The authors would like to thank Gabriel Arom and Michael Yeranosian for their technical contributions to earlier iterations of this project. This project was funded by the OREF Clinician Scientist Training Grant (NL), H H Lee Surgical Research Grant (NL), Veterans Administration BLR&#38;D Merit Review 1 I01 BX00012601 (DM) and Musculoskeletal Transplantation Foundation Young Investigator Award (FP).

NOTE: All animal surgeries were approved by the local veterinary staff and animal use committee prior to commencing the experiments.
1. Preparation of Electrospun Polycaprolactone Scaffolds
<ol>
	<li>Weigh and dissolve medical grade ester terminated poly (&#949;-caprolactone) in granule form in 1,1,1,3,3,3-hexafluoro-2-propanol to create a 10% w/w solution of the PCL polymer. Let the solution stir using a stir plate for at least 3 hr to ensure a homogenous solution.</li>
	<li>Electrospin the PCL solution to create a cuff of highly aligned PCL fibers for scaffold fabrication.
	<ol>
		<li>Prepare the electrospinning setup in a chemical fume hood with the fan on at all times. This consists of a large acrylic box that will serve as an isolated vacuum medium for the electrospinning process and has entry points for the source PCL solution driven by a voltage source, the motor-powered collecting mandrel, and a vacuum port. Clean the acrylic box thoroughly with ethanol and cover all surfaces with Parafilm sheets to remove any impurities that may compromise the quality of the electrospun product.</li>
		<li>Load approximately 3 ml of the above solution into a 10 ml syringe with a blunt ended 18 G, 1 &#189; inch needle. Remove any air bubbles by pushing the syringe up. Lock solution into a programmable syringe pump. Insert the needle through a small hole into the acrylic box while leaving about &#189; inch of the needle outside of the acrylic box for attachment of the voltage source wire.</li>
		<li>Use a 30 mm rotating lathe mandrel as the collector for the highly aligned PCL fibers; cover the mandrel tightly with a thin strip of aluminum foil. Lock the mandrel into the motor on the opposite side of the box about 15 cm away from the syringe needle.</li>
		<li>Insert the plastic hose into the vacuum port and connect to the fume hood vacuum source. Turn on the vacuum source and cover the acrylic box with a lid.</li>
		<li>Set the infusion rate of the programmable syringe pump to 2.5 ml/hr. Turn on the motor to operate the mandrel at 3,450 rpm and attach the positive lead of the voltage source to the needle tip outside of the box using an alligator clip.</li>
		<li>Once infusion of the PCL solution has begun, turn on the voltage source and set to a 20 kV operating voltage.</li>
		<li>Infuse the solution for 12 min to create a homogenous cuff from 0.5 ml of the PCL solution. 
		NOTE: On average, each cuff has enough electrospun material to create two six-strip sheets, which can be used to create a total of three four-layered scaffolds.</li>
	</ol>
	</li>
	<li>Laser cut the PCL cuff to form multiple small sheets on a VersaLaser Cutter 2.3 operated at low-vacuum setting, 10.0 keV landing voltage, 6.4 mm working distance, and probe diameter of 3.0. 
	NOTE: In this example, a computer aided design was used to instruct the cutter to yield multiple sheets of 1.5 mm x 35 mm x 150 &#181;m scaffolds with evenly distributed 150 &#181;m diameter holes at 15% pore area.</li>
	<li>Plasma etch the PCL scaffolds using a plasma cleaner to induce hydrophilicity of the PCL surface with ion acceleration. Set the vacuum to 450 mTorr and the treat the scaffolds for 30 sec at high power (29.6 W).</li>
	<li>Bathe the scaffolds in 70% ethanol in a sterile environment.</li>
	<li>Coat the individual scaffolds with collagen to facilitate cellular adhesion and proliferation in vivo.
	<ol>
		<li>Create a collagen coating solution by diluting a 8:1:2.5 sterile solution of Purecol collagen 3 mg/ml standard solution, 10x PBS and 0.1 N NaOH 1:9 in 1x PBS at 4 &#176;C. Mix thoroughly to ensure solution homogeneity.</li>
		<li>Coat individual 1.5 mm x 35 mm x 150 &#181;m scaffolds with a thin layer film of the above collagen solution. Allow to dry for 24 hr in a sterile environment.</li>
	</ol>
	</li>
	<li>Using 5-0 Vicryl sutures, stack and affix four individual 1.5 mm x 35 mm x 150 &#181;m scaffolds using a Krackow stitch to create a final 0.6 mm thick, multi-layered, collagen-coated scaffold that is ready for implantation.</li>
</ol>
2. Rat Surgery Protocol
<ol>
	<li>Induce anesthesia by placing rat in inhalation chamber and delivering 2% isoflurane with 2 L/min oxygen. Confirm the rat is adequately anesthetized by applying pressure to hind foot and evaluating for any response.</li>
	<li>On the non-sterile back table, subcutaneously inject 25 mg/kg ampicillin and 0.03 mg/kg buprenorphine.</li>
	<li>Apply ophthalmic ointment to the eyes. Clip the fur from the operative hind limb and prep the surgical site with three alternating scrubs of chlorhexidine and 70% ethanol.</li>
	<li>Transfer the rat to the operating table, on a heated pad to prevent hypothermia. Secure nose cone, and maintain anesthesia through the procedure with 2% isoflurane in 2 L/min oxygen, delivered nose cone. Drape in a sterile manner, leaving the operative limb exposed.&#160;</li>
	<li>Before starting the surgery, first confirm adequate anesthetization by lack of a response to hind foot pressure.</li>
	<li>Make a 2 cm long vertical incision medial to the knee, centered at the level of the patella. Retract the skin laterally until the incision is centered over the knee.</li>
	<li>Use a scalpel to make a medial parapatellar arthrotomy by cutting just medial to the patella and extending proximally to the level of the musculotendinous junction of the quadriceps and distally to the level of the patellar tendon insertion on the tibial tubercule. Take care not to cut the patellar or quadriceps tendons.</li>
	<li>Release patella laterally by making a 1 cm vertical incision through the knee capsule just lateral to the patellar tendon.</li>
	<li>Ensure the knee is extended. Take a pair of fine scissors and pass under the patella from lateral to medial. Spread the scissors a couple times so that the extensor mechanism can be translated to either side.</li>
	<li>While flexing the knee, translate the patella laterally to expose the inside of the knee joint. Ensure clear visualization of the intercondylar notch and femoral condyles. Using a scalpel, transect the ACL and PCL in the notch.</li>
	<li>Load power drill with a 1.6 mm k-wire. Place k-wire tip on ACL origin in the intercondylar notch. Drill superolaterally and visualize the exit point on the lateral aspect of the femur, removing any soft tissue as necessary with a scalpel. Pass the k-wire in and out a few times to ensure clear passage for the graft.</li>
	<li>Place the k-wire on the ACL footprint on the tibial plateau. Drill anterolaterally and visualize exit point on the anterolateral proximal tibia. Use scalpel to clear soft tissue as necessary so that the point where the k-wire exits the tibia is fully visualized.</li>
	<li>Pass a shortened Keith needle (ideally no more than 2 inches long) through the femoral bone tunnel. Thread the two suture ends from one end of the graft through the eye of the Keith needle. Use the needle to pull one end of the graft through the femoral tunnel.</li>
	<li>Repeat the prior step to pass the other end of the graft through the tibial tunnel.</li>
	<li>Use 4-0 Vicryl suture to affix the femoral end of the graft to surrounding periosteum or other soft tissue with a figure-of-eight stitch. Manually tension the graft with the knee in extension. Affix the tibial end of the graft to surrounding periosteum or other soft tissue with a figure-of-eight stitch.</li>
	<li>Use a scissor to cut off excess graft on both ends, leaving 1-2 mm on each end past the figure-of-eight stitch.</li>
	<li>Extend the knee and reduce the patella. Using 4-0 vicryl, place a single figure-of-eight stitch to close the medial joint capsule, preventing lateral subluxation of the patella.</li>
	<li>Close the skin with a running subcuticular 5-0 Monocryl or Vicryl suture, with care not to suture the underlying muscle or have any visible suture once the skin is closed.</li>
	<li>Inject rats subcutaneously with buprenorphine every 12 hr for a total of three days postoperatively. Check surgical site for any drainage or wound dehiscence at the time of injection. Limping and some swelling are normal in the first few days after surgery, but promptly address any postoperative concerns in conjunction with veterinary staff. &#160;The animal may be return to social housing at 2 weeks postoperatively, when surgical incisions are completely healed.</li>
</ol>
3. Data Collection Protocol
<ol>
	<li>At the time of sacrifice, asphyxiate rats individually in a closed CO2 chamber followed by thoracotomy.</li>
	<li>Harvest both the surgically reconstructed and contralateral limbs by separating at the hip joint.
	<ol>
		<li>For the reconstructed limbs, remove all soft tissue, including the posterior cruciate ligament and the remnants from the surgically disrupted native ACL, by fine dissection to isolate only the femur, tibia, and graft.</li>
		<li>For the contralateral limbs, remove all soft tissue except the native ACL as well as the femur and tibia by fine dissection.</li>
		<li>Use a rotary tool such as Dremel, to remove all but &#190; to 1 cm of bone from each end of the femur-graft-tibia complex.</li>
		<li>During this process and throughout biomechanical testing, regularly and frequently spray the ligamentous regions with normal saline to prevent desiccation of the harvested knee which may falsely alter results.</li>
	</ol>
	</li>
	<li>For histological analysis, fix each knee individually in 4% paraformaldehyde solution at 25 &#176;C for 48 hr. Next, submerge the knee in a solution of Immunocal reagent for complete decalcification; this process is dependent on the calcific contents of the sample and may take up to five days. Check individual samples daily to assess progress as incomplete decalcification can lower sample quality. Once complete, perform sectioning, slide mounting, and staining as desired.</li>
	<li>Perform biomechanical testing to assess the functional capacity of the tissue engineered ligament.
	<ol>
		<li>Secure the femur and tibia by wrapping 28 G&#160;galvanized steel wire around the epiphysis of each bone separately. This is to prevent inaccurate biomechanical testing data from premature tensile failure of the sample at the bone rather than at the ligament of interest.</li>
		<li>Pot the femur into a mixture of polymethylmethacrylate (PMMA) bone cement. To do this, mix the two cement components and immediately use the viscous mixture to secure the femur into the metal, completely encasing the diaphysis of the bone in the cemented pot with the epiphysis and attached ligament protruding freely. Allow spontaneous free radical polymerization to gradually transform the mixed viscous components to a doughy material and eventually into a solid hardened matrix. 
		NOTE: This process takes several minutes and can be monitored by manually assessing the temperature of a bolus made from the remaining cement; the temperature should transiently increase during the exothermic polymerization reaction and subside to RT after the material solidifies.</li>
		<li>Repeat the same process above for cementing the tibia, except while maintaining the knee ligament at 20&#176; flexion for ideal mechanical testing.</li>
		<li>Mount the cemented femur-graft-tibia complex onto a tensile testing apparatus, and prepare to record load and displacement as a function of time from the beginning of tension to failure. In this example, we used an Instron Model 5564 with a 1 kN load cell.</li>
		<li>Pre-tension the graft to 2 N at a ramp rate of 0.5 N/min and then test the graft to failure at a strain rate of 0.5 mm/sec. During the process, be sure that the ligament is failing at the mid-substance and that the bony femur and tibia are secure and not prematurely failing, which may inaccurately assess biomechanical properties of the tested ligament.</li>
		<li>Use the generated load-displacement curves to compute the failure load and stiffness of the tested ligament.</li>
	</ol>
	</li>
</ol>

<ol>
	<li>Fetto, J. F., Marshall, J. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+natural+history+and+diagnosis+of+anterior+cruciate+ligament+insufficiency.">The natural history and diagnosis of anterior cruciate ligament insufficiency.</a> Clin Orthop Relat Res. (147), 29-38 (1980).</li><li>Kim, Y. M., Lee, C. A., Matava, M. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Clinical+results+of+arthroscopic+single-bundle+transtibial+posterior+cruciate+ligament+reconstruction:+a+systematic+review.">Clinical results of arthroscopic single-bundle transtibial posterior cruciate ligament reconstruction: a systematic review.</a> Am J Sports Med. 39 (2), 425-434 (2011).</li><li>Andersson, C., Odensten, M., Gillquist, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Knee+function+after+surgical+or+nonsurgical+treatment+of+acute+rupture+of+the+anterior+cruciate+ligament:+a+randomized+study+with+a+long-term+follow-up+period.">Knee function after surgical or nonsurgical treatment of acute rupture of the anterior cruciate ligament: a randomized study with a long-term follow-up period.</a> Clin Orthop Relat Res. (264), 255-263 (1991).</li><li>Klimkiewicz, J. J., Petrie, R. S., Harner, C. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surgical+treatment+of+combined+injury+to+anterior+cruciate+ligament,+posterior+cruciate+ligament,+and+medial+structures.">Surgical treatment of combined injury to anterior cruciate ligament, posterior cruciate ligament, and medial structures.</a> Clin Sports Med. 19 (3), 479-492 (2000).</li><li>Petrigliano, F. A., McAllister, D. R., Wu, B. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Tissue+engineering+for+anterior+cruciate+ligament+reconstruction:+a+review+of+current+strategies.">Tissue engineering for anterior cruciate ligament reconstruction: a review of current strategies.</a> Arthroscopy. 22 (4), 441-451 (2006).</li><li>Groot, J. H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Use+of+porous+polyurethanes+for+meniscal+reconstruction+and+meniscal+prostheses.">Use of porous polyurethanes for meniscal reconstruction and meniscal prostheses.</a> Biomaterials. 17 (2), 163-173 (1996).</li><li>Leong, N. L., Petrigliano, F. A., McAllister, D. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Current+tissue+engineering+strategies+in+anterior+cruciate+ligament+reconstruction.">Current tissue engineering strategies in anterior cruciate ligament reconstruction.</a> J Biomed Mater Res A. 102 (5), 1614-1624 (2014).</li><li>Duling, R. R., Dupaix, R. B., Katsube, N., Lannutti, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Mechanical+characterization+of+electrospun+polycaprolactone+(PCL):+a+potential+scaffold+for+tissue+engineering.">Mechanical characterization of electrospun polycaprolactone (PCL): a potential scaffold for tissue engineering.</a> J Biomech Eng. 130 (1), 011006 (2008).</li><li>Shao, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Polycaprolactone+electrospun+mesh+conjugated+with+an+MSC+affinity+peptide+for+MSC+homing+in+vivo.">Polycaprolactone electrospun mesh conjugated with an MSC affinity peptide for MSC homing in vivo.</a> Biomaterials. 33 (12), 3375-3387 (2012).</li><li>Tillman, B. W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+in+vivo+stability+of+electrospun+polycaprolactone-collagen+scaffolds+in+vascular+reconstruction.">The in vivo stability of electrospun polycaprolactone-collagen scaffolds in vascular reconstruction.</a> Biomaterials. 30 (4), 583-588 (2009).</li><li>Wise, S. G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+multilayered+synthetic+human+elastin/polycaprolactone+hybrid+vascular+graft+with+tailored+mechanical+properties.">A multilayered synthetic human elastin/polycaprolactone hybrid vascular graft with tailored mechanical properties.</a> Acta Biomater. 7 (1), 295-303 (2011).</li><li>Vargel, I., Korkusuz, P., Mencelo&#287;lu, Y. Z., Pi&#351;kin, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+vivo+performance+of+antibiotic+embedded+electrospun+PCL+membranes+for+prevention+of+abdominal+adhesions.">In vivo performance of antibiotic embedded electrospun PCL membranes for prevention of abdominal adhesions.</a> J Biomed Mater Res B Appl Biomater. 81 (2), 530-543 (2007).</li><li>Cao, H., McHugh, K., Chew, S. Y., Anderson, J. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+topographical+effect+of+electrospun+nanofibrous+scaffolds+on+the+in+vivo+and+in+vitro+foreign+body+reaction.">The topographical effect of electrospun nanofibrous scaffolds on the in vivo and in vitro foreign body reaction.</a> J Biomed Mater Res A. 93 (3), 1151-1159 (2010).</li><li>Joshi, V. S., Lei, N. Y., Walthers, C. M., Wu, B., Dunn, J. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Macroporosity+enhances+vascularization+of+electrospun+scaffolds.">Macroporosity enhances vascularization of electrospun scaffolds.</a> J Surg Res. 183 (1), 18-26 (2013).</li><li>Pham, Q. P., Sharma, U., Mikos, A. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrospun+poly(epsilon-caprolactone)+microfiber+and+multilayer+nanofiber/microfiber+scaffolds:+characterization+of+scaffolds+and+measurement+of+cellular+infiltration.">Electrospun poly(epsilon-caprolactone) microfiber and multilayer nanofiber/microfiber scaffolds: characterization of scaffolds and measurement of cellular infiltration.</a> Biomacromolecules. 7 (10), 2796-2805 (2006).</li><li>Vaz, C. M., van Tuijl, S., Bouten, C. V., Baaijens, F. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Design+of+scaffolds+for+blood+vessel+tissue+engineering+using+a+multi-layering+electrospinning+technique.">Design of scaffolds for blood vessel tissue engineering using a multi-layering electrospinning technique.</a> Acta Biomater. 1 (5), 575-582 (2005).</li><li>Kawamura, S., Ying, L., Kim, H. J., Dynybil, C., Rodeo, S. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Macrophages+accumulate+in+the+early+phase+of+tendon-bone+healing.">Macrophages accumulate in the early phase of tendon-bone healing.</a> J Orthop Res. 23 (6), 1425-1432 (2005).</li><li>Hays, P. L., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+role+of+macrophages+in+early+healing+of+a+tendon+graft+in+a+bone+tunnel.">The role of macrophages in early healing of a tendon graft in a bone tunnel.</a> J Bone Joint Surg Am. 90 (3), 565-579 (2008).</li><li>Dagher, E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Immobilization+modulates+macrophage+accumulation+in+tendon-bone+healing.">Immobilization modulates macrophage accumulation in tendon-bone healing.</a> Clin Orthop Relat Res. 467 (1), 281-287 (2009).</li><li>Bedi, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+early+and+delayed+mechanical+loading+on+tendon-to-bone+healing+after+anterior+cruciate+ligament+reconstruction.">Effect of early and delayed mechanical loading on tendon-to-bone healing after anterior cruciate ligament reconstruction.</a> J Bone Joint Surg Am. 92 (14), 2387-2401 (2010).</li><li>Bedi, A., Kawamura, S., Ying, L., Rodeo, S. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Differences+in+tendon+graft+healing+between+the+intra-articular+and+extra-articular+ends+of+a+bone+tunnel.">Differences in tendon graft healing between the intra-articular and extra-articular ends of a bone tunnel.</a> HSS J. 5 (1), 51-57 (2009).</li><li>Fu, S. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+graft+tensioning+on+mechanical+restoration+in+a+rat+model+of+anterior+cruciate+ligament+reconstruction+using+free+tendon+graft.">Effect of graft tensioning on mechanical restoration in a rat model of anterior cruciate ligament reconstruction using free tendon graft.</a> Knee Surg Sports Traumatol Arthrosc. 21 (5), 1226-1233 (2013).</li><li>Fan, H., Liu, H., Wong, E. J., Toh, S. L., Goh, J. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+vivo+study+of+anterior+cruciate+ligament+regeneration+using+mesenchymal+stem+cells+and+silk+scaffold.">In vivo study of anterior cruciate ligament regeneration using mesenchymal stem cells and silk scaffold.</a> Biomaterials. 29 (23), 3324-3337 (2008).</li><li>Landis, J. R., Koch, G. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+measurement+of+observer+agreement+for+categorical+data.">The measurement of observer agreement for categorical data.</a> Biometrics. 33 (1), 159-174 (1977).</li><li>Joshi, S. M., Mastrangelo, A. N., Magarian, E. M., Fleming, B. C., Murray, M. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Collagen-platelet+composite+enhances+biomechanical+and+histologic+healing+of+the+porcine+anterior+cruciate+ligament.">Collagen-platelet composite enhances biomechanical and histologic healing of the porcine anterior cruciate ligament.</a> Am J Sports Med. 37 (12), 2401-2410 (2009).</li><li>Leong, N. L., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+vitro+and+in+vivo+evaluation+of+heparin+mediated+growth+factor+release+from+tissue-engineered+constructs+for+anterior+cruciate+ligament+reconstruction.">In vitro and in vivo evaluation of heparin mediated growth factor release from tissue-engineered constructs for anterior cruciate ligament reconstruction.</a> J Orthop Res. 10, (2014).</li><li>Seo, Y. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Increase+in+cell+migration+and+angiogenesis+in+a+composite+silk+scaffold+for+tissue-engineered+ligaments.">Increase in cell migration and angiogenesis in a composite silk scaffold for tissue-engineered ligaments.</a> J Orthop Res. 27 (4), 495-503 (2009).</li><li>Freeman, J. W., Woods, M. D., Laurencin, C. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Tissue+engineering+of+the+anterior+cruciate+ligament+using+a+braid-twist+scaffold+design.">Tissue engineering of the anterior cruciate ligament using a braid-twist scaffold design.</a> J Biomech. 40 (9), 2029-2036 (2007).</li><li>Bashur, C. A., Shaffer, R. D., Dahlgren, L. A., Guelcher, S. A., Goldstein, A. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+fiber+diameter+and+alignment+of+electrospun+polyurethane+meshes+on+mesenchymal+progenitor+cells.">Effect of fiber diameter and alignment of electrospun polyurethane meshes on mesenchymal progenitor cells.</a> Tissue Eng Part A. 15 (9), 2435-2445 (2009).</li><li>Dash, T. K., Konkimalla, V. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Poly-&#1108;-caprolactone+based+formulations+for+drug+delivery+and+tissue+engineering:+A+review.">Poly-&#1108;-caprolactone based formulations for drug delivery and tissue engineering: A review.</a> J Control Release. 158 (1), 15-33 (2012).</li><li>Yoshimoto, H., Shin, Y. M., Terai, H., Vacanti, J. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+biodegradable+nanofiber+scaffold+by+electrospinning+and+its+potential+for+bone+tissue+engineering.">A biodegradable nanofiber scaffold by electrospinning and its potential for bone tissue engineering.</a> Biomaterials. 24 (12), 2077-2082 (2003).</li><li>Xu, Y., Ao, Y. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Histological+and+biomechanical+studies+of+inter-strand+healing+in+four-strand+autograft+anterior+cruciate+ligament+reconstruction+in+a+rabbit+model.">Histological and biomechanical studies of inter-strand healing in four-strand autograft anterior cruciate ligament reconstruction in a rabbit model.</a> Knee Surg Sports Traumatol Arthrosc. 17 (7), 770-777 (2009).</li><li>Shino, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Replacement+of+the+anterior+cruciate+ligament+by+an+allogeneic+tendon+graft.+An+experimental+study+in+the+dog.">Replacement of the anterior cruciate ligament by an allogeneic tendon graft. An experimental study in the dog.</a> J Bone Joint Surg Br. 66 (5), 672-681 (1984).</li><li>Stasiak, M. E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+novel+device+to+apply+controlled+flexion+and+extension+to+the+rat+knee+following+anterior+cruciate+ligament+reconstruction.">A novel device to apply controlled flexion and extension to the rat knee following anterior cruciate ligament reconstruction.</a> J Biomech Eng. 134 (4), 041008 (2012).</li><li>Brophy, R. H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+short-duration+low-magnitude+cyclic+loading+versus+immobilization+on+tendon-bone+healing+after+ACL+reconstruction+in+a+rat+model.">Effect of short-duration low-magnitude cyclic loading versus immobilization on tendon-bone healing after ACL reconstruction in a rat model.</a> J Bone Joint Surg Am. 93 (4), 381-393 (2011).</li></ol>

The authors declare that they have no competing financial interests.

ACL injuries are a common condition in orthopaedic sports surgery, with limited options for reconstruction at the present time. In order to develop an appropriate tissue-engineered substitute for the ACL that will allow regeneration in vivo, a suitable animal model is required. In this study, the fabrication of a biodegradable engineered graft is described, as is its in vivo implantation using a reproducible model of ACL reconstruction in an athymic rat. This model can be utilized to evaluate different ...

Rupture of the anterior cruciate ligament (ACL) is one of most common ligament injuries of the knee1. Because the ruptured ACL&#8217;s is unable to heal without surgical intervention, the limitations in activities of daily living as well as participation in sports drive over 175,000 patients to undergo surgery each year2, with an estimated cost of one billion dollars annually3. Currently, either autograft or allograft tendon is used for ligament reconstruction. Though high success rates can be achieved with both autograft and allograft replacement, serious complications are associated with these reconstruction options4. Autograft tissue is associated with donor site morbidity and is limited in supply, especially in instances of re-rupture or multi-ligamentous injury. On the other hand, allograft tissue is linked with delayed graft integration, adverse inflammatory response, theoretical infectious risk, and limited supply5. Synthetic non-degradable grafts were developed in the 1970s and 1980s but were hampered by premature graft rupture, foreign body reactions, osteolysis, and synovitis6. As a result of these serious concerns, there are currently no synthetic grafts available for clinical use in the United States.
Due to these limitations with existing graft options and to recent developments in biology, engineering, and regenerative medicine, there has been great interest in a tissue engineered solution for ACL grafting. Current tissue engineering strategies employ degradable biological and synthetic materials to allow for host tissue ingrowth while avoiding the limitations associated with permanent synthetic material implantation7.
Polycaprolactone (PCL) is a biodegradable polymer that is FDA approved for a number of medical applications including adhesion barrier and wound dressing8, that has been used in a wide variety of applications including vascular, bone, cartilage, nerve, skin, and esophageal tissue engineering5,9-16. Favorable biocompatibility, relatively long in-vivo half-life, adequate mechanical strength, and high elasticity contribute to the popularity of this polymer in tissue engineering. In a rodent model of wound healing, implanted electrospun PCL was shown to be non-immunogenic and to integrate into local tissue without adverse reactions13. An SEM image of electrospun PCL is shown in Figure 1.
With current FDA regulatory standards, efficacy and safety in both small and large animal models would be required for a PCL or any other engineered ACL graft to move into clinical trials in the United States. Additionally, in vivo conditions can often augment the properties of an in vitro tissue engineered ACL graft. A rat model of autologous ACL reconstruction with flexor digitorum longus tendon has been previously described, in which the native ACL was severed, femoral and tibial tunnels were drilled, and the graft was passed and secured in place with suture17-22. In this paper, we will describe a modification of this model for the evaluation of engineered ACL replacements rather than for autograft-based reconstruction (Figure 2).
Although many animal models exist for ligament tissue engineering, the rat is advantageous compared to larger models for a number of reasons. These advantages include easier husbandry and handling, fewer ethical considerations, and reduced cost17,23. In addition, the rat model has been used extensively as a model for orthopaedic tissue regeneration, including cartilage, tendon, and bone tissue engineering24. In particular, athymic nude rats were chosen due to their lack of cell-mediated immune response25, allowing for the eventual implantation of xenogeneic donor cells in this model to further enhance the engineered graft in the future. In this methods paper, we describe the fabrication and surgical implantation of an acellular, biodegradable polymer graft in an athymic rat model of ACL reconstruction.

<table border="0" cellpadding="0" cellspacing="0" width="888">
	<tbody>
		<tr height="34">
			<td height="34" style="height:34px;width:347px;">Name of Material/ Equipment</td>
			<td style="width:147px;">Company</td>
			<td style="width:77px;">Catalog Number</td>
			<td style="width:317px;">Comments/Description</td>
		</tr>
		<tr height="34">
			<td height="34" style="height:34px;width:347px;">Medical grade ester terminated poly (&#949;-caprolactone), granule form (MW = 110,000)</td>
			<td style="width:147px;">Lactel Absorbable Polymers</td>
			<td style="width:77px;"></td>
			<td style="width:317px;">Custom synthesized polymer to desired molecular weight</td>
		</tr>
		<tr height="17">
			<td height="17" style="height:17px;width:347px;">1,1,1,3,3,3-hexafluoro-2-propanol</td>
			<td style="width:147px;">Sigma-Aldrich</td>
			<td>105228</td>
			<td style="width:317px;">Solvent for PCL polymer</td>
		</tr>
		<tr height="17">
			<td height="17" style="height:17px;width:347px;">18G x 1 1/2&#34;bevel needle</td>
			<td style="width:147px;">BD Medical</td>
			<td>305196</td>
			<td style="width:317px;"></td>
		</tr>
		<tr height="17">
			<td height="17" style="height:17px;width:347px;">Remote Infuse/Withdraw Programmable Syringe Pump</td>
			<td style="width:147px;">Harvard Apparatus</td>
			<td style="width:77px;">702101</td>
			<td style="width:317px;"></td>
		</tr>
		<tr height="17">
			<td height="17" style="height:17px;width:347px;">VersaLaser VLS2.30 Laser Engraver</td>
			<td style="width:147px;">Microgeo USA</td>
			<td style="width:77px;">VLS2.30</td>
			<td style="width:317px;"></td>
		</tr>
		<tr height="34">
			<td height="34" style="height:34px;width:347px;">Expanded Plasma Cleaner 115V</td>
			<td style="width:147px;">Harrick Plasma</td>
			<td style="width:77px;">PDC-001</td>
			<td style="width:317px;">Plasma etch just prior to collagen coating for surface modification</td>
		</tr>
		<tr height="34">
			<td height="34" style="height:34px;width:347px;">PureCol&#160; Collagen Standard Solution, 3 mg/ml</td>
			<td style="width:147px;">Advanced Biomatrix</td>
			<td style="width:77px;">5015-A</td>
			<td style="width:317px;">Mix 8:1:2.5 solution of PureCol, 10x PBS, 0.1N NaOH 1:9 in 1x PBS</td>
		</tr>
		<tr height="17">
			<td height="17" style="height:17px;width:347px;">Suture, 5-0 Vicryl</td>
			<td style="width:147px;">Henry Schein</td>
			<td style="width:77px;">1086471</td>
			<td style="width:317px;"></td>
		</tr>
		<tr height="17">
			<td height="17" style="height:17px;">Suture, 4-0 Vicryl</td>
			<td style="width:147px;">Henry Schein</td>
			<td style="width:77px;">6540072</td>
			<td style="width:317px;"></td>
		</tr>
		<tr height="17">
			<td height="17" style="height:17px;width:347px;">Sharp-pointed Dissecting Scissors (Straight; 4.5 inch)</td>
			<td style="width:147px;">Fisher Scientific</td>
			<td style="width:77px;">8940</td>
			<td style="width:317px;"></td>
		</tr>
		<tr height="34">
			<td height="34" style="height:34px;width:347px;">Buphrenorphine hydrochloride</td>
			<td style="width:147px;">Sigma-Aldrich</td>
			<td style="width:77px;">B9275</td>
			<td style="width:317px;">Use 0.03 mg/kg for both intra- and post-operatively for pain control</td>
		</tr>
		<tr height="17">
			<td height="17" style="height:17px;width:347px;">Ampicillin, injectable</td>
			<td style="width:147px;">Henry Schein</td>
			<td style="width:77px;">1185678</td>
			<td style="width:317px;">Use 25 mg/kg subcutaneously during the procedure</td>
		</tr>
		<tr height="17">
			<td height="17" style="height:17px;width:347px;">K-wire, 1.6 mm</td>
			<td style="width:147px;">Spectrum Surgical</td>
			<td style="width:77px;">SI040062</td>
			<td style="width:317px;"></td>
		</tr>
		<tr height="20">
			<td height="20" style="height:20px;width:347px;">Keith Needle, Straight 1 1/2&#34;</td>
			<td style="width:147px;">Delasco Dermatology Lab &#38; Supply</td>
			<td style="width:77px;">KE-112</td>
			<td style="width:317px;"></td>
		</tr>
		<tr height="17">
			<td height="17" style="height:17px;width:347px;">Immunocal Decalcifying Solution</td>
			<td style="width:147px;">Fisher Scientific</td>
			<td>NC9491030</td>
			<td style="width:317px;"></td>
		</tr>
		<tr height="34">
			<td height="34" style="height:34px;width:347px;">Opticryl Acrylic Resin Bone Cement (PMMA) (Monomer and polymer)</td>
			<td style="width:147px;">US Dental Depot</td>
			<td style="width:77px;">OPTICRYL 100410&#160;</td>
			<td style="width:317px;"></td>
		</tr>
		<tr height="23">
			<td height="23" style="height:23px;width:347px;">Instron Model 5564 Tensile Testing Machine</td>
			<td style="width:147px;">Instron</td>
			<td style="width:77px;">5564</td>
			<td style="width:317px;">Any comparable tensile testing apparatus is suitable</td>
		</tr>
	</tbody>
</table>

athymic rat model for evaluation of engineered anterior cruciate ligament grafts

Anterior cruciate ligament (ACL) rupture is a common ligamentous injury that often requires surgery because the ACL does not heal well without intervention. Current treatment strategies include ligament reconstruction with either autograft or allograft, which each have their associated limitations. Thus, there is interest in designing a tissue-engineered graft for use in ACL reconstruction. We describe the fabrication of an electrospun polymer graft for use in ACL tissue engineering. This polycaprolactone graft is biocompatible, biodegradable, porous, and is comprised of aligned fibers. Because an animal model is necessary to evaluate such a graft, this paper describes an intra-articular athymic rat model of ACL reconstruction that can be used to evaluate engineered grafts, including those seeded with xenogeneic cells. Representative histology and biomechanical testing results at 16 weeks postoperatively are presented, with grafts tested immediately post-implantation and contralateral native ACLs serving as controls. The present study provides a reproducible animal model with which to evaluate tissue engineered ACL grafts, and demonstrates the potential of a regenerative medicine approach to treatment of ACL rupture.

In our experience of 92 rat surgeries by a single surgeon, mean operative time from incision to completion of wound was 16.9 min, with a standard deviation of 4.7 min. At the time of sacrifice, rats weighed 356 &#177; 23 g. All rats tolerated the surgery well, and experienced no complications. Immediately after surgery, the rats were noted to bear weight on the operative extremity, but exhibited a slight limp. By one week post-operatively, all rats were ambulating with no appreciable limp. The animals all gained weight s...

Watch this Scientific Journal Video about Athymic Rat Model for Evaluation of Engineered Anterior Cruciate Ligament Grafts at JoVE.com

Athymic Rat Model for Evaluation of Engineered Anterior Cruciate Ligament Grafts

Animal models are important tools for the evaluation of tissue-engineered grafts. This paper presents the protocol for preparing an electrospun biodegradable polymer graft for use in anterior cruciate ligament tissue engineering, as well as a surgical protocol for implantation in a rat model.

Anterior cruciate ligament (ACL) rupture is a common ligamentous injury that often requires surgery because the ACL does not heal well without ...

athymic-rat-model-for-evaluation-engineered-anterior-cruciate

Research

JoVE Journal

Bioengineering

10.3K Views.  University of California Los Angeles. Animal models are important tools for the evaluation of tissue-engineered grafts. This paper presents the protocol for preparing an electrospun biodegradable polymer graft for use in anterior cruciate ligament tissue engineering, as well as a surgical protocol for implantation in a rat model.