1. Methods
1.1 Cell Flow Chamber
A flow chamber, shown in Figure 1, was constructed so that cells could be grown under a shear of 1.0 Pa (10 dyn/cm2) and then transferred directly to an Asylum MFP3D AFM (Santa Barbara, CA).
<ol>
	<li>The flow chamber was prepared for the experiment by first cleaning the glass slides in piranha solution (3:1 H2SO4:H2O2) for 15 min and then washing them with di...

<ol>
	<li>Clifford, C., Seah, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanoindentation+measurement+of+young's+modulus+for+compliant+layers+on+stiffer+substrates+including+the+effect+of+poisson's+ratios.">Nanoindentation measurement of young's modulus for compliant layers on stiffer substrates including the effect of poisson's ratios.</a> Nanotechnology. , (2009).</li><li>Gouverneur, M., Spaan, J. A. E., Pannekoek, H., Fontijn, R. D., Vink, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fluid+shear+stress+stimulates+incorporation+of+hyaluronan+into+endothelial+cell+glycocalyx.">Fluid shear stress stimulates incorporation of hyaluronan into endothelial cell glycocalyx.</a> Am. J. Physiol. Heart. Circ. Physiol. 290 (1), 458-452 (2006).</li><li>Hocde, S. A., Hyrien, O., Waugh, R. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cell+adhesion+molecule+distribution+relative+to+neutrophil+surface+topography+assessed+by+tirfm.">Cell adhesion molecule distribution relative to neutrophil surface topography assessed by tirfm.</a> Biophysical Journal. 97 (1), 379-387 (2009).</li><li>Lipowski, H. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+endothelial+glycocalyx+as+a+barrier+to+leukocyte+adhesion+and+its+mediation+by+extracellular+proteases.">The endothelial glycocalyx as a barrier to leukocyte adhesion and its mediation by extracellular proteases.</a> Annals of biomedical engineering. 40 (4), 840-848 (2012).</li><li>Lu, L., Oswald, S. J., Ngu, H., Yin, F. C. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Mechanical+properties+of+actin+stress+fibers+in+living+cells.">Mechanical properties of actin stress fibers in living cells.</a> Biophysical Journal. 95 (12), 6060-6071 (2008).</li><li>Pries, A. R., Secomb, T. W., Gaehtgens, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+endothelial+surface+layer.">The endothelial surface layer.</a> Pflugers Archiv. European Journal of Physiology. 440 (5), 653-666 (2000).</li><li>Spillmann, C. M., Lomakina, E., Waugh, R. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Neutrophil+adhesive+contact+dependence+on+impingement+force.">Neutrophil adhesive contact dependence on impingement force.</a> Biophysical Journal. 87 (6), 4237-4245 (2004).</li><li>vanden Berg, B. M., Vink, H., Spaan, J. A. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+endothelial+glycocalyx+protects+against+myocardial+edema.">The endothelial glycocalyx protects against myocardial edema.</a> Circulation Research. 92 (6), 592-594 (2003).</li><li>Williams, T. E., Nagarajan, S., Selvaraj, P., Zhu, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Quantifying+the+impact+of+membrane+microtopology+on+effective+two-dimensional+affinity.">Quantifying the impact of membrane microtopology on effective two-dimensional affinity.</a> J. Biol. Chem. 276 (16), 13283-138 (2001).</li><li>Vink, H., Duling, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Identification+of+Distinct+Luminal+Domains+for+Macromolecules,+Erythrocytes,+and+Leukocytes+Within+Mammalian+Capillaries.">Identification of Distinct Luminal Domains for Macromolecules, Erythrocytes, and Leukocytes Within Mammalian Capillaries.</a> Circulation Research. 79, 581-589 (1996).</li></ol>

We used values calculated from the two-layer model and Hertz theory to model the interaction of a leukocyte circulating in the blood with the endothelial wall. We have calculated that a microvillus on the leukocyte with a diameter of 50 nm under a 10 pN load would indent approximately 150 nm into the glycocalyx, only a fraction of the total thickness. This indicates that the glycocalyx, with properties as measured in this experiment, is a significant barrier to cell-cell interaction and can be a large steric hindrance wh...

<table border="1">
 <tbody>
 <tr>
 <td>Name of Reagent/Material</td>
 <td>Company</td>
 <td>Catalog Number</td>
 <td>Comments</td>
 </tr>
 <tr>
 <td>McCoy's Medium</td>
 <td>Gibco</td>
 <td>16600-082</td>
 <td></td>
 </tr>
 <tr>
 <td>Fetal Calf Serum</td>
 <td>Hyclone</td>
 <td>SH30070</td>
 <td></td>
 </tr>
 <tr>
 <td>Endothelial Cell Growth Medium</td>
 <td>Vec Technologies</td>
 <td>MCDB-131</td>
 <td></td>
 </tr>
 <tr>
 <td>Pooled Human Umbilical Vein Endothelial Cells</td>
 <td>Vec Technologies</td>
 <td>PHUVEC/T-25</td>
 <td></td>
 </tr>
 <tr>
 <td>Sulfuric Acid</td>
 <td>JT Baker</td>
 <td>9681-02</td>
 <td></td>
 </tr>
 <tr>
 <td>Hydrogen Peroxide</td>
 <td>VWR</td>
 <td>BDH3742-1</td>
 <td></td>
 </tr>
 <tr>
 <td>(3-aminopropyl)triethoxysilane</td>
 <td>Aldrich</td>
 <td>440140-100ML</td>
 <td></td>
 </tr>
 <tr>
 <td>Isopropyl Alcohol</td>
 <td>VWR</td>
 <td>BDH8999-4</td>
 <td></td>
 </tr>
 <tr>
 <td>Trypsin</td>
 <td>Cellgro</td>
 <td>25-054-C1</td>
 <td></td>
 </tr>
 <tr>
 <td>Hank's Buffered Salt Solution</td>
 <td>Gibco</td>
 <td>14175-095</td>
 <td></td>
 </tr>
 <tr>
 <td>sulfo-NHS-LC-Biotin</td>
 <td>Thermo Scientific</td>
 <td>21335</td>
 <td></td>
 </tr>
 <tr>
 <td>Streptavadin beads</td>
 <td>Dynabeads</td>
 <td>112.06D</td>
 <td></td>
 </tr>
 <tr>
 <td>MFP-3D AFM</td>
 <td>Asylum Research</td>
 <td></td>
 <td></td>
 </tr>
 <tr>
 <td>Tipless Cantilevers</td>
 <td>Nanoworld</td>
 <td>ARROW-TL1-50</td>
 <td></td>
 </tr>
 <tr>
 <td>Silhouette SD</td>
 <td>Quickutz</td>
 <td>Silhouette-SD</td>
 <td></td>
 </tr>
 <tr>
 <td>Silicone Rubber</td>
 <td>Stockwell Elastomerics</td>
 <td>SE50-RS</td>
 <td></td>
 </tr>
 <tr>
 <td>30 ml Syringes</td>
 <td>Benton Dickinson</td>
 <td>309650</td>
 <td></td>
 </tr>
 <tr>
 <td>18 gauge needles</td>
 <td>Benton Dickinson</td>
 <td>305196</td>
 <td></td>
 </tr>
 <tr>
 <td>Extension Sets</td>
 <td>Hospira</td>
 <td>4429-48</td>
 <td></td>
 </tr>
 <tr>
 <td>4 way valves</td>
 <td>Teleflex</td>
 <td>W21372</td>
 <td></td>
 </tr>
 <tr>
 <td>Male/Female Port Caps</td>
 <td>Smith's Medical</td>
 <td>MX491B</td>
 <td></td>
 </tr>
 <tr>
 <td>Peristaltic Pump</td>
 <td>Watson-Marlow</td>
 <td>401U/D</td>
 <td></td>
 </tr>
 <tr>
 <td>Peristaltic Tubing</td>
 <td>Watson-Marlow</td>
 <td>903.0016.016</td>
 <td></td>
 </tr>
 <tr>
 <td>sterile filters</td>
 <td>Pall Life Science</td>
 <td>4652</td>
 <td></td>
 </tr>
 </tbody>
</table>

quantifying the mechanical properties of the endothelial glycocalyx with atomic force microscopy

Our understanding of the interaction of leukocytes and the vessel wall during leukocyte capture is limited by an incomplete understanding of the mechanical properties of the endothelial surface layer. It is known that adhesion molecules on leukocytes are distributed non-uniformly relative to surface topography 3, that topography limits adhesive bond formation with other surfaces 9, and that physiological contact forces (&asymp; 5.0 &minus; 10.0 pN per microvillus) can compress the microvilli to as little as a third of their resting length, increasing the accessibility of molecules to the opposing surface 3, 7. We consider the endothelium as a two-layered structure, the relatively rigid cell body, plus the glycocalyx, a soft protective sugar coating on the luminal surface 6. It has been shown that the glycocalyx can act as a barrier to reduce adhesion of leukocytes to the endothelial surface 4. In this report we begin to address the deformability of endothelial surfaces to understand how the endothelial mechanical stiffness might affect bond formation. Endothelial cells grown in static culture do not express a robust glycocalyx, but cells grown under physiological flow conditions begin to approximate the glycocalyx observed in vivo 2. The modulus of the endothelial cell body has been measured using atomic force microscopy (AFM) to be approximately 5 to 20 kPa 5. The thickness and structure of the glycocalyx have been studied using electron microscopy 8, and the modulus of the glycocalyx has been approximated using indirect methods, but to our knowledge, there have been no published reports of a direct measurement of the glycocalyx modulus in living cells. In this study, we present indentation experiments made with a novel AFM probe on cells that have been cultured in conditions to maximize their glycocalyx expression to make direct measurements of the modulus and thickness of the endothelial glycocalyx.

In a typical experiment, 20 force-vs-distance curves were obtained from a given region of the cell, typically in the perinuclear region, near, but not on, the nucleus (within ~2 &mu;m). The curves were aligned to account for any sample drift over the duration of the measurement and then averaged to remove cantilever noise, as shown in Figure 4. The curves were analyzed and fit with the two layer model that was developed for determining the modulus and thickness of thin polymer films 1. From fi...

Watch this Scientific Journal Video about Quantifying the Mechanical Properties of the Endothelial Glycocalyx with Atomic Force Microscopy at JoVE.com

Quantifying the Mechanical Properties of the Endothelial Glycocalyx with Atomic Force Microscopy

The mechanical characteristics of endothelial glycocalyx were measured by indentation using micron sized spheres on AFM cantilevers. Endothelial cells were cultured in a custom chamber under physiological flow conditions to induce glycocalyx expression. Data were analyzed using a thin film model to determine the glycocalyx thickness and modulus.

Our  understanding of the interaction of leukocytes and the vessel wall during  leukocyte capture is limited by an incomplete understanding of the ...

quantifying-mechanical-properties-endothelial-glycocalyx-with-atomic

Research

JoVE Journal

Bioengineering

13.1K Views.  University of Rochester. The mechanical characteristics of endothelial glycocalyx were measured by indentation using micron sized spheres on AFM cantilevers. Endothelial cells were cultured in a custom chamber under physiological flow conditions to induce glycocalyx expression. Data were analyzed using a thin film model to determine the glycocalyx thickness and modulus.