Name: production of single tracks of ti-6al-4v by directed energy deposition to determine the layer thickness for multilayer deposition
Uploaded: 2018-03-13T13:00:00
Description: Watch this Scientific Journal Video about Production of Single Tracks of Ti-6Al-4V by Directed Energy Deposition to Determine the Layer Thickness for Multilayer Deposition at JoVE.com

The authors would like to acknowledge the European research project belonging to the Horizon 2020 research and innovation program Borealis - the 3A energy class Flexible Machine for the new Additive and Subtractive Manufacturing on next generation of complex 3D metal parts

1. Powder Characterization
<ol>
	<li>Put 3 g of starting Ti-6Al-4V powders on a double-sided sticky carbon tape, which is located on an aluminum pin stub, and insert inside the specimen chamber of a Field-Emission Scanning Electron Microscope (FESEM) to analyze the morphology of the powder16.</li>
	<li>Measure the apparent density of the powder by filling a 30 cm3 container, and measure the weight of powder according to the ASTM-B212 standard.</li>
	<li>Perform chemical analysis of st...

<ol>
	<li>Banerjee, D., Williams, J. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Perspectives+on+Titanium+Science+and+Technology.">Perspectives on Titanium Science and Technology.</a> Acta Mater. 61 (3), 844-879 (2013).</li><li>Peters, M., Leyens, C., Peters, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Titanium and Titanium Alloys. , (2003).</li><li>Lin, J., Lv, Y., Liu, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microstructural+evolution+and+mechanical+property+of+Ti-6Al-4V+wall+deposited+by+continuous+plasma+arc+additive+manufacturing+without+post+heat+treatment.">Microstructural evolution and mechanical property of Ti-6Al-4V wall deposited by continuous plasma arc additive manufacturing without post heat treatment.</a> J Mech Behav Biomed Mater. 69 (December 2016), 19-29 (2017).</li><li>Saboori, A., Gallo, D., Biamino, S., Fino, P., Lombardi, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+Overview+of+Additive+Manufacturing+of+Titanium+Components+by+Directed+Energy+Deposition:+Microstructure+and+Mechanical+Properties.">An Overview of Additive Manufacturing of Titanium Components by Directed Energy Deposition: Microstructure and Mechanical Properties.</a> Appl Sci. 7 (9), (2017).</li><li>Wu, X., Liang, J., Mei, J., Mitchell, C., Goodwin, P. S., Voice, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microstructures+of+laser-deposited+Ti-6Al-4V.">Microstructures of laser-deposited Ti-6Al-4V.</a> Mater Des. 25 (2), 137-144 (2004).</li><li>Trevisan, F., Calignano, F., Aversa, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Additive+manufacturing+of+titanium+alloys+in+the+biomedical+field:+processes,+properties+and+applications.">Additive manufacturing of titanium alloys in the biomedical field: processes, properties and applications.</a> J Appl Biomater Funct Mater. , (2017).</li><li>Mahamood, R. M., Akinlabi, E. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Scanning+speed+and+powder+flow+rate+influence+on+the+properties+of+laser+metal+deposition+of+titanium+alloy.">Scanning speed and powder flow rate influence on the properties of laser metal deposition of titanium alloy.</a> Int J Adv Manuf Technol. 91 (5-8), (2017).</li><li>Shim, D., Baek, G., Seo, J., Shin, G., Kim, K., Lee, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+layer+thickness+setting+on+deposition+characteristics+in+direct+energy+deposition+(+DED+)+process.">Effect of layer thickness setting on deposition characteristics in direct energy deposition ( DED ) process.</a> Opt Laser Technol. 86, 69-78 (2016).</li><li>Gharbi, M., Peyre, P., Gorny, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Influence+of+various+process+conditions+on+surface+finishes+induced+by+the+direct+metal+deposition+laser+technique+on+a+Ti-6Al-4V+alloy.">Influence of various process conditions on surface finishes induced by the direct metal deposition laser technique on a Ti-6Al-4V alloy.</a> J Mater Process Technol. 213 (5), 791-800 (2013).</li><li>Davim, J. P., Oliveira, C., Cardoso, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Predicting+the+geometric+form+of+clad+in+laser+cladding+by+powder+using+multiple+regression+analysis+(MRA).">Predicting the geometric form of clad in laser cladding by powder using multiple regression analysis (MRA).</a> Mater Des. 29 (2), 554-557 (2008).</li><li>Kobryn, P. A., Moore, E. H., Semiatin, S. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+Effect+Of+Laser+Power+And+Traverse+Speed+On+Microstructure,+Porosity,+And+Build+Height+In+Laser-Deposited+Ti-6Al-4V.">The Effect Of Laser Power And Traverse Speed On Microstructure, Porosity, And Build Height In Laser-Deposited Ti-6Al-4V.</a> Scripta Materialia. 43, 299-305 (2000).</li><li>Bi, G., Gasser, A., Wissenbach, K., Drenker, A., Poprawe, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Characterization+of+the+process+control+for+the+direct+laser+metallic+powder+deposition.">Characterization of the process control for the direct laser metallic powder deposition.</a> Surf Coatings Technol. 201 (6), 2676-2683 (2006).</li><li>Choi, J., Chang, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Characteristics+of+laser+aided+direct+metal/material+deposition+process+for+tool+steel.">Characteristics of laser aided direct metal/material deposition process for tool steel.</a> Int J Mach Tools Manuf. 45 (4-5), 597-607 (2005).</li><li>Ruan, J., Tang, L., Liou, F. W., Landers, R. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Direct+Three-Dimensional+Layer+Metal+Deposition.">Direct Three-Dimensional Layer Metal Deposition.</a> J Manuf Sci Eng. 132 (6), 64502-64506 (2010).</li><li>Chen, X., Tao, Z. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Maximum+thickness+of+the+laser+cladding.">Maximum thickness of the laser cladding.</a> Key Eng Mater. 46, 381-386 (1989).</li><li>Slotwinski, J. A., Garboczi, E. J., Stutzman, P. E., Ferraris, C. F., Watson, S. S., Peltz, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Characterization+of+Metal+Powders+Used+for+Additive+Manufacturing.">Characterization of Metal Powders Used for Additive Manufacturing.</a> J Res Natl Inst Stand Technol. 119, 460-493 (2014).</li><li>Manfredi, D., Calignano, F., Krishnan, M., Canali, R., Ambrosio, E. P., Atzeni, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=From+Powders+to+Dense+Metal+Parts:+Characterization+of+a+Commercial+AlSiMg+Alloy+Processed+through+Direct+Metal+Laser+Sintering.">From Powders to Dense Metal Parts: Characterization of a Commercial AlSiMg Alloy Processed through Direct Metal Laser Sintering.</a> Materials. 6 (3), 856-869 (2013).</li></ol>

In this work, the focus was on the slicing thickness setting in the DED process of Ti-6Al-4V, according to the geometry of melt pool characteristics. For this purpose, a two-step protocol was defined and utilized. The first part of the protocol was an optimization of process parameters for single scan deposition and, during this step, the optimum parameters were achieved and the melt pool geometries were measured. In the second part of the protocol, the specific energy density of specimens at the optimum parameters was c...

Ti-6Al-4V is the most commonly used Ti alloy in the aerospace, aircraft, automotive, and biomedical industries because of its high strength-to-weight ratio, excellent fracture toughness, low specific gravity, excellent corrosion resistance, and heat treatability. However, its further developments in other applications are challenging, owing to its low thermal conductivity and high reactivity features, which result in its poor machinability. Moreover, due to the heat hardening phenomena during the cutting, a specific heat treatment must be undertaken1,2,3,4.
Nonetheless, additive manufacturing (AM) technologies showed great potential to be used as new manufacturing techniques that can reduce the price and energy consumption, and address some of the current challenges in the fabrication of Ti-6Al-4V alloy.
Additive manufacturing techniques are known as innovative and can fabricate a near net shape component in a layer-by-layer fashion. A layer-by-layer additive manufacturing approach, which slices a Computer Aided Design (CAD) model into thin layers and then builds the component layer by layer, is fundamental for all AM methods. In general, additive manufacturing of metallic materials can be divided into four different processes: powder bed, powder feed (blown powder), wire feed, and other routes3,5,6.
Directed Energy Deposition (DED) is a class of additive manufacturing and is a blown powder process that fabricates three-dimensional (3D) near net shape solid parts from a CAD file similar to other AM methods. In contrast with other techniques, DED can not only be used as a manufacturing method, but also can be employed as a repairing technique for high value parts. In the DED process, metallic powder or wire material is fed by a carrier gas or motors into the melt pool, which is generated by the laser beam on either the substrate or previously deposited layer. The DED process is a promising advanced manufacturing process that is capable of decreasing the buy-to-fly ratio, and also is capable of repairing high value parts that previously were prohibitively expensive to replace or irreparable7.
In order to achieve the desired geometric dimensions and material properties, it is vital to establish appropriate parameters8. Several studies have been undertaken to elucidate the relationship between the process parameters and the final properties of the deposited sample. Peyre et al.9 built some thin walls with different process parameters, and then characterized them by using 2D and 3D profilometry. They showed that layer thickness and melt pool volume affect the roughness parameters noticeably. Vim et al.10 proposed a model in order to analyze the relation between the process parameters and geometrical characteristics of a single cladding layer (clad height, clad width, and depth of penetration).
To date, several studies on DED of Ti alloys have been reported, most of which focused on the influence of the combination of parameters on properties of massive samples11,12,4. Rasheedat et al. studied the effect of scan speed and powder flow rate on the resulting properties of the laser metal deposited Ti-6Al-4V alloy. They found that by increasing the scan speed and powder flow rate the microstructure changed from Widmanst&#228;tten to a martensitic microstructure, which results in an increment of surface roughness and the microhardness of deposited specimens7. Nevertheless, less attention has been paid to designing the layer thickness setting. Choi et al. have investigated the correlation between the layer thickness and process parameters. They have found that the main sources of error between the present height and the actual height are the powder mass flow rate and layer thickness setting13. Their studies did not properly implement layer thickness setting because they involved lengthy and inaccurate processes in the layer thickness setting. Ruan et al. have investigated the effect of laser scanning speed on the deposited layer height at a constant laser power and powder feeding rate14. They have proposed some empirical models for layer thickness setting which were obtained under specific processing conditions, and thus the layer thickness setting may not be precise due to the utilization of specific process parameters15. In contrast to previous works, the layer thickness setting process proposed in this manuscript is a rapid method which can be performed without wasting time and materials.
The main focus of this work is to develop a rapid method for the determination of layer thickness based on the characteristics of the single tracks of the Ti-6Al-4V alloy at optimum DED process parameters. Thereafter, the optimal process parameters are employed to determine a layer thickness and fabricate high-density Ti-6Al-4V blocks without wasting time and materials.

<table>
	<tbody>
		<tr>
			<td>Ti-6Al-4V powder</td>
			<td>Xi&#8217;Tianrui new material</td>
			<td></td>
			<td>As starting material</td>
		</tr>
		<tr>
			<td>ISOMET precision cutter</td>
			<td>Bohler</td>
			<td></td>
			<td>To cut the samples</td>
		</tr>
		<tr>
			<td>Polishing machine</td>
			<td>Presi</td>
			<td></td>
			<td>To polish the samples</td>
		</tr>
		<tr>
			<td>EpoFix resin</td>
			<td>Presi</td>
			<td></td>
			<td>To mount the samples</td>
		</tr>
		<tr>
			<td>Diamond paste</td>
			<td>Presi</td>
			<td></td>
			<td>For polishing</td>
		</tr>
		<tr>
			<td>Optical Microscope</td>
			<td>Leica</td>
			<td></td>
			<td>Microstructural observation</td>
		</tr>
		<tr>
			<td>Field emission scanning electron microscope</td>
			<td>Merlin-Zeiss</td>
			<td></td>
			<td>Microstructural observation</td>
		</tr>
		<tr>
			<td>Stereo microscope</td>
			<td>Leica</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>LEC1- CS444 ANALYSER</td>
			<td>IncoTest</td>
			<td></td>
			<td>Chemical analysis</td>
		</tr>
		<tr>
			<td>LEC3 - ELTRA OHN2000 ANALYSER</td>
			<td>IncoTest</td>
			<td></td>
			<td>Chemical analysis</td>
		</tr>
		<tr>
			<td>LEC2 - LECO TC436AR ANALYSER</td>
			<td>IncoTest</td>
			<td></td>
			<td>Chemical analysis</td>
		</tr>
		<tr>
			<td>ICP</td>
			<td>IncoTest</td>
			<td></td>
			<td>Chemical analysis</td>
		</tr>
		<tr>
			<td>IRB 4600</td>
			<td>ABB</td>
			<td></td>
			<td>Antropomorphic robot</td>
		</tr>
		<tr>
			<td>GTV PF</td>
			<td>GTV</td>
			<td></td>
			<td>Powder feeding system</td>
		</tr>
		<tr>
			<td>YW 52</td>
			<td>Precitec</td>
			<td></td>
			<td>Laser head</td>
		</tr>
		<tr>
			<td>Nozzles</td>
			<td>IRIS</td>
			<td></td>
			<td>Nozzle for feeding powders</td>
		</tr>
		<tr>
			<td>YLS 3000</td>
			<td>IPG Photonics</td>
			<td></td>
			<td>Laser source</td>
		</tr>
	</tbody>
</table>

production of single tracks of ti-6al-4v by directed energy deposition to determine the layer thickness for multilayer deposition

Directed Energy Deposition (DED), which is an additive manufacturing technique, involves the creation of a molten pool with a laser beam where metal powder is injected as particles. In general, this technique is employed to either fabricate or repair different components. In this technique, the final characteristics are affected by many factors. Indeed, one of the main tasks in building components by DED is the optimization of process parameters (such as laser power, laser speed, focus, etc.) which is usually carried out through an extensive experimental investigation. However, this sort of experiment is extremely lengthy and costly. Thus, in order to accelerate the optimization process, an investigation was conducted to develop a method based on the melt pool characterizations. In fact, in these experiments, single tracks of Ti-6Al-4V were deposited by a DED process with multiple combinations of laser power and laser speed. Surface morphology and dimensions of single tracks were analyzed, and geometrical characteristics of melt pools were evaluated after polishing and etching the cross-sections. Helpful information regarding the selection of optimal process parameters can be achieved by examining the melt pool features. These experiments are being extended to characterize the larger blocks with multiple layers. Indeed, this manuscript describes how it would be possible to quickly determine the layer thickness for the massive deposition, and avoid over or under-deposition according to the calculated energy density of the optimum parameters. Apart from the over or under-deposition, time and materials saving are the other great advantages of this approach in which the deposition of multilayer components can be started without any parameter optimization in terms of layer thickness.

For the experimental studies, irregular Ti-6Al-4V powder with an average size of 50 - 150 &#181;m and apparent density of 1.85 g/cm3 was employed as depositing material (Figure 1). The chemical analysis of the powder confirmed that the oxygen and nitrogen contents of the powder did not change before and after the deposition process, while in both cases the oxygen content was higher than the standard oxygen content of Ti-6Al-4V powder for additive m...

Watch this Scientific Journal Video about Production of Single Tracks of Ti-6Al-4V by Directed Energy Deposition to Determine the Layer Thickness for Multilayer Deposition at JoVE.com

Production of Single Tracks of Ti-6Al-4V by Directed Energy Deposition to Determine the Layer Thickness for Multilayer Deposition

In this research, a rapid method based on melt pool characterization is developed to estimate the layer thickness of Ti-6Al-4V components produced by directed energy deposition.

Directed Energy Deposition (DED), which is an additive manufacturing technique, involves the creation of a molten pool with a laser beam where metal ...

Research

JoVE Journal

Engineering

Harvesting Solar Energy by Means of Charge-Separating Nanocrystals and Their Solids

Conjoining different semiconductor materials in a single nano-composite provides synthetic means for the development of novel optoelectronic materials ...

Fabrication of Nano-engineered Transparent Conducting Oxides by Pulsed Laser Deposition

Nanosecond Pulsed  Laser Deposition (PLD) in the presence of a background gas allows the deposition  of metal oxides with tunable morphology, structure, ...

Casting Protocols for the Production of Open Cell Aluminum Foams by the Replication Technique and the Effect on Porosity

Metal foams are interesting materials from both a fundamental understanding and practical applications point of view. Uses have been proposed, and in many ...

Making Record-efficiency SnS Solar Cells by Thermal Evaporation and Atomic Layer Deposition

Tin sulfide (SnS) is a candidate absorber material for Earth-abundant, non-toxic solar cells. SnS offers easy phase control and rapid growth by congruent ...

Formation of Thick Dense Yttrium Iron Garnet Films Using Aerosol Deposition

Aerosol deposition (AD) is a thick-film deposition process that can produce layers up to several hundred micrometers thick with densities greater than 95% ...

Synthesis and Characterization of High c-axis ZnO Thin Film by Plasma Enhanced Chemical Vapor Deposition System and its UV Photodetector Application

In this study, zinc oxide (ZnO) thin films with high c-axis (0002) preferential orientation have been successfully and effectively synthesized onto ...

Integration of Light Trapping Silver Nanostructures in Hydrogenated Microcrystalline Silicon Solar Cells by Transfer Printing

One of the potential applications of metal nanostructures is light trapping in solar cells, where unique optical properties of nanosized metals, commonly ...

Electrospray Deposition of Uniform Thickness Ge23Sb7S70 and As40S60 Chalcogenide Glass Films

Electrospray Deposition of Uniform Thickness Ge23Sb7S70 and As40S60 Chalcogenide Glass Films

Solution-based electrospray film deposition, which is compatible with continuous, roll-to-roll processing, is applied to chalcogenide glasses. Two ...

High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia (YSZ) Scaffolds by In Situ Carbon Templating Xerogels

High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia YSZ Scaffolds by In Situ Carbon Templating Xerogels

We demonstrate a method for the high temperature fabrication of porous, nanostructured yttria-stabilized-zirconia (YSZ, 8 mol% yttria - 92 mol% zirconia) ...

Fabrication of Ultra-thin Color Films with Highly Absorbing Media Using Oblique Angle Deposition

Ultra-thin film structures have been studied extensively for use as optical coatings, but performance and fabrication challenges remain.&#160; We present ...