The work described in this paper was supported by a grant from the CII-HK/PolyU Innovation Fund. Further support was provided by the Shenzhen Peacock Plan (KQTD2015071616442225) and the Chinese Government &#34;Thousand Talent&#34; Program (Y62HB31601). Also, the help from the Department of Applied Biology &#38; Chemical Technology of the Hong Kong Polytechnic University and the Hong Kong Polytechnic University Research Institute for Sustainable Urban Development (RISUD) is appreciated.

1. Pre-treatment of HGM
<ol>
	<li>Place the HGM into a 500-mL beaker with 200 mL of absolute alcohol; the low density of unbroken HGM causes it to suspend in the alcohol, but because the density of broken HGM is larger than that of alcohol, it precipitates in the solution. After 30 min, collect the suspended HGM using a clean spoon and dry at 80 &#176;C in an oven for further application.</li>
</ol>
2. Synthesis of MCHGM
<ol>
	<li>Place 5 g of unbroken HGM, 47.5 mL of ethanol, and 2.5 mL of DI...

<ol>
	<li>Yung, K. C., Zhu, B. L., Yue, T. M., Xie, C. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+and+properties+of+hollow+glass+microsphere-filled+epoxy-matrix+composites.">Preparation and properties of hollow glass microsphere-filled epoxy-matrix composites.</a> Compos. Sci. Technol. 69 (2), 260-264 (2008).</li><li>Xu, N., Dai, J., Zhu, Z., Huang, X., Wu, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+and+characterization+of+hollow+glass-ceramics+microspheres.">Synthesis and characterization of hollow glass-ceramics microspheres.</a> Compos. Sci. Technol. 72 (4), 528-532 (2011).</li><li>Li, B., Yuan, J., An, Z., Zhang, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+microstructure+and+physical+parameters+of+hollow+glass+microsphere+on+insulation+performance.">Effect of microstructure and physical parameters of hollow glass microsphere on insulation performance.</a> Mater. Lett. 65 (12), 1992-1994 (2011).</li><li>Hu, Y., Mei, R., An, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Silicon+rubber/hollow+glass+microsphere+composites:+Influence+of+broken+hollow+glass+microsphere+on+mechanical+and+thermal+insulation+property.">Silicon rubber/hollow glass microsphere composites: Influence of broken hollow glass microsphere on mechanical and thermal insulation property.</a> Compos. Sci. Technol. 79, 64-69 (2013).</li><li>Geleil, A. S., Hall, M. M., Shelby, J. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Hollow+glass+microspheres+for+use+in+radiation+shielding.">Hollow glass microspheres for use in radiation shielding.</a> J. Non-Cryst. Solids. 352, 620-625 (2006).</li><li>Khimiya. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Handbook of Fillers for Polymeric Composite Materials [Russian translation]. , (1981).</li><li>Greiner-Bar, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=HoNe+Mikroglaskugeln.+Herstellung,+Eigenschaften+und+Anwendung.">HoNe Mikroglaskugeln. Herstellung, Eigenschaften und Anwendung.</a> Silikattechnik. 40 (1), 23-25 (1989).</li><li>Kool, L. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Method+for+storing+hydrogen,+and+related+articles+and+systems.">Method for storing hydrogen, and related articles and systems.</a> United States Patent. , (2010).</li><li>Brow, R. K., Schmitt, M. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+survey+of+energy+and+environmental+application+of+glass.">A survey of energy and environmental application of glass.</a> J. Eur. Ceram. Soc. 29, 1193-1201 (2009).</li><li>Awaja, F., Arhatari, B. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=X-ray+Micro+Computed+Tomography+investigation+of+accelerated+thermal+degradation+of+epoxy+resin/glass+microsphere+syntactic+foam.">X-ray Micro Computed Tomography investigation of accelerated thermal degradation of epoxy resin/glass microsphere syntactic foam.</a> Composites Part A. 40 (8), 1217-1222 (2009).</li><li>Wang, S., Luo, R., Ni, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+and+characterization+of+resin-derived+carbon+foams+reinforced+by+hollow+ceramic+microspheres.">Preparation and characterization of resin-derived carbon foams reinforced by hollow ceramic microspheres.</a> Mater. Sci. Eng., A. 527 (15), 3392-3395 (2010).</li><li>Carp, O., Huisman, C. L., Reller, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Photoinduced+reactivity+of+titanium+dioxide.">Photoinduced reactivity of titanium dioxide.</a> Prog. Solid State Chem. 32 (1), 33-177 (2004).</li><li>Fujishima, A., Rao, T. N., Tryk, D. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Titanium+dioxide+photocatalysis.">Titanium dioxide photocatalysis.</a> J. Photochem. Photobiol. C. 1 (1), 1-21 (2000).</li><li>Fujishima, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrochemical+photolysis+of+water+at+a+semiconductor+electrode.">Electrochemical photolysis of water at a semiconductor electrode.</a> Nature. 238 (5358), 37-38 (1972).</li><li>Hoffmann, M. R., Martin, S. T., Choi, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Environmental+applications+of+semiconductor+photocatalysis.">Environmental applications of semiconductor photocatalysis.</a> Chem. Rev. 95 (1), 69-96 (1995).</li><li>Chen, X., Mao, S. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Titanium+dioxide+nanomaterials:+synthesis,+properties,+modifications,+and+applications.">Titanium dioxide nanomaterials: synthesis, properties, modifications, and applications.</a> Chem. Rev. 107 (7), 2891-2959 (2007).</li><li>Yuan, J., An, Z., Li, B., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Facile+aqueous+synthesis+and+thermal+insulating+properties+of+low-density+glass/TiO2+core/shell+composite+hollow+spheres.">Facile aqueous synthesis and thermal insulating properties of low-density glass/TiO2 core/shell composite hollow spheres.</a> Particuology. 10 (4), 475-479 (2012).</li><li>Yan, H., Yuanhao, W., Hongxing, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=TEOS/silane+coupling+agent+composed+double+layers+structure:+A+novel+super-hydrophilic+coating+with+controllable+water+contact+angle+value.">TEOS/silane coupling agent composed double layers structure: A novel super-hydrophilic coating with controllable water contact angle value.</a> Appl. Energy. , (2015).</li><li>Wang, Y., Yang, H., Lu, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Three-dimensional+double+deck+meshlike+dye-sensitized+solar+cells.">Three-dimensional double deck meshlike dye-sensitized solar cells.</a> J. Appl. Phys. 108 (6), 064510 (2010).</li><li>Wang, Y., Yang, H., Xu, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=DNA-like+dye-sensitized+solar+cells+based+on+TiO+2+nanowire-covered+nanotube+bilayer+film+electrodes.">DNA-like dye-sensitized solar cells based on TiO 2 nanowire-covered nanotube bilayer film electrodes.</a> Mater. Lett. 64 (2), 164-166 (2010).</li><li>Wang, Y., Lu, L., Yang, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Development+of+high+dispersed+TiO2+paste+for+transparent+screen-printable+self-cleaning+coatings+on+glass.">Development of high dispersed TiO2 paste for transparent screen-printable self-cleaning coatings on glass.</a> J. Nanopart. Res. 15 (1), 1-6 (2013).</li><li>Kwok, D. Y., Neumann, A. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Contact+angle+measurement+and+contact+angle+interpretation.">Contact angle measurement and contact angle interpretation.</a> Adv. Colloid Interface Sci. 81 (3), 167-249 (1999).</li><li>Pierce, E., Carmona, F. J., Amirfazli, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Understanding+of+sliding+and+contact+angle+results+in+tilted+plate+experiments.">Understanding of sliding and contact angle results in tilted plate experiments.</a> Colloids Surf., A. 323 (1), 73-82 (2008).</li><li>Kim, W. S., Kim, T. H., Kim, E. S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microwave+dielectric+properties+and+far+infrared+reflectivity+spectra+of+the+(Zr0.+8Sn0.+2)+TiO4+ceramics+with+additives.">Microwave dielectric properties and far infrared reflectivity spectra of the (Zr0. 8Sn0. 2) TiO4 ceramics with additives.</a> Jpn. J. Appl. Phys. 37 (9S), 5367 (1998).</li><li>Hasselman, D. P. H., Johnson, L. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effective+thermal+conductivity+of+composites+with+interfacial+thermal+barrier+resistance.">Effective thermal conductivity of composites with interfacial thermal barrier resistance.</a> J. Compos. Mater. 21 (6), 508-515 (1987).</li><li>Cassie, A. B. D., Baxter, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Wettability+of+porous+surfaces.">Wettability of porous surfaces.</a> Trans. Faraday Soc. 40, 546-551 (1944).</li><li>Wenzel, R. N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Resistance+of+solid+surfaces+to+wetting+by+water.">Resistance of solid surfaces to wetting by water.</a> Ind. Eng. Chem. Res. 28 (8), 988-994 (1936).</li><li>Shirtcliffe, N. J., McHale, G., Newton, M. I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Intrinsically+superhydrophobic+organosilica+sol-gel+foams.">Intrinsically superhydrophobic organosilica sol-gel foams.</a> Langmuir. 19 (14), 5626-5631 (2003).</li><li>Rothstein, J. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Slip+on+superhydrophobic+surfaces.">Slip on superhydrophobic surfaces.</a> Annu. Rev. Fluid Mech. 42, 89-109 (2010).</li><li>Rodo&#353;ek, M., Kreta, A., Gaber&#353;&#269;ek, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ex+situ+IR+reflection-absorption+and+in+situ+AFM+electrochemical+characterisation+of+the+1,+2-bis+(trimethoxysilyl)+ethane-based+protective+coating+on+AA+2024+alloy.">Ex situ IR reflection-absorption and in situ AFM electrochemical characterisation of the 1, 2-bis (trimethoxysilyl) ethane-based protective coating on AA 2024 alloy.</a> Corros. Sci. 102, 186-199 (2016).</li><li>Jiang, J., Zhang, J., Zhu, P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High+pressure+studies+of+Ni+3[(C+2+H+5+N+5)+6+(H+2+O)+6](NO+3)+6·+1.5+H+2+O+by+Raman+scattering,+IR+absorption,+and+synchrotron+X-ray+diffraction.">High pressure studies of Ni 3[(C 2 H 5 N 5) 6 (H 2 O) 6](NO 3) 6· 1.5 H 2 O by Raman scattering, IR absorption, and synchrotron X-ray diffraction.</a> RSC Adv. 6 (69), 65031-65037 (2016).</li><li>Arukalam, I. O., Oguzie, E. E., Li, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fabrication+of+FDTS-modified+PDMS-ZnO+nanocomposite+hydrophobic+coating+with+anti-fouling+capability+for+corrosion+protection+of+Q235+steel.">Fabrication of FDTS-modified PDMS-ZnO nanocomposite hydrophobic coating with anti-fouling capability for corrosion protection of Q235 steel.</a> Journal of Colloid and Interface Science. 484, 220-228 (2016).</li><li>Hou, W., Xiao, Y., Han, G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Serrated,+flexible+and+ultrathin+polyaniline+nanoribbons:+An+efficient+counter+electrode+for+the+dye-sensitized+solar+cell.">Serrated, flexible and ultrathin polyaniline nanoribbons: An efficient counter electrode for the dye-sensitized solar cell.</a> J. Power Sources. 322, 155-162 (2016).</li></ol>

In this manuscript, the critical step in the protocol is the hydrothermal process. It influences the formation of TiO2, the final reflectivity, and the superhydrophobicity. The temperature control and reaction time are also quite significant. If the reaction conditions change, the final products can be flawed.
This method provides a simple way to synthesize superhydrophobic and highly IR-reflective HGM in one step. In previous research, the superhydrophobic and reflectivity properti...

Hollow glass microspheres (HGM) are inorganic materials ranging in size from 10 to 100 &#181;m. They demonstrate many useful features, such as excellent dispersion, high flow ability, low density, and superior thermal insulation properties1,2,3,4. Because of their hollow structure, HGM have an extremely low thermal conductivity10,11. For these reasons, they are applied in many areas, including aerospace engineering5, deep-sea exploration6,7, hydrogen storage8,9, etc. However, they still demonstrate some disadvantages, such as low strength. In addition, IR light is able to transmit through HGM and heat the subject behind. Therefore, surface modifications on HGM are essential to reduce the radiative thermal transfer. An effective method is to coat an IR-blocking material onto the HGM surface. As a semiconductor, TiO2 has been used in many areas, such as photo-catalysis12,13, solar cell development, sensor fabrication14, environmental applications15, and energy storage16. In addition, it also shows low emissivity in the visible light and infrared band17,18,19. Therefore, for our purposes, TiO2 was a prudent selection due to its relatively low price and high performance.
However, the coating is quite easy for pollutants to foul, which seriously affects the reflectivity of TiO2. The reflectivity must reduce gradually. Therefore, a self-cleaning coating is essential to prevent the coating from fouling and to prolong the working time of such a coating.
In this manuscript, a soft-chemistry method was used to develop superhydrophobic TiO2-coated HGM. Tetrabutyl titanate (TBT) and 1H,1H,2H,2H-perfluorooctyltriethoxysilane (PFOTES) were selected as the Ti source and superhydrophobic agent, respectively. They were hydrolyzed and deposited on the HGM surface. Then, after the hydrothermal process, the anatase TiO2 formed on the HGM surface, and the superhydrophobic properties remained. For comparison, PFOTES single-coated HGM (F-SCHGM) and TiO2 single-coated HGM (Ti-SCHGM) were synthesized as well. The synthesis scheme is shown in Figure 1.

<table border="0" cellpadding="0" cellspacing="0" width="471">
	<tbody>
		<tr height="19">
			<td height="19" style="height:19px;width:207px;">HGM</td>
			<td style="width:88px;">Technical Institute of Physics and Chemistry, Chinese Academy of Science</td>
			<td style="width:88px;">N/A</td>
			<td style="width:88px;">N/A</td>
		</tr>
		<tr height="19">
			<td height="19" style="height:19px;">TBT</td>
			<td>Sigma-Aldrich</td>
			<td>CAS#: 5593-70-4</td>
			<td>Analytical grade</td>
		</tr>
		<tr height="19">
			<td height="19" style="height:19px;">Ethyl Alcohol</td>
			<td>Sigma-Aldrich</td>
			<td>CAS#: 64-17-5</td>
			<td>Analytical grade</td>
		</tr>
		<tr height="19">
			<td height="19" style="height:19px;">PFOTES</td>
			<td>Sigma-Aldrich</td>
			<td>CAS#: 51851-37-7</td>
			<td align="right">98%</td>
		</tr>
	</tbody>
</table>

tio2-coated hollow glass microspheres with superhydrophobic and high ir-reflective properties synthesized by a soft-chemistry method

This manuscript proposes a soft-chemistry method to develop superhydrophobic and highly IR-reflective hollow glass microspheres (HGM). The anatase TiO2 and a superhydrophobic agent were coated on the HGM surface in one step. TBT and PFOTES were selected as the Ti source and the superhydrophobic agent, respectively. They were both coated on the HGM, and after the hydrothermal process, the TBT turned to anatase TiO2. In this way, a PFOTES/TiO2-coated HGM (MCHGM) was prepared. For comparison, PFOTES single-coated HGM (F-SCHGM) and TiO2 single-coated HGM (Ti-SCHGM) were synthesized as well. The PFOTES and TiO2 coatings on the HGM surface were demonstrated through X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive detector (EDS) characterizations. The MCHGM showed a higher contact angle (153&#176;) but a lower sliding angle (16&#176;) than F-SCHGM, with a contact angle of 141.2&#176; and a sliding angle of 67&#176;. In addition, both Ti-SCHGM and MCHGM displayed similar IR reflectivity values, which were about 5.8% higher than the original HGM and F-SCHGM. Also, the PFOTES coating barely changed the thermal conductivity. Therefore, F-SCHGM, with a thermal conductivity of 0.0479 W/(m&#183;K), was quite like the original HGM, which was 0.0475 W/(m&#183;K). MCHGM and Ti-SCHGM were also similar. Their thermal conductivity values were 0.0543 W/(m&#183;K) and 0.0543 W/(m&#183;K), respectively. The TiO2 coating slightly increased the thermal conductivity, but with the increase in reflectivity, the overall heat-insulation property was enhanced. Finally, since the IR-reflecting property is provided by the HGM coating, if the coating is fouled, the reflectivity decreases. Therefore, with the superhydrophobic coating, the surface is protected from fouling, and its lifetime is also prolonged.

The tests in step 4.4 reveal many features and properties of the samples. The XRD (Figure 2) reflects the formation of anatase TiO2. The SEM (Figure 3) and EDS (Figure 4) display the TiO2 and PFOTES that are coated on the HGM surface. The contact angle (Figure 5) and sliding angle (Figure 6) tests represent the superhydrophobicity. The Vis-NIR transmittance test (Figure 8</st...

Watch this Scientific Journal Video about TiO2-coated Hollow Glass Microspheres with Superhydrophobic and High IR-reflective Properties Synthesized by a Soft-chemistry Method at JoVE.com

TiO2-coated Hollow Glass Microspheres with Superhydrophobic and High IR-reflective Properties Synthesized by a Soft-chemistry Method

This manuscript proposes a soft-chemistry method to synthesize superhydrophobic, TiO2-coated hollow glass microspheres (HGM) with high IR-reflective properties.

TiO2-coated Hollow Glass Microspheres with Superhydrophobic and High IR-reflective Properties Synthesized by a Soft-chemistry Method

This manuscript proposes a soft-chemistry method to develop superhydrophobic and highly IR-reflective hollow glass microspheres (HGM). The anatase TiO2 ...

The overall goal of this experiment is to synthesize superhydrophobic, highly IR-reflective hollow glass microspheres in a single step. This technique can help with the development of simple masses to synthesize HGM with multiple functions, such as the self-cleaning and IR-reflective properties. The advantage of this mass is that it is a performer in the single-stat, making the mass simple and energy-saving compared with the existing mass.The implications of this technique extended toward a better understanding of sliding angles as HGM samples with different coatings can have similar connected angles but different sliding angles. To prepare the hollow glass microspheres, first place over five grams of original HGM in a 500-milliliter beaker. Add 200 milliliters of absolute ethanol to the mixture of broken and unbroken HGM.Allow the mixture to sit for 30 minutes to ensure that all unbroken HGM have floated to the top, leaving only broken HGM at the bottom of the beaker. Use a clean scoop to collect the unbroken HGM from the surface of the ethanol. Dry the unbroken HGM at 80 degrees Celsius for four hours.Repeat this process as needed to obtain five grams of unbroken HGM. To begin the synthesis, combine five grams of unbroken HGM, 47.5 milliliters of absolute ethanol, and 2.5 milliliters of deionized water. Add it into a three-necked flask.And then stir the mixture at 400 RPM for 20 minutes. Place 30 milliliters of absolute ethanol, 15 grams of tetrabutyl titanate, and one gram of PFOTES in a beaker and stir until dissolved. Pour the mixture into a pressure-equalized dropping funnel.Connect the dropping funnel to the three-necked flask and reduce the stirring rate 350 RPM. Add the TBT-PFOTES mixture to the HGM suspension at a rate of one drop every seven seconds. The dropping speed must be carefully set to the correct rate and stay in that rate until the mixture have been completely added.Once addition of the TBT-PFOTES mixture is complete, continue stirring at 350 RPM until three hours have elapsed since the start of addition. Then, pour the HGM mixture into a hydrothermal reactor with a well-fitting cover. Insert the reactor into an appropriately-sized steel sleeve and seal the reactor.Heat the HGM mixture at 180 degrees Celsius for six hours. Once the reaction is complete, allow the reactor to cool to room temperature. Open the hydrothermal reactor and use a large, clean scoop to collect the suspended HGM samples.Dry the samples at 80 degrees Celsius for four hours to obtain MCHGM. To synthesize PFOTES or titanium oxide single-coated HGM, follow this procedure without addition of TBT or PFOTES respectively. Perform X-ray defraction and measure the reflectivity and thermal conductivity of the coated and uncoated HGM samples.Acquire scanning electron microscopy images and perform energy dispersive X-ray spectroscopy. Use a contact angle goniometer to measure the contact angle between the HGM surface and a 10-microliter drop of water. To measure the sliding angle, first apply double-sided tape to a glass slide.Evenly distribute the HGM powder sample over the double-sided tape. Place 0.05 milliliter drop of water on the powder surface. Place the coated slide on the goniometer motor platform.While monitoring the water drop, tilt the glass slide at a rate of one degree per second. When the water drop begins to move, stop tilting the slide and record the sliding angle. The successful coating of HGM samples was confirmed by EDS.Fluorine was detected in both F-SCHGM and MCHGM, and titanium was detected in both titanium-SCHGM and MCHGM. The single PFOTES coating was not observable by SEM. But rough coatings were observed for titanium-SCHGM and MCHGM.The coated HGM samples were compared to the starting material and to standard anatase titanium oxide by X-ray defraction. The MCHGM and titanium-SCHGM samples both showed peaks matching anatase titanium oxide indicating that the titanium coating was in the anatase form. Both titanium-SCHGM and MCHGM showed about 5%higher reflectivity values than uncoated or F-SCHGM.A small increase in thermal conductivity was also observed for titanium-SCHGM and MCHGM. The measured contact angle of uncoated HGM was 59 degrees. Titanium SCHGM did not show a large increase from this contact angle, but both F-SCHGM and MCHGM did.Further, MCHGM had a much lower sliding angle than F-SCHGM, indicating greater hydrophobicity compared to F-SCHGM. Once mastered, this technique can be done in nine hours if it is performed properly. While attempting this procedure, it is important to remember to precisely set the TBT-PFOTES addition rate to one drop every seven seconds.After its development, this technique paved the way for the researchers in the hidden civilization field to explore highly IR-reflective HGM with superhydrophobic self-cleaning properties to protect the surface from falling.

tio2-coated-hollow-glass-microspheres-with-superhydrophobic-high-ir

Research

JoVE Journal

Chemistry

9.9K 조회수.  City University of Hong Kong. The overall goal of this experiment is to synthesize superhydrophobic, highly IR-reflective hollow glass microspheres in a single step. This technique can help with the development of simple masses to synthesize HGM with multiple functions, such as the self-cleaning and IR-reflective properties. The advantage of this mass is that it is a performer in the single-stat, making the mass simple and energy-saving compared with the existing mass.The implications of this technique extended tow...