Wet Chemistry and Peptide Immobilization on Polytetrafluoroethylene for Improved Cell-adhesion

Podsumowanie

Cell-adhesiveness is key to many approaches in biomaterial research and tissue engineering. A step-by-step technique is presented using wet-chemistry for the surface modification of the important polymer PTFE with peptides.

Streszczenie

Endowing materials surface with cell-adhesive properties is a common strategy in biomaterial research and tissue engineering. This is particularly interesting for already approved polymers that have a long standing use in medicine because these materials are well characterized and legal issues associated with the introduction of newly synthesized polymers may be avoided. Polytetrafluoroethylene (PTFE) is one of the most frequently employed materials for the manufacturing of vascular grafts but the polymer lacks cell adhesion promoting features. Endothelialization, i.e., complete coverage of the grafts inner surface with a confluent layer of endothelial cells is regarded key to optimal performance, mainly by reducing thrombogenicity of the artificial interface.

This study investigates the growth of endothelial cells on peptide-modified PTFE and compares these results to those obtained on unmodified substrate. Coupling with the endothelial cell adhesive peptide Arg-Glu-Asp-Val (REDV) is performed via activation of the fluorin-containing polymer using the reagent sodium naphthalenide, followed by subsequent conjugation steps. Cell culture is accomplished using Human Umbilical Vein Endothelial Cells (HUVECs) and excellent cellular growth on peptide-immobilized material is demonstrated over a two-week period.

Wprowadzenie

Various polymers used in medicine that have been approved for some time do not exhibit enhanced biocompatibility, i.e., lack of cell-adhesiveness, induction of fibrotic encapsulation and thrombogenicity, to mention a few. Interactions between the biomaterial and the biological system takes place mainly at the surface of the implant. As a consequence, research has focused on surface modification in order to create appropriate properties for a desired application while leaving the bulk properties of the material unaffected. Polytetrafluoroethylene (PTFE) as a physiologically inert polymer is used in many medical fields such as hernia surgical mesh ¹, medical ports ² and, most importantly, vascular grafts ³.

Especially in blood contacting situations the hydrophobic nature of PTFE causes unspecific adsorption of plasma components and as a consequence platelet adhesion, often resulting in thrombotic events and occlusion of the graft ⁴. Furthermore, PTFE, like most polymers, does not support cellular adhesion and coverage which would be a desirable feature to induce the formation of a beneficial layer of endothelial cells (ECs) on the inner (luminal) surface of the vascular graft ⁵. A biomimetic endothelium is expected to fulfil many of the functions of its natural equivalent, notably its antithrombogenic properties ⁶. A general biomimetic modification strategy is based upon the concept of exclusively endowing the material with cell-adhesiveness while leaving the materials bulk properties unaffected. In addition, platelet adhesion may be reduced by incorporating anti-adhesive (anti-fouling) attributes ⁷. Various peptides — mostly derived from proteins of the extracellular matrix — have been described that strongly enhance cell-adhesion by binding to cellular receptors, belonging to the class of integrins ⁸. The best-known example in this regard is the peptide Arg-Gly-Asp (RGD) that interacts with most cell types. Other amino acid sequences are recognized by integrins exclusively expressed on specific cells. For example, Arg-Glu-Asp-Val (REDV) and Tyr-Ile-Gly-Ser-Arg (YIGSR) have been found to bind to ECs in a specific manner ⁹. Covalent immobilization of such peptides has been carried out on a plethora of inherently non-adhesive materials including metals and polymers ^10,11.

Porous PTFE, more precisely expanded PTFE (ePTFE) — along with polyethylene terephthalate (PET) - is the most important material for the production of vascular grafts ¹². Established physical techniques for appropriate treatments, such as plasma modification ¹³ or by photochemical methods ¹⁴, are hampered by the fact that porous and/or tubular structures are not readily treatable inside the pores or the lumen respectively. Wet chemistry on PTFE is a difficult task because of the highly inert nature of the fluorin-containing polymer that resists most chemical attacks ¹⁵.

In this paper we describe a comparatively facile method for a covalent modification strategy. Adapted from a procedure to render PTFE bondable, functional groups were created on the materials surface that serve as anchor points for further conjugation of biologically active molecules.

Protokół

1. Preparation of Sodium Naphthalenide Activating Solution and Surface Activation

Note: Carry out reactions in a well-ventilated fume hood. Follow general rules for handling highly flammable solvents and corrosive metals like metallic sodium. Naphthalene has a very unpleasant smell (mothball), even in very small amounts! If not indicated otherwise reactions are performed at room temperature. Sodium azide is highly toxic! THF (99.9%, see List of Materials) was stored over approximately 20% (by volume) molecular sieve. Distill THF with a noticeable water content over sodium. The formation of sodium naphthalenide does not occur if trace amounts of water are present.

1. To a solution of 1.4 g (10.9 mmol) of naphthalene in 20 ml tetrahydrofuran (THF, dried over 3 Å molecular sieve), add 0.25 g (10.9 mmol) sodium metal in a screw-capped 100 ml glass bottle equipped with a PTFE-coated magnetic stirring bar.
   Note: Dissolution can be greatly enhanced by cutting the sodium into small pieces and modest heating (35 - 40 °C). The final solution has a dark, slightly greenish color and may be stored under strictly dry conditions.
2. Punch out PTFE discs of 12 mm diameter from 0.5 mm thick foil material. Mark one side (e.g., using a letter stamp punch) and clean with iso-propanol.
3. Incubate PTFE-samples individually in the activating solution (step 1.1) for 1 - 2 min using forceps. Note: The color change from white to dark brown indicates successful treatment.
4. Subsequently rinse twice with THF and then with iso-propanol.
   Note: The naphthalenide solution is exhausted when its color changes to a watery light brown. Unused naphthalenide solution (possibly containing metallic sodium) has to be decomposed by slowly adding iso-propanol prior to disposal.
5. Oxidize treated samples in hydrogen peroxide (30%) containing 20% (w/v) trichloroacetic acid for 3 hr. Wash with water and dry. The surface now has a slight brownish appearance. Note: Activation and oxidation result in a drastically increased wettability of the surface. This finding was examined in detail previously ¹⁴.
6. Treat oxidized discs with 50% (v/v) hexamethylene diisocyanate (HMDI) in dry THF for 2 hr, rinse with THF and leave to dry.
7. Hydrolyze isocyanate bearing samples in water for 2 - 3 hr and dry. Note: The final amino-functionalized PTFE surface is far more stable than the isocyanate-bearing samples and is compatible with many standard crosslinkers for further coupling.

2. Peptide Immobilization

1. Prepare a solution of 20% (v/v) diethyleneglycol diglycidyl ether (diepoxide) in 50 mM carbonate buffer, pH 9.
2. Place the aminated discs with the marked side up individually into a 24 well plate and add 1.5 ml of the epoxide solution. Ensure full coverage of the samples. Incubate for 2 hr and wash two times with water and once with carbonate buffer.
3. Add 50 µl of a 0.5 mg/ml peptide (e.g., REDV) in 50 mM carbonate buffer, pH 9 containing 0.01% NaN₃, to the bottom of individual wells of a fresh 24 well plate and carefully place the epoxy-functionalized discs upside-down (i.e., marked side down) onto the drop of the peptide solution. Make sure that the space between the bottom of the well and the PTFE disc is completely wetted due to capillary action.
4. Incubate in a wet chamber (e.g., any sealable plastic box with a tight closing lid) with humidified atmosphere (by placing wet tissue paper on the bottom) for at least 3 hr or overnight.
   Note: Albeit the REDV motif may be regarded as well-characterized, a scrambled or reverse amino acid sequence may be included as an additional negative control.
5. Wash three times with water and sterilize in 50% iso-propanol/water for at least 30 min. Prior to cell seeding, rinse the samples in sterile phosphate buffered saline (PBS).

3. Cell Seeding

1. Grow HUVECs using standard cell culture procedures ^17,18.
2. Place the peptide-conjugated samples with the modified side up in a 24 well plates. Use untreated PTFE discs as a control.
3. Seed 5 x 10⁴ HUVECs in 2 ml medium per well and incubate for 4 hr at 37 °C and 5% CO₂ in an incubator.
4. Remove the discs, rinse carefully to remove unattached cells and transfer to a fresh 24 well plate. Add 2 ml of fresh medium and incubate for the desired period (e.g., 24 hr, 1 w, etc.). Change medium every two days.
5. Prepare a stock solution of 1 mg/ml Calcein-AM in dimethyl sulfoxide (DMSO).
6. After growing the cells remove the medium, wash with PBS and add PBS containing 1 µl/ml Calcein-AM stain (e.g., 1 µl of a stock solution per ml PBS). Gently agitate and incubate at 37 °C for 45 min in the dark.
7. Wash with PBS and immediately take micrographs on a fluorescence microscope equipped with standard FITC filters (Ex 488 nm, Em 515 nm). Use 100-fold magnification. Perform triplicates from unmodified as well as treated samples.
8. Using ImageJ software determine the area colonized by the cells. Alternatively count the cells manually or use ImageJ. Both methods will give similar information about the attachment and growth of cells on the respective surfaces.

Wyniki

The results of the crucial chemical reaction steps were monitored by IR spectroscopy (Figure 1). The initial activation with sodium naphthalenide generates double bonds — and to a minor extent — OH-functionalities. The signal indicating C=C bonds disappear upon oxidation, yielding a surface bearing almost exclusively hydroxyl-groups. Analysis of further standard conjugation steps are not shown here. The color changes due to activation and oxidation are in agre...

Dyskusje

The detailed description of surface modification protocol of PTFE consists of successive steps starting with the elimination of fluorine from the polymer backbone as depicted in Figure 6. As a result, a layer is formed that contains an abundant amount of conjugated carbon-carbon double bonds in accordance with the dark brownish color that developed upon naphthalenide treatment. Standard oxidation with acidic hydrogen peroxide yields a hydroxylated surface accompanied by brightening to a pale brown, this ...

Materiały

Name	Company	Catalog Number	Comments
PTFE foil 0.5 mm	Cadillac Plastic	n/a
REDV peptide	Genecust	n/a	custom synthesis >95% purity
iso-propanol	Sigma Aldrich	34965
tetrahydrofurane (THF)	Sigma Aldrich	401757
dimethylsulfoxide	Sigma Aldrich	D8418
molecular sieve 3 Å	Sigma Aldrich	208574
sodium metal	Sigma Aldrich	483745
phosphate buffered saline (PBS)	Sigma Aldrich	D8537
naphthalene	Sigma Aldrich	147141
hydrogen peroxide 30%	Sigma Aldrich	95321
trichloroacetic acid	Sigma Aldrich	T6399
diethylene glycol diglycidyl ether	Sigma Aldrich	17741
hexamethylene diisocyanate (HMDI)	Sigma Aldrich	52650
Calcein-AM	Sigma Aldrich	56496
sodium bicarbonate	Sigma Aldrich	S6014
sodium azide	Sigma Aldrich	71290
24 well plates	Greiner-Bio-One	662 160
ATR-FTIR spectrophotometer Nicolet Magna-IR 850	Nicolet	n/a
fluorescence microscope Olympus X-70	Olympus	n/a
humbilical vein endothelial cells (HUVECs)	Lonza	n/a
ePTFE vascular graft	Gore	n/a