials from both a fundamental understanding and practical applications point of view. Uses have been proposed, and in many cases validated experimentally, for light weight or impact energy absorbing structures, as high surface area heat exchangers or electrodes, as implants to the body, and many more. Although great progress has been made in understanding their structure-properties relationships, the large number of different processing techniques, each producing material with different characteristics and structure, means that understanding of the individual effects of all aspects of structure is not complete. The replication process, where molten metal is infiltrated between grains of a removable preform material, allows a markedly high degree of control and has been used to good effect to elucidate some of these relationships. Nevertheless, the process has many steps that are dependent on individual &#8220;know-how&#8221;, and this paper aims to provide a detailed description of all stages of one embodiment of this processing method, using materials and equipment that would be relatively easy to set up in a research environment. The goal of this protocol and its variants is to produce metal foams in an effective and simple way, giving the possibility to tailor the outcome of the samples by modifying certain steps within the process. By following this, open cell aluminum foams with pore sizes of 1&#8211;2.36 mm diameter and 61% to 77% porosity can be obtained.

Replication is one of the processing techniques used for the production of porous metal sponges. In this paper one implementation of the method for the production of open celled porous aluminum is shown in detail.

Metal foams are interesting materials from both a fundamental understanding and practical applications point of view. Uses have been proposed, and in many ...

Detection and Recovery of Palladium, Gold and Cobalt Metals from the Urban Mine Using Novel Sensors/Adsorbents Designated with Nanoscale Wagon-wheel-shaped Pores

Developing low-cost, efficient processes for recovering and recycling palladium, gold and cobalt metals from urban mine remains a significant challenge in industrialized countries. Here, the development of optical mesosensors/adsorbents (MSAs) for efficient recognition and selective recovery of Pd(II), Au(III), and Co(II) from urban mine was achieved. A simple, general method for preparing MSAs based on using high-order mesoporous monolithic scaffolds was described. Hierarchical cubic Ia3d wagon-wheel-shaped MSAs were fabricated by anchoring chelating agents (colorants) into three-dimensional pores and micrometric particle surfaces of the mesoporous monolithic scaffolds. Findings show, for the first time, evidence of controlled optical recognition of Pd(II), Au(III), and Co(II) ions and a highly selective system for recovery of Pd(II) ions (up to ~95%) in ores and industrial wastes. Furthermore, the controlled assessment processes described herein involve evaluation of intrinsic properties (e.g., visual signal change, long-term stability, adsorption efficiency, extraordinary sensitivity, selectivity, and reusability); thus, expensive, sophisticated instruments are not required. Results show evidence that MSAs will attract worldwide attention as a promising technological means of recovering and recycling palladium, gold and cobalt metals.

Because of the importance and extensive use of palladium, gold and cobalt metals in high-technology equipment, their recovery and recycling constitute an important industrial challenge. The metal recovery system described herein is a simple, low-cost means for the effective detection, removal, and recovery of these metals from the urban mine.

Developing low-cost, efficient processes for recovering and recycling palladium, gold and cobalt metals from urban mine remains a significant challenge in ...

Emission Spectroscopic Boundary Layer Investigation during Ablative Material Testing in Plasmatron

Ablative Thermal Protection Systems (TPS) allowed the first humans to safely return to Earth from the moon and are still considered as the only solution for future high-speed reentry missions. But despite the advancements made since Apollo, heat flux prediction remains an imperfect science and engineers resort to safety factors to determine the TPS thickness. This goes at the expense of embarked payload, hampering, for example, sample return missions. 
Ground testing in plasma wind-tunnels is currently the only affordable possibility for both material qualification and validation of material response codes. The subsonic 1.2MW Inductively Coupled Plasmatron facility at the von Karman Institute for Fluid Dynamics is able to reproduce a wide range of reentry environments. This protocol describes a procedure for the study of the gas/surface interaction on ablative materials in high enthalpy flows and presents sample results of a non-pyrolyzing, ablating carbon fiber precursor. With this publication, the authors envisage the definition of a standard procedure, facilitating comparison with other laboratories and contributing to ongoing efforts to improve heat shield reliability and reduce design uncertainties.
The described core techniques are non-intrusive methods to track the material recession with a high-speed camera along with the chemistry in the reactive boundary layer, probed by emission spectroscopy. Although optical emission spectroscopy is limited to line-of-sight measurements and is further constrained to electronically excited atoms and molecules, its simplicity and broad applicability still make it the technique of choice for analysis of the reactive boundary layer. Recession of the ablating sample further requires that the distance of the measurement location with respect to the surface is known at all times during the experiment. Calibration of the optical system of the applied three spectrometers allowed quantitative comparison. At the fiber scale, results from a post-test microscopy analysis are presented.

Development of new ablative materials and their numerical modeling requires extensive experimental investigation. This protocol describes procedures for material response characterization in plasma flows with the core techniques being non-intrusive methods to track the material recession along with the chemistry in the reactive boundary layer by emission spectroscopy.

Ablative Thermal Protection Systems (TPS) allowed the first humans to safely return to Earth from the moon and are still considered as the only solution ...

Adsorption Device Based on a Langatate Crystal Microbalance for High Temperature High Pressure Gas Adsorption in Zeolite H-ZSM-5

We present a high-temperature and high-pressure gas adsorption measurement device based on a high-frequency oscillating microbalance (5 MHz langatate crystal microbalance, LCM) and its use for gas adsorption measurements in zeolite H-ZSM-5. Prior to the adsorption measurements, zeolite H-ZSM-5 crystals were synthesized on the gold electrode in the center of the LCM, without covering the connection points of the gold electrodes to the oscillator, by the steam-assisted crystallization (SAC) method, so that the zeolite crystals remain attached to the oscillating microbalance while keeping good electroconductivity of the LCM during the adsorption measurements. Compared to a conventional quartz crystal microbalance (QCM) which is limited to temperatures below 80 &#176;C, the LCM can realize the adsorption measurements in principle at temperatures as high as 200-300 &#176;C (i.e., at or close to the reaction temperature of the target application of one-stage DME synthesis from the synthesis gas), owing to the absence of crystalline-phase transitions up to its melting point (1,470 &#176;C). The system was applied to investigate the adsorption of CO2, H2O, methanol and dimethyl ether (DME), each in the gas phase, on zeolite H-ZSM-5 in the temperature and pressure range of 50-150 &#176;C and 0-18 bar, respectively. The results showed that the adsorption isotherms of these gases in H-ZSM-5 can be well fitted by Langmuir-type adsorption isotherms. Furthermore, the determined adsorption parameters, i.e., adsorption capacities, adsorption enthalpies, and adsorption entropies, compare well to literature data. In this work, the results for CO2 are shown as an example.

A protocol for high-temperature and high-pressure gas adsorption measurements on zeolite H-ZSM-5 using an adsorption measurement device based on a langatate crystal microbalance is presented. Prior to the adsorption measurements, the synthesis of zeolite H-ZSM-5 on the langatate crystal microbalance sensor by the steam-assisted crystallization (SAC) method is demonstrated.

We present a high-temperature and high-pressure gas adsorption measurement device based on a high-frequency oscillating microbalance (5 MHz langatate ...

Combustion Characterization and Model Fuel Development for Micro-tubular Flame-assisted Fuel Cells

Combustion based power generation has been accomplished for many years through a number of heat engine systems. Recently, a move towards small scale power generation and micro combustion as well as development in fuel cell research has created new means of power generation that combine solid oxide fuel cells with open flames and combustion exhaust. Instead of relying upon the heat of combustion, these solid oxide fuel cell systems rely on reforming of the fuel via combustion to generate syngas for electrochemical power generation. Procedures were developed to assess the combustion by-products under a wide range of conditions. While theoretical and computational procedures have been developed for assessing fuel-rich combustion exhaust in these applications, experimental techniques have also emerged. The experimental procedures often rely upon a gas chromatograph or mass spectrometer analysis of the flame and exhaust to assess the combustion process as a fuel reformer and means of heat generation. The experimental techniques developed in these areas have been applied anew for the development of the micro-tubular flame-assisted fuel cell. The protocol discussed in this work builds on past techniques to specify a procedure for characterizing fuel-rich combustion exhaust and developing a model fuel-rich combustion exhaust for use in flame-assisted fuel cell testing. The development of the procedure and its applications and limitations are discussed.

A protocol for creating a model fuel-rich combustion exhaust is developed through combustion characterization and is applied for micro-tubular flame-assisted fuel cell testing and research.

Combustion based power generation has been accomplished for many years through a number of heat engine systems. Recently, a move towards small scale power ...

Experimental Procedure for Warm Spinning of Cast Aluminum Components

High performance, cast aluminum automotive wheels are increasingly being incrementally formed via flow forming/metal spinning at elevated temperatures to improve material properties. With a wide array of processing parameters which can affect both the shape attained and resulting material properties, this type of processing is notoriously difficult to commission. A simplified, light-duty version of the process has been designed and implemented for full-size automotive wheels. The apparatus is intended to assist in understanding the deformation mechanisms and the material response to this type of processing. An experimental protocol has been developed to prepare for, and subsequently perform forming trials and is described for as-cast A356 wheel blanks. The thermal profile attained, along with instrumentation details are provided. Similitude with full-scale forming operations which impart significantly more deformation at faster rates is discussed.

An experimental protocol for instrumented warm rotary forming of cast aluminum alloys employing a bespoke industrially scaled apparatus is presented. Experimental considerations including thermal and mechanical effects are discussed, as well as similitude with full-scale processing of automotive wheels.

High performance, cast aluminum automotive wheels are increasingly being incrementally formed via flow forming/metal spinning at elevated temperatures to ...

Two-way Valorization of Blast Furnace Slag: Synthesis of Precipitated Calcium Carbonate and Zeolitic Heavy Metal Adsorbent

The aim of this work is to present a zero-waste process for storing CO2 in a stable and benign mineral form while producing zeolitic minerals with sufficient heavy metal adsorption capacity. To this end, blast furnace slag, a residue from iron-making, is utilized as the starting material. Calcium is selectively extracted from the slag by leaching with acetic acid (2 M CH3COOH) as the extraction agent. The filtered leachate is subsequently physico-chemically purified and then carbonated to form precipitated calcium carbonate (PCC) of high purity (&lt;2 wt% non-calcium impurities, according to ICP-MS analysis). Sodium hydroxide is added to neutralize the regenerated acetate. The morphological properties of the resulting calcitic PCC are tuned for its potential application as a filler in papermaking. In parallel, the residual solids from the extraction stage are subjected to hydrothermal conversion in a caustic solution (2 M NaOH) that leads to the predominant formation of a particular zeolitic mineral phase (detected by XRD), namely analcime (NaAlSi2O6&#8729;H2O). Based on its ability to adsorb Ni2+, as reported from batch adsorption experiments and ICP-OES analysis, this product can potentially be used in wastewater treatment or for environmental remediation applications.

A protocol for the parallel production of precipitated calcium carbonate and zeolitic material from blast furnace slag via mineral carbonation and alkaline hydrothermal conversion, respectively, is presented. The performance of the zeolitic material towards nickel adsorption is tested.

The aim of this work is to present a zero-waste process for storing CO2 in a stable and benign mineral form while producing zeolitic minerals with ...

Measurements of Soil Carbon by Neutron-Gamma Analysis in Static and Scanning Modes

The herein described application of the inelastic neutron scattering (INS) method for soil carbon analysis is based on the registration and analysis of gamma rays created when neutrons interact with soil elements. The main parts of the INS system are a pulsed neutron generator, NaI(Tl) gamma detectors, split electronics to separate gamma spectra due to INS and thermo-neutron capture (TNC) processes, and software for gamma spectra acquisition and data processing. This method has several advantages over other methods in that it is a non-destructive in situ method that measures the average carbon content in large soil volumes, is negligibly impacted by local sharp changes in soil carbon, and can be used in stationary or scanning modes. The result of the INS method is the carbon content from a site with a footprint of ~2.5 - 3 m2 in the stationary regime, or the average carbon content of the traversed area in the scanning regime. The measurement range of the current INS system is &#62;1.5 carbon weight % (standard deviation &#177; 0.3 w%) in the upper 10 cm soil layer for a 1 hmeasurement.

Here, we present the protocol for in situ measurement of soil carbon using the neutron-gamma technique for single point measurements (static mode) or field averages (scanning mode). We also describe system construction and elaborate data treatment procedures.

The herein described application of the inelastic neutron scattering (INS) method for soil carbon analysis is based on the registration and analysis of ...

Simultaneous Multi-surface Anodizations and Stair-like Reverse Biases Detachment of Anodic Aluminum Oxides in Sulfuric and Oxalic Acid Electrolyte

After reporting on the two-step anodization, nanoporous anodic aluminum oxides (AAOs) have been widely utilized in the versatile fields of fundamental sciences and industrial applications owing to their periodic arrangement of nanopores with relatively high aspect ratio. However, the techniques reported so far, which could be only valid for mono-surface anodization, show critical disadvantages, i.e., time-consuming as well as complicated procedures, requiring toxic chemicals, and wasting valuable natural resources. In this paper, we demonstrate a facile, efficient, and environmentally clean method to fabricate nanoporous AAOs in sulfuric and oxalic acid electrolytes, which can overcome the limitations that result from conventional AAO fabricating methods. First, plural AAOs are produced at one time through simultaneous multi-surfaces anodization (SMSA), indicating mass-producibility of the AAOs with comparable qualities. Second, those AAOs can be separated from the aluminum (Al) substrate by applying stair-like reverse biases (SRBs) in the same electrolyte used for the SMSAs, implying simplicity and green technological characteristics. Finally, a unit sequence consisting of the SMSAs sequentially combined with SRBs-based detachment can be applied repeatedly to the same Al substrate, which reinforces the advantages of this strategy and also guarantees the efficient usage of natural resources.

A protocol for fabricating nanoporous anodic aluminum oxides via simultaneous multi-surfaces anodization followed by stair-like reverse biases detachments is presented. It can be applied repeatedly to the same aluminum substrate, exhibiting a facile, high-yield, and environmentally clean strategy.

After reporting on the two-step anodization, nanoporous anodic aluminum oxides (AAOs) have been widely utilized in the versatile fields of fundamental ...

Enhanced Electron Injection and Exciton Confinement for Pure Blue Quantum-Dot Light-Emitting Diodes by Introducing Partially Oxidized Aluminum Cathode

Stable and efficient red (R), green (G), and blue (B) light sources based on solution-processed quantum dots (QDs) play important roles in next-generation displays and solid-state lighting technologies. The brightness and efficiency of blue QDs-based light-emitting diodes (LEDs) remain inferior to their red and green counterparts, due to the inherently unfavorable energy levels of different colors of light. To solve these problems, a device structure should be designed to balance the injection holes and electrons into the emissive QD layer. Herein, through a simple autoxidation strategy, pure blue QD-LEDs which are highly bright and efficient are demonstrated, with a structure of ITO/PEDOT:PSS/Poly-TPD/QDs/Al:Al2O3. The autoxidized Al:Al2O3 cathode can effectively balance the injected charges and enhance radiative recombination without introducing an additional electron transport layer (ETL). As a result, high color-saturated blue QD-LEDs are achieved with a maximum luminance over 13,000 cd m-2, and a maximum current efficiency of 1.15 cd A-1. The easily controlled autoxidation procedure paves the way for achieving high-performance blue QD-LEDs.

A protocol is presented for fabricating high-performance, pure blue ZnCdS/ZnS-based quantum dots light-emitting diodes by employing an autoxidized aluminum cathode.

Stable and efficient red (R), green (G), and blue (B) light sources based on solution-processed quantum dots (QDs) play important roles in next-generation ...