The authors are grateful to Stephen Steiner at Aerogel Technologies for his inspiration and technical insights, and to Dr. Deryn Chu at the Army Research Laboratory-Sensors and Electron Devices Directorate, Dr. Christopher Haines at the Armament Research, Development and Engineering Center, U.S. Army RDECOM-ARDEC, and Dr. Stephen Bartolucci at the U.S. Army Benet Laboratories for their assistance. This work was supported by a Faculty Development Research Fund grant from the United States Military Academy, West Point.

CAUTION: Consult all relevant safety data sheets (SDS) before use. Use appropriate safety practices when performing chemical reactions, to include the use of a fume hood and personal protective equipment. Rapid hydrogen gas evolution can cause high pressure in reaction tubes causing caps to pop and solutions to spray out. Ensure that reaction tube caps remain open as specified in the protocol.
1. Metal Gel Preparation
<ol>
	<li>Preparation of metal ion solutions. 
	<ol>
		<l...

<ol>
	<li>Rolison, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Catalytic+Nanoarchitectures-the+Importance+of+Nothing+and+the+Unimportance+of+Periodicity.">Catalytic Nanoarchitectures-the Importance of Nothing and the Unimportance of Periodicity.</a> Science. 299, 1698-1701 (2003).</li><li>Wei, T., Chen, C., Chang, K., Lu, S., Hu, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cobalt+Oxide+Aerogels+of+Ideal+Supercapacitive+Properties+Prepared+with+an+Epoxide+Synthetic+Route.">Cobalt Oxide Aerogels of Ideal Supercapacitive Properties Prepared with an Epoxide Synthetic Route.</a> Chemistry of Materials. 21, 3228-3233 (2009).</li><li>Anderson, M., Morris, C., Stroud, R., Merzbacher, C., Rolison, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Colloidal+Gold+Aerogels:+Preparation,+Properties,+and+Characterization.">Colloidal Gold Aerogels: Preparation, Properties, and Characterization.</a> Langmuir. 15, 674-681 (1999).</li><li>Gaponik, N., Herrmann, A., Eychmuller, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Colloidal+Nanocrystal-Based+Gels+and+Aerogels:+Material+Aspects+and+Application+Perspectives.">Colloidal Nanocrystal-Based Gels and Aerogels: Material Aspects and Application Perspectives.</a> Journal of Physical Chemistry Letters. 3, 8-17 (2012).</li><li>Olsson, R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Making+flexible+magnetic+aerogels+and+stiff+magnetic+nanopaper+using+cellulose+nanofibrils+as+templates.">Making flexible magnetic aerogels and stiff magnetic nanopaper using cellulose nanofibrils as templates.</a> Nature Nanotechnology. 5, 584-588 (2010).</li><li>Anderson, M., Morris, C., Stroud, R., Merzbacher, C., Rolison, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Colloidal+Gold+Aerogels:+Preparation,+Properties,+and+Characterization.">Colloidal Gold Aerogels: Preparation, Properties, and Characterization.</a> Langmuir. 15, 674-681 (1999).</li><li>Gaponik, N., Herrmann, A., Eychmuller, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Colloidal+Nanocrystal-Based+Gels+and+Aerogels:+Material+Aspects+and+Application+Perspectives.">Colloidal Nanocrystal-Based Gels and Aerogels: Material Aspects and Application Perspectives.</a> Journal of Physical Chemistry Letters. 3, 8-17 (2012).</li><li>Hodge, A., Hayes, J., Cao, J., Biener, J., Hamza, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Characterization+and+Mechanical+Behavior+of+Nanoporous+Gold.">Characterization and Mechanical Behavior of Nanoporous Gold.</a> Advanced Engineering Materials. 8, 853-857 (2006).</li><li>Hodge, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Scaling+equation+for+yield+strength+of+nanoporous+open-cell+foams.">Scaling equation for yield strength of nanoporous open-cell foams.</a> Acta Materialia. 55, 1343-1349 (2007).</li><li>Ambrosi, A., Chua, C., Bonanni, A., Pumera, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrochemistry+of+Graphene+and+Related+Materials.">Electrochemistry of Graphene and Related Materials.</a> Chemical Reviews. 114, 7150-7188 (2014).</li><li>Maillard, F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Influence+of+particle+agglomeration+on+the+catalytic+activity+of+carbon-supported+Pt+nanoparticles+in+CO+monolayer+oxidation.">Influence of particle agglomeration on the catalytic activity of carbon-supported Pt nanoparticles in CO monolayer oxidation.</a> Physical Chemistry Chemical Physics. 7, 385-393 (2005).</li><li>Zhao, P., Li, N., Astruc, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=State+of+the+art+in+gold+nanoparticle+synthesis.">State of the art in gold nanoparticle synthesis.</a> Coordination Chemistry Reviews. 257, 638-665 (2013).</li><li>Wen, D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Controlling+the+Growth+of+Palladium+Aerogels+with+High-Performance+toward+Bioelectrocatalytic+Oxidation+of+Glucose.">Controlling the Growth of Palladium Aerogels with High-Performance toward Bioelectrocatalytic Oxidation of Glucose.</a> Journal of American Chemical Society. 136, 2727-2730 (2014).</li><li>Jana, N., Gearheart, L., Murphy, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Seed-Mediated+Growth+Approach+for+Shape-Controlled+Synthesis+of+Spheroidal+and+Rod-like+Gold+Nanoparticles+Using+a+Surfactant+Template.">Seed-Mediated Growth Approach for Shape-Controlled Synthesis of Spheroidal and Rod-like Gold Nanoparticles Using a Surfactant Template.</a> Advanced Materials. 13, 1389-1392 (2001).</li><li>Ding, Y., Chen, M., Erlebacher, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Metallic+Mesoporous+Nanocomposites+for+Electrocatalysis.">Metallic Mesoporous Nanocomposites for Electrocatalysis.</a> Journal of American Chemical Society. 126, 6876-6877 (2004).</li><li>Liu, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-Performance+Electrocatalysis+on+Palladium+Aerogels.">High-Performance Electrocatalysis on Palladium Aerogels.</a> Angewandte Chemie. International Edition. 51, 5743-5747 (2012).</li><li>Herrmann, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Multimetallic+Aerogels+by+Template-Free+Self-Assembly+of+Au,+Ag,+Pt,+and+Pd+Nanoparticles.">Multimetallic Aerogels by Template-Free Self-Assembly of Au, Ag, Pt, and Pd Nanoparticles.</a> Chemistry of Materials. 26, 1074-1083 (2014).</li><li>Ameen, K., Rajasekharan, T., Rajasekharan, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Grain+size+dependence+of+physico-optical+properties+of+nanometallic+silver+in+silica+aerogel+matrix.">Grain size dependence of physico-optical properties of nanometallic silver in silica aerogel matrix.</a> Journal of Non-Crystalline Solids. 352, 737-746 (2006).</li><li>Qin, G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+Facile+and+Template-Free+Method+to+Prepare+Mesoporous+Gold+Sponge+and+Its+Pore+Size+Control.">A Facile and Template-Free Method to Prepare Mesoporous Gold Sponge and Its Pore Size Control.</a> Journal of Physical Chemistry C. 112, 10352-10358 (2008).</li><li>Krishna, K., Sandeep, C., Philip, R., Eswaramoorthy, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Mixing+Does+the+Magic:+A+Rapid+Synthesis+of+High+Surface+Area+Noble+Metal+Nanosponges+Showing+Broadband+Nonlinear+Optical+Response.">Mixing Does the Magic: A Rapid Synthesis of High Surface Area Noble Metal Nanosponges Showing Broadband Nonlinear Optical Response.</a> ACS Nanotechnology. 5, 2681-2688 (2010).</li><li>Kistler, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Coherent+Expanded+Aerogels+and+Jellies.">Coherent Expanded Aerogels and Jellies.</a> Nature. 127, 741-741 (1931).</li><li>Du, A., Zhou, B., Zhang, Z., Shen, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+Special+Material+or+a+New+State+of+Matter:+A+Review+and+Reconsideration+of+the+Aerogel.">A Special Material or a New State of Matter: A Review and Reconsideration of the Aerogel.</a> Materials. 6, 941-968 (2013).</li><li>Tappan, B., Steiner, S., Luther, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanoporous+Metal+Foams.">Nanoporous Metal Foams.</a> Angewandte Chemie. International Edition. 49, 4544-4565 (2010).</li><li>Burpo, F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Direct+solution-based+reduction+synthesis+of+Au,+Pd,+and+Pt+aerogels.">Direct solution-based reduction synthesis of Au, Pd, and Pt aerogels.</a> Journal of Materials Research. 32, 4153-4165 (2017).</li><li>Ostwald, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Blocking+of+Ostwald+ripening+allowing+long-term+stabilization.">Blocking of Ostwald ripening allowing long-term stabilization.</a> PhysicalChemistry. 37, 385 (1901).</li><li>Wang, S., Tseng, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Aggregate+structure+and+crystallite+size+of+platinum+nanoparticles+synthesized+by+ethanol+reduction.">Aggregate structure and crystallite size of platinum nanoparticles synthesized by ethanol reduction.</a> Journal of Nanoparticle Research. 11, 947-953 (2009).</li><li>Schneider, C., Rasband, W., Eliceiri, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=NIH+Image+to+ImageJ:+25+years+of+image+analysis.">NIH Image to ImageJ: 25 years of image analysis.</a> Nature Methods. 9, 671-675 (2012).</li><li>Thommes, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Physisorption+of+gases,+with+special+reference+to+the+evaluation+of+surface+area+and+pore+size+distribution+(IUPAC+Technical+Report).">Physisorption of gases, with special reference to the evaluation of surface area and pore size distribution (IUPAC Technical Report).</a> Pure and Applied Chemistry. 87, 1051-1069 (2015).</li><li>Barrett, E., Joyner, L., Halenda, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+Determination+of+Pore+Volume+and+Area+Distributions+in+Porous+Substances.+I.+Computations+from+Nitrogen+Isotherms.">The Determination of Pore Volume and Area Distributions in Porous Substances. I. Computations from Nitrogen Isotherms.</a> Journal of the American Chemical Society. 73, 373-380 (1951).</li><li>Brunauer, B., Emmett, P., Teller, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Adsorption+of+Gases+in+Multimolecular+Layers.">Adsorption of Gases in Multimolecular Layers.</a> Journal of the American Chemical Society. 60, 309-319 (1938).</li><li>Herrmann, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Multimetallic+Aerogels+by+Template-Free+Self-Assembly+of+Au,+Ag,+Pt,+and+Pd+Nanoparticles.">Multimetallic Aerogels by Template-Free Self-Assembly of Au, Ag, Pt, and Pd Nanoparticles.</a> Chemistry of Materials. 26, 1074-1083 (2014).</li><li>Kornyshev, A., Irbakh, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Double-layer+capacitance+on+a+rough+metal+surface.">Double-layer capacitance on a rough metal surface.</a> Physical Review E. 53, 6192-6199 (1996).</li><li>Bisquert, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Influence+of+the+boundaries+in+the+impedance+of+porous+film+electrodes.">Influence of the boundaries in the impedance of porous film electrodes.</a> Physical Chemistry Chemical Physics. 2, 4185-4192 (2000).</li><li>Bisquert, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Theory+of+the+Impedance+of+Electron+Diffusion+and+Recombination+in+a+Thin+Layer.">Theory of the Impedance of Electron Diffusion and Recombination in a Thin Layer.</a> Journal of Physical Chemistry B. 106, 325-333 (2002).</li><li>Lu, K., Yuan, L., Xin, X., Xu, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Hybridization+of+graphene+oxide+with+commercial+graphene+for+constructing+3D+metal-free+aerogel+with+enhanced+photocatalysis.">Hybridization of graphene oxide with commercial graphene for constructing 3D metal-free aerogel with enhanced photocatalysis.</a> Applied Catalysis B. 226, 16-22 (2018).</li><li>Nystron, G., Roder, L., Fernandez-Ronco, M., Mezzenga, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Amyloid+Templated+Organic+Inorganic+Hybrid+Aerogels.">Amyloid Templated Organic Inorganic Hybrid Aerogels.</a> Advanced Functional Materials. , 1703609-1703620 (2017).</li></ol>

The authors have nothing to disclose.

The noble metal aerogel synthesis method presented here results in the rapid formation of porous, high surface area monoliths that are comparable to slower synthesis techniques. The 1:1 (v/v) metal ion solution to reducing agent solution ratio is critical in facilitating the proposed gel formation model. The rapid hydrogen gas evolution as a by-product of the electrochemical reduction of metal ions serves as a secondary reducing agent and facilitates the densification, and fusion of growing nanoparticles during gel forma...

A wide range of energy storage and conversion, catalysis, and sensor applications benefit from three-dimensional metallic nanostructures which provide control over chemical reactivity, and mass transport properties1,2,3,4,5. Such 3-dimensional metallic nanostructures further enhance conductivity, ductility, malleability, and strength8,9. Integration into devices necessitates that materials be free-standing or combined with support materials. Incorporation of nanomaterials onto support structures provides a means of minimizing active material, but may suffer from weak adsorption and eventual agglomeration during device operation10,11.
While there are a variety of synthesis methods to control individual nanoparticle size and shape, few approaches enable control over contiguous 3-dimensional nanomaterials12,13,14. Noble metal 3-dimensional nanostructures have been formed through dithiol linkage of monodisperse nanoparticles, sol-gel formation, nanoparticle coalescence, composite materials, nanosphere chains, and biotemplating15,16,17,18. Many of these approaches require synthesis times on the order of days to weeks to yield desired materials. Noble metal nanofoams synthesized from the direct reduction of precursor salt solutions have been prepared with a faster synthesis timescale and with short-range order of hundreds of micrometers in length, but require mechanical pressing for device integration19,20.
First reported by Kistler, aerogels provide a synthesis route to achieve porous structures with high specific surface areas that are orders of magnitude less dense than their bulk material counterparts21,22,23. Extending 3-dimensional structures to the macroscopic length scale of bulk materials offers an advantage over nanoparticle aggregates or nanofoams that require support materials or mechanical processing. While aerogels provide a synthesis route to control porosity and particle feature size, however, extended synthesis times, and in some cases the use of capping agents or linker molecules, increases overall processing steps and time.
Here a method to synthesize gold, palladium, and platinum aerogels via a rapid, direct solution-based reduction is presented24. Combining various precursor noble metal ions with reducing agents in a 1:1 (v/v) ratio results in the formation of metal gels within seconds to minutes compared to much longer synthesis times for other techniques such as sol-gel. The use of a microcentrifuge tube or small volume conical tube takes advantage of the vigorous hydrogen gas evolution as a by-product of the reduction step facilitating a proposed nucleation, growth, densification, fusion, equilibration model for gel formation. A close correlation in aerogel nanostructure feature sizes is determined with scanning electron microscopy image analysis, X-ray diffractometry, nitrogen gas adsorption, electrochemical impedance spectroscopy, and cyclic voltammetry. The solvent accessible specific surface area is determined with both electrochemical impedance spectroscopy and cyclic voltammetry. This synthesis method for noble metal aerogels demonstrates that high specific surface area monoliths may be achieved with a rapid and direct reduction approach.

<table border="0" cellpadding="0" cellspacing="0" width="691">
	<tbody>
		<tr height="25">
			<td height="25" style="height:25px;width:215px;">HAuCl4&#376;&#8226;3H2O&#160;</td>
			<td style="width:128px;">Sigma-Aldrich</td>
			<td style="width:119px;">16961-25-4</td>
			<td style="width:229px;"></td>
		</tr>
		<tr height="25">
			<td height="25" style="height:25px;width:215px;">Na2PdCl4</td>
			<td style="width:128px;">Sigma-Aldrich</td>
			<td style="width:119px;">13820-40-1</td>
			<td></td>
		</tr>
		<tr height="25">
			<td height="25" style="height:25px;width:215px;">K2PtCl6</td>
			<td style="width:128px;">Sigma-Aldrich</td>
			<td style="width:119px;">16921-30-5</td>
			<td></td>
		</tr>
		<tr height="25">
			<td height="25" style="height:25px;">Pd(NH3)4Cl2</td>
			<td style="width:128px;">Sigma-Aldrich</td>
			<td style="width:119px;">13933-31-8</td>
			<td></td>
		</tr>
		<tr height="25">
			<td height="25" style="height:25px;">K2PtCl4</td>
			<td style="width:128px;">Sigma-Aldrich</td>
			<td style="width:119px;">10025-99-7</td>
			<td></td>
		</tr>
		<tr height="25">
			<td height="25" style="height:25px;">Pt(NH3)4Cl2&#376;&#8226;H2O</td>
			<td style="width:128px;">Sigma-Aldrich</td>
			<td style="width:119px;">13933-31-8</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:215px;">dimethylamine borane (DMAB)</td>
			<td style="width:128px;">Sigma-Aldrich</td>
			<td style="width:119px;">74-94-2</td>
			<td></td>
		</tr>
		<tr height="25">
			<td height="25" style="height:25px;width:215px;">NaBH4</td>
			<td style="width:128px;">Sigma-Aldrich</td>
			<td style="width:119px;">16940-66-2</td>
			<td></td>
		</tr>
		<tr height="25">
			<td height="25" style="height:25px;width:215px;">NaH2PO2&#376;&#8226;H2O</td>
			<td style="width:128px;">Sigma-Aldrich</td>
			<td style="width:119px;">10039-56-2</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:215px;">Ethanol</td>
			<td style="width:128px;">Sigma-Aldrich</td>
			<td>792780</td>
			<td></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:215px;">Snap Cap Microcentrifuge Tubes, 2.0 mL</td>
			<td style="width:128px;">Cole Parmer</td>
			<td>UX-06333-70</td>
			<td></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:215px;">Snap Cap Microcentrifuge Tubes, 1.7 mL</td>
			<td style="width:128px;">Cole Parmer</td>
			<td>UX-06333-60</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:215px;">Conical Centrifuge Tubes 15mL</td>
			<td style="width:128px;">Stellar Scientific</td>
			<td>T15-101&#160;</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:215px;">Ag/AgCl Reference Electrode</td>
			<td style="width:128px;">BASi</td>
			<td style="width:119px;">MF-2052</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:215px;">Pt wire electrode</td>
			<td style="width:128px;">BASi</td>
			<td style="width:119px;">MF-4130</td>
			<td></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:215px;">Miccrostop Lacquer</td>
			<td style="width:128px;">Tober Chemical Division</td>
			<td style="width:119px;">NA</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:215px;">Potentiostat</td>
			<td style="width:128px;">Biologic-USA</td>
			<td style="width:119px;">VMP-3</td>
			<td>Electrochemical analysis-EIS, CV</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:215px;">Freeze Dryer</td>
			<td style="width:128px;">Labconco</td>
			<td style="width:119px;">Freezone 2.5 Liter</td>
			<td>Aerogel freeze drying</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:215px;">XRD</td>
			<td style="width:128px;">PanAlytical</td>
			<td style="width:119px;">Empyrean</td>
			<td>X-ray diffractometry</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:215px;">Surface and Pore Analyzer</td>
			<td style="width:128px;">Quantachrome</td>
			<td style="width:119px;">NOVA 4000e</td>
			<td>Nitrogen gas adsorption</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:215px;">ImageJ, Image analysis software</td>
			<td style="width:128px;">National Institute of Health</td>
			<td style="width:119px;">NA</td>
			<td>SEM image analysis</td>
		</tr>
	</tbody>
</table>

a rapid synthesis method for au, pd, and pt aerogels via direct solution-based reduction

Here, a method to synthesize gold, palladium, and platinum aerogels via a rapid, direct solution-based reduction is presented. The combination of various precursor noble metal ions with reducing agents in a 1:1 (v/v) ratio results in the formation of metal gels within seconds to minutes compared to much longer synthesis times for other techniques such as sol-gel. Conducting the reduction step in a microcentrifuge tube or small volume conical tube facilitates a proposed nucleation, growth, densification, fusion, equilibration model for gel formation, with final gel geometry smaller than the initial reaction volume. This method takes advantage of the vigorous hydrogen gas evolution as a by-product of the reduction step, and as a consequence of reagent concentrations. The solvent accessible specific surface area is determined with both electrochemical impedance spectroscopy and cyclic voltammetry. After rinsing and freeze drying, the resulting aerogel structure is examined with scanning electron microscopy, X-ray diffractometry, and nitrogen gas adsorption. The synthesis method and characterization techniques result in a close correspondence of aerogel ligament sizes. This synthesis method for noble metal aerogels demonstrates that high specific surface area monoliths may be achieved with a rapid and direct reduction approach.

The addition of metal ion and reducing agent solutions together results in solutions immediately turning a dark black color with vigorous gas evolution. Observation of the reaction progress suggests the proposed gel formation mechanism shown in Figure 1. Gel formation proceeds through five steps of 1) nanoparticle nucleation, 2) growth, 3) densification, 4) fusion, and 5) equilibration. The first four steps are observed to occur during the first few minutes o...

Watch this Scientific Journal Video about A Rapid Synthesis Method for Au, Pd, and Pt Aerogels Via Direct Solution-Based Reduction at JoVE.com

A Rapid Synthesis Method for Au, Pd, and Pt Aerogels Via Direct Solution-Based Reduction

A rapid, direct solution-based reduction synthesis method to obtain Au, Pd, and Pt aerogels is presented.

Here, a method to synthesize gold, palladium, and platinum aerogels via a rapid, direct solution-based reduction is presented. The combination of various ...

This method can help answer key questions in the aerogel field about the possibility of directly synthesizing metal aerogels from aqueous solutions rather than from preformed nanoparticles. Other methods, such as sol gels, require much longer times for nanoparticle coalescence. The implications of this technique extend toward catalysis and sensing applications due to the high surface area of the noble metal aerogels and the lack of support materials.Though this method can provide insight into direct aerogel synthesis, it can also be applied to other synthesis techniques, such as biotemplating, to achieve better shape control over aerogel monoliths. To begin the procedure, prepare two milliliters each of 0.1 molar solutions of gold(III)chloride trihydrate and sodium tetrachloropalladate in deionized water. Vigorously shake and vortex the solutions to dissolve the salts.Let the palladium solution sit for a few hours to ensure complete dissolution. Prepare two milliliters of 0.1 molar potassium hexachloroplatinate in a one to one by volume mixture of deionized water and ethanol. Vigorously shake and vortex the mixture until the salts have dissolved.Prepare 10 milliliters each of 0.1 molar solutions of dimethylamine borane and sodium borohydride in deionized water. Vortex the solutions for one to two minutes to ensure complete dissolution. Then, transfer 0.5 milliliters of the gold solution to a 1.7-milliliter or two-milliliter microcentrifuge tube.Forcefully pipette 0.5 milliliters of DMAB into the tube to rapidly mix the salt and reducing agent. Place the microcentrifuge tube in a rack, leaving the cap open to allow hydrogen gas to escape. In the same way, combine 0.5 milliliters of the platinum solution with 0.5 milliliters of DMAB and 0.5 milliliters of the palladium solution with 0.5 milliliters of sodium borohydride.Approximately five minutes after starting the reaction, cap the microcentrifuge tubes, and gently invert them three to five times to aid coalescence of metal particles not part of the metal gel. Immediately uncap the tubes, and return them to the rack after inversion. Leave the nascent metal gels in the reducing agent solutions for three to six hours to allow complete reduction of metal ions and surface free energy minimization to occur.Then, carefully remove excess reducing agent from each tube, ensuring that enough solution remains so that the meniscus does not contact the gel. Slowly pipette deionized water into the microcentrifuge tubes until they are filled completely. Then, fill three 50-milliliter conical tubes with deionized water.Submerge each microcentrifuge tube in a tube of deionized water, and allow each gel to slide from its microcentrifuge tube into the larger tube. Gently move the gel with a spatula if needed. Cap the tubes, and leave the gels in deionized water for 24 hours.Replace the water after 12 hours by solvent exchange. Do not allow the meniscus to contact the gels while replacing the water. To begin the EIS procedure for wet metal gels, remove as much water as possible without the meniscus contacting the rinsed gels.Add 50 milliliters of 0.5 molar potassium chloride to each tube, and allow the gels to soak for 24 hours. Then, use a fine bristle brush to coat a one-millimeter potassium wire electrode with non-reactive lacquer, leaving four to five millimeters exposed at the tip. Allow the lacquer to dry for 20 minutes.Apply at least one more coat of lacquer in the same way. Next, cut a 50-milliliter conical tube in half to serve as the electrochemical vial. Insert a saturated silver-silver chloride reference electrode and a 0.5-millimeter potassium wire counter electrode through a perforated cap or gasket for the modified tube.Connect the three electrodes to a potentiostat. Transfer one of the gels and its electrolyte to the modified tube by gently pouring the electrolyte and equilibrated gel into the tube without letting the gel contact the liquid-air interface. Ensure that the gel is settled at the bottom of the tube, and add electrolyte if necessary.Then, place the cap on the tube, and adjust the reference and counter electrodes as needed. For the gold gel, gently insert the bare tip of the lacquer-coated working electrode into the gel. For the palladium and platinum gels, place the lacquer-coated working electrode in the conical vial along the inner surface, and rest the metal gel on top of the bare platinum wire tip.Perform potentiostatic EIS scans with frequencies between 100 megahertz and one millihertz using a 10 millivolt amplitude sine wave. In the event of current overflow, use a galvanostatic EIS with the same frequency range and a 100 to 200 milliamp sine wave amplitude. Following electrochemical characterization, rinse the gels with deionized water for 24 hours as described at the end of the gel synthesis.Then, remove as much of the rinse as possible without letting the meniscus contact the gels. Freeze the gels at negative 80 degrees Celsius for 30 minutes. Lastly, freeze dry the gels in a freeze dryer with a pressure set point of four pascals or lower to obtain the metal aerogels.The gold, palladium, and platinum aerogels all showed characteristic hydrophobicity and had properties comparable to gels formed by slower synthesis techniques. Scanning electron microscopy showed that gold aerogels had large nanopores and smooth ligaments. Palladium and platinum aerogels had a beads-on-a-string structure with fused nanoparticles and narrower ligaments.The platinum aerogel had a greater range of macropore structure diameters than the palladium aerogel, which was attributed to platinum nanoparticle stability requiring the use of ethanol to drive coalescence and the consequent ease of large hydrogen gas bubble evolution during gel formation. X-ray diffraction showed characteristic peaks for the respective metals with no detectable oxides. Nitrogen gas physisorption isotherms were Type IV, which is characteristic of mesoporous materials.The pore size distribution and cumulative pore volume modeled from the isotherms showed pore sizes predominantly in the two to 50 nanometer range, confirming that the aerogels were mesoporous. The electrochemical impedance spectra were fit with a transmission line model based on a modified Randle's equivalent circuit model. The specific capacitances and specific surface areas were calculated from the EIS data.These values were consistent with the specific capacitances and surface areas determined from cyclic voltammetry experiments. We first developed the idea for this method based on combining 100 millimolar noble metal solutions and reducing agents for other projects prior to discarding them and observing the rapid formation of metal gels. Once mastered, this technique can result in noble metal gels within minutes prior to rinsing and drying steps.While attempting this procedure, remember to avoid contact of the metal gels with the liquid-air interface in order to prevent gel compaction. Following this procedure, other methods like biotemplating may be performed to address the challenges of aerogel shape control.

a-rapid-synthesis-method-for-au-pd-pt-aerogels-via-direct-solution

Research

JoVE Journal

Chemistry

8.6K 조회수.  United States Military Academy, West Point. This method can help answer key questions in the aerogel field about the possibility of directly synthesizing metal aerogels from aqueous solutions rather than from preformed nanoparticles. Other methods, such as sol gels, require much longer times for nanoparticle coalescence. The implications of this technique extend toward catalysis and sensing applications due to the high surface area of the noble metal aerogels and the lack of support materials.Though this method can provide insig...