This work was conducted while Bian, Chen, and Wang were visiting Ph.D. students at the US Forest Service, Forest Products Laboratory (FPL), Madison, WI, and on official government time of Zhu. This work was partially supported by the USDA Agriculture and Food Research Initiative (AFRI) Competitive Grant (No. 2011-67009-20056), the Chinese State Forestry Administration (Project No. 2015-4-54), the National Natural Science Foundation of China (Project No. 31470599), Guangzhou Elite Project of China, and China Scholarship Fund. Funding from these programs made the visiting appointments of Bian, Chen, and Wang at FPL possible.

NOTE: Bleached eucalyptus kraft pulp (BEP) and unbleached mixed hardwood kraft pulp (UMHP) fibers from commercial sources were used as feedstock for producing CNC and CNF. Commercial maleic acids purchased were used for hydrolysis. Hydrolysis conditions were acid concentrations of 60 wt% at 100 &#176;C for 60 min and 120 &#176;C (no boiling at atmospheric pressure) for 120 min, for BEP and UMHP, respectively.
1. Preparation of Concentrated Dicarboxylic Acid Solution
<ol>
	<li>Heat 40 mL deio...

<ol>
	<li>Giese, M., Blusch, L. K., Khan, M. K., MacLachlan, M. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Functional+Materials+from+Cellulose-Derived+Liquid-Crystal+Templates.">Functional Materials from Cellulose-Derived Liquid-Crystal Templates.</a> Angew Chem Int Ed. 54 (10), 2888-2910 (2015).</li><li>Zhu, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Wood-Derived+Materials+for+Green+Electronics,+Biological+Devices,+and+Energy+Applications+.">Wood-Derived Materials for Green Electronics, Biological Devices, and Energy Applications .</a> Chem. Rev. , (2016).</li><li>Wang, Q. Q., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Approaching+zero+cellulose+loss+in+cellulose+nanocrystal+(CNC)+production:+recovery+and+characterization+of+cellulosic+solid+residues+(CSR)+and+CND.">Approaching zero cellulose loss in cellulose nanocrystal (CNC) production: recovery and characterization of cellulosic solid residues (CSR) and CND.</a> Cellulose. 19 (6), 2033-2047 (2012).</li><li>Hamad, W. Y., Hu, T. Q. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Structure-process-yield+interrelations+in+nanocrystalline+cellulose+extraction.">Structure-process-yield interrelations in nanocrystalline cellulose extraction.</a> Can J Chem Eng. 88 (3), 392-402 (2010).</li><li>Chen, L. H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Tailoring+the+yield+and+characteristics+of+wood+cellulose+nanocrystals+(CNC)+using+concentrated+acid+hydrolysis.">Tailoring the yield and characteristics of wood cellulose nanocrystals (CNC) using concentrated acid hydrolysis.</a> Cellulose. 22 (3), 1753-1762 (2015).</li><li>Mukherjee, S. M., Woods, H. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=X-ray+and+electron+microscope+studies+of+the+degradation+of+cellulose+by+sulphuric+acid.">X-ray and electron microscope studies of the degradation of cellulose by sulphuric acid.</a> Biochim Biophys Acta. 10 (4), 499-511 (1953).</li><li>Camarero Espinosa, S., Kuhnt, T., Foster, E. J., Weder, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Isolation+of+thermally+stable+cellulose+nanocrystals+by+phosphoric+acid+hydrolysis.">Isolation of thermally stable cellulose nanocrystals by phosphoric acid hydrolysis.</a> Biomacromolecules. 14 (4), 1223-1230 (2013).</li><li>Yu, H. Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Facile+extraction+of+thermally+stable+cellulose+nanocrystals+with+a+high+yield+of+93%+through+hydrochloric+acid+hydrolysis+under+hydrothermal+conditions.">Facile extraction of thermally stable cellulose nanocrystals with a high yield of 93% through hydrochloric acid hydrolysis under hydrothermal conditions.</a> J Mater Chem, A. 1 (12), 3938-3944 (2013).</li><li>Leung, A. C. W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Characteristics+and+properties+of+carboxylated+cellulose+nanocrystals+prepared+from+a+novel+one-step+procedure.">Characteristics and properties of carboxylated cellulose nanocrystals prepared from a novel one-step procedure.</a> Small. 7 (3), 302-305 (2011).</li><li>Saito, T., Isogai, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=TEMPO-mediated+oxidation+of+native+cellulose.+The+effect+of+oxidation+conditions+on+chemical+and+crystal+structures+of+the+water-insoluble+fractions.">TEMPO-mediated oxidation of native cellulose. The effect of oxidation conditions on chemical and crystal structures of the water-insoluble fractions.</a> Biomacromolecules. 5 (5), 1983-1989 (2004).</li><li>Yang, H., Chen, D. Z., van de Ven, T. G. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+and+characterization+of+sterically+stabilized+nanocrystalline+cellulose+obtained+by+periodate+oxidation+of+cellulose+fibers.">Preparation and characterization of sterically stabilized nanocrystalline cellulose obtained by periodate oxidation of cellulose fibers.</a> Cellulose. 22 (3), 1743-1752 (2015).</li><li>Huang, Y. B., Fu, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Hydrolysis+of+cellulose+to+glucose+by+solid+acid+catalysts.">Hydrolysis of cellulose to glucose by solid acid catalysts.</a> Green Chem. 15 (5), 1095-1111 (2013).</li><li>Shimizu, K. I., Satsuma, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Toward+a+rational+control+of+solid+acid+catalysis+for+green+synthesis+and+biomass+conversion.">Toward a rational control of solid acid catalysis for green synthesis and biomass conversion.</a> Energy &amp; Environ Sci. 4 (9), 3140-3153 (2011).</li><li>Wang, Q. Q., Zhu, J. Y., Considine, J. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Strong+and+optically+transparent+films+prepared+using+cellulosic+solid+residue+(CSR)+recovered+from+cellulose+nanocrystals+(CNC)+production+waste+stream.">Strong and optically transparent films prepared using cellulosic solid residue (CSR) recovered from cellulose nanocrystals (CNC) production waste stream.</a> ACS Appl Mater Interfaces. 5 (7), 2527-2534 (2013).</li><li>Chen, L. H., Zhu, J. Y., Baez, C., Kitin, P., Elder, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Highly+thermal-stable+and+functional+cellulose+nanocrystals+and+nanofibrils+produced+using+fully+recyclable+organic+acids.">Highly thermal-stable and functional cellulose nanocrystals and nanofibrils produced using fully recyclable organic acids.</a> Green Chem. 18, 3835-3843 (2016).</li><li>Fischer, E., Speier, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Darstellungder+der+Ester.">Darstellungder der Ester.</a> Chemische Berichte. 28 (3), 3252-3258 (1895).</li><li>Allen, T. C., Cuculo, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cellulose+derivatives+containing+carboxylic+acid+groups.">Cellulose derivatives containing carboxylic acid groups.</a> J Polym Sci: Macromol Rev. 7 (1), 189-262 (1973).</li><li>Wang, Q. Q., Zhao, X. B., Zhu, J. Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Kinetics+of+strong+acid+hydrolysis+of+a+bleached+kraft+pulp+for+producing+cellulose+nanocrystals+(CNCs).">Kinetics of strong acid hydrolysis of a bleached kraft pulp for producing cellulose nanocrystals (CNCs).</a> Ind Eng Chem Res. 53 (27), 11007-11014 (2014).</li><li>Segal, L., Creely, J. J., Martin, A. E., Conrad, C. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+empirical+method+for+estimating+the+degree+of+crystallinity+of+native+cellulose+using+the+X-ray+diffractometer.">An empirical method for estimating the degree of crystallinity of native cellulose using the X-ray diffractometer.</a> Text Res J. 29 (10), 786-794 (1959).</li></ol>

The thicker CNC diameters of the CNC samples from maleic acid hydrolysis resulted in a moderate average aspect ratio 7.24 and 8.53, for the CNCs from BEP and UMHP, respectively, despite their long lengths as discussed above. The CNFs had a longer length and a thinner diameter, which resulted in a large aspect ratio of 13.9 and 19.0, for the CNCs from BEP and UMHP, respectively, both greater than their respective CNCs. It is possible to use severe mechanical fibrillation to reduce CNF diameter to improve the aspect ratio ...

Sustainable economic development requires not only using feedstocks that are renewable and biodegradable but also uses green and environmental friendly manufacturing technologies to produce a variety of bioproducts and biochemicals from these renewable feedstocks. Cellulose nanomaterials, such as cellulose nanocrystals (CNC) and cellulose nanofibrils (CNF), produced from renewable lignocelluloses are biodegradable and have unique mechanical and optical properties suitable for developing a range of bioproducts 1, 2. Unfortunately, existing technologies for producing cellulose nanomaterials are either energy intensive when using pure mechanical fibrillation or environmentally unsustainable due to non-recycling or insufficient recycling of processing chemicals, such as when using the concentrated mineral acid hydrolysis process 3-8 or oxidation methods 9-11. Furthermore, oxidation methods may also produce environmentally toxic compounds by reacting with lignocelluloses. Therefore, developing green manufacturing technologies for producing cellulose nanomaterials is critically important to make full use of the abundant and renewable material - lignocelluloses.
Using acid hydrolysis to dissolve hemicellulose and depolymerize cellulose is an effective approach for producing cellulose nanomaterials. Solid acids have been used for sugar production from cellulose with the advantage of easing acid recovery 12, 13. Previous studies using concentrated mineral acids indicated that a lower acid concentration improved CNC yield and crystallinity 3, 5. This suggests that a strong acid may damage cellulose crystals while a milder acid hydrolysis might improve the properties and yield of cellulose nanomaterials through the approach of integrated production and CNC with CNF 3, 14. Here we document a method using concentrated solid dicarboxylic acids hydrolysis to produce CNC along with CNF 15. These dicarboxylic acids have low solubility at low or ambient temperatures, and therefore they can be easily recovered through the mature crystallization technology. They also have good solubility at elevated temperatures which facilitates concentrated acid hydrolysis without boiling or using pressure vessels. Since these acids also have a higher pKa than typical mineral acids used for CNC production, their use results in good CNC crystallinity, and despite lower CNC yields, with a substantial amount of fibrous cellulosic solid residue (FCSR or partially hydrolyzed fibers) remaining due to incomplete cellulose depolymerization. The FCSR can be used to produce CNF through subsequent mechanical fibrillation using low energy inputs. Therefore, cellulose loss to sugars is minimal as compared to using mineral acids.
It is well known that carboxylic acids can esterify cellulose through Fisher-Speier esterification 16. Applying dicarboxylic acids to cellulose can result in semi-acid un-crosslinked esters 17 (or carboxylation), to produce carboxylated CNC and CNF as we demonstrated 15 previously. The method documented here can produce carboxylated and thermally stable CNF and CNC that is also highly crystalline from either bleached or unbleached pulps while having relatively simple and high chemical recovery and using low energy inputs.

<table border="0" cellpadding="0" cellspacing="0" width="1222">
	<tbody>
		<tr height="21">
			<td height="21" style="height:21px;width:349px;">Bleached eucalypus pulp&#160;</td>
			<td style="width:327px;">Aracruz Cellulose</td>
			<td style="width:248px;"></td>
			<td style="width:299px;"></td>
		</tr>
		<tr height="19">
			<td height="19" style="height:19px;width:349px;">Unbleached mixed hardwood kraft pulp&#160;</td>
			<td>International Paper&#160;</td>
			<td></td>
			<td></td>
		</tr>
		<tr height="26">
			<td height="26" style="height:27px;">Maleic acid</td>
			<td>Sigma-Aldrich</td>
			<td>M0375-1KG/CAS110-16-7</td>
			<td style="width:299px;">Powder; assay: 99.0%(HPLC)</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Glycerol</td>
			<td>Sigma-Aldrich</td>
			<td>G5516-4L/CAS56-81-5</td>
			<td></td>
		</tr>
		<tr height="37">
			<td height="37" style="height:38px;">Sodium hydroxide</td>
			<td>Fisher Scientific</td>
			<td style="width:248px;">S318-500/CAS1310-73-2, 497-19-8</td>
			<td>Certified ACS</td>
		</tr>
		<tr height="24">
			<td height="24" style="height:25px;">Sodium chloride</td>
			<td>Mallinckrodt</td>
			<td>7581-12/CAS7647-14-5</td>
			<td>Crystal,AR</td>
		</tr>
		<tr height="41">
			<td height="41" style="height:42px;">Cupriethylenediamine solution</td>
			<td>GFS Chemicals</td>
			<td>E32103-1L/CAS14552-35-3</td>
			<td style="width:299px;">1M, for determination of solution viscosity of pulps</td>
		</tr>
		<tr height="24">
			<td height="24" style="height:25px;">Acetone</td>
			<td>Fisher Scientific</td>
			<td>A18-500/CAS67-64-1</td>
			<td>Certified ACS</td>
		</tr>
		<tr height="40">
			<td height="40" style="height:40px;">Accu-TestTM Vials for COD Testing</td>
			<td>Bioscience,Inc.</td>
			<td>01-215-28</td>
			<td style="width:299px;">COD testing for 20 to 900mg/L standard range concentration</td>
		</tr>
		<tr height="23">
			<td height="23" style="height:23px;">Heating plate</td>
			<td>IKA</td>
			<td></td>
			<td>Mode: C-MAD HS7 digital</td>
		</tr>
		<tr height="29">
			<td height="29" style="height:30px;">Magnetic stir bar</td>
			<td>ACE Glass</td>
			<td></td>
			<td></td>
		</tr>
		<tr height="29">
			<td height="29" style="height:30px;">Pyrex three-neck round-bottom flask</td>
			<td>Sigma-Aldrich</td>
			<td>CLS4965B500-1EA</td>
			<td></td>
		</tr>
		<tr height="38">
			<td height="38" style="height:39px;">Dialysis tubing cellulose membrane</td>
			<td>Sigma-Aldrich</td>
			<td>D9402-100FT</td>
			<td style="width:299px;">Typical molecular weight cut-off = 14000</td>
		</tr>
		<tr height="22">
			<td height="22" style="height:23px;">Disposable aluminum dishes</td>
			<td>Sigma-Aldrich</td>
			<td>Z154857-1PAK</td>
			<td>Circles, 60mm</td>
		</tr>
		<tr height="19">
			<td height="19" style="height:19px;">Disintegrator</td>
			<td>Testing Machines Inc.(TMI)</td>
			<td></td>
			<td style="width:299px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Microfluidizer</td>
			<td>Microfluidics Corporation</td>
			<td></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Sonicator</td>
			<td>Qsonica LLC.</td>
			<td></td>
			<td>Mode: 3510R-MT, 50-60 Hz,180 W</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Zeta potential analyzer</td>
			<td>Brookhaven Instruments Corporation</td>
			<td></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">FTIR</td>
			<td>PerkinElmer</td>
			<td></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Conductometric titrator</td>
			<td>Yellow Springs Instrument (YSI)</td>
			<td></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">TGA analyzer</td>
			<td>PerkinElmer</td>
			<td></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">X-ray diffractometer</td>
			<td>Bruker Corporation</td>
			<td></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">AFM imging&#160;</td>
			<td>AFM Workshop</td>
			<td></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">SEM imaging</td>
			<td>Carl Zeiss</td>
			<td></td>
			<td></td>
		</tr>
	</tbody>
</table>

green and low-cost production of thermally stable and carboxylated cellulose nanocrystals and nanofibrils using highly recyclable dicarboxylic acids

Here we demonstrate potentially low cost and green productions of high thermally stable and carboxylated cellulose nanocrystals (CNCs) and nanofibrils (CNF) from bleached eucalyptus pulp (BEP) and unbleached mixed hardwood kraft pulp (UMHP) fibers using highly recyclable dicarboxylic solid acids. Typical operating conditions were acid concentrations of 50 - 70 wt% at 100 &#176;C for 60 min and 120 &#176;C (no boiling at atmospheric pressure) for 120 min, for BEP and UMHP, respectively. The resultant CNCs have a higher thermal degradation temperature than their corresponding feed fibers and carboxylic acid group content from 0.2 - 0.4 mmol/g. The low strength (high pKa of 1.0 - 3.0) of organic acids also resulted in CNCs with both longer lengths of approximately 239 - 336 nm and higher crystallinity than CNCs produced using mineral acids. Cellulose loss to sugar was minimal. Fibrous cellulosic solid residue (FCSR) from the dicarboxylic acid hydrolysis was used to produce carboxylated CNFs through subsequent mechanical fibrillation with low energy input.

Typical AFM images of the CNC and CNF from BEP and UMHP along with corresponding SEM images of the feed acid hydrolyzed fibers are shown in Figures 1 and 2. The images clearly show the substantial reductions in fiber length by acid hydrolysis with minimal change in fiber diameters (comparing Figure 1a with 1b, and 2a with 2b). The shortened fiber length was also reflected by the measured cellulose degree of polymerizatio...

Watch this Scientific Journal Video about Green and Low-cost Production of Thermally Stable and Carboxylated Cellulose Nanocrystals and Nanofibrils Using Highly Recyclable Dicarboxylic Acids at JoVE.c

Green and Low-cost Production of Thermally Stable and Carboxylated Cellulose Nanocrystals and Nanofibrils Using Highly Recyclable Dicarboxylic Acids

Here we demonstrate a novel method for green and sustainable productions of highly thermally stable and carboxylated cellulose nanocrystals (CNC) and nanofibrils (CNF) using highly recyclable solid dicarboxylic acids.

Here we demonstrate potentially low cost and green productions of high thermally stable and carboxylated cellulose nanocrystals (CNCs) and nanofibrils ...

The overall goal of this procedure is to demonstrate the integrated production of carboxylated, thermally stable cellulose nanocrystals with cellulose nanofibrils from cellulosic feedstock using solid dicarboxylic acids with easy acid recovery. This method is to help us answer the question how to produce with nanomaterials. The main advantages of this technique is that the results of materials are similarly highly most stable, carboxylated, and the acids we use can be easily recycled, therefore to achieve even stability.To begin the procedure, place 40mL of deionized water and a magnetic stir bar into a three-neck, round-bottomed flask. Heat the water to 85 degrees Celsius with a liquid glycerol bath. Then, add 60g anhydrous maleic acid to the flask and stir until completely dissolved to obtain a 60 weight percent moleic acid solution.Heat the solution to 100 degrees Celsius while stirring. Then, add 10g of oven-dried, bleached, eucalyptus kraft pulp, and stir the mixture for one hour to hydrolyze the pulp. During hydrolysis, prepare a vacuum filtration flask and buchner funnel with filter paper.Then, add 160mL of 80 degrees Celsius DI water to the reaction flask to terminate hydrolysis. After an hour has elapsed, take a 2mL aliquot of the acid hydrolyzate for concentration analysis. Immediately collect the solids by vacuum filtration.Wash the solids with DI water and retain the filtrate for acid recovery. Transfer the washed solids to a centrifuge bottle and add DI water to obtain an approximately 1%by weight mixture. Centrifuge the pulp mixture at 11, 960G for 10 minutes, and then discard the supernatant.Continue washing the solids by centifugation until the supernatant appears turbid. Resuspend the solids in the turbid supernatant. Dialyze the mixture against DI water until the conductivity of the pulp mixture is close to that of DI water.Then, centrifuge the dialyzed sample at 3, 500 G for 10 minutes. Decant the supernatant to separate the aqueous dispersion of CNCs from the fibrous cellulosic solid residue. Then, prepare a 0.5%by weight fiber suspension in DI water using the fibrous cellulosic solid residue.Pass the suspension through a 200 micrometer homogenizer chamber at 100 millipascals three times, And then through an 87 micrometer chamber at 100 millipascals twice to obtain CNFs by mechanical fibrillation. To determine the nanomaterial length and diameter distributions, first sonicate a 0.01 weight percent suspension of CNCs or CNFs for two minutes. Apply a drop of the suspension to a mica AFM substrate and allow the sample to air dry.Acquire AFM images in vibrating tapping mode. Once the images include at least 100 individual CNCs or CNFs, process the images with analysis software to obtain the size distributions. Next, combine a suspension containing 50mg of cellulose nanomaterials with 120mL of one millimolar sodium chloride.Perform conductometic titration with 0.2mL portions of 10 millimolars sodium hydroxide at 30 second intervals and determine the inflection point. Calculate the caarboxylic acid group content of the sample. Purge the instrument furnace with high purity nitrogen at 20mL per minute.Next, dry CNC and CNF samples at 50 degrees Celsius for four hours to prepare for thermogravimetric analysis. Load 5mg of a dry cellulose nanomaterial sample into the instrument. Heat the furnace from room temperature to 600 degrees Celsius at a rate of 10 degrees Celsius per minute, and evaluate sample decomposition with the instrument's software.Check the thermal stability of the CNC and CNF samples at 105 degrees Celsius for four and 24 hours. Use wide-angle x-ray defraction and FTIR spectrophotometry to further characterize the cellulose nanomaterial samples. Using this procedure, CNCs and CNFs were produced from bleached eucalyptus kraft pulp, and unbleached mixed hardwood kraft pulp.Hydrolysis with dicarboxylic acids such as moleic acid reduced fiber length without significantly affecting fiber diameter. The CNC yield was comparatively low when moleic acid was used. CNFs were obtained by mechanical fibrillation of the fibrous cellulosic solid residue from hydrolysis, and were correspondingly longer and thinner than the CNCs.While attempting this procedure, it is important to remember to use dialysis to separate the CNCs. After its development, this technique will pave the way for the scientists in the field of material science, medical science and electronic industry to develop body parts and using this material. After watching this video, you should have a good understanding how to produce similarly stable carboxylated cellulose nanomaterials using dicarboxylic acids.Don't forget, and always remember, working with a concentrated acid can be extremely hazardous, so precautions have to be taken while performing this procedure.

green-low-cost-production-thermally-stable-carboxylated-cellulose

Research

JoVE Journal

Chemistry

11.7K 조회수.  Nanjing Forestry University. The overall goal of this procedure is to demonstrate the integrated production of carboxylated, thermally stable cellulose nanocrystals with cellulose nanofibrils from cellulosic feedstock using solid dicarboxylic acids with easy acid recovery. This method is to help us answer the question how to produce with nanomaterials. The main advantages of this technique is that the results of materials are similarly highly most stable, carboxylated, and the acids we use can be easily recycled, therefo...

비디오: Green and Low-cost Production of Thermally Stable and Carboxylated Cellulose Nanocrystals and Nanofibrils Using Highly Recyclable Dicarboxylic Acids